Cubic-phase GaN light-emitting diodes

The feasibility of growing device-quality cubic GaN/GaAs(001) films by metal organic chemical vapor deposition has been demonstrated. The optical quality of the GaN films was characterized by room-temperature photoluminescence measurements, which shows a full width at half maximum of 46 meV. The structural quality of the films was investigated by transmission electron microscopy. There are submicron-size grains free from threading dislocations and stacking faults. More importantly, a cubic-phase GaN blue light-emitting diode has been fabricated. The device process, which is very simple and compatible with current GaAs technology, indicates a promising future for the blue light-emitting diode. (C) 1999 American Institute of Physics. [S0003-6951(99)01416-3].

Improvement of GaN-based light emitting diodes performance grown on sapphire substrates patterned by wet etching - art. no. 684107

An effective approach to enhance the light output power of InGaN/GaN light emitting diodes (LED) was proposed using pyramidal patterned sapphire substrates (PSS). The sapphire substrates were patterned by a selective chemical wet etching technique. GaN-based LEDs were fabricated on patterned sapphire substrates through metal organic chemical deposition (MOCVD). The LEDs fabricated on patterned sapphire substrates exhibit excellent device performance compared to the conventional LEDs fabricated on planar sapphire substrates in the case of the same growth and device fabricating conditions. The light output power of the LEDs fabricated on patterned sapphire substrates was about 37% higher than that of LEDs on planar sapphire substrates at an injection current of 20 mA. The significant enhancement is attributable to the improvement of the quality of GaN-based epilayers and improvement of the light extraction efficiency by patterned sapphire substrates.

Novel photonic crystal structure GaN-based light-emitting diodes - art. no. 68410J

For enhancing the output efficiency of GaN light-emitting diode(LED), we calculated the band structure of photonic crystal(PhC), and designed and fabricated several novel GaN LEDs with photonic crystal on Indium-Tin-Oxide(ITO), which as p-type transparent contact of GaN LED. In this fabricating process, we developed conventional techniques in order that these methods can be easily applied to industrial volume-production. And we have done some preliminary experiments and obtained some results.

Plasma induced damage in GaN-based light emitting diodes - art. no. 68410X

The effects of plasma induced damage in different conditions of ICP and PECVD processes on LEDs were presented. For ICP mesa etch, in an effort to confirm the effects of dry etch damage on the optical properties of p-type GaN, a photoluminescence (PL) measurement was investigated with different rf chuck power. It was founded the PL intensity of the peak decreased with increasing DC bias and the intensity of sample etched at a higher DC bias of -400V is less by two orders of magnitude than that of the as-grown sample. Meanwhile, In the IN curve for the etched samples with different DC biases, the reverse leakage current of higher DC bias sample was obviously degraded than the lower one. In addition, plasma induced damage was also inevitable during the deposition of etch masks and surface passivation films by PECVD. The PL intensity of samples deposited with different powers sharply decreased when the power was excessive. The PL spectra of samples deposited under the fixed condition with the different processing time were measured, indicating the intensity of sample deposited with a lower power did not obviously vary after a long time deposition. A two-layer film was made in order to improve the compactness of sparse dielectric film deposited with a lower power.

Monolithic Integration of Light Emitting Diodes, Photodetector and Receiver Circuit in Standard CMOS Technology

A monolithic silicon CMOS optoelectronic integrated circuit (OEIC) is designed and fabricated with standard 0.35 mu m CMOS technology. This OEIC circuit consists of light emitting diodes (LED), silicon dioxide waveguide, photodiodes and receiver circuit. The silicon LED operates in reverse breakdown mode and can be turned on at 8.5V 10mA. The silicon dioxide waveguide is composed of multiple layers of silicon dioxide between different metals layers. A two PN-junctions photodetector composed of n-well/p-substrate junction and p(+) active implantation/n-well junction maximizes the depletion region width. The readout circuitry in pixels is exploited to handle as small as 0.1nA photocurrent. Simulation and testing results show that the optical emissions powers are about two orders higher than the low frequency detectivity of silicon CMOS photodetcctor and receiver circuit.

Vertical PIN ultraviolet photodetectors based on 4H-SiC homoepilayers

Vertical PIN ultraviolet photodetectors based on 4H-SiC homoepilayers are presented. The growth of the 4H-SiC homoepilayers was carried out in a LPCVD system. The size of the active area of the photodetector was 300 x 300 mu m(2). The dark and illuminated I-V characteristics were measured at reverse biases from 0 V to 30 V at room temperature. The illuminated current was at least two orders of magnitude higher than the dark current at a bias of below 12 V. The photoresponse was measured from 200 nm to 400 nm at different reverse biases and the peak values of the photo response were located at 3 10 nm. The calculated spectral detectivity D* was shown to be higher than 10(13) cmHz(1/2)/W from 260 to 360 nm with a peak value of 5.9 x 10(13) cmHz(1/2) /W at 310 nm. The peak value of the photoresponse was hundreds of times higher than the response at 400 nm, which showed the device had good visible blind performance. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Highly efficient and stable organic light-emitting diodes employing MoO3-doped perylene-3, 4, 9, 10-tetracarboxylic dianhydride as hole injection layer

We report highly efficient and stable organic light-emitting diodes (OLEDs) with MoO3-doped perylene-3, 4, 9, 10-tetracarboxylic dianhydride (PTCDA) as hole injection layer (HIL). A green OLED with structure of ITO/20 wt% MoO3: PTCDA/NPB/Alq(3)/LiF/Al shows a long lifetime of 1012 h at the initial luminance of 2000 cd/m(2), which is 1.3 times more stable than that of the device with MoO3 as HIL. The current efficiency of 4.7 cd/A and power efficiency of 3.7 lm/W at about 100 cd/m(2) have been obtained. The charge transfer complex between PTCDA and MoO3 plays a decisive role in improving the performance of OLEDs.

Improved electroluminescence from n-ZnO/AlN/p-GaN heterojunction light-emitting diodes

n-ZnO/p-GaN heterojunction light-emitting diodes with and without a sandwiched AlN layer were fabricated. The electroluminescence (EL) spectrum acquired from the n-ZnO/p-GaN displays broad emission at 650 nm originating from ZnO and weak emission at 440 nm from GaN, whereas the n-ZnO/AlN/p-GaN exhibits strong violet emission at 405 nm from ZnO without GaN emission. The EL intensity is greatly enhanced by inserting a thin AlN intermediate layer and it can be attributed to the suppressed formation of the GaOx interfacial layer and confinement effect rendered by the AlN potential barrier layer.

Tandem organic light-emitting diodes with an effective charge-generation connection structure

The tandem organic light-emitting diodes (OLEDs) with an effective charge-generation connection structure of Mg-doped tris(8-hydroxyquinoline) aluminum (Alq(3))/Molybdenum oxide (MoO3)-doped 3, 4, 9, 10-perylenetetracarboxylic dianhydride (PTCDA) were presented. At a current density of 50 mA/cm(2), the current efficiency of the tandem OLED with two standard NPB/Alq(3) emitting units is 4.2 cd/A, which is 1.7 times greater than that of the single EL device. The tandem OLED with the similar connection structure of Mg-doped PTCDA/MoO3-doped PTCDA was also fabricated and the influences of the different connection units on the current efficiency of the tandem OLED were discussed as well.

The fabrication of GaN-based nanopillar light-emitting diodes

InGaN/GaN multiple quantum well-based light-emitting diode (LED) nanopillar arrays were fabricated using Ni self-assembled nanodots as etching mask. The Ni nanodots were fabricated with a density of 6 x 10(8)-1.5 x 10(9) cm(-2) and a dimension of 100-250 nm with varying Ni thickness and annealing duration time. Then LED nanopillar arrays with diameter of approximately 250 nm and height of 700 nm were fabricated by inductively coupled plasma etching. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence (PL) intensity is achieved for the nanopillars and a blueshift as well as a decrease in full width at half maximum of the PL peak are also observed. The method of additional chemical etching was used to remove the etching-induced damage. Then nano-LED devices were further completed using a planarization approach to deposit p-type electrode on the tips of nanopillars. The current-voltage curves of both nanopillars and planar LED devices are measured for comparison.

Room-Temperature Continuous-Wave Operation of InGaN-Based Blue-Violet Laser Diodes with a Lifetime of 15.6 Hours

We report our recent progress of investigations on InGaN-based blue-violet laser diodes (LDs). The room-temperature (RT) cw operation lifetime of LDs has extended to longer than 15.6 h. The LD structure was grown on a c-plane free-standing (FS) GaN substrate by metal organic chemical vapor deposition (MOCVD). The typical threshold current and voltage of LD under RT cw operation are 78 mA and 6.8 V, respectively. The experimental analysis of degradation of LD performances suggests that after aging treatment, the increase of series resistance and threshold current can be mainly attributed to the deterioration of p-type ohmic contact and the decrease of internal quantum efficiency of multiple quantum well (MQW), respectively.

InP-base resonant tunneling diodes

We have fabricated In_0.53Ga_0.47As/AlAs/InP resonant tunneling diodes (RTDs) based on the air-bridge technology by using electron beam lithography processing.The epitaxial layers of the RTD were grown on semi-insulating (100) InP substrates by molecular beam epitaxy.RTDs with a peak current density of 24.6 kA/cm~2 and a peak-to-valley current ratio of 8.6 at room temperature have been demonstrated.