Self-formed InGaAs/GaAs quantum dot superlattice and direct observation on strain distribution in the capped superlattice

We have demonstrated a 20 period dislocation-free InGaAs/GaAs quantum dot superlattice which is self-formed by the strain from the superlattice taken as a whole rather than by the strain from the strained single layer. The island formation does not take place while growing the corresponding strained single layer. From the variation of the average dot height in each layer, the strain distribution and relaxation process in the capped superlattice have been examined. It is found that the strain is not uniformly distributed and the greatest strains occur at two interfaces between the superlattice and the substrate and the cap layer in the capped superlattice. (C) 1997 American Institute of Physics.

Photoelectric behaviour of lattice-matched GaAs/AlxGa1-xAs quantum well electrodes

The photoelectric properties of the lattice-matched GaAs/AlxGa1-xAs quantum well electrodes and the influence of the electrode structure such as well width, the thickness of outer barrier and the number of period were studied in a nonaqueous electrolyte. A new kind of structure of multiple quantum well electrode with varied well width, possessing the quantum yield three times that of GaAs bulk materials, was designed and fabricated.

Current oscillations and stable electric field domains in doped GaAs/AlAs superlattices

The crossover between two regimes has been observed in the vertical electric transport of weakly coupled GaAs/AlAs superlattices (SLs). At fixed d.c. bias, the SLs can be triggered by illumination to switch from a regime of temporal current oscillation to the formation of a stable electric field domain. The conversion can be reversed by raising the sample temperature to about 200 K. An effective carrier injection model is proposed to explain the conversion processes, taking into account the contact resistance originating from DX centres in the n(+)-Al0.5Ga0.5As contact layers which is sensitive to light illumination and temperature. In addition, quasiperiodic oscillations have been observed at a particular d.c. bias voltage.

Reflectance-difference spectroscopy study of the Fermi-level position of low-temperature-grown GaAs

The results of a reflectance-difference spectroscopy study of GaAs grown on (100) GaAs substrates by low-temperature molecular-beam epitaxy (LT-GaAs) are presented. In-plane optical anisotropy resonances which come from the linear electro-optic effect produced by the surface electric field are observed. The RDS line shape of the resonances clearly shows that the depletion region of LT-GaAs is indeed extremely narrow (much less than 200 Angstrom). The surface potential is obtained from the RDS resonance amplitude without the knowledge of space-charge density. The change of the surface potential with post-growth annealing temperatures reflects a complicated movement of the Fermi level in LT-GaAs. The Fermi level still moves for samples annealed at above 600 degrees C, instead of being pinned to the As precipitates. This behavior can be explained by the dynamic properties of defects in the annealing process.

Photoluminescence studies on the interaction of near-surface GaAs/AlxGa1-xAs quantum wells with chemical adsorbates

The chemical adsorption of sodium sulphide, ferrocene, hydroquinone and p-methyl-nitrobenzene onto the surface of a GaAs/AlxGa1-xAs multiquantum well semiconductor was characterized by steady state and time-resolved photoluminescence (PL) spectroscopy. The changes in the PL response, including the red shift of the emission peak of the exciton in the quantum well and the enhancement of the PL intensity, are discussed in terms of the interactions of the adsorbed molecules with surface states.

Structural ordering and interface morphology in symmetrically strained (GaIn)As/Ga(PAs) superlattices grown on off-oriented GaAs(100)

In this work we investigate the structural properties of symmetrically strained (GaIn)As/GaAs/Ga(PAs)/GaAs superlattices by means of x-ray diffraction, reciprocal-space mapping, and x-ray reflectivity. The multilayers were grown by metalorganic vapor-phase epitaxy on (001) GaAs substrates intentionally off-oriented towards one of the nearest [110] directions. High-resolution triple-crystal reciprocal-space maps recorded for different azimuth angles in the vicinity of the (004) Bragg diffraction clearly show a double periodicity of the x-ray peak intensity that can be ascribed to a lateral and a vertical periodicity occurring parallel and perpendicular to the growth surface. Moreover, from the intensity modulation of the satellite peaks, a lateral-strain gradient within the epilayer unit cell is found, varying from a tensile to a compressive strain. Thus, the substrate off-orientation promotes a lateral modulation of the layer thickness (ordered interface roughness) and of the lattice strain, giving rise to laterally ordered macrosteps. In this respect, contour maps of the specular reflected beam in the vicinity of the (000) reciprocal lattice point were recorded in order to inspect the vertical and lateral interface roughness correlation, A semiquantitative analysis of our results shows that the interface morphology and roughness is greatly influenced by the off-orientation angle and the lateral strain distribution. Two mean spatial wavelengths can be determined, one corresponding exactly to the macrostep periodicity and the other indicating a further interface waviness along the macrosteps. The same spatial periodicities were found on the surface by atomic-force-microscopy images confirming the x-ray results and revealing a strong vertical correlation of the interfaces up to the outer surface.

Liquid encapsulated-melt zone processing of GaAs

A liquid encapsulated melt Bone process has been developed for single crystal growth of GaAs. Single crystals of 40 mm long have been grown with this technique. To avoid unwanted nucleation events and maintain a constant crystal diameter, from top to bottom growth using a short zone with a convex zone surface was found to give the best results. An arsenic overpressure was used to in conjunction with a B2O3 encapsulant in order to suppress arsenic dissociation from the melt and maintain the stoichiometry of the crystal.

Properties of GaAs single crystals grown by molecular beam epitaxy at low temperatures

Properties of GaAs single crystals grown at low temperatures by molecular beam epitaxy (LTMBE GaAs) have been studied. The results shaw that excessive arsenic atoms of about 10(20) cm(-3) exist in LTMBE GaAs in the form of arsenic interstitial couples, and cause the dilation in lattice parameter of LTMBE GaAs, The arsenic interstitial couples will be decomposed, and the excessive arsenic atoms will precipitate during the annealing above 300 degrees C. Arsenic precipitates accumulate in the junctions of epilayers with the increase in the temperature of annealing. The depletion regions caused by arsenic precipitates overlap each other in LTMBE GaAs, taking on the character of high resistivity, and the effects of backgating or sidegating are effectively restrained.

Assessment of the structural properties of GaAs/Si epilayers using X-ray (004) and (220) reflections

We improved the method previously used to determine the lattice constants and misorientation of GaAs/Si by recording the patterns of X-ray (004) and (220) reflections. The (220) reflection was measured from the (110) cross section of a GaAs/Si epilayer. The structural properties of the GaAs/Si epilayers grown by metal-organic chemical-vapor deposition (MOCVD) using an ultrathin a-Si buffer layer were investigated. The rotation angle of GaAs/Si epilayers grown by MOCVD using an a-Si buffer layer is very small and the lattice constants of these GaAs/Si epilayers agree quite well with elastic theory.

Evidence of Gamma-X sequential resonant tunneling in GaAs/AlAs superlattices

We have studied the sequential resonant tunneling of doped weakly coupled GaAs/AlAs superlattices under hydrostatic pressure up to 4.5 kbar. The pressure coefficient obtained from the experiment, 15.3 meV/kbar, provides a strong evidence for the formation of the electric field domain due to Gamma-X sequential resonant tunneling, At the same time, we have observed the transition between two kinds of sequential resonant tunneling processes within the pressure range from 0 to 4.5 kbar, where the transition pressure between Gamma-Gamma and Gamma-X sequential resonant tunneling is P-t similar to 1.6 kbar. For P < P-t, the electric field domain is formed by Gamma-Gamma sequential resonant tunneling, while for P > P-t, the electric field domain is preferably formed by Gamma-X sequential resonant tunneling. (C) 1996 American Institute of Physics.

Threshold behavior in backgating in GaAs metal-semiconductor field-effect transistors: Induced by limitation of channel-substrate junction to leakage current

An analytical model is proposed to understand backgating in GaAs metal-semiconductor field-effect transistors (MESFETs), in which the effect of channel-substrate (CS) junction is included. We have found that the limitation of CS junction to leakage current will cause backgate voltage to apply directly to CS junction and result in a threshold behavior in backgating effect. A new and valuable expression for the threshold voltage has been obtained. The corresponding threshold electric field is estimated to be in the range of 1000-4000 V/cm and for the first time is in good agreement with reported experimental data. More, the eliminated backgating effect in MESFETs that are fabricated on the GaAs epitaxial layer grown at low temperature is well explained by our theory. (C) 1997 American Institute of Physics.

Characterization of deep centers in AlGaAs/InGaAs/GaAs pseudomorphic HEMT structures grown by molecular beam epitaxy and hydrogen treatment

In AlGaAs/InGaAs/GaAs PM-HEMT structures, the characterization of deep centers, the degradation in electrical and optical properties and their effects on electrical performance of the PM-HEMTs have been investigated by DLTS, SIMS, PL and conventional van der Pauw techniques. The experimental results confirm that the deep level centers correlate strongly with the oxygen content in the AlGaAs layer, the PL response of PM-HEMTs, and the electrical performance of the PM-HEMTs. Hydrogen plasma treatment was used to passivate/annihilate these centers, and the effects of hydrogenation were examined.

Deep centers in AlGaAs/GaAs GRIN-SCH SQW laser structures grown by MBE and MOCVD

The deep centers in AlGaAs/GaAs graded index-separate confinement heterostructure single quantum well (GRIN-SCHSQW) laser structures grown by MBE and MOCVD have been investigated using deep level transient spectroscopy (DLTS) technique, The majority and minority carrier DLTS spectra show that the deep (hole and electron) traps (Hi and E3), having large capture cross sections and concentrations, are observed in the graded n-AlxGa1-xAs layer of laser structures in addition to the well-known DX centers. For laser structures grown by MBE, the deep hole trap H1 and the deep electron trap E3 may be spatially localized in the interface regions of discontinuous variation Al mole fraction of the n-AlxGa1-xAs layer with x = 0.20-0.43. For laser structures grown by MOCVD, the deep electron trap E3 may be spatially localized in the n-AlxGa1-xAs layer with x = 0.18-0.30, and the DX center may be spatially localized in the interface regions of discontinuous variation Al mole fraction of the AlxGa1-xAs layer with x = 0.22-0.30.

An investigation of the formation mechanisms of electric field domains in GaAs/AlAs superlattices

We have studied the vertical transport and formation mechanisms of electric field domains in doped weakly-coupled GaAs/AlAs superlattices. Under hydrostatic pressure two kinds of sequential resonant tunneling are observed within the pressure range from 0 to 4.5 kbar. A transition from Gamma-Gamma to Gamma-X sequential resonant tunneling occurs at P-t approximate to 1.6 kbar. For P < P-t, the high electric field domain is formed by the Gamma-Gamma process, while for P > P-t it is preferentially formed by the Gamma-X process.