Defect Cluster-Induced X-Ray Diffuse Scattering in GaN Films Grown by MOCVD

High-resolution X-ray diffraction has been employed to investigate the diffuse scattering in a (0001) oriented GaN epitaxial film grown on sapphire substrate. The analysis reveals that defect clusters are present in GaN films and their concentration increases as the density of threading dislocations increases. Meanwhile, the mean radius of these defect clusters shows a reverse tendency. This result is explained by the effect of clusters preferentially forming around dislocations, which act as effective sinks for the segregation of point defects. The electric mobility is found to decrease as the cluster concentration increases.

Resonant Raman Scattering and Photoluminescence Emissions from Above Bandgap Levels in Dilute GaAsN Alloy

The transitions of E0 ,E0 ＋A0, and E＋ in dilute GaAs（1-x） Nx alloys with x = 0.10% ,0.22% ,0.36% ,and 0.62% are observed by micro-photoluminescence. Resonant Raman scattering results further confirm that they are from the intrinsic emissions in the studied dilute GaAsN alloys rather than some localized exciton emissions in the GaAsN alloys. The results show that the nitrogen-induced E E＋ and E0 ＋ A0 transitions in GaAsN alloys intersect at a nitrogen content of about 0.16%. It is demonstrated that a small amount of isoelectronic doping combined with micro-photoluminescence allows direct observation of above band gap transitions that are not usually accessible in photoluminescence.

Second-Order Raman Scattering from n- and p-Type 4H-SiC

The results of second-order Raman-scattering experiments on n- and p-type 4H-SiC are presented,covering the acoustic and the optical overtone spectral regions.Some of the observed structures in the spectra are assigned to particular phonon branches and the points in the Brillouin zone from which the scattering originates.There exists a doublet at 626/636cm-1 with energy difference about 10cm-1 in both n- and p-type 4H-SiC,which is similar to the doublet structure with the same energy difference founded in hexagonal GaN,ZnO, and AlN.The cutoff frequency at 1926cm-1 of the second-order Raman is not the overtone of the A1(LO) peak of the n-type doping 4H-SiC,but that of the undoping one.The second-order Raman spectrum of 4H-SiC can hardly be affected by doping species or doping density.

Preparation of Semi-Insulating Material by Annealing Undoped InP

Semi-insulating (SI) InP wafers of 50 and 75mm in diameter can be obtained by annealing of undoped liquid encapsulated Czochralski (LEC) InP at 930 ℃ for 80h. The annealing ambient can be pure phosphorus (PP) or iron phosphide (IP). The IP-SI InP wafers have good electrical parameters and uniformity of whole wafer. However, PP-SI InP wafers exhibit poor uniformity and electrical parameters, Photoluminescence which is subtle to deep defect appears in IP-annealed semi-insulating InP. Traps in annealed SI InP are detected by the spectroscopy of photo-induced current transient. The results indicate that there are fewer traps in IP-annealed undoped SI InP than those in as-grown Fe-doped and PP-undoped SI-undoped SI InP. The formation mechanism of deep defects in annealed undoped InP is discussed.

Annealing ambient controlled deep defect formation in InP

Deep defects in annealed InP have been investigated by deep level transient capacitance spectroscopy (DLTS), photo induced current transient spectroscopy (PICTS) and thermally stimulated current spectroscopy (TSC). Both DLTS results of annealed semiconducting InP and PICTS and TSC results of annealed semi-insulating InP indicate that InP annealed in phosphorus ambient has five defects, while lid? annealed in iron phospbide ambient has two defects. Such a defect formation phenomenon is explained in terms of defect suppression by the iron atom diffusion process. The correlation of the defects and the nature of the defects in annealed InP are discussed based on the results.

Characterization of diphasic nc-Si/a-Si : H thin films and solar cells

Hydrogenated silicon films with diphasic structure have been prepared by using a new regime of plasma enhanced chemical vapor deposition (PECVD) in the region adjacent to the phase transition from amorphous to crystal. line state. The photoelectronic and microstructural properties of the films have been characterized by the constant photocurrent method (CPM), Raman scattering and nuclear magnetic resonance (NMR). In comparison with typical hydrogenated amorphous silicon (a-Si:H), these diphasic films with a crystalline fraction less than 0.3 show a similar optical absorption coefficient, lower deep-defect densities and higher stability upon light soaking. By using the diphasic nc-Si/a-Si films a p-i-n junction solar cell has been prepared With an initial efficiency of 8.51 % and a stabilized efficiency of 8.02 % on an area of 0.126 cm(2) (AM1.5, 100 mW/cm(2)).

Observation of deep electron states in n-type Al-doped ZnS1-xTex grown by molecular beam epitaxy

Deep level transient spectroscopy (DLTS) technique was used to investigate deep electron states in n-type Al-doped ZnS1-xTex epilayers grown by molecular fiction epitaxy (MBE), Deep level transient Fourier spectroscopy (DLTFS) spectra of the Al-doped ZnS1-xTex (x = 0. 0.017, 0.04 and 0.046. respectively) epilayers reveal that At doping leads to the formation of two electron traps at 0.21 and 0.39 eV below the conduction hand. 1)DLTFS results suggest that in addition to the rules of Te as a component of [lie alloy as well as isoelectronic centers, Te is also involved in the formation of all electron trip, whose energy level relative to the conduction hand decreases a, Te composition increases.

Raman scattering and infrared absorption of silicon nanocrystals in silicon oxide matrix

Structural dependence on annealing of a-SiOx:H was studied by using infrared absorption and Raman scattering. The appearance of Raman peaks in the range of 513-519cm(-1) after 1170 degreesC annealing was interpreted as the formation nanocrystalline silicon with the sizes from 3-10nm. The Raman spectra also show the existence of amorphous-like silicon phase, which is associated with Si-Si bond re-construction at boundaries of silicon nanocrystallites. The presence of the shoulder at 980cm(-1) of Si-O-Si stretching vibration at 1085cm(-1) in infrared spectra imply that except that SiO2 phase, there is silicon sub-oxide phase in the films annealed at 1170 degreesC. This sub-oxide phase is located at the interface between Si crystallites and SiO2, and thus support the shell model for the mixed structures of Si grains and SiO2 matrix.

Yellow luminescence mechanism and persistent photoconductivity in n-GaN single crystal films grown on alpha-Al2O3(0001) substrates by LP-MOCVD

Unintentionally doped and Si-doped single crystal n-GaN films have been grown on alpha-Al2O3 (0001) substrates by LP-MOCVD. Room temperature photoluminescence measurement showed that besides the bandedges, the spectrum of an undoped sample was a broad deep-level emission band peaking from 2.19 to 2.30eV, whereas the spectrum for a Si-doped sample was composed of a dominant peak of 2.19eV and a shoulder of 2.32eV. At different temperatures, photoconductance buildup and its decay were also observed for both samples.. The likely origins of persistent photoconductivity and yellow luminescence, which might be associated with deep defects inclusive of either Ga vacancy(V-Ga)/Ga vacancy complex induced by impurities or N antisite (N-Ga), will be proposed.

The role of hydrogen in semi-insulating INP

Complexes of vacancy at indium site with one to four hydrogen atoms and isolated hydrogen or hydrogen dimer and other infrared absorption lines, tentatively be assigned to hydrogen related defects were investigated by FTIR. Hydrogen cam passivate imperfections, thereby eliminating detrimental electronic states from the energy bandgap. Incorporated hydrogen can introduce extended defects and generate electrically-active defects. Hydrogen also can acts as an actuator for creating of antistructure defects. Isolated hydrogen related defects(e.. H-2*) may play an important role in the conversion of the annealed wafers from semiconducting to the semi-insulating behavior. H-2* may be a deep donor, whose energy level is very near the iron deep acceptor level in the energy gap.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Electronic and vibrational Raman scattering in resonance with yellow luminescence transitions in GaN on sapphire substrate

We analyze low-temperature Raman and photoluminescence spectra of MBE-grown GaN layers on sapphire. Strong and sharp Raman peaks are observed in the low frequency region. These peaks, which are enhanced by excitation in resonance with yellow luminescence transitions, are attributed to electronic transitions related to shallow donor levels in hexagonal GaN. It is proposed that a low frequency Raman peak at 11.7 meV is caused by a pseudo-local vibration mode related to defects involved in yellow luminescence transitions. The dependence of the photoluminescence spectra on temperature gives additional information about the residual impurities in these GaN layers.

Size-dependent inelastic behavior of particle-reinforced metal-matrix composites

The strengthening behavior of particle-reinforced metal-matrix composites (MMCp) is primarily attributed to the dislocation strengthening effect and the load-transfer effect. To account for these two effects in a unified way, a new hybrid approach is developed in this paper by incorporating the geometrically necessary dislocation strengthening effect into the incremental micromechanical scheme. By making use of this hybrid approach, the particle-size-dependent inelastic deformation behavior of MMCp is given. Some comparisons with the available experimental results demonstrate that the present approach is satisfactory.

Flame Propagation of H_2-Air in a Semi-Open Obstructed Tube

针对氢／空气混合物,通过实验研究了其预混火焰在半开口管道中的火焰传播加速现象,结果表明,火焰传播状态随着氢气当量比的变化而发生改变。当氢／空气混合物被点燃后,由于障碍物的扰动,火焰在管道中不断加速传播,并最终到达一准稳态传播。在氢气当量比0.31附近时,火焰速度发生跃变。当氢气当量比足够大时,火焰传播由爆燃态转变为爆轰态。在本实验条件下,爆燃转准爆轰的临界条件是d/Lambda>=2.6（d是圆环形障碍物内径,人是爆轰格胞尺度）。障碍物阻塞比的变化对最大火焰速度和压力提升的影响不明显。