Vertical PIN ultraviolet photodetectors based on 4H-SiC homoepilayers

Vertical PIN ultraviolet photodetectors based on 4H-SiC homoepilayers are presented. The growth of the 4H-SiC homoepilayers was carried out in a LPCVD system. The size of the active area of the photodetector was 300 x 300 mu m(2). The dark and illuminated I-V characteristics were measured at reverse biases from 0 V to 30 V at room temperature. The illuminated current was at least two orders of magnitude higher than the dark current at a bias of below 12 V. The photoresponse was measured from 200 nm to 400 nm at different reverse biases and the peak values of the photo response were located at 3 10 nm. The calculated spectral detectivity D* was shown to be higher than 10(13) cmHz(1/2)/W from 260 to 360 nm with a peak value of 5.9 x 10(13) cmHz(1/2) /W at 310 nm. The peak value of the photoresponse was hundreds of times higher than the response at 400 nm, which showed the device had good visible blind performance. (c) 2007 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Micro-raman investigation of defects in a 4H-SiC homoepilayer

Three types of defects, namely defect I, defect 11, defect 111, in the 4H-SiC homoepilayer were investigated by micro-raman scattering measurement. These defects all originate from a certain core and are composed of (1) a wavy tail region, (11) two long tails, the so called comet and (111) three plaits. It was found that there are 3C-SiC inclusions in the cores of defect 11 and defect III and the shape of inclusion determines the type of defect II or defect III. If the core contains a triangle-shaped inclusion, the defect III would be formed; otherwise, the defect 11 was formed. No inclusion was observed in the core of the defect I. The mechanisms of these defects are discussed.

Growth and characterization of 4H-SiC by horizontal hot-wall CVD

4H-SiC layers have been homoepitaxially grown at 1500 degrees C with the use of a horizontal hot-wall chemical vapor deposition (CVD) system, which was built in the author's group. The typical growth rate was 2 mu m/h at a pressure of 40 Torr. The background donor concentration has been reduced to 2.3 x 10(15) cm(-3) during a prolonged growth run. It confirmed the idea that the high background concentration of thin films was caused by the impurities inside the susceptor and thermal insulator The FWHM of x-ray co-rocking curves show 9 similar to 15 aresecs in five different areas of a 32-mu m-thick 4H-SiC epilayer The free exciton peaks dominated in the near-band-edge low-temperature photoluminescence spectrum (LTPL), indicating high crystal quality.

Homoepitaxial growth and MOS structures of 4H-SiC on off oriented n-type (0001)Si-faces

Homoepitaxial growth of 4H-SiC on off-oriented n-type Si-face (0001) substrates was performed in a home-made hot-wall low pressure chemical vapor deposition (LPCVD) reactor with SiH4 and C2H4 at temperature of 1500 C and pressure of 20 Torr. The surface morphology and intentional in-situ NH3 doping in 4H-SiC epilayers were investigated by using atomic force microscopy (AFM) and secondary ion mass spectroscopy (SIMS). Thermal oxidization of 4H-SiC homoepitaxial layers was conducted in a dry O-2 and H-2 atmosphere at temperature of 1150 C. The oxide was investigated by employing x-ray photoelectron spectroscopy (XPS). 4H-SiC MOS structures were obtained and their C-V characteristics were presented.

Epitaxial growth on 4H-SiC by TCS as a silicon precursor

Epitaxial growth on n-type 4H-SiC 8°off-oriented substrates with a size of 10 × 10 mm~2 at different tem-peratures with various gas flow rates has been performed in a horizontal hot wall CVD reactor, using trichlorosilane (TCS) as a silicon precursor source together with ethylene as a carbon precursor source. The growth rate reached 23 μm/h and the optimal epilayer was obtained at 1600 ℃ with a TCS flow rate of 12 sccm in C/Si of 0.42, which has a good surface morphology with a low RMS of 0.64 nm in an area of 10 × 10μm~2. The homoepitaxial layer was oh-tained at 1500 ℃ with low growth rate (< 5μm/h) and the 3C-SiC epilayers were obtained at 1650 ℃ with a growth rate of 60-70μm/h. It is estimated that the structural properties of the epilayers have a relationship with the growth temperature and growth rate. Silicon droplets with different sizes are observed on the surface of the homoepitaxial layer in a low C/Si ratio of 0.32.

Homoepitaxial Growth of 4H-SiC and Ti/4H-SiC SBDs

Homoepitaxial growth of4H-SiC on off-oriented Si-face （0001） 4H-SiC substrates was performed at 1500℃ by using the step controlled Epitaxy. Ti/4H-SiC Schottky barrier diodes （SBDs） with blocking voltage over lkV have been made on an undoped epilayer with 32μm in thick and 2-5 × 10^15 cm^-3 in carrier density. The diode rectification ratio of forward to reverse （defined at ± 1V） is over 107 at room temperature and over 10^2 at 538K. Their electrical characteristics were studied by the current-voltage measurements in the temperature range from 20 to 265 ℃. The ideality factor and Schottky barrier height obtained at room temperature are 1.33 and 0. 905eV, respectively. The SBDs have on-state current density of 150A/cm^2 at a forward voltage drop of about 2.0V. The specific on-resistance for the rectifier is found to be as 7.9mΩ · cm^2 and its variation with temperature is T^2.0.

水平冷壁CVD生长4H-SiC同质外延膜

采用自行设计的水平冷壁低压化学气相沉积(LPCVD)方法在偏向〈1120〉晶向8°的n型4H-SiC(0001)衬底上进行了同质外延生长.在5.3×103Pa的低压下,外延膜生长速率超过3μm/h.电容-电压法测试表明在非有意掺杂外延膜中净施主浓度为8.4×10 15cm-3.Nomarski显微镜观察表明厚外延膜的表面光滑,生长缺陷密度很低.AFM测试显示表面均方根粗糙度为0.3nm,没有观察到宏观台阶结构.Raman谱线清晰锐利,表现出典型的4H-SiC特征.在低温PL谱中,近带边区域出现很强的自由激子峰,表明样品是高质量的.

Second-Order Raman Scattering from n- and p-Type 4H-SiC

The results of second-order Raman-scattering experiments on n- and p-type 4H-SiC are presented,covering the acoustic and the optical overtone spectral regions.Some of the observed structures in the spectra are assigned to particular phonon branches and the points in the Brillouin zone from which the scattering originates.There exists a doublet at 626/636cm-1 with energy difference about 10cm-1 in both n- and p-type 4H-SiC,which is similar to the doublet structure with the same energy difference founded in hexagonal GaN,ZnO, and AlN.The cutoff frequency at 1926cm-1 of the second-order Raman is not the overtone of the A1(LO) peak of the n-type doping 4H-SiC,but that of the undoping one.The second-order Raman spectrum of 4H-SiC can hardly be affected by doping species or doping density.

Homoepitaxial Growth and Characterization of 4H-SiC Epilayers by Low-Pressure Hot-Wall Chemical Vapor Deposition

Horizontal air-cooled low-pressure hot-wall CVD (LP-HWCVD) system is developed to get highly qualitical 4H-SiC epilayers.Homoepitaxial growth of 4H-SiC on off-oriented Si-face (0001) 4H-SiC substrates is performed at 1500℃ with a pressure of 1.3×103Pa by using the step-controlled epitaxy.The growth rate is controlled to be about 1.0μm/h.The surface morphologies and structural and optical properties of 4H-SiC epilayers are characterized with Nomarski optical microscope,atomic force microscopy (AFM),X-ray diffraction,Raman scattering,and low temperature photoluminescence (LTPL).N-type 4H-SiC epilayers are obtained by in-situ doping of NH3 with the flow rate ranging from 0.1 to 3sccm.SiC p-n junctions are obtained on these epitaxial layers and their electrical and optical characteristics are presented.The obtained p-n junction diodes can be operated at the temperature up to 400℃,which provides a potential for high-temperature applications.

离子辐照后4H-SiC晶体退火前后的光谱研究

分析了高能Pb27+辐照预注入12C+的和未预注入12C+ 4H-SiC样品在,退火前后傅立叶变换红外光谱和拉曼散射光谱的变化。从傅立叶变换红外光谱可以知道,900℃以上的退火使损伤层发生显著恢复;在拉曼散射光谱中可以看到1200℃退火后有石墨相的存在。实验结果说明,高温退火有利于损伤的恢复,使注入到碳化硅中的碳原子发生聚集并引起相变。

铅离子辐照注碳4H-SiC的红外光谱特性研究

主要研究了铅离子辐照注碳4H-SiC样品在3个不同退火温度下傅立叶变换红外光谱的变化。从红外谱的变化可以知道铅辐照注碳4H-SiC样品在一定深度内出现了非晶层,波数在960—1 450 cm-1范围内出现了干涉带,干涉带强度随着退火温度的升高而变弱。1 373 K退火后样品的卢瑟福背散射分析结果显示,一定深度内硅原子的背散射产额明显减少。

Study on nanohardness of helium-implanted 4H-SiC

The hardness of 4H-SiC, which was high-temperature (500 K) helium-Implanted to fluences of 3 x 10(16) Ions cm(-2) and subsequently thermally annealed at the temperature ranging from 773 to 1273 K, was studied by nanoindentation It is found that the hardness of the implanted 4H-SiC increases at the first, then decreases, and then increases again with increasing annealing tempeature in the temperature range of 500-1273 K, and significant increase in hardness is observed at 773 K. The behavior is ascribed to the changes of the density, length, and tangling of the covalent Si-C bond through the recombination of point defects, clustering of He-vacancy, and growth of helium bubbles during the thermal annealing

氦离子注入4H-SiC晶体的纳米硬度研究；Study on nanohardness of helium-implanted 4H-SiC

4H-SiC晶体经能量为100keV,剂量为3×1016cm-2的氦离子高温(500K)注入后,再在773—1273K温度范围内进行了退火处理,最后使用纳米压痕仪测量了样品注入面的硬度.测试结果表明,在500—1273K温度范围内样品的硬度随退火温度升高呈现先增大后减小再增大的趋势,其中773K退火样品的硬度增大明显.分析认为,退火样品的硬度变化是由退火过程中缺陷复合与氦泡生长导致样品内部的Si—C键密度、键长和键角改变引起的.