CONSTRUCTION AND APPLICATIONS OF A DUAL MASS-SELECTED LOW-ENERGY ION-BEAM SYSTEM

A direct ion beam deposition system designed for heteroepitaxy at a low substrate temperature and for the growth of metastable compounds has been constructed and tested. The system consists of two mass-resolved low-energy ion beams which merge at the target with an incident energy range 50-25 000 eV. Each ion beam uses a Freeman ion source for ion production and a magnetic sector for mass filtering. While a magnetic quadrupole lens is used in one beam for ion optics, an electrostatic quadrupole lens focuses the other beam. Both focusing approaches provide a current density more than 100-mu-A/cm2, although the magnetic quadrupole gives a better performance for ion energies below 200 eV. The typical current of each beam reaches more than 0.3 mA at 100 eV, with a ribbon beam of about 0.3-0.5 x 2 cm2. The target is housed in an ultrahigh vacuum chamber with a base pressure of 1 x 10(-7) Pa and a typical pressure of 5 x 10(-6) Pa when a noncondensable beam like argon is brought into the chamber. During deposition, the target can be heated to 800-degrees-C and scanned mechanically with an electronic scanning control unit. The dual beam system has been used to grow GaN using a Ga+ and a N+ beam, and to study the oxygen and hydrogen ion beam bombardment effects during carbon ion beam deposition. The results showed that the simultaneous arrival of two beams at the target is particularly useful in compound formation and in elucidation of growth mechanisms.

Diffusion of ion implanted as in Si1-xGex epilayers

Diffusion of implanted As ion in relaxed Si1-xGex was studied as a function of Ge content over a wide range of Ge fractions (0-43%) and annealing temperature, and was compared to diffusion in Si. Experimental results showed that the As diffusion is enhanced with increasing annealing temperature for certain Ge content and strongly dependent on the higher Ge content and the faster As diffusion.

Photoluminescence and activation on SI-GaAs by Si+ implantation and following rapid thermal annealing

Photoluminescence (PL) and electrical characteristics of SI-GaAs, Si+-implanted and following rapid thermal annealing (RTA), were investigated, The PL spectra of Si-GA-C-As, Ga-i-Si-As, and V-As-Si-As were obtained. This paper concentrates on the PL peak at 1.36 eV which was proven as an emission of the Si-Ga-V-Ga combination by Si+ + P+ dual implantation. The results indicate that the peak at 1.36 eV appears when the ratio of As:Ga increased during the processing. Also high activation was obtained for the sample under the same conditions. More discussion on the mechanism of Si+ implanted SI-GaAs has been made based on the Morrow model [J. Appl. Phys, 64 (1988) 1889].

High quality CeO2 film grown on Si(111) substrate by using low energy dual ion beam deposition technology

By using the mass-analyzed low energy dual ion beam deposition technique, a high quality epitaxial, insulating cerium dioxide thin film with a thickness of about 2000 Angstrom, has been grown on a silicon (111) substrate. The component species, cerium and oxygen, are homogeneous in depth, and have the correct stoichiometry for CeO2. X-ray double-crystal diffraction shows that the full width at half maximum of the (222) and (111) peaks of the film are less than 23 and 32 s, respectively, confirming that the film is a perfect single crystal. (C) 1995 American Institute of Physics.

Sidegating effect on Schottky contact in ion-implanted GaAs

The sidegating effect on the Schottky barrier in ion-implanted GaAs was investigated with capacitance-voltage profiling at various negative substrate voltages. It was demonstrated that the negative substrate voltage modulates the Schottky depletion region width as well as the space charge region at the substrate-active channel interface. (C) 1995 American Institute of Physics.

HIGH-EFFICIENCY TOP SURFACE-EMITTING LASERS FABRICATED BY 4 IMPLANTATION USING TUNGSTEN WIRE AS MASK

We report the results of a high efficiency room temperature continuous wave (cw) vertical-cavity surface-emitting laser. The structure is obtained by four deep H+ implantation using tungsten wires as the mask. The fabrication process is the simplest ever reported in vertical-cavity surface-emitting laser fabrication. The largest differential quantum efficiency of 65% and maximum cw light output power over 4 mW have been achieved for the 15X15 mu m(2) device. (C) 1995 American Institute of Physics.

Sensitivity of Total-Dose Radiation Hardness of SIMOX Buried Oxides to Doses of Nitrogen Implantation into Buried Oxides

In order to improve the total-dose radiation hardness of the buried oxides(BOX) in the structure of separa tion-by-implanted-oxygen(SIMOX) silicon-on-insulator(SOI), nitrogen ions are implanted into the buried oxides with two different doses,2 × 1015 and 3 × 1015 cm-2 , respectively. The experimental results show that the radiation hardness of the buried oxides is very sensitive to the doses of nitrogen implantation for a lower dose of irradiation with a Co-60 source. Despite the small difference between the doses of nitrogen implantation, the nitrogen-implanted 2 × 1015 cm-2 BOX has a much higher hardness than the control sample (i. e. the buried oxide without receiving nitrogen implantation) for a total-dose irradiation of 5 × 104rad(Si), whereas the nitrogen-implanted 3 × 1015 cm-2 BOX has a lower hardness than the control sample. However,this sensitivity of radiation hardness to the doses of nitrogen implantation reduces with the increasing total-dose of irradiation (from 5 × 104 to 5 × 105 rad (Si)). The radiation hardness of BOX is characterized by MOS high-frequency (HF) capacitance-voltage (C-V) technique after the top silicon layers are removed. In addition, the abnormal HF C-V curve of the metal-silicon-BOX-silicon(MSOS) structure is observed and explained.