Determination of the direct band-gap energy of InAlAs matched to InP by photoluminescence excitation spectroscopy

A series of InxAl1-xAs samples (0.51≪x≪0.55)coherently grown on InP was studied in order to measure the band-gap energy of the lattice matched composition. As the substrate is opaque to the relevant photon energies, a method is developed to calculate the optical absorption coefficient from the photoluminescence excitation spectra. The effect of strain on the band-gap energy has been taken into account. For x=0.532, at 14 K we have obtained Eg0=1549±6 meV

Alloy inhomogeneities in InAlAs strained layers grown by MBE

Transmission electron microscopy studies have been performed to characterize InxAl1−xAs layers grown by molecular beam epitaxy on (100) InP substrates. The first observations of compositional nonuniformities in strained InAlAs layers are reported. The coarse quasiperiodic structure present in each sample has been found to be dependent upon the growth parameters and the sample characteristics.

Determination of the direct band-gap energy of InAlAs matched to InP by photoluminescence excitation spectroscopy

A series of InxAl12xAs samples (0.51,x,0.55) coherently grown on InP was studied in order to measure the band-gap energy of the lattice matched composition. As the substrate is opaque to the relevant photon energies, a method is developed to calculate the optical absorption coefficient from the photoluminescence excitation spectra. The effect of strain on the band-gap energy has been taken into account. For x50.532, at 14 K we have obtained Eg05154966 meV. © 1997 American Institute of Physics.

Caracterización estructural de capas epitaxiadas de InGaAs/InAlAs crecidas sobre substratos (111) de InP

Se ha analizado por microscopía electrónica en transmisión (TEM) la estructura de transistores HEMT basados en un pozo cuántico tensionado de InGaAs/InAlAs crecido sobre un sustrato {111} de InP. Se han observado dislocaciones filiformes y defectos planares que cruzan la capa superior hacia la superficie, así como maclas paralelas a la interficie y grandes complejos defectivos en forma de V que se nuclean unos pocos nanometres por encima de la interficie entre el pozo cuántico y la capa superior que lo confina. La estructura de los defectos es muy diferente de la observada en heteroestructuras similares crecidas sobre sustratos {100}, hecho que sugiere que hay que tener en cuenta consideraciones sobre el proceso mismo de nucleación de los defectos junto con las convencionales relacionadas con el desajuste de redes.

Determination of the direct band-gap energy of InAlAs matched to InP by photoluminescence excitation spectroscopy

A series of InxAl1-xAs samples (0.51≪x≪0.55)coherently grown on InP was studied in order to measure the band-gap energy of the lattice matched composition. As the substrate is opaque to the relevant photon energies, a method is developed to calculate the optical absorption coefficient from the photoluminescence excitation spectra. The effect of strain on the band-gap energy has been taken into account. For x=0.532, at 14 K we have obtained Eg0=1549±6 meV

Electrical transport quantum effects in the In0.53Ga0.47As/In0.52Al0.48As heterostructure on silicon

Electrical transport in a modulation doped heterostructure of In0.53Ga0.47As/In0.52Al0.48As grown on Si by molecular beam epitaxy has been measured. Quantum Hall effect and Subnikov¿De Haas oscillations were observed indicating the two¿dimensional character of electron transport. A mobility of 20¿000 cm2/V¿s was measured at 6 K for an electron sheet concentration of 1.7×1012 cm¿2. Transmission electron microscopy observations indicated a significant surface roughness and high defect density of the InGaAs/InAlAs layers to be present due to the growth on silicon. In addition, fine¿scale composition modulation present in the In0.53Ga0.47As/In0.52Al0.48As may further limit transport properties.

Hydrogen-induced changes in the breakdown voltage of InP HEMTs

In this work, electrical measurements show that the breakdown voltage,BVDG, of InP HEMTs increases following exposure to H2. This BVDG shift is nonrecoverable. The increase in BVDG is found to be due to a decrease in the carrier concentration in the extrinsic portion of the device.We provide evidence that H2 reacts with the exposed InAlAs surface in the extrinsic region next to the gate, changing the underlying carrier concentration. Hall measurements of capped and uncapped HEMT samples show that the decrease in sheet carrier concentration can be attributed to a modification of the exposed InAlAs surface. Consistent with this, XPS experiments on uncapped heterostructures give evidence of As loss from the InAlAs surface upon exposure to hydrogen.

Design and construction of precision heat fluxmeters

InAlAs/InGaAs/InP based high electron mobility transistor devices have been structurally and electrically characterized, using transmission electron microscopy and Raman spectroscopy and measuring Hall mobilities. The InGaAs lattice matched channels, with an In molar fraction of 53%, grown at temperatures lower than 530¿°C exhibit alloy decomposition driving an anisotropic InGaAs surface roughness oriented along [1math0]. Conversely, lattice mismatched channels with an In molar fraction of 75% do not present this lateral decomposition but a strain induced roughness, with higher strength as the channel growth temperature increases beyond 490¿°C. In both cases the presence of the roughness implies low and anisotropic Hall mobilities of the two dimensional electron gas.