Modification of emission wavelength of self-assembled In(Ga)As/GaAs quantum dots covered by InxGa1-xAs(0 <= x <= 0.3) layer

Red shifts of emission wavelength of self-organized In(Cla)As/GaAs quantum dots (QDs) covered by 3 nm thick InxGa1-xAs layer with three different In mole fractions (x = 0.1, 0.2 and 0.3, respectively) have been observed. Transmission electron microscopy images demonstrate that the stress along growth direction in the InAs dots was reduced due to introducing the InxGa1-xAs (x = 0.1, 0.2 and 0.3) covering layer instead of GaAs layer. Atomic force microscopy pictures show a smoother surface of InAs islands covered by an In0.2Ga0.8As layer. It is explained by the calculations that the redshifts of the photoluminescence (PL) spectra from the QDs covered by the InxGa1-xAs (x greater than or equal to 0.1) layers were mainly due to the reducing of the strain other than the InAs/GaAs intermixing in the InAs QDs. The temperature dependent PL spectra further confirm that the InGaAs covering layer can effectively suppress the temperature sensitivity of PL emissions. 1.3 mum emission wavelength with a very narrow linewidth of 19.2 mcV at room temperature has been obtained successfully from In,In0.5Ga0.5As/GaAs self-assembled QDs covered by a 3-nm In0.2Ga0.2As strain reducing layer. (C) 2001 Elsevier Science B.V. All rights reserved.

Room temperature 1.55 mu m emission from InAs quantum dots grown on (001)InP substrate by molecular beam epitaxy

Self-assembled InAs nanostructures on (0 0 1)InP substrate have been grown by molecular beam epitaxy (MBE) and evaluated by transmission electron microscopy (TEM) and photoluminescence (PL). It is found that the morphologies of InAs nanostructures depend strongly on the underlying alloy. Through introducing a lattice-matched underlying InAlGaAs layer on InAlAs buffer layer, the InAs quantum dots (QDs) can be much more uniform in size and great improvement in PL properties can be attained at the same time. In particular, 1.55 mu m luminescence at room temperature (RT) can be realized in InAs QDs deposited on (0 0 1)InP substrate with underlying InAlGaAs layer. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

Long-Wavelength Emission InAs Quantum Dots Grown on InGaAs Metamorphic Buffers

In this work, InAs quantum dots (QDs) grown on a linear graded InGaAs metamorphic buffer layer by molecular beam epitaxy have been investigated. The growth of the metamorphic buffer layers was carefully optimized, yielding a smooth surface with a minimum root mean square of roughness of less than 0.98 nm as measured by atomic force microscopy (AFM). InAs QDs were then grown on the buffer layers, and their emission wavelength at room-temperature is 1.49 mu m as measured by photoluminescence (PL). The effects of post-growth rapid thermal annealing (RTA) on the optical properties of the InAs QDs were investigated. After the RTA, the PL peak of the QDs was blue-shifted and the full width at half maximum decreased.

Tuning of emission wavelength of InAs/GaAs quantum dots sandwiched by combination layers

We investigate about controlling of photoluminescence (PL) wavelengths of InAs/GaAs self-assembled quantum dots (QDs) sandwiched with combination strained-buffer layer (CSBL) and combination strained-reducing layer (CSRL). The emission peak position of QDs is red-shifted to 1.37 mu m. The density of the QDs is increased to 1.17x10(10) cm(-2). It is indicated that optical properties of QDs could be improved by optimizing of the buffer and covering layers for the QDs. These results may provide a new way to further developing GaAs-based 1.3 mu m light sources.

Two-dimensional excitonic emission in InAs submonolayers

Photoluminescence (PL) and time-resolved photoluminescence (TRPL) were used to study optical emissions of ultrathin InAs layers with average layer thickness ranging from 1/12 to 1 ML grown on GaAs substrates. We have found that the inhomogeneous broadening of the PL from InAs layers can be well described by the quantum-well model with InAs islands coupling to each other and being regarded as a quasiwell. From the temperature dependence of the exciton linewidth, the exciton-LO-phonon scattering coefficient was found to be comparable to that in conventional two-dimensional quantum wells. In the TRPL measurements, the PL decay time increases linearly with temperature, which is a typical characteristic of free excitons in quantum wells. All these results indicate that the excitons localized in InAs exhibit two-dimensional properties of quantum wells, despite the topographical islandlike structure.

Stable Temperature Characteristics of InAs/GaAs Quantum Dots at Long Wavelength Emission

The time-resolved photoluminescence and steady photoluminescence (TRPL and PL) spectra on self-assembled InAs/GaAs quantum dots (QDs) are investigated. By depositing GaAs/InAs short period superlattices (SLs), 1. 48 μtm emission is obtained at room temperature. Temperature dependent PL measurements show that the PL intensity of the emission is very steady. It decays only to half as the temperature increases from 15 K to room temperature, while at the same time, the intensity of the other emission decreases by a factor of 5 orders of magnitude. These two emissions are attributed to large-size QDs and short period superlattices (SLs), respectively. Large-size QDs are easier to capture and confine carriers,which benefits the lifetime of PL, and therefore makes the emission intensity insensitive to the temperature.

Strong red light emission from silicon nanocrystals embedded in SIO2 matrix

In this study, silicon nanocrystals embedded in SiO2 matrix were formed by conventional plasma enhanced chemical vapor deposition (PECVD) followed by high temperature annealing. The formation of silicon nanocrystals (nc-Si), their optical and micro-structural properties were studied using various experimental techniques, including Fourier transform infrared spectroscopy, micro-Raman spectra, high resolution transmission electron microscopy and x-ray photoelectron spectroscopy. Very strong red light emission from silicon nanocrystals at room temperature (RT) was observed. It was found that there is a strong correlation between the PL intensity and the substrate temperature, the oxygen content and the annealing temperature. When the substrate temperature decreases from 250degreesC to RT, the PL intensity increases by two orders of magnitude.

Iron related emission spectra in InP

This paper presents a detailed PL study of Fe2+ related four zero-phonon(ZP) lines and their related phonon sidebands. Four zero-phonon transitions at approximate to 2800 cm(-1) along with the accompanying phonon sidebands extending down to 2400 cm(-1). There are ta two prominent regions in the phonon sidebands. One is ascribed to coupling to acoustic-type phonons (2700 cm(-1) region), the other is due to coupling to optic-type phonons (2500 cm(-1) region). Beside broad coupling with lattice modes, there are several groups of lines. They are ascribed to resonant modes, impurities induced gap modes and local modes.

Correlation between Er3+ emission and the microstructure of a-SiOx : H < Er > films

Photoluminescence (PL) from Er-implanted hydrogenated amorphous silicon suboxide (a-SiOX:H(x<2.0)) films was measured. Two luminescence bands with maxima at lambda congruent to 750 nm and lambda congruent to 1.54mum, ascribed to the a-SiOX:H intrinsic emission and Er3+ emission, were observed. Peak intensities of the two bands follow the same trend as a function of annealing temperature from 300 to 1000degreesC. Micro-Raman results indicate that the a-SiOX:H films are a mixture of two phases, an amorphous SiOX matrix and amorphous silicon (a-Si) domains embedded there in. FTIR spectra confirm that hydrogen effusion from a-SiOX:H films occurs during annealing. Hydrogen effusion leads to a reconstruction of the microstructure of a-Si domains, thus having a strong influence on Er3+ emission. Our study emphasizes the role of a-Si domains on Er3+ emission in a-SiOX:H films.

Modification of emission wavelength of self-assembled In(Ga)As/GaAs quantum dots covered by InxGa1-xAs(0 <= x <= 0.3) layer

Red shifts of emission wavelength of self-organized In(Cla)As/GaAs quantum dots (QDs) covered by 3 nm thick InxGa1-xAs layer with three different In mole fractions (x = 0.1, 0.2 and 0.3, respectively) have been observed. Transmission electron microscopy images demonstrate that the stress along growth direction in the InAs dots was reduced due to introducing the InxGa1-xAs (x = 0.1, 0.2 and 0.3) covering layer instead of GaAs layer. Atomic force microscopy pictures show a smoother surface of InAs islands covered by an In0.2Ga0.8As layer. It is explained by the calculations that the redshifts of the photoluminescence (PL) spectra from the QDs covered by the InxGa1-xAs (x greater than or equal to 0.1) layers were mainly due to the reducing of the strain other than the InAs/GaAs intermixing in the InAs QDs. The temperature dependent PL spectra further confirm that the InGaAs covering layer can effectively suppress the temperature sensitivity of PL emissions. 1.3 mum emission wavelength with a very narrow linewidth of 19.2 mcV at room temperature has been obtained successfully from In,In0.5Ga0.5As/GaAs self-assembled QDs covered by a 3-nm In0.2Ga0.2As strain reducing layer. (C) 2001 Elsevier Science B.V. All rights reserved.

Investigation of PL properties of C-doped SiO2/Si samples after high energy Pb ion irradiation

Amorphous SiO2 thin films with about 400-500 nm in thickness were thermally grown on single crystalline silicon. These SiO2/Si samples were firstly implanted at room temperature (RT) with 100 keV carbon ions to 2.0 x 10(17),5.0 X 10(17) or 1.2 x 10(18) ions/cm(2), then irradiated at RT by 853 MeV Pb ions to 5.0 x 10(11), 1.0 X.10(12) 2.0 x 10(12) or 5.0 x 10(12) ions/cm(2), respectively. The variation of photoluminescence (PL) properties of these samples was analyzed at RT using a fluorescent spectroscopy. The obtained results showed that Pb-ion irradiations led to significant changes of the PL properties of the carbon ion implanted SiO2 films. For examples, 5.0 x 10(12) Pb-ions/cm(2) irradiation produced huge blue and green light-emitters in 2.0 x 10(17) C-ions/cm(2) implanted samples, which resulted in the appearance of two intense PL peaks at about 2.64 and 2.19 eV. For 5.0 x 10(17) carbon-ions/cm(2) implanted samples, 2.0 x 10(12) Pb-ions/cm(2) irradiation could induce the formation of a strong and wide violet band at about 2.90 eV, whereas 5.0 x 10(12) Pb-ionS/cm(2) irradiation could,create double peaks of light emissions at about 2.23 and 2.83 eV. There is no observable PL peak in the 1.2 x 10(18) carbon-ions/cm(2) implanted samples whether it was irradiated with Pb ions or not. All these results implied that special light emitters could be achieved by using proper ion implantation and irradiation conditions, and it will be very useful for the synthesis of new type Of SiO2-based light-emission materials.

Structural and PL properties of Cu-doped ZnO films

Cu-doped ZnO films with hexagonal wurtzite structure were deposited on silicon (1 1 1) substrates by radio frequency (RF) sputtering technique. An ultraviolet (UV) peak at similar to 380nm and a blue band centered at similar to 430nm were observed in the room temperature photoluminescent (PL) spectra. The UV emission peak was from the exciton transition. The blue emission band was assigned to the Zn interstitial (Zn-i) and Zn vacancy (V-Zn) level transition. A strong blue peak (similar to 435 nm) was observed in the PL spectra when the alpha(Cu) (the area ratio of Cu-chips to the Zn target) was 1.5% at 100 W, and ZnO films had c-axis preferred orientation and smaller lattice mismatch. The influence of alpha(Cu) and the sputtering power on the blue band was investigated.

High PL-efficiency ZnO nanocrystallites/PPV composite nanofibers

In this paper, we report for the first time on the synthesis of ZnO nanocrystallites in conjugated polymer (PPV) nanofibers by the coupling of the in situ/blend methods and electrospinning. These composite nanofibers were characterized by fluorescence microscopy, atomic force microscope (AFM), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), photoluminescence (PL) spectra, Fourier transform infrared (FT-IR) spectroscopy, and X-ray powder diffraction (XRD).

LaGaO3 : A (A=Sm3+ and/or Tb3+) as promising phosphors for field emission displays

LaGaO3:Sm3+, LaGaO3:Tb3+ and LaGaO3: Sm3+, Tb3+ phosphors were prepared through a Pechini-type sol-gel process. X-Ray diffraction, field emission scanning electron microscopy, photoluminescence (PL), and cathodoluminescence (CL) spectroscopy were utilized to characterize the synthesized phosphors. Under excitation with ultraviolet light (250-254 nm), the LaGaO3: Sm3+, LaGaO3: Tb3+ and LaGaO3: Sm3+, Tb3+ phosphors mainly show the characteristic broadband emission (from 300 to 600 nm with a maximum around 430 nm) of the LaGaO3 host lattice, accompanied by the weak emission of Sm3+ ((4)G(5/2) -> H-6(5/2), H-6(7/2), H-6(9/2) transitions) and/or Tb3+ (D-5(3,4) -> F-7(6,5,4,3) transitions). However, under excitation by low-voltage electron beams (1-3 kV), the LaGaO3: Sm3+, LaGaO3: Tb3+ and LaGaO3: Sm3+, Tb3+ phosphors exhibit exclusively the characteristic emissions of Sm3+ and/or Tb3+ with yellow (Sm3+), blue (Tb3+, with low concentrations) and white (Sm3+ + Tb3+) colors, respectively.