Etching Behavior of GaN/GaAs(001) Epilayers Grown by MOVPE

Wet etching characteristics of cubic GAN (c-GaN) thin films grown on GaAs(001) by metalorganic vapor phase epitaxy (MOVPE) are investigated. The samples are etched in HCl, H_3PO_4, KOH aqueous solutions, and molten KOH at temperatures in the range of 90～300 ℃. It is found that different solution produces different etch figure on the surfaces of a sample. KOH-based solutions produce rectangular pits rather than square pits. The etch pits elongate in [1(1-bar)0] direction, indicating asymmetric etching behavior in the two orthogonal <110> directions. An explanation based on relative reactivity of the various crystallographic planes is employed to interpret qualitatively the asymmetric etching behavior. In addition, it is found that KOH aqueous solution would be more suitable than molten KOH and the two acids for the evaluation of stacking faults in c-GaN epilayers.

MOCVD growth of high quality crack-free GaN on Si(III) substrates

High quality crack free GaN epilayers were grown on Si(111) substrates. Low temperature AlN interlayer grown under low V/III ratio was used to effectively eliminate the formation of micro-cracks. It is found that tensile stress in the GaN epilayer decreases as the N/Al ratio decreases used for AlN interlayer growth. The high optical and structural qualities of the GaN/Si samples were characterized by RBS, PL and XRD measurements. The RT-PL FWHM of the band edge emission is only 39.5meV The XRD FWHM of the GaN/Si sample is 8.2arcmin, which is among the best values ever reported.

MOCVD growth of cubic GaN: Materials and devices

Many impressive progresses have been made recently on the growth of cubic-phase GaN by MBE and MOCVD. In this paper, some of our recent progress will be reviewed, including the growth of high quality cubic InGaN films, InGaN/GaN heterostructure blue and green LEDs. Cubic-phase GaN films were grown on GaAs (100) substrates by MOCVD. Growth conditions were optimized to obtain pure cubic phase GaN films up to a thickness of 4 mum. An anomalous compressive strain was found in the as-grown GaN films in spite of a smaller lattice constant for GaN compared with that of GaAs substrates. The photoluminescence FWHM of high quality InGaN epilayers was less than 100 meV The InGaN/GaN heterostructure blue LED has intense electroluminescence with a FWHM of 20 nm.

Single ridge waveguide electroabsorption modulated DFB laser for 2.5Gb/s transmission

In this paper we proposed a single ridge waveguide electroabsorption modulated distributed feedback laser (EML) for long-haul high-speed optical fiber communication system. This EML was successfully fabricated by two step metal organic vapor phase epitaxy (MOVPE) including selective area growth (SAG) and helium partially implantation. No obvious changes of the threshold current (< 0.2 mA), extinction ratio (< 0.1 dB), output power (< 0.2 dBm) and isolation resistance were achieved in the preliminary aging test. With 2.5 Gb/s NRZ modulation, no power penalty was observed after the optical signal was transmitted through 280 Km normal single mode fiber.

Indium-doping enhanced two-dimensional-electron-gas performance in AlGaN/GaN heterostructures

Indium (In)-doping was applied in GaN layers during growth of AlGaN/GaN heterostructure with unintentionally doped or modulation Si-doped AlGaN layers. It was found that In-doping was effective in improving electron sheet density of two-dimensional-electron-gas (2DEG) in the heterostructures. Furthermore, In-doping also improved mobility in heterostructures with Si modulation-doped in AlGaN layers. The possible reasons were discussed. X-ray diffraction (XRD) and wet chemical etching revealed that crystalline quality of GaN was improved by In-doping. It was proposed that In-doping modified growth kinetics of GaN.

The SPER and characteristics of Si1-yCy alloys

\Si1-yCy alloys with carbon composition of 0.5 at.% were successfully grown on n-Si(100) substrate by solid phase epitaxy recraystallization. The result was presented in this paper. With the help of the SiO2 capping layer, rather uniform carbon profile in amorphous Si layer was obtained by dual-energy implantation. Since ion-flow was small and implantation time was long enough, the emergency of beta-SiC was avoided and the dynamic annealing effect was depressed. The pre-amorphization of the Si substrate increased the fraction of the substitutions carbon and the two-step annealing reduced point defects. As a result, Si1-yCy alloys with high quality was recrystallized on Si substrate.

The effect of low temperature GaAs nucleation on the growth of GaN on Silicon (001) during MOVPE process

High quality cubic GaN was grown on Silicon (001) by metalorganic vapor phase epitaxy (MOVPE) using a GaAs nucleation layer grown at low temperature. The influence of various nucleation conditions on the GaN epilayers' quality was investigated. We found that the GaAs nucleation layer grown by atomic layer epitaxy (ALE) could improve the quality of GaN films by depressing the formation of mixed phase. Photoluminescence (PL) and X-ray diffraction were used to characterize the properties of GaN epilayers. High quality GaN epilayers with PL full width at half maximum (FWHM) of 130meV at room temperature and X-ray FWHM of 70 arc-min were obtained by using 10-20nm GaAs nucleation layer grown by ALE.

Visible vertical cavity surface emitting laser

We have designed and fabricated the visible vertical-cavity surface-emitting lasers (VCSEL's) by using metalorganic vapor phase epitaxy (MOVPE). We use the 8 lambda optical cavities with 3 quantum wells in AlGaInP/AlGaAs red VCSEL's to reduce the drift leakage current and enhance the model gain in AlGaInP active region. The structure has a p-type stack with 36 DBR pairs on the top and an n-type with 55-1/2 pairs on the bottom. Using micro-area reflectance spectrum, we try to get a better concordance between the center wavelength of DBR and the emitting wavelength of the active region. We used a component graded layer of 0.05 lambda thick (x = 0.5 similar to 0.9) at the p-type DBR AlGaAs/AlAs interface to reduce the resistance of p-type DBR. We use selective oxidation to define the current injection path. Because the oxidation rate of a thick layer is faster than a thinner one, we grown a thick AlAs layer close to the active region. In this way, we got a smaller active region for efficient confinement of injected carriers (the aperture area is 3 x 3 mu m) to reduce the threshold and, at the same time, a bigger conductive area in the DBR layers to reduce the resistance. We employ Zn doping on the p-side of the junction to improve hole injection and control the Zn dopant diffusion to get proper p-i-n junction. At room temperature, pulse operation of the laser has been achieved with the low threshold current of 0.8mA; the wavelength is about 670nm.

Self-assembled InAs quantum wires on InP(001)

Self-assembled InAs quantum wires (QWRs) embedded in In0.52Al0.48As In0.53Ga0.47As, and (In0.52Al0.48As)(2)/(In(0.53)Ga(0.47)AS)(2)-short-period-lattice matrixes on InP (001) were fabricated with molecular beam epitaxy (MBE). These QWR lines are along [110], x4 direction in the 2x4 reconstructed (001) surface as revealed with high energy electron diffraction (RHEED). Alignment of quantum wires in a multilayer structure depends on the composition of spacer layers.

In situ annealing treatment and In-doping of GaN epilayers grown by MOVPE

The effects of in situ annealing treatment in the initial growth stage and In-doping during growth of the GaN on the material properties were investigated. GaN was grown by LP-MOVPE. In situ annealing reduced the full-width at half-maximum (FWHM) of X-ray rocking curves and reduced etch pit density of GaN films. It improved the optical properties of the epilayer. Undoped and In-doped GaN films of initial growth stage were investigated. It was found that morphology and optical properties were improved in In-doped samples. (C) 2000 Elsevier Science B.V. All rights reserved.

Optical properties of self-assembled ternary In(GA/Al)As quantum dots on (100) and (N 1 1)B InP substrates

In this paper, we investigated the self-assembled quantum dots formed on (100) and (N11)B (N = 2, 3, 4, 5) InP substrates by molecular beam epitaxy (MBE). Two kinds of ternary QDs (In0.9Ga0.1As and In0.9Al0.1As QDs) are grown on the above substrates; Transmission electron microscopy (TEM) and photoluminescence (PL) results confirm QDs formation for all samples. The PL spectra reveal obvious differences in integral luminescence, peak position, full-width at half-maximum and peak shape between different oriented surfaces. Highest PL integral intensity is observed from QDs on (411)B surfaces, which shows a potential for improving the optical properties of QDs by using high-index surface. (C) 2000 Elsevier Science B.V. All rights reserved.

Influence of precipitates on GaN epilayer quality

GaN epilayers grown on pre-nitridated (0001) sapphire substrates by metallorganic vapor phase epitaxy were investigated by wavelength dispersive X-ray spectroscopy and energy dispersive S-ray spectroscopy. Precipitates were observed to mainly consist of O impurity whose strengths were weaker than surrounding matrix. The precipitates were larger in size and distributed more sparsely and inhomogeneously in < 11-20 > directions of the epilayers grown on substrates pre-nitridated for longer periods. The larger precipitates often joined to cracks in the TEM specimens. The crack formation seems to be attributed to the compressive stress concentration at edge angles of the larger precipitates. Yellow luminescence of the epilayers was imaged by cathodoluminescence. The distribution similarity between the cathodoluminescence and the precipitates suggested that the precipitates were responsible for the yellow luminescence band. (C) 2000 Elsevier Science S.A, All rights reserved.

MOVPE growth of GaN and LED on (111) MgAl2O4

The growth of wurtzite GaN by low-pressure metalorganic vapor-phase epitaxy on (1 1 1) magnesium aluminate (MgAl2O4) substrates have been studied. The morphological, crystalline, electrical and optical properties are investigated. A p-n junction GaN LED was fabricated on the MgAl2O4 substrate. (C) 1998 Elsevier Science B.V. All rights reserved.

Characterization of GaSb substrate wafers for MOCVD III-V antimonides

The qualities of GaSb substrates commonly used for the preparation of III-V antimonide epilayers were studied before and after growing GaInAsSb multi-layers by MOCVD using PL, FTIR and DCXD together with the electrical properties and EPD value. The correlation between the substrate qualities and epilayer properties was briefly discussed. The good property epilayers of GaInAsSb and, then, the high preformance of 2.3 um photodetectors were achieved only using the good quality GaSb wafers as the substrates.

Microphotoluminescence investigation of InAs quantum dot active region in 1.3 mu m vertical cavity surface emitting laser structure

Microphotoluminescence (mu-PL) investigation has been performed at room temperature on InAs quantum dot (QD) vertical cavity surface emitting laser (VCSEL) structure in order to characterize the QD epitaxial structure which was designed for 1.3 mu m wave band emission. Actual and precise QD emission spectra including distinct ground state (GS) and excited state (ES) transition peaks are obtained by an edge-excitation and edge-emission (EEEE) mu-PL configuration. Conventional photoluminescence methods for QD-VCSELs structure analysis are compared and discussed, which indicate the EEEE mu-PL is a useful tool to determine the optical features of the QD active region in an as-grown VCSEL structure. Some experimental results have been compared with simulation results obtained with the aid of the plane-wave admittance method. After adjustment of epitaxial growth according to EEEE mu-PL measurement results, QD-VCSEL structure wafer with QD GS transition wavelength of 1300 nm and lasing wavelength of 1301 nm was obtained.