Temperature and power-density-dependent inter-shell energy states in InAs/GaAs quantum dots

We have investigated the evolution of exciton state filling in InAs/GaAs quantum dot (QD) structures as a function of the excitation power density by using rnicro-photoluminescence spectroscopy at different temperatures. In addition to the emission bands of exciton recombination corresponding to the atom-like S, P and D, etc. shells of QDs, it was observed that some extra states V between the S and P shells, and D' between the P and D shells appear in the spectra with increasing number of excitons occupying the QDs at a certain temperature. The emergence of these inter-shell excitonic levels is power density and temperature dependent, which is an experimental demonstration of strong exciton-exciton exchange interaction, state hybridization, and coupling of a multi-exciton system in QDs. (c) 2006 Elsevier B.V. All rights reserved.

Time-resolved photoluminescence spectra of self-assembled InAs/GaAs quantum dots

Two types of InAs self-assembled Quantum dots (QDs) were prepared by Molecular beam epitaxy. Atomic force microscopy (AFM) measurements showed that, compared to QDs grown on GaAs substrate, QDs grown on InGaAs layer has a significantly enhanced density. The short spacing (several nanometer) among QDs stimulates strong coupling and leads to a large red-shift of the 1.3 mu m photoluminescence (PL) peak. We study systematically the dependence of PL lifetime on the QDs size, density and temperature (1). We found that, below 50 K, the PL lifetime is insensitive to temperature, which is interpreted from the localization effects. As T increases, the PL lifetime increases, which can be explained from the competition between the carrier redistribution and thermal emission at higher temperature. The increase of carriers in QDs migrated from barriers and wetting layer (WL), and the redistribution of carriers among QDs enhance the PL lifetime as T increases. The thermal emission and non-radiative recombination have effects to reduce the PL lifetime at higher T. As a result, the radiative recombination lifetime is determined by the wave function overlapping of electrons and holes in QDs, and QDs with different densities have different PL lifetime dependence on the QDs size. (c) 2005 Elsevier B.V. All rights reserved.

Temperature-dependent modulation characteristics for 1.3 mu m InAs/GaAs quantum dot lasers

Temperature-dependent modulation characteristics of 1.3 mu m InAs/GaAs quantum dot (QD) lasers under small signals have been carefully studied at various bias currents. Based on experimental observations, it is found that the modulation bandwidth significantly increases when excited state (ES) lasing emerges at high temperature. This is attributed to additional photons emitted by ES lasing which contribute to the modulation response. A rate equation model including two discrete electron energy levels and the level of wetting layer has been used to investigate the temperature-dependent dynamic behavior of the QD lasers. Numerical investigations confirm that the significant jump for the small signal modulation response is indeed caused by ES photons. Furthermore, we identify how the electron occupation probabilities of the two discrete energy levels can influence the photon density of different states and finally the modulation rate. Both experiments and numerical analysis show that the modulation bandwidth of QD lasers at high temperature can be increased by injecting more carriers into the ES that has larger electron state degeneracy and faster carrier's relaxation time than the ground state.

A 10 Gb/s Directly-Modulated 1.3 mu m InAs/GaAs Quantum-Dot Laser

We demonstrate 10 Gb/s directly-modulated 1.3 mu m InAs quantum-dot (QD) lasers grown on GaAs substrates by molecular beam epitaxy. The active region of the QD lasers consists of five-stacked InAs QD layers. Ridge-waveguide lasers with a ridge width of 4 mu m and a cavity length of 600 mu m are fabricated with standard lithography and wet etching techniques. It is found that the lasers emit at 1293 nm with a very low threshold current of 5 mA at room temperature. Furthermore, clear eye-opening patterns under 10 Gb/s modulation rate at temperatures of up to 50 degrees C are achieved by the QD lasers. The results presented here have important implications for realizing low-cost, low-power-consumption, and high-speed light sources for next-generation communication systems.

Optimization of VI/II pressure ratio in ZnTe growth on GaAs(001) by molecular beam epitaxy

ZnTe epilayers were grown on GaAs(0 0 1) substrates by molecular beam epitaxy (MBE) at different VI/II beam equivalent pressure (BEP) ratios (R-VI/II) in a wide range of 0.96-11 with constant Zn flux. Based on in situ reflection high-energy electron diffraction (RHEED) observation, two-dimensional (2D) growth mode can be formed by increasing the R-VI/II to 2.8. The Te/Zn pressure ratios lower than 4.0 correspond to Zn-rich growth state, while the ratios over 6.4 correspond to Te-rich one. The Zn sticking coefficient at various VI/II ratios are derived by the growth rate measurement. The ZnTe epilayer grown at a R-VI/II of 6.4 displays the narrowest full-width at half-maximum (FWHM) of double-crystal X-ray rocking curve (DCXRC) for (0 0 4) reflection. Atomic force microscopy (AFM) characterization shows that the grain size enlarges drastically with the R-VI/II. The surface root-mean-square (RMS) roughness decreases firstly, attains a minimum of 1.14 nm at a R-VI/II of 4.0 and then increases at higher ratios. It is suggested that the most suitable R-VI/II be controlled between 4.0 and 6.4 in order to grow high-quality ZnTe epitaxial thin films.

Temperature dependent photoluminescence of an In(Ga)As/GaAs quantum dot system with different areal density

We have systematically studied the temperature dependent photoluminescence of a self-assembled In(Ga)As/GaAs quantum dot (QD) system with different areal densities from similar to 10(9) to similar to 10(11) cm(-2). Different carrier channels are revealed experimentally and confirmed theoretically via a modified carrier equation model considering a new carrier transfer channel, i.e. continuum states ( CS). The wetting layer is demonstrated to be the carrier quenching channel for the low-density QDs but the carrier transfer channel for the high-density QDs. In particular, for the InGaAs/GaAs QDs with a medium density of similar to 10(10) cm(-2), the CS is verified to be an additional carrier transfer channel in the low temperature regime of 10-60 K, which is studied in detail via our models. The possible carrier channels that act on different temperature regimes are further discussed, and it is demonstrated that density is not a crucial factor in determining the carrier lateral coupling strength.

Abnormal temperature dependent photoluminescence of self-assembled InAs/GaAs surface quantum dots with high areal density

We have investigated temperature dependent photoluminescence of both buried and surface self-assembled InAs/GaAs quantum dots with an areal density up to similar to 10(11)/cm(2). Different from the buried quantum dots, the peak energy of surface quantum dots shows a blueshift relative to the bulk material variation from 15 to 130K. Besides the line width and the integrated intensity both first decrease and then increase in this temperature interval. The observed phenomena can be explained by carrier trapping effects by some shallow localized centers near the surface quantum dots.

Molecular beam epitaxy of GaSb on GaAs substrates with AlSb/GaSb compound buffer layers

GaSb films with AlSb/GaSb compound buffer layers were grown by molecular beam epitaxy on GaAs (001) substrates. The crystal quality and optical properties were studied by high resolution transition electron microscopy and low temperature photoluminescence spectra (PL), respectively. It was found that the AlSb/GaSb compound buffer layers can restrict the dislocations into GaSb epilayers. The intensity of PL spectra of GaSb layer becomes large with the increasing the periods of AlSb/GaSb superlattices, indicating that the optical quality of GaSb films is improved.

EFFECTIVE-MASS THEORY FOR GAAS/GA1-XALXAS QUANTUM WIRES AND CORRUGATED SUPERLATTICES GROWN ON (311)-ORIENTED SUBSTRATES

The electronic structures of GaAs/Ga1-xAlxAs quantum wires (corrugated superlattices) grown on (311)-oriented substrates are studied in the framework of the effective-mass envelope-function method. The electron and hole subband structure and optical transition matrix elements are calculated. When x=1, the results are compared with experiments, and it is found that the direct transition becomes an indirect transition as the widths of well and barrier become smaller.

HIGH-RESOLUTION PHOTOLUMINESCENCE STUDIES OF (211) CDTE GROWN ON (211)B GAAS SUBSTRATE

Sharp and rich photoluminescence lines accociated with free exciton (FE), excitons bound to neutral acceptors (A0X) and donors (D0X) in molecular beam epitaxially (MBE) grown (211) CdTe/(211)B GaAs have been reported for the first time. The results show that the (211) CdTe/(211)B GaAs grown under optimized conditions could have as high a crystal perfection as those grown on lattice-matched substrates.

RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

HIGH-QUALITY INGAP AND INGAP/INALP MULTIPLE-QUANTUM-WELL GROWN BY GAS-SOURCE MOLECULAR-BEAM EPITAXY

Using gas-source molecular beam epitaxy, we have obtained high-quality GaInP and (AlGa)InP epilayers lattice-matched to (100) GaAs substrates. All grown layers exhibited mirror-like surfaces. For a 1.7 mum thick Ga0.5In0.5P film, the Hall electron mobility was 3400 and 30,000 CM2/V. s at 300 and 77 K, respectively. The luminescence wavelength of (AlxGa1-x)InP samples ranged from 680 nm (for GaInP) to 590 nm (for AlInP) at room temperature, and from 644 to 513 nm at 77 K. The multiple quantum well (MQW) structure with well width of 40 angstrom showed strong luminescence intensity with wavelength of 647 nm (300 K) or 622 nm (80 K). The satellite peaks can be detected in double-crystal X-ray (DCXR) diffraction measurements of the MQW samples, which indicates the perfect structural periodicity.

BAND-OFFSET OF GAAS-GAINP HETEROJUNCTIONS

N+ GaAs-n GaInP lattice-matched heterostructures, grown by metalorganic vapour phase epitaxy, have been studied by capacitance-voltage, current-voltage and current-temperature techniques. This allowed the determination of the conduction band offset in three different and independent ways. The value obtained (0.24-0.25 eV) has been verified by photoluminescence and photoluminescence excitation on a 90 angstrom thick GaAs well in GaInP grown under the same conditions.

OPTICAL CHARACTERISTICS OF GAAS/ALGAAS RIDGE-QUANTUM-WELL-WIRES GROWN BY MBE ON NONPLANAR SUBSTRATES

With conventional photolithography and wet chemical etching, we have realized GaAs/AlGaAs buried ridge-quantum-well-wires (RQWWs) with vertically stacked wires in lateral arrays promising for device application, which were grown in situ by a single-step molecular beam epitaxy growth and formed at the ridge tops of mesas on nonplanar substrates. Confocal photoluminescence (CPL) and polarization-dependent photoreflectance (PR) are applied to study optical characteristics of RQWWs. Lateral bandgap modulation due to lateral variation of QW layer thickness is demonstrated not only by CPL but also by PR. As one evidence for RQWWs, a large blue shift is observed at the energy level positions for electronic transitions corresponding to quantum wells (QWs) at the ridge tops of mesas compared with those corresponding to QWs on nonpatterned areas of the same sample. The blue shift is in contradiction with the fact that the GaAs QW layers at the tops of the mesas are thicker than those on nonpatterned areas. The other evidence for RQWWs, optical anisotropy is provided by the polarization-dependent PR, which results from lateral quantum size effect existing at the tops of the mesas.