Strong visible photoluminescence from amorphous silicon grains in a-SiOx:H films

Two strong luminescence bands were observed from a-SiOx:H in the spectral range of 550-900 nm at room temperature. One is a main broad peak which blueshifts with oxygen content and the other is a shoulder fixed at about 835 nm. In conjunction with TR and micro-Raman spectra, we have proposed that the main band may originate from the amorphous silicon grains embedded in SiOx network, while the shoulder might be due to some defects induced by excess-silicon in these films. (C) 1997 Elsevier Science Ltd.

Microcrystalline silicon films and tandem solar cells prepared by triode PECVD

This paper investigates the effects of the diphasic structure on the optoelectronic properties of hydrogenated microcrystalline silicon (mu c-Si:H) films prepared in a triode three-chamber plasma-enhanced chemical vapor deposition (PECVD) system. The influences of boron-compensation doping on the dark-and photo-conductivity of mu c-Si:H films are also described. A tandem solar cell with an entirely mu c-Si:H p-i-n bottom cell and an a-Si:H top cell has been prepared with an initial conversion efficiency of 8.91% (0.126 cm(2), AM1.5, 100 mW/cm(2)).

Polycrystalline silicon thin films and solar cells prepared by rapid thermal CVD

Polycrystalline silicon (poly-Si) films(similar to 10 mu m) were grown from dichlorosilane by a rapid thermal chemical vapor deposition (RTCVD) technique, with a growth rate up to 100 Angstrom/s at the substrate temperature (T-s) of 1030 degrees C. The average grain size and carrier mobility of the films were found to be dependent on the substrate temperature and material. By using the poly-Si films, the first model pn(+) junction solar cell without anti-reflecting (AR) coating has been prepared on an unpolished heavily phosphorus-doped Si wafer, with an energy conversion efficiency of 4.54% (AM 1.5, 100 mW/cm(2), 1 cm(2)).

Low-temperature (10 K) infrared measurement of interstitial oxygen in heavily antimony-doped silicon via wafer thinning

A new technique is reported for the rapid determination of interstitial oxygen in heavily Sb-doped silicon. This technique includes wafer thinning and low-temperature 10 K infrared measurement on highly thinned wafers. The fine structure of the interstitial oxygen absorption band around 1136 cm(-1) is obtained. Our results show that this method efficiently reduces free-carrier absorption interference, allowing a high reliability of measurement, and can be used at resistivities down to 1 x 10(-2) Omega cm for heavily Sb-doped silicon.

Temperature-stimulated abnormal annealing of neutron-induced damage in high-resistivity silicon detectors

Neutron-irradiated high-resistivity silicon detectors have been subjected to elevated temperature annealing (ETA). It has been found that both detector full depletion voltage and leakage current exhibit abnormal annealing (or ''reverse annealing'') behaviour for highly irradiated detectors: increase with ETA. Laser induced current measurements indicate a net increase of acceptor type space charges associated with the full depletion voltage increase after ETA. Current deep level transient spectroscopy (I-DLTS) and thermally stimulated current (TSC) data show that the dominant effect is the increase of a level at 0.39 eV below the conduction band (E(c) - 0.39 eV) or a level above the valence band (E(v) + 0.39 eV). Candidates tentatively identified for this level are the singly charged double vacancy (V-V-) level at E(c) - 0.39 eV, the carbon interstitial-oxygen interstitial (C-i-O-i) level at E(v) + 0.36 eV, and/or the tri-vacancy-oxygen center (V3O) at E(v) + 0.40 eV.

A transmission electron microscopy study of microstructural defects in proton implanted silicon

The microstructure of silicon on defect layer, a new type of silicon-on-insulator material using proton implantation and two-step annealing to obtain a high resistivity buried layer beneath the silicon surface, has been investigated by transmission electron microscopy. Implantation induced a heavily damaged region containing two types of extended defects involving hydrogen: {001} platelets and {111} platelets. During the first step annealing, gas bubbles and {111} precipitates formed. After the second step annealing, {111} precipitates disappeared, while the bubble microstructure still remained and a buried layer consisting of bubbles and dislocations between the bubbles was left. This study shows that the dislocations pinning the bubbles plays an important role in stabilizing the bubbles and in the formation of the defect insulating layer. (C) 1996 American Institute of Physics.