Stoichiometric defects in semi-insulating GaAs

The influences of arsenic interstitials and dislocations on the lattice parameters of undoped semi-insulating (SI) GaAs single crystals were analyzed. It was shown that the dislocations in such crystals serve as effective gettering sites for arsenic interstitials due to the deformation energy of dislocations. The average excess arsenic in GaAs epilayers grown by molecular-beam epitaxy (MBE) at low temperatures (LT) is about 1%, and the lattice parameters of these epilayers are larger than those of liquid-encapsulated Czochralski-grown (LEG) SI-GaAs by about 0.1%. The atomic ratio, [As]/([Ga] + [As]), in SI-GaAs grown by low-pressure (LP) LEC is the nearest to the strict stoichiometry compared with those grown by high-pressure (HP) LEC and vertical gradient freeze (VGF). After multiple wafer annealing (MWA), the crystals grown by HPLEC become closer to be strictly stoichiometric.

High-performance electroabsorption modulator

A 100-μm-long electroabsorption modulator monolithically integrated with passive waveguides at the input and output ports is fabricated through ion implantation induced quantum well intermixing, using only a two-step low-pressure metal-organic vapor phase epitaxial process. An InGaAsP/InGaAsP intra-step quantum well is introduced to the active region to improve the modulation properties. In the experiment high modulation speed and high extinction ratio are obtained simultaneously, the electrical-to-optical frequency response (E/O response) without any load termination reaches to 22 GHz, and extinction ration is as high as 16 dB.

Stress and resistivity controls on in situ boron doped LPCVD polysilicon films for high-Q MEMS applications

The simultaneous control of residual stress and resistivity of polysilicon thin films by adjusting the deposition parameters and annealing conditions is studied. In situ boron doped polysilicon thin films deposited at 520 ℃ by low pressure chemical vapor deposition (LPCVD) are amorphous with relatively large compressive residual stress and high resistivity. Annealing the amorphous films in a temperature range of 600-800 ℃ gives polysilicon films nearly zero-stress and relatively low resistivity. The low residual stress and low resistivity make the polysilicon films attractive for potential applications in micro-electro-mechanical-systems (MEMS) devices, especially in high resonance frequency (high-f) and high quality factor (high-Q MEMS resonators. In addition, polysilicon thin films deposited at 570 ℃ and those without the post annealing process have low resistivities of 2-5 mΩ·cm. These reported approaches avoid the high temperature annealing process (> 1000℃), and the promising properties of these films make them suitable for high-Q and high-f MEMS devices.

Heteroepitaxial Growth of 3C-SiC Films on Maskless Patterned Silicon Substrates

Heteroepitaxial growth of 3C-SiC on patterned Si substrates by low pressure chemical vapor deposition (LPCVD) has been investigated to improve the crystal quality of 3C-SiC films. Si substrates were patterned with parallel lines, 1 to 10μm wide and spaced 1 to 10μm apart, which was carried out by photolithography and reactive ion etching. Growth behavior on the patterned substrates was systematically studied by scanning electron microscopy (SEM). An air gap structure and a spherical shape were formed on the patterned Si substrates with different dimensions. The air gap formed after coalescence reduced the stress in the 3C-SiC films, solving the wafer warp and making it possible to grow thicker films. XRD patterns indicated that the films grown on the maskless patterned Si substrates were mainly composed of crystal planes with (111) orientation.

Graded tensile-strained bulk InGaAs/InP superluminescent diode with very wide emission spectrum

A kind of novel broad-band superluminescent diodes (SLDs) using graded tensile-strained bulk InGaAs is developed. The graded tensile-strained bulk InGaAs is obtained by changing only group-III trimethyl-gallium source flow during low-pressure metal organic vapor-phase epitaxy. At the injection current of 200 mA, the fabricated SLDs with such structure demonstrate full-width at half-maximum spectral width of 106 nm and the output light power of 13.6 mW, respectively.

Preparation of 50mm 3C-SiC/Si(111) as Substrates Suited for Ⅲ-Nitrides

50mm SiC films with high electrical uniformity are grown on Si(111) by a newly developed vertical low-pressure chemical vapor deposition (LPCVD) reactor.Both in-situ n- and p-type doping of 3C-SiC are achieved by intentional introduction of ammonia and boron into the precursor gases.The dependence of growth rate and surface morphology on the C/Si ratio and optimized growth conditions is obtained.The best electrical uniformity of 50mm 3C-SiC films obtained by non-contact sheet resistance measurement is ±2.58%.GaN films are grown atop the as-grown 3C-SiC/Si(111) layers using molecular beam epitaxy (MBE).The data of both X-ray diffraction and low temperature photoluminescence of GaN/3C-SiC/Si(111) show that 3C-SiC is an appropriate substrate or buffer layer for the growth of Ⅲ-nitrides on Si substrates with no cracks.

1.78 μm Strained InGaAs-InGaAsP-InP Distributed Feedback Quantum Well Lasers

Ridge-waveguide distributed-feedback(DFB) lasers with highly strained InGaAs/InGaAsP active regions,emitting at 1.78 μm were fabricated by low pressure metal-organic vapor phase epitaxy(LP-MOVPE) and tested.The lasers exhibited threshold current of 33 mA for 900 μm long cavities at room temperature.A maximum light output power of 8 mW from one facet and an external differential quantum efficiency of 7% were also obtained.In oddition,the side mode suppression ratio (SMSR) is 27.5 dB.

Metal-organic Vapor Phase Epitaxy Growth and Characterization of InAlGaN Epilayers

In order to improve crystal quality for growth of quaternary InAlGaN, a series of InAlGaN films were grown on GaN buffer layer under different growth temperatures and carrier gases by low-pressure metal-organic vapor phase epitaxy. Energy dispersive spectroscopy (EDS) was employed to measure the chemical composition of the quaternary, high resolution X-ray diffraction (HRXRD) and photoluminescence (PL) technique were used to characterize structural and optical properties of the epilayers, respectively. The PL spectra of InAlGaN show with and without the broad-deep level emission when only N2 and a N2+H2 mixture were used as carrier gas, respectively. At pressure of 1.01×104 Pa and with mixed gases of nitrogen and hydrogen as carrier gas, different alloy compositions of the films were obtained by changing the growth temperature while keeping the fluxes of precursors of indium (In), aluminum (Al), gallium (Ga) and nitrogen (N2) constant. A combination of HRXRD and PL measurements enable us to explore the relative optimum growth parameters-growth temperature between 850℃ and 870℃,using mixed gas of N2+H2 as carrier gas.

High Temperature Characteristics of 3C-SiC/Si Heterojunction Diodes Grown by LPCVD

The high temperature (300～480K) characteristics of the n-3C-SiC/p-Si heterojunction diodes (HJD) fabricated by low-pressure chemical vapor deposition on Si (100) substrates are investigated.The obtained diode with best rectifying properties has 1.8×104 of ratio at room temperature,and slightly rectifying characteristics with 3.1 of rectification ratio is measured at 480K of an ambient temperature .220V of reverse breakdown voltage is acquired at 300K.Capacitance-voltage characteristics show that the abrupt junction model is applicable to the SiC/Si HJD structure and the built-in voltage is 0.75V.An ingenious equation is employed to perfectly simulate and explain the forward current density-voltage data measured at various temperatures.The 3C-SiC/Si HJD represents a promising approach for the fabrication of high quality heterojunction devices such as SiC-emitter heterojunction bipolar transistors.

Selective Area Growth InGaAsP by MOVPE

The wide stripe (ISjum) selective area growth (SAG) of InGaAsP by low pressure MOVPE is systematically investigated. The characteristics of the growth ratios,thickness enhancement factors .bandgap modulation,and composition modulation vary with the growth conditions such as mask width,growth pressure. Flux of III-group precursors are outlined and the rational mechanism behind SAG MOVPE is explained. In addition,the surface spike of the SAG InGaAsP is shown and the course of it is given by the variation of V /III .

Heteroepitaxial Growth and Heterojunction Characteristics of Voids-Free n-3C-SiC on p-Si(100)

Highly oriented voids-free 3C-SiC heteroepitaxial layers are grown on φ50mm Si (100) substrates by low pressure chemical vapor deposition (LPCVD). The initial stage of carbonization and the surface morphology of carbonization layers of Si(100) are studied using reflection high energy electron diffraction (RHEED) and scanning electron microscopy (SEM). It is shown that the optimized carbonization temperature for the growth of voids-free 3S-SiC on Si (100) substrates is 1100 ℃. The electrical properties of SiC layers are characterized using Van der Pauw method. The I-V, C-V, and the temperature dependence of I-V characteristics in n-3C-SiC-p-Si heterojunctions with AuGeNi and Al electrical pads are investigated. It is shown that the maximum reverse breakdown voltage of the n-3C-SiC-p-Si heterojunction diodes reaches to 220V at room temperature. These results indicate that the SiC/Si heterojunction diode can be used to fabricate the wide bandgap emitter SiC/Si heterojunction bipolar transistors (HBT's).

The growth and characterization of GaN grown on a gamma-Al2O3/(001) Si substrate by metalorganic vapor phase epitaxy

Wurtzite single crystal GaN films have been grown onto a gamma-Al2O3/Si(001) substrate in a horizontal-type low pressure MOVPE system. A thin gamma-Al2O3 layer is an intermediate layer for the growth of single crystal GaN on Si although it is only an oriented polycrystal film as shown by reflection high electron diffraction. Moreover, the oxide is not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN layer as studied by transmission electron microscopy. Double crystal x-ray linewidth of (0002) peak of the 1.3 mu m sample is 54 arcmin and the films have heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature is observed by photoluminescence spectroscopy. Raman scattering does not detect any cubic phase coexistence.

Growth and fabrication of high performance 980nm strained InGaAs quantum well lasers using novel hybrid material system of InGaAsP and AlGaAs

In this paper, we report on the design, growth and fabrication of 980nm strained InGaAs quantum well lasers employing novel material system of Al-free active region and AlGaAs cladding layers. The use of AlGaAs cladding instead of InGaP provides potential advantages in laser structure design, improvement of surface morphology and laser performance. We demonstrate an optimized broad-waveguide structure for obtaining high power 980nm quantum well lasers with low vertical beam divergence. The laser structure was grown by low-pressure metalorganic chemical vapor deposition, which exhibit a high internal quantum efficiency of similar to 90% and a low internal loss of 1.5-2.5 cm(-1). The broad-area and ridge-waveguide laser devices are both fabricated. For 100 mu m wide stripe lasers with cavity length of 800 mu m, a low threshold current of 170mA, a high slope efficiency of 1.0W/A and high output power of more than 3.5W are achieved. The temperature dependences of the threshold current and the emitting spectra demonstrate a very high characteristic temperature coefficient (T-o) of 200-250K and a wavelength shift coefficient of 0.34nm/degrees C. For 4 mu m-width ridge waveguide structure laser devices, a maximum output power of 340mW with GOD-free thermal roll-over characteristics is obtained.

Heteroepitaxial growth and annealing of gamma-Al2O3 thin films on silicon

The gamma-Al2O3 films were grown on Si (100) substrates using the sources of TMA (Al (CH3)(3)) and O-2 by very low-pressure chemical vapor deposition (VLP-CVD). It has been found that the gamma-Al2O3 film has a mirror-like surface and the RMS was about 2.5nm. And the orientation relationship was gamma-Al2O3(100)/Si(100). The thickness uniformity of gamma-Al2O3 films for 2-inch epi-wafer was less than 5%. The X-ray diffraction (XRD) and reflection high-energy electron diffraction (RHEED) results show that the crystalline quality of the film was improved after the film was annealed at 1000degreesC in O-2 atmosphere. The high-frequency C-V and leakage current of Al/gamma-Al2O3/Si capacitor were also measured to verify the annealing effect of the film. The results show that the dielectric constant increased from 4 to 7 and the breakdown voltage for 65-nm-thick gamma-Al2O3 film on silicon increases from 17V to 53V.

In situ doping of 3C-SiC grown on (0001) sapphire substrates by LPCVD

The heteroepitaxial growth of n-type and p-type 3C-SiC on (0001) sapphire substrates has been performed with a supply of SiH4+C2H4+H-2 system by introducing ammonia (NH3) and diborane (B2H6) precursors, respectively, into gas mixtures. Intentionally incorporated nitrogen impurity levels were affected by changing the Si/C ratio within the growth reactor. As an acceptor, boron can be added uniformly into the growing 3C-SiC epilayers. Nitrogen-doped 3C-SiC epilayers were n-type conduction, and boron-doped epilayers were p-type and probably heavily compensated.