Low -temperature preparation of ZnO films on Si substrates by MOCVD

ZnO films were deposited on Si（100） substrates at 300℃ by metal - organic chemical vapor deposition（MOCVD）. The effect of different ratios of DEZn to N2O on crystal quality was analyzed. It is found that the optimum ratio of DEZn to N2O is 2.1. And in this optimum growth condition, X - ray diffraction （XRD） and scanning probe morphology （SPM） images indicate that the films grow along the c - axis orientation. ZnO film exhibits a strong UV optical absorption near 388 nm. And the optical absorbance is close to zero,that indicates nearly 100% optical transparence. Photoluminescence （PL） spectrum shows only strong near - band - edge emissions with little or no deep - level emission related to defects. The full - width at half - maximum （FWHM） of the ultraviolet emission peak is 80meV. The results indicate that better crystal quality can be obtained.

Raman Investigatins of 3C-SiC Films Grown on Si (100) and Sapphire (0001) by LPCVD

The Raman measurements have been performed with the back-scattering geometry on the SiC films grown on Si(100) and sapphire (0001) by LPCVD. Typical TO and LO phonon peaks of 3C-SiC were observed for all the samples grown on Si and apphire substrates, indicating the epilayers are 3C-SiC polytype. Using a free-standing 3C-SiC film removed from Si(100) as a free-stress sample, the stresses of 3C-SiC on Si(100) and sapphire (0001) were estimated according to the shift of TO and LO phonons.

Characterization of polymorphous silicon thin film and solar cells

Polymorphous silicon (pm-Si:H) films have been prepared by a new regime of plasma enhanced chemical vapour deposition in the region adjacent of phase transition from amorphous to microcrystalline state. Comparing to the conventional amorphous silicon (a-Si:H), the pm-Si:H has higher photoconductivity (sigma(ph)), better stability, and a broader light spectral response range in the longer wavelength range. It can be found from Raman spectra that there is a notable improvement in the medium range order. There are a blue shift for the stretching mode of IR spectra and a red shift for the wagging mode. The shifts are attributed to the variation of the microstructure. By using pm-Si:H film as intrinsic layer, a p-i-n junction solar cell was prepared with the initial efficiency of 8.51% and a stabilized efficiency of 8.01% (AM1.5, 100mw/cm(2)) at room temperature (T-R).

Influence of the rapid thermal annealing on the properties of thin a-Si films

The variation of the structure, morphology and the electrical properties of thin amorphous silicon films caused by Rapid Thermal Annealing is studied. The films annealed at 1200degreesC for 2 minutes change their structure to polycrystalline and as a result their resistivity decreases by 4 orders of magnitude. Due to the small thickness of the as deposited amorphous silicon the obtained poly-Si is strongly irregular and has many discontinuities in its texture.

Microstructure of the silicon film prepared near the phase transition regime from amorphous to nanocrystalline

A kind of hydrogenated diphasic silicon films has been prepared by a new regime of plasma enhanced chemical vapor deposition (PECVD) near the phase transition regime from amorphous to nanocrystalline. The microstructural properties of the films have been investigated by the micro-Raman and Fourier transformed Infrared (FT-IR) spectra and atom force microscopy (AFM). The obtained Raman spectra show not only the existence of nanoscaled crystallites, but also a notable improvement in the medium-range order of the diphasic films. For the FT-IR spectra of this kind of films, it notes that there is a blueshift in the Si-H stretching mode and a redshift in the Si-H wagging mode in respect to that of typical amorphous silicon film. We discussed the reasons responsible for these phenomena by means of the phase transition, which lead to the formation of a diatomic hydrogen complex, H-2* and their congeries.

Raman scattering and infrared absorption of silicon nanocrystals in silicon oxide matrix

Structural dependence on annealing of a-SiOx:H was studied by using infrared absorption and Raman scattering. The appearance of Raman peaks in the range of 513-519cm(-1) after 1170 degreesC annealing was interpreted as the formation nanocrystalline silicon with the sizes from 3-10nm. The Raman spectra also show the existence of amorphous-like silicon phase, which is associated with Si-Si bond re-construction at boundaries of silicon nanocrystallites. The presence of the shoulder at 980cm(-1) of Si-O-Si stretching vibration at 1085cm(-1) in infrared spectra imply that except that SiO2 phase, there is silicon sub-oxide phase in the films annealed at 1170 degreesC. This sub-oxide phase is located at the interface between Si crystallites and SiO2, and thus support the shell model for the mixed structures of Si grains and SiO2 matrix.

The growth and characterization of GaN grown on a gamma-Al2O3/(001) Si substrate by metalorganic vapor phase epitaxy

Wurtzite single crystal GaN films have been grown onto a gamma-Al2O3/Si(001) substrate in a horizontal-type low pressure MOVPE system. A thin gamma-Al2O3 layer is an intermediate layer for the growth of single crystal GaN on Si although it is only an oriented polycrystal film as shown by reflection high electron diffraction. Moreover, the oxide is not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN layer as studied by transmission electron microscopy. Double crystal x-ray linewidth of (0002) peak of the 1.3 mu m sample is 54 arcmin and the films have heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature is observed by photoluminescence spectroscopy. Raman scattering does not detect any cubic phase coexistence.

Applications of dielectric thin film by electron cyclotron resonance plasma chemical vapor deposition for semiconductor photoelectronic devices

The paper reports a method of depositing SiO2, SiNx, a:Si, Si3N4 and SiOxNy dielectric thin films by electron cyclotron resonance plasma chemical vapor deposition (ECR CVD) on InP, InGaAs and other compound semiconductor optoelectronic devices,and give a technology of depositing dielectric thin films and optical coatings by ECR CVD on Laser's Bars. The experiment results show the dielectric thin films and optical coatings are stable at thermomechanical property,optical properties and the other properties. In addition, the dielectric thin film deposition that there is low leakage current is reported for using as diffusion and ion implatation masks in the paper. In the finally, the dielectric film refractive index can be accurately controlled by the N-2/O-2/Ar gas flow rate.

Dielectric properties of Bi2Ti2O7 films grown on Si(100) substrate by APMOCVD

The growth of Bi2Ti2O7 films with (111) orientation on Si(100) substrate by atmospheric pressure metal-organic chemical vapor deposition(APMOCVD) technique at 480similar to550 degreesC is presented. The films were characterized by X-ray diffraction analysis, atomic force microscopy and electron diffraction. The results show high quality Bi2Ti2O7 films with smooth shinning surface. The dielectric properties and C-V characterization of the films were studied. The dielectric constant (epsilon) and loss tangent (tgdelta) were found to be 180 and 0.01 respectively. The charge storage density was 31.9fC/mum(2). The resistivity is higher than 1x10(12) Omega. .cm under the applied voltage of 5V. The Bi2Ti2O7 films are suitable to be used as a new insulating gate material in dynamic random access memory (DRAM).

Raman study on residual strains in thin 3C-SiC epitaxial layers grown on Si(001)

Raman scattering measurement has been used to study the residual strains in the thin 3C-SiC/Si(001) epilayers with a variation of film thickness from 0.1 to 1.2 mu m. which were prepared by chemical vapor deposition (CVD)growth. Two methods have been exploited to figure our the residual strains and the exact LO bands. The final analyzing results show that residual strains exist in the 3C-SiC epilayers. The average stress is 1.3010 GPa, and the relative change of the lattice constant is 1.36 parts per thousand. Our measurements also show that 3C-SiC phonons are detectable even for the samples with film thickness in the range of 0.1 to 0.2 mu m. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Structural properties of SI-GaAs grown in space

The structural properties of Semi-insulating gallium arsenide (SI-GaAs) crystal grown with power-travelling technique in space have been studied by double-crystal x-ray diffractometry and chemical etching. The quality of the crystal was first evaluated by x-ray rocking-curve method. The full width at half maximum of x-ray rocking curve in space-grown SI-GaAs is 9.4+/-0.08 are seconds. The average density of dislocations revealed by molten KOH is 2.0 X 10(4) cm(-2), and the highest density is 3.1 X 10(4) cm(-2). The stoichiometry in the single crystal grown in space is improved as well. Unfortunately, the rear of the ingot grown in space is polycrystalline owing to being out of control of power. (C) 1999 COSPAR. Published by Elsevier Science Ltd.

The effects of carbonized buffer layer on the growth of SiC on Si

Carbonized buffer layers were formed with C2H4 on Si(100) and Si(111) substrates using different methods and SIC epilayers were grown on each buffer layer at 1050 degrees C with simultaneous supply of C2H4 and Si2H6. The structure of carbonized and epitaxy layers was analyzed with in situ RHEED. The buffer layers formed at 800 degrees C were polycrystalline on both Si(100) and Si(111) substrates whereas they were single crystals, with twins on Si(100) and without tu ins on Si(111)substrates. when formed with a gradual rise in substrate temperature from 300 degrees C to growth temperature. Raising the substrate temperature slowly results in the formation of more twins. Epilayers grown on carbonized polycrystalline lavers are polycrystalline. Single crystal epilayers without twins grow on single crystalline buffer layers without twins or with a few twins. (C) 1999 Elsevier Science B.V. All rights reserved.

Electrical instability in vanadyl-phthalocyanine thin-film transistors

We investigated the electrical instability of vanadyl-phthalocyanine (VOPc) thin-film transistors (TFTs) at various temperatures. The results demonstrate a slow threshold voltage shift in the bias stress process and a rapid recovery after the removal of bias stress, which indicates that a slower degradation process occurs in the on state while a faster removal in the off state of VOPc TFTs. The shift of threshold voltage comes from traps generated at the organic/dielectrics interface. Additionally, a relaxation time of 10(7) s was obtained at room temperature according to the stretched exponential model, which is comparable to a-Si: H TFTs. Therefore, VOPc TFTs are suitable to be applied in flat panel displays.

Surface potential images of polycrystalline organic semiconductors obtained by Kelvin probe force microscopy

P-type copper phthalocyanine (CuPc) and n-type hexadecafluorophthalocyanina-tocopper (F16CuPc) polycrystalline films were investigated by Kelvin probe force microscopy (KPFM). Topographic and corresponding surface potential images are obtained simultaneously. Surface potential images are related with the local work function of crystalline facets and potential barriers at the grain boundaries (GBs) in organic semiconductors. Based on the spatial distribution of surface potential at GBs, donor- and acceptor-like trapping states in the grain boundaries (GBs) of p-CuPc and n-F16CuPc films are confirmed respectively.

Thickness dependence of mobility in CuPc thin film on amorphous SiO2 substrate

Hole mobility in a copper-phthalocyanine (CuPc)-based top-contact transistor has been studied with various organic layer thicknesses. It is found that the transistor performance depends on the thickness of the CuPc layer, and the mobility increases with the increase in the CuPc layer and saturated at the thickness of 6 ML. The upper layers do not actively contribute to the carrier transport in the organic films. The morphology of the organic layer grown on the bare SiO2/Si substrate is also presented. The analysis of spatial correlations shows that the CuPc films grow on the SiO2 according to the mixed-layer mode.