GSMBE growth and characterization of InxGa1-xAs/InP strained-layer MQWs in a P-i-N configuration

InxGa1-xAs/InP (0.39 less than or equal to x less than or equal to 0.68) strained-layer quantum wells having 20 wells with thickness of 50 Angstrom in a P-i-N configuration were grown by gas source molecular beam epitaxy (GSMBE). High-resolution X-ray diffraction rocking curves show the presence of up to seven orders of sharp and intense satellite reflection, indicative of the structural perfection of the samples. Low-temperature photoluminescence and low-temperature absorption spectra were used to determine the exciton transition energies as a function of strain. Good agreement is achieved between exciton transition energies obtained experimentally at low temperature with those calculated using the deformation potential theory.

穿透型V形坑对GaN基p-i-n结构紫外探测器反向漏电的影响

研究了GaN基p-i-n(p-AlGaN/i-GaN,n-GaN)结构紫外探测器的漏电机理.实验发现,在位错密度几乎相同的情况下,基于表面有较高密度的V形坑缺陷材料制备的器件表现出较高的反向漏电.进一步的SEM测试发现,这种V形坑穿透到有源区i-GaN、甚至n-GaN层.在制备p-AlGaN电极时,许多金属会落在V形坑中,从而与i-GaN形成了肖特基接触.有些甚至直接和n-GaN形成欧姆接触.正是由于并联的肖特基接触和欧姆接触的存在导致了漏电的增加.

以弱p型为有源区的新型p-n结构GaN紫外探测器

提出了以弱p型(p~--GaN)为有源区的p-n结构GaN紫外探测器.由于弱p型层的载流子浓度较低,很容易增加耗尽区的宽度,从而可以增加器件的量子效率.通过模拟计算,研究了金属与p~--GaN层的肖特基接触势垒高度、p~--GaN层厚度等参数对器件性能的影响.研究结果表明,降低金属与p~--GaN层的接触势垒高度、适当减小p~--GaN层厚度能够实现有源层方向单一的内建电场,从而提高器件的量子效率.要制备出具有良好性能的p-n结构紫外探测器,必须减小p~--GaN层厚度,降低金属与p~--GaN层的接触势垒高度.

Ni基电极淀积前后表面处理对p-GaN欧姆接触的影响

在p-GaN上蒸发Ni/Au电极前,采用王水、HCl、缓冲HF进行前表面处理,O_2气氛下退火后,比较各电极样品的I-V特性和表面形貌.结果显示无表面处理时接触电阻最小,且溶剂处理后残留的电解质会影响电极的电流特性和稳定性.用俄歇电子能谱(AES)测试不同元素随深度分布情况,发现高温退火过程中NiO的形成有自动清洁p-GaN表面的作用,因此对于Ni基电极前表面处理不是必需的.再将样品用10%草酸溶液处理,其I-V特性显示接触电阻率明显下降;X射线光电子能谱(XPS)测试显示草酸溶液处理后电极表面Ni含量显著减少,而Au元素信号峰增强,说明表面高阻P型NiO被有效除去,对改善接触性能具有实际意义.

NiO removal of Ni/Au Ohmic contact to p-GaN after annealing

The Ni/Au contact was treated with oxalic acid after annealing in O_2 ambient, and its I-V characteristic showed the property of contact has been obviously improved. An Auger electron spectroscopy (AES) depth pro-file of the contact as-annealed showed that the top layer was highly resistive NiO, while an X-ray photo-electron spectroscopy (XPS) of oxalic acid treated samples indicated that the NiO has been removed effectively. A scanning electron microscope (SEM) was used to observe the surface morphology of the contacts, and it was found that the lacunaris surface right after annealing became quite smooth with lots of small Au exposed areas after oxalic acid treatment. When the test probe or the subsequently deposited Ti/Au was directly in contact with these small Au areas, they worked as low resistive current paths and thus decrease the specific contact resistance.

p型掺杂1.3 μm InAs/GaAs量子点激光器的最大模式增益特性的研究

对p型掺杂1.3 μm InAs/GaAs量子点激光器的最大模式增益进行了实验和理论分析.实验上,测量了不同腔长激光器阈值电流密度与总损耗的对应关系,拟合出的最大模式增益为17.5 cm~(-1),与相同结构非掺杂量子点激光器的最大模式增益一致.同时理论分析表明,p型掺杂对InAs/GaAs量子点激光器的最大模式增益并无影响,并且最大模式增益的计算结果与实验值相符.具有较小高度或高宽比的量子点能达到更高的最大模式增益,而较高的最大模式增益对p型掺杂1.3 μm InAs/GaAs自组织量子点激光器在光通信系统中的应用具有重要意义.

两步合金法制作p-GaN高反电极

利用两步合金法获得了能与p-GaN形成良好欧姆接触的高反射电极。电极的构成采用透明电极+高反射金属方案,厚的Ag层或Al层覆盖在合金后的Ni/Au上以提高电极的反射率,以Pt和Au作为覆盖层,可有效地防止Ag的氧化和团聚,短时间的热处理有助于Ag基电极反射率的提高。可靠性测试表明Ag基电极的稳定性较好,对于Al基电极,热处理后反射镜上出现暗斑,导致其反射率的下降。最终获得了波长在460nm处反射率为74%的Ag基高反射电极。

p-GaN层厚度对GaN基p-i-n结构紫外探测器性能的影响

研究了p-GaN层厚度对GaN基pin结构紫外探测器性能的影响.模拟计算表明:较厚的p-GaN层会减小器件的量子效率,然而同时也会减小器件的暗电流,较薄的p-GaN层会增加器件的量子效率,但是同时也增加了器件的暗电流.进一步的分析表明,金属和p-GaN之间的结电场是出现这种现象的根本原因.在实际的器件设计中,应该根据实际需要选择p型层的厚度.

n-GaAs和p-GaN晶片的直接键合

采用直接键合的方法成功实现了n-GaAs和p-GaN晶片的高质量键合.扫描电子显微镜观测结果表明,键合界面没有空洞.键合前后光致发光谱测试表明,键合工艺对材料质量影响不大.室温下界面的电流-电压特性表明,键合得到的n-GaAs/p-GaN异质结为肖特基二极管并且理想因子为1.08.n-GaAs和p-GaN材料直接键合的成功对于集成GaAs和GaN材料制备光电集成器件有重要意义.

表面处理对p-GaN欧姆接触的影响

分别用稀盐酸、王水以及(NH_4)_2S溶液处理p-GaN表面,通过测试样品表面Ols的X射线光电子能谱(XPS),比较了这些溶液去除p-GaN表面氧化层的能力;在经不同溶液处理后的样品表面,以相同的条件制作Ni/Au电极,并测试其与p-GaN的比接触电阻,结果表明经稀盐酸处理后的样品表面,由于其氧含量较高,不能与Ni/Au形成良好的欧姆接触,而经王水和(NH_4)_2S溶液处理后的p-GaN表面,能与Ni/Au形成良好的欧姆接触;最后,通过比较样品表面的Ga/N原子浓度比,探讨了王水处理p-GaN表面能够形成良好欧姆接触的原因.

PECVD沉积SiO_2和SiN_x对p-GaN的影响

在等离子增强化学气相沉积法（PECVD）沉积SiO_2和SiNx掩蔽层过程中，分解等离子体中浓度较高的H原子使Mg~-受主钝化，同时在p-GaN材料表面发生反应形成浅施主特性的N_v~+，空位。高能量离子轰击造成的材料深能级缺陷增多以及沉积形成致密的SiO_2和SiN_x材料，阻碍了H原子向外扩散，使H原子在Ni／Au电极与p-GaN的界面处聚集，造成p-GaN近表面附近区域Mg-H络合物密度的提高，空穴浓度急剧下降，导致Ni／Au透明电极I-V特性严重恶化。选择较低的射频功率（15W，13．56MHz）沉积模式，经过适当的退火，可以减小沉积SiO_2过程对p-GaN的影响。