Low threading-dislocation-density Ge film on Si grown on a pitting Ge buffer layer

A Ge layer with a pitting surface can be obtained when the growth temperature is lowered to 290 degrees C. On the low temperature Ge buffer layer with pits, high quality Ge layer was grown at 600 degrees C with a threading dislocation density of similar to 1x10(5)cm(-2). According to channeling and random Rutherford backscattering spectrometry spectra, a chi(min) value of 10% and 3.9% was found, respectively, at the Ge/Si interface and immediately under the surface peak. The root-mean-square surface roughness of Ge film was 0.33nm.

High responsivity ultraviolet photodetector based on crack-free GaN on Si (111)

A Schottky-based metal-semiconductor-metal photodetector is fabricated on 1 mu m-thick, crack-free GaN on Si (I 11) substrate using an optimized AlxGal-xN/AlN complex buffer layer. It exhibits a high responsivity of 4600A/W at 366nm which may be due to both a crack-free sample and high internal gain. The relationship between responsivity and bias voltage is also investigated. The experiment results indicate that the responsivity increases with the bias voltage and shows a tendency to saturate. (c) 2007 WILEY-VCH Verlag GmbH &Co. KGaA, Weinheim.

Photoluminescence mechanism of Si nanocrystals embedded in SiO2 matrix

The interface state recombination effect from the quantum confinement effect in PL signals from the SRO material system was studied. The results show that the larger the size of Si NCs, the more beneficial for the interface state recombination process to surpass the quantum confinement process, in support of Qin's model.

Heavily doped polycrystalline 3C-SiC growth on SiO2/Si(100) substrates for resonator applications

3C-SiC is a promising material for the development of microelectromechanical systems (MEMS) applications in harsh environments. This paper presents the LPCVD growth of heavily nitrogen doped polycrystalline 3C-SiC films on Si wafers with 2.0 mu m-thick silicon dioxide (SiO2) films for resonator applications. The growth has been performed via chemical vapor deposition using SiH4 and C2H4 precursor gases with carrier gas of H-2 in a newly developed vertical CVD chamber. NH3 was used as n-type dopant. 3C-SiC films were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), secondary ion mass spectroscopy (SIMS), and room temperature Hall Effect measurements. It was shown that there is no voids at the interface between 3C-SiC and SiO2. Undoped 3C-SiC films show n-type conduction with resisitivity, Hall mobility, and carrier concentration at room temperature of about 0.56 Omega center dot cm, 54 cm(2)/Vs, and 2.0x 10(17) cm(-3), respectively. The heavily nitrogen doped polycrystalline 3C-SiC with the resisitivity of less than 10(-3) Omega center dot cm was obtained by in-situ doping. Polycrystalline SiC resonators have been fabricated preliminarily on these heavily doped SiC films with thickness of about 2 mu m. Resonant frequency of 49.1 KHz was obtained under atmospheric pressure.

Influence of Al content on electrical and structural properties of Si-doped AlxGa1-xN/GaN HEMT structures

Improved electrical properties of AlxGa1-xN/GaN high electron mobility transistor (HEMT) structures grown by metalorganic chemical vapor deposition (MOCVD) were achieved through increasing the Al mole fraction in the AlGaN barrier layers. An average sheet resistance of 326.6 Omega/sq and a good resistance uniformity of 98% were obtained for a 2-inch Al0.38Ga0 62N/GaN HEMT structure. The surface morphology of AlxGa1-xN/GaN HEMT structures strongly correlates with the Al content. More defects were formed with increasing Al content due to the increase of tensile strain, which limits further reduction of the sheet resistance. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

Optical and structural properties of ZnO films grown on Si(100) substrates by MOCVD - art. no. 60290G

High quality ZnO films have been successfully grown on Si(100) substrates by Metal-organic chemical vapor deposition (MOCVD) technique. The optimization of growth conditions (II-VI ratio, growth temperature, etc) and the effects of film thickness and thermal treatment on ZnO films' crystal quality, surface morphology and optical properties were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), and photoluminescence (PL) spectrum, respectively. The XRD patterns of the films grown at the optimized temperature (300 degrees C) show only a sharp peak at about 34.4 degrees corresponding to the (0002) peak of hexagonal ZnO, and the FWHM was lower than 0.4 degrees. We find that under the optimized growth conditions, the increase of the ZnO films' thickness cannot improve their structural and optical properties. We suggest that if the film's thickness exceeds an optimum value, the crystal quality will be degraded due to the large differences of lattice constant and thermal expansion coefficient between Si and ZnO. In PL analysis, samples all displayed only ultraviolet emission peaks and no observable deep-level emission, which indicated high-quality ZnO films obtained. Thermal treatments were performed in oxygen and nitrogen atmosphere, respectively. Through the analysis of PL spectra, we found that ZnO films annealing in oxygen have the strongest intensity and the low FWHM of 10.44 nm(106 meV) which is smaller than other reported values on ZnO films grown by MOCVD.

Si-based membrane resonant cavity enhanced photodetectors

Si-based membrane RCE photodetectors were introduced. The RCE photodiodes were fabricated on silicon membranes formed from SOI substrate. Compared with the conventional p-i-n photodiode, the responsivity has a threefold enhancement.

Molecular beam epitaxial growth of GaN on 3c-SiC/Si(111) substrates using a thick AIN buffer layer

Hexagonal GaN films (similar to 3 mu m) were grown on 3c-SiC/Si(111) and carbonized Si(111) substrates using a thick AlN buffer Cracks are observed on the surface of the GaN film grown on the carbonized Si(111), while no cracks are visible on the 3c-SiC/Si(111). XRD exhibits polycrystalline nature of the GaN film grown on the carbonized Si(111) due to poorer crystalline quality of this substrate. Raman spectra reveal that all GaN layers are under tensile stress, and the GaN layer grown on 3c-SiC/Si(111) shows a very low stress value of sigma(xx) = 0.65 Gpa. In low-temperature Photoluminescence spectra the remarkable donor-acceptor-pair recombination and yellow band can be attributed to the incorporation of Si impurities from the decomposition of SiC.

The difference of Si doping efficiency in GaN and AlGaN in GaN-based HBT structure

An AlGaN/GaN HBT structure was grown by low-pressure metalorganic chemical vapor deposition (MOCVD) on sapphire substrate. From the high-resolution x-ray diffraction and transmission electron microscopy (TEM) measurements, it was indicated that the structure is of good quality and the AlGaN/GaN interfaces are abrupt and smooth. In order to obtain the values of Si doping and electronic concentrations in the AlGaN emitter and GaN emitter cap layers, Secondary Ion Mass Spectroscopy (SIMS) and electrochemical CV measurements were carried out. The results showed that though the flow rate of silane (SiH4) in growing the AlGaN emitter was about a quarter of that in growing GaN emitter cap and subcollector layer, the Si sputtering yield in GaN cap layer was much smaller than that in the AlGaN emitter layer. The electronic concentration in GaN was about half of that in the AlGaN emitter layer. It is proposed that the Si, Al co-doping in growing the AlGaN emitter layer greatly enhances the Si dopant efficiency in the AlGaN alloy. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

High quality microcrystalline Si films by hydrogen dilution profile

Novel hydrogen dilution profiling (HDP) technique was developed to improve the uniformity in the growth direction of mu c-Si:H thin films prepared by hot wire chemical vapor deposition (HWCVD). It was found that the high H dilution ratio reduces the incubation layer from 30 nm to less than 10 nm. A proper design of hydrogen dilution profiling improves the uniformity of crystalline content, X-c, in the growth direction and restrains the formation of micro-voids as well. As a result the compactness of mu c-Si:H films with a high crystalline content is enhanced and the stability of mu c-Si:H thin film against the oxygen diffusion is much improved. Meanwhile the HDP mu c-Si:H films exhibit the low defect states. The high nucleation density from high hydrogen dilution at early stage is a critical parameter to improve the quality of mu c-Si:H films. (c) 2006 Published by Elsevier B.V.

Morphological defects and uniformity issues of 4H-SiC homoepitaxial layers grown on off-oriented (0001)Si faces

The morphological defects and uniformity of 4H-SiC epilayers grown by hot wall CVD at 1500 degrees C on off-oriented (0001) Si faces are characterized by atomic force microscope, Nomarski optical microscopy, and Micro-Raman spectroscopy. Typical morphological defects including triangular defects, wavy steps, round pits, and groove defects are observed in mirror-like SiC epilayers. The preparation of the substrate surface is necessary for the growth of high-quality 4H-SiC epitaxial layers with low-surface defect density under optimized growth conditions. (c) 2006 Elsevier Ltd. All rights reserved.

Development of current-based microscopic defect analysis method using optical filling techniques for the defect study on heavily irradiated high-resistivity Si sensors/detectors

Current-based microscopic defect analysis method such as current deep level transient spectroscopy (I-DLTS) and thermally stimulated current have been developed over the years at Brookhaven National Laboratory (BNL) for the defect characterizations on heavily irradiated (Phi(n) >= 10(13) n/cm(2)) high-resistivity (>= 2 k Omega cm) Si sensors/detectors. The conventional DLTS method using a capacitance transient is not valid on heavily irradiated high-resistivity Si sensors/detectors. A new optical filling method, using lasers with various wavelengths, has been applied, which is more efficient and suitable than the traditional voltage-pulse filling. Optimum defect-filling schemes and conditions have been suggested for heavily irradiated high-resistivity Si sensors/detectors. (c) 2006 Published by Elsevier Ltd.

Heterojunction solar cells with n-type nanocrystalline silicon emitters on p-type c-Si wafers

Hydrogenated nanocrystalline silicon (nc-Si:H) n-layers have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) wafers. The nc-Si:H n-layers were deposited by radio-frequency (RF) plasma enhanced chemical vapor deposition (PECVD), and characterized using Raman spectroscopy, optical transmittance and activation energy of dark-conductivity. The nc-Si:H n-layers obtained comprise fine grained nanocrystallites embedded in amorphous matrix, which have a wider bandgap and a smaller activation energy. Heterojunction solar cells incorporated with the nc-Si n-layer were fabricated using configuration of Ag (100 nm)/1T0 (80 nm)/n-nc-Si:H (15 nm)/buffer a-Si:H/p-c-Si (300 mu m)/Al (200 nm), where a very thin intrinsic a-Si:H buffer layer was used to passivate the p-c-Si surface, followed by a hydrogen plasma treatment prior to the deposition of the thin nanocrystalline layer. The results show that heterojunction solar cells subjected to these surface treatments exhibit a remarkable increase in the efficiency, up to 14.1% on an area of 2.43 cm(2). (c) 2006 Elsevier B.V. All rights reserved.

Study on surface morphology of GaN growth by MOCVD on GaN/Si(111) template

The surface morphology of GaN grown by MOCVD on GaN/Si template was studied. Rough morphology and deep pinhole defects on some surface areas of the samples were observed and studied. The formation of rough morphology is possibly related to Ga-Si alloy produced due to poor thermal stability of template at high temperature. The deep pinhole defects generated are deep down to the surface of MBE-grown GaN/Si template. The stress originated from the large thermal expansion coefficient difference between GaN and Si may be related to the formation of the pinhole defects. The surface morphology of the GaN can be improved by optimizing the GaN/Si template and decreasing the growth temperature.

Luminescence properties of Er3+ - Doped SiOx films containing amorphous Si nanoparticles

PL properties of Er3+ doped SiOx films containing Si nanoparticles have been studied. Er3+ emission intensity does not depend strongly upon crystallinity of Si clusters. The films can yield efficient Er3+ emission.