Kinetics of dissociative water adsorption on stepped Si(001), on Si(115), Si(113), Si(5,5,12) and Si(112)

We present photoelectron spectroscopic and low energy electron diffraction measurements of water adsorption on flat Si samples of the orientations (001), (115), (113), (5,5,12) and (112) as well as on curved samples covering continuously the ranges (001)-(117) and (113)-(5,5,12)-(112). On all orientations, water adsorption is dissociative (OH and H) and non-destructive. On Si(001) the sticking coefficient S and the saturation coverage Theta(sat) are largest. On Si(001) and for small miscuts in the [110]-azimuth, S is constant nearly up to saturation which proves that the kinetics involves a weakly bound mobile precursor state. For (001)-vicinals with high miscut angles (9-13 degrees), the step structure breaks down, the precursor mobility is affected and the adsorption kinetics changed. On (115), (113), (5,5,12) and (112), the values of S and Theta(sat) are smaller which indicates that not all sites are able to dissociate and bind water. For (113) the shape of the adsorption curves Theta versus exposure shows the existence of two adsorption processes, one with mobile precursor kinetics and one with Langmuir-like kinetics. On (5,5,12), two processes with mobile precursor kinetics are observed which are ascribed to adsorption on different surface regions within the large surface unit cell. From the corresponding values of S and Theta(sat), data for structure models are deduced. (C) 1997 Elsevier Science B.V.

Dissociated screw dislocation which can relieve strain energy in the epitaxial layer of GeSi on Si(001)

A dissociated screw dislocation parallel to the interface was found in the epitaxial layer of the Ge0.17Si0.83 Si(001) system. It is shown that this dissociated screw dislocation which consists of two 30 degrees partials can relieve misfit strain energy, and the relieved misfit energy is proportional to the width of the stacking fault between the two partials.

DCXRD Investigation of a Ge/Si（001） Island Multilayer Structure

A Ge/Si（001） island multilayer structure is investigated by double crystal X-ray diffraction, transmission electron microscopy,and atomic force microscopy. We fit the satellite peaks in the rocking curve by two Lorentz lineshapes, which originate from the wetting layer region and the island region. Then from the ratio of the thick- nesses of the Si and Ge （GeSi） layers as determined by TEM,tbe Ge compositions of the wetting layer and islands are estimated to be about 0. 51 and 0. 67, respectively,according to the positions of the fitted peaks. This proves to be a relatively simple way to investigate the Ge/Si （001） island multilayer structure.

在复合衬底γ-Al2O3／Si（001）上生长GaN

采用分子束外延（MBE）生长方法，使用γ-Al2O3材料作为新型过渡层，在Si（001）衬底上获得了没有裂纹的GaN外延层，实验结果表明使用γ-Al2O3过渡层有效地缓解了外延层中的应力．通过生长并测试分析几种不同结构的外延材料，研究了复合衬底γ-Al2O3／Si（001）生长GaN情况，得到了六方相GaN单晶材料，实现了GaNC面生长．预铺薄层Al及高温AIN层可以提高GaN晶体质量，低温AIN缓冲层可以改善GaN表面的粗糙度．为解决Si（001）衬底上GaN的生长问题提供了有益的探索。

Si（001）衬底上APCVD生长3C-SiC薄膜的微孪晶及含量

于2010-11-23批量导入

Si（001）衬底上方形3C-SiC岛的LPCVD生长

于2010-11-23批量导入

Al_2O_3/Si(001)衬底上GaN外延薄膜的制备

于2010-11-23批量导入

Optical characterization of the Ge/Si (001) islands in multilayer structure

We show that the observed temperature dependence of the photoluminescence (PL) features can be consistently explained in terms of thermally activated carrier transfer processes in a multilayer structure of the self-organized Ge/Si(001) islands. The type II (electron confinement in Si) behavior of the Ge/Si islands is verified. With elevated temperature, the thermally activated electrons and holes enter the Ge islands from the Si and from the wetting layer (WL), respectively. An involvement of the type I (spatially direct) into type II (spatially indirect) recombination transition takes place at a high temperature.

Raman study on residual strains in thin 3C-SiC epitaxial layers grown on Si(001)

Raman scattering measurement has been used to study the residual strains in the thin 3C-SiC/Si(001) epilayers with a variation of film thickness from 0.1 to 1.2 mu m. which were prepared by chemical vapor deposition (CVD)growth. Two methods have been exploited to figure our the residual strains and the exact LO bands. The final analyzing results show that residual strains exist in the 3C-SiC epilayers. The average stress is 1.3010 GPa, and the relative change of the lattice constant is 1.36 parts per thousand. Our measurements also show that 3C-SiC phonons are detectable even for the samples with film thickness in the range of 0.1 to 0.2 mu m. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Boron diffusion in Ge+ premorphized and BF2+ implanted Si(001)

The annealing behavior of Si implanted with Ge and then BF2 has been characterized by double crystal X-ray diffraction (DCXRD) and secondary ion mass spectroscopy (SIMS). The results show that annealing at 600 degrees C for 60 minutes can only remove a little damage induced by implantation and nearly no redistribution of Ge and B atoms has occurred during the annealing. The initial crystallinity of Si is fully recovered after annealing at 950 degrees C for 60 minutes and accompanied by Ge diffusion. Very shallow boron junction depth has been formed. When annealing temperature rises to 1050 degrees C, B diffusion enhances, which leads to a deep diffusion and good distribution of B atoms into the Si substrate. The X-ray diffraction (004) rocking curves from the samples annealed at 1050 degrees C for 60 minutes display two SiGe peaks, which may be related to the B concentration profiles.

The growth and characterization of GaN grown on a gamma-Al2O3/(001) Si substrate by metalorganic vapor phase epitaxy

Wurtzite single crystal GaN films have been grown onto a gamma-Al2O3/Si(001) substrate in a horizontal-type low pressure MOVPE system. A thin gamma-Al2O3 layer is an intermediate layer for the growth of single crystal GaN on Si although it is only an oriented polycrystal film as shown by reflection high electron diffraction. Moreover, the oxide is not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN layer as studied by transmission electron microscopy. Double crystal x-ray linewidth of (0002) peak of the 1.3 mu m sample is 54 arcmin and the films have heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature is observed by photoluminescence spectroscopy. Raman scattering does not detect any cubic phase coexistence.

Research progress of self-organized Ge quantum dots on Si substrate

A review is presented on recent research development of self-organized Ge/Si quantum dots (QDs). Emphasis is put on the morphological evolution of the Ge quantum dots grown on Si (001) substrate, the structure analysis of multilayer Ge QDs, the optical and electronic properties of these nanostructures, and the approaches to fabricating ordered Ge quantum dots.

Electro-optic coefficients of Si0.75Ge0.25/Si/Si0.5Ge0.5 asymmetric superlattice measured by polarization-maintaining fiber-optic Mach-Zehnder interferometer

Ten-period 5.5 nm Si0.75Ge0.25/10.3 nm Si/2.5 nm Si0.5Ge0.5 trilayer asymmetric superlattice was prepared on Si (001) substrate by ultrahigh vacuum chemical vapor deposition at 500 degrees C. The stability of Mach-Zehnder interferometer was improved by utilizing polarization-maintaining fibers. According to the electro-optic responses of the superlattice with the light polarization along [110] and [-110], respectively, both electro-optic coefficients gamma(13) and gamma(63) of such asymmetric superlattice were measured. gamma(13) and gamma(63) are 2.4x10(-11) and 1.3x10(-11) cm/V, respectively, with the incident light wavelength at 1.55 mu m. (c) 2006 American Institute of Physics.

Investigation of Mn-doped Si films prepared by magnetron cosputtering

Mn-doped Si films were prepared on Si(001) substrates by magnetron cosputtering and post-annealing process. The structural, morphological and magnetic properties of the films have been investigated. X-ray diffraction results show that the as-prepared film is amorphous. By annealing at 800 degrees C, however, the film is crystallized. There is no secondary phase found except Si in the two films. Chemical mapping shows that no segregation of the Mn atoms appears in the annealed film. Atomic force microscopy images of the films indicate that the annealed film has a granular feature that covers uniformly the film surface while there is no such kind of characteristic in the as-prepared film. The field dependence of magnetization was measured using an alternating gradient magnetometer, and it has been indicated that the annealed film shows room-temperature ferromagnetism. (c) 2006 Elsevier B.V. All rights reserved.

Study on in-plane optical anisotropy of Si0.75Ge0.25/Si/Si0.5Ge0.5 asymmetric superlattice by reflectance difference spectroscopy - art. no. 071908

Si0.75Ge0.25/Si/Si0.5Ge0.5 trilayer asymmetric superlattices were prepared on Si (001) substrate by ultrahigh vacuum chemical vapor deposition at 500 degrees C. The nonlinear optical response caused by inherent asymmetric interfaces in this structure predicted by theories was verified by in-plane optical anisotropy in (001) plane measured via reflectance difference spectroscopy. The results show Si0.75Ge0.25/Si/Si0.5Ge0.5 asymmetric superlattice is optically biaxial and the two optical eigen axes in (001) plane are along the directions [110] and [-110], respectively. Reflectance difference response between the above two eigen axes can be influenced by the width of the trilayers and reaches as large as similar to 10(-4)-10(-3) in 15-period 2.7 nm-Si0.75Ge0.25/8 nm-Si/1.3 nm-Si0.5Ge0.5 superlattice when the normal incident light wavelength is in the range of 500-1100 nm, which is quite remarkable because the optical anisotropy does not exist in bulk Si.