Proton irradiation-induced defects in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Undoped GaSb was irradiated by 2.6 MeV protons. The irradiation-induced defects were studied by positron lifetime spectroscopy (PLS) and photoluminescence (PL). Positron lifetime measurements showed that vacancy-type defects were introduced after irradiation, and divacancies were formed at higher irradiation dose. Annealing experiments revealed there were different annealing steps between the as grown and proton-irradiated samples, the reason for which was tentatively attributed to the formation of divacancies in the proton-irradiated samples during annealing. All the vacancy defects could be annealed out at around 500 degrees C. The PL intensity quickly fell down after proton irradiation and decreased with increasing irradiation dose, indicating that irradiation induced non-irradiative recombination centers, whose candidates were assigned to the vacancy defects induced by proton irradiation.

Defects around self-organized InAs quantum dots measured by slow positron beam

Self-organized InAs quantum dots (QDs) have been fabricated by molecular beam epitaxy. The authors try to use a slow positron beam to detect defects in and around self-organized QDs, and point defects are observed in GaAs cap layer above QDs. For the self-organized InAs QDs without strain-reducing layer, it is free of defects. However, by introducing a strain-reducing layer, the density of point defects around larger sized InAs QDs increased. The above results suggest that low energy positron beam measurements may be a good approach to detect depth profiles of defects in QD materials. (c) 2007 American Institute of Physics.

Dependence of intrinsic defects in ZnO films on oxygen fraction studied by positron annihilation

Defects in ZnO films grown by radio-frequency reactive magnetron sputtering under variable ratios between oxygen and argon gas have been investigated by using the monoenergetic positron beam technique. The dominate intrinsic defects in these ZnO samples are O vacancies (V-O) and Zn interstitials (Zn-i) when the oxygen fraction in the O-2/Ar feed gas does not exceed 70% in the processing chamber. On the other hand, zinc vacancies are preponderant in the ZnO Elms fabricated in richer oxygen environment. The concentration of zinc vacancies increases with the increasing (2) fraction. For the oxygen fraction 85%, the number of zinc vacancies that could trap positrons will be smaller. It is speculated that some unknown defects could shield zinc vacancies. The concentration of zinc vacancies in the ZnO films varies with the oxygen fraction in the growth chamber, which is in agreement with the results of photoluminescence spectra.

Gallium vacancy and the residual acceptor in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Positron lifetime, photoluminescence (PL), and Hall measurements were performed to study undoped p-type gallium antimonide materials. A 314 ps positron lifetime component was attributed to Ga vacancy (V-Ga) related defect. Isochronal annealing studies showed at 300 degreesC annealing, the 314 ps positron lifetime component and the two observed PL signals (777 and 797 meV) disappeared, which gave clear and strong evidence for their correlation. However, the hole concentration (similar to2x10(17) cm(-3)) was observed to be independent of the annealing temperature. Although the residual acceptor is generally related to the V-Ga defect, at least for cases with annealing temperatures above 300 degreesC, V-Ga is not the acceptor responsible for the p-type conduction. (C) 2002 American Institute of Physics.

Positron-annihilation study of compensation defects in InP

Positron-annihilation lifetime and positron-annihilation Doppler-broadening (PADB) spectroscopies have been employed to investigate the formation of vacancy-type compensation defects in n-type undoped liquid encapsulated Czochrolski grown InP, which undergoes conduction-type conversions under high temperature annealing. N-type InP becomes p-type semiconducting by short time annealing at 700 degreesC, and then turns into n-type again after further annealing but with a much higher resistivity. Long time annealing at 950 degreesC makes the material semi-insulating. Positron lifetime measurements show that the positron average lifetime tau(av) increases from 245 ps to a higher value of 247 ps for the first n-type to p-type conversion and decreases to 240 ps for the ensuing p-type to n-type conversion. The value of tau(av) increases slightly to 242 ps upon further annealing and attains a value of 250 ps under 90 h annealing at 950 degreesC. These results together with those of PADB measurements are explained by the model proposed in our previous study. The correlation between the characteristics of positron annihilation and the conversions of conduction type indicates that the formation of vacancy-type defects and the progressive variation of their concentrations during annealing are related to the electrical properties of the bulk InP material. (C) 2002 American Institute of Physics.

Growing process of CdS nanoclusters in zeolite Y studied by positron annihilation

Zeolite Y has been used as the host to generate CdS nanoclusters. The location of CdS nanoclusters inside zeolite hosts was confirmed by the blue-shifted reflection absorption spectra with respect to that of bulk CdS materials. But which kind of cage inside zeolite Y, sodalite cage or supercage, was preferred for the CdS clusters remained unclear. In this paper, we conducted positron annihilation spectroscopy (PAS) measurements for the first time on a series of CdS/Y zeolite samples and concluded that CdS clusters were not located in supercages but in smaller sodalite cages. The stability of CdS clusters inside the sodalite units was due to the coordination of Cd atoms with the framework oxygen atoms of the double six-ring windows. Moreover, PAS revealed some important information of surface states existing on the interfacial layers between CdS clusters and zeolite Y. (C) 2001 Elsevier Science B,V, All rights reserved.

Photoluminescence spectroscopy and positron annihilation spectroscopy probe of alloying and annealing effects in nonpolar m-plane ZnMgO thin films

Temperature-dependent photoluminescence characteristics of non-polar m-plane ZnO and ZnMgO alloy films grown by metal organic chemical vapor deposition have been studied. The enhancement in emission intensity caused by localized excitons in m-plane ZnMgO alloy films was directly observed and it can be further improved after annealing in nitrogen. The concentration of Zn vacancies in the films was increased by alloying with Mg, which was detected by positron annihilation spectroscopy. This result is very important to directly explain why undoped Zn1-xMgxO thin films can show p-type conduction by controlling Mg content, as discussed by Li [Appl. Phys. Lett. 91, 232115 (2007)].

Role of Ga vacancies in enhancing the leakage current of GaN Schottky barrier ultraviolet photodetectors

The leakage current of GaN Schottky barrier ultraviolet photodetectors is investigated. It is found that the photodetectors adopting undoped GaN instead of lightly Si-doped GaN as an active layer show a much lower leakage current even when they have a higher dislocation density. It is also found that the density of Ga vacancies in undoped GaN is much lower than in Si-doped GaN. The Ga vacancies may enhance tunneling and reduce effective Schottky barrier height, leading to an increase of leakage current. It suggests that when undoped GaN is used as the active layer, it is necessary to reduce the leakage current of GaN Schottky barrier ultraviolet photodetector.

Influence of electron irradiation on hydrothermally grown zinc oxide single crystals

The resistivity of hydrothermally grown ZnO single crystals increased from similar to 10(3) Omega cm to similar to 10(6) Omega cm after 1.8 MeV electron irradiation with a fluence of similar to 10(16) cm(-2), and to similar to 10(9) Omega cm as the fluence increased to similar to 10(18) cm(-2). Defects in samples were studied by thermally stimulated current (TSC) spectroscopy and positron lifetime spectroscopy (PLS). After the electron irradiation with a fluence of 10(18) cm(-2), the normalized TSC signal increased by a factor of similar to 100. A Zn vacancy was also introduced by the electron irradiation, though with a concentration lower than expected. After annealing in air at 400 degrees C, the resistivity and the deep traps concentrations recovered to the levels of the as-grown sample, and the Zn vacancy was removed.

Investigation on the structural origin of n-type conductivity in InN films

This work presents a study of the correlation between the electrical properties and the structural defects in nominally undoped InN films. It is found that the density of edge-type threading dislocations (TDs) considerably affects the electron concentration and mobility in InN films. The Hall-effect measured electron concentration increases, while the Hall mobility decreases with the increase in the edge-type TD density. With the combination of secondary ion mass spectrometry and positron annihilation analysis, we suggest that donor-type point defects at the edge-type TD lines may serve as dominant donors in InN films and affect the carrier mobility.

Evolution of structural defects in SiOx films fabricated by electron cyclotron resonance plasma chemical vapour deposition upon annealing treatment

We study the structural defects in the SiOx film prepared by electron cyclotron resonance plasma chemical vapour deposition and annealing recovery evolution. The photoluminescence property is observed in the as-deposited and annealed samples. [-SiO3](2-) defects are the luminescence centres of the ultraviolet photoluminescence (PL) from the Fourier transform infrared spectroscopy and PL measurements. [-SiO3](2-) is observed by positron annihilation spectroscopy, and this defect can make the S parameters increase. After 1000 degrees C annealing, [-SiO3](2-) defects still exist in the films.

Does an enhanced yellow luminescence imply a reduction of electron mobility in n-type GaN?

It is studied whether there is any regular relationship between the yellow luminescence band and electron mobility of n-type GaN. For a series of GaN samples grown with the same Si doping, it is found that the electron mobility decreases with an increase of relative intensity of yellow luminescence, accompanied by an increase of edge dislocation density. Further research indicates that it is acceptors introduced by edge dislocations which lead to the concomitant changes of yellow luminescence and electron mobility. Similar changes are induced by Si doping in the n-type GaN samples with relatively low edge dislocation density. However, the relationship between the yellow luminescence and electron mobility of n-type GaN is not a simple one. A light Si doping may simultaneously increase yellow luminescence and electron mobility when Si doping plays a dominant role in reducing the carrier scattering. This means that even the intensity of yellow luminescence is often used as an indicator of material quality for GaN, it does not have any monotonous correlation with the electron mobility of GaN. (c) 2007 American Institute of Physics.

Gallium antisite defect and residual acceptors in undoped GaSb

Undoped Ga-Sb samples were investigated by positron lifetime spectroscopy (PAS) and the coincident Doppler broadening (CDB) technique. PAS measurement indicated that there were monovacancy-type defects in undoped Ga-Sb samples, which were identified to be predominantly Ca vacancy (V-Ga) related defects by combining the CDB measurements. After annealing of these samples at 520 C, positron shallow trapping have been observed and should be due to Ga-Sb defects. Undoped Ga-Sb is intrinsically p-type having a residual carrier density of 10(16)-10(17) cm(-3). And the Ga-Sb antisite defects are stable in the (0), (1-) and (2-) charge states and act as a double acceptor. Thus, we infer that Ga-Sb antisite defects are the acceptor contributing to the p-type conduction for undoped samples. (C) 2004 Elsevier B.V All rights reserved.