Growing 20 cm Long DWNTs/TWNTs at a Rapid Growth Rate of 80-90 mu m/s

Submitted by 阎军 (yanj@red.semi.ac.cn) on 2010-04-13T16:03:37Z No. of bitstreams: 1 Growing 20 cm Long DWNTsTWNTs at a Rapid Growth Rate of 80-90 mu ms .pdf: 3229914 bytes, checksum: 0259795afb443dc6901c11df5ecd325a (MD5)

Study of GaN epilayers growth on freestanding Si cantilevers

Five-micron thick freestanding Si cantilevers were fabricated on bulk Si (1 1 1) substrates with surface/bulk micromachining (SBM) process. Then 1-mu m thick GaN layers were deposited on the Si cantilevers by metal-organic chemical vapor deposition (MOCVD). Epilayers on cantilever areas were obtained crack-free, and the photoluminescence (PL) spectra verified the stress reduction and better material quality in these suspended parts of GaN. Back sides of the cantilevers were also covered with GaN layers, which prevented the composite beams from bending dramatically. This paper had proved the feasibility of integrating high-quality GaN epilayers with Si micromechanical structures to realize GaN-based micro electro-mechanical system (MEMS). (C) 2009 Elsevier Ltd. All rights reserved.

An experimental study about the influence of well thickness on the electroluminescence of InGaN/GaN multiple quantum wells

The influence of well thickness on the electroluminescence (EL) of InGaN/GaN multiple quantum wells (MQWs) grown by metalorganic chemical vapor deposition is investigated. It is found that the peak wavelength of EL increases with the increase of well thickness when the latter is located in the range of 3.0-5.1 nm. The redshift is mainly attributed to the quantum confined Stark effect (QCSE). As a contrast, it is found that the EL intensity of InGaN/GaN MQWs increases with the increase of well thickness in spite of QCSE. The result of X-ray diffraction demonstrates that the interface become smoother with the increase of well thickness and suggests that the reduced interface roughness can be an important factor leading to the increase of EL intensity of InGaN/GaN MQWs. (C) 2009 Elsevier B.V. All rights reserved.

Defects in gallium nitride nanowires: First principles calculations

Atomic configurations and formation energies of native defects in an unsaturated GaN nanowire grown along the [001] direction and with (100) lateral facets are studied using large-scale ab initio calculation. Cation and anion vacancies, antisites, and interstitials in the neutral charge state are all considered. The configurations of these defects in the core region and outermost surface region of the nanowire are different. The atomic configurations of the defects in the core region are same as those in the bulk GaN, and the formation energy is large. The defects at the surface show different atomic configurations with low formation energy. Starting from a Ga vacancy at the edge of the side plane of the nanowire, a N-N split interstitial is formed after relaxation. As a N site is replaced by a Ga atom in the suboutermost layer, the Ga atom will be expelled out of the outermost layers and leaves a vacancy at the original N site. The Ga interstitial at the outmost surface will diffuse out by interstitialcy mechanism. For all the tested cases N-N split interstitials are easily formed with low formation energy in the nanowires, indicating N-2 molecular will appear in the GaN nanowire, which agrees well with experimental findings.

Cathodoluminescence study on in composition inhomogeneity of thick InGaN layer

We have investigated the optical properties of thick InGaN film grown on GaN by cathodeluminescence (CL) spectroscopy. It is found that there is obvious In composition variation in both growth and lateral direction of InGaN film. The depth distribution of In composition is closely related to the strain relaxation process of InGaN film. Accompanied with the relaxation of compressive strain, the In composition of InGaN layer increases and the CL peak energy shifts towards red. Moreover, a rather apparent In composition fluctuation is found in the relaxed upper part of InGaN layer as confirmed by CL imaging.

Theoretical analysis and experimental study of the space-charge-screening effect in uni-traveling-carrier photodiode

A new optimized structure of an UTC (uni-traveling-carrier) photodiode is developed and epitaxied by metal-organic chemical vapor deposition. We fabricated a UTC photodiode of 30 mu m in diameter. Theoretical simulation based on drift-diffusion model was used to analyze the space-charge-screening effect in UTC photodiode primarily in two aspects: the carrier concentrations and the space electric field. The simulation results were generally in agreement with the experimental data.

Microstructure and strain analysis of GaN epitaxial films using in-plane grazing incidence x-ray diffraction

This paper investigates the major structural parameters, such as crystal quality and strain state of (001)-oriented GaN thin films grown on sapphire substrates by metalorganic chemical vapour deposition, using an in-plane grazing incidence x-ray diffraction technique. The results are analysed and compared with a complementary out-of-plane x-ray diffraction technique. The twist of the GaN mosaic structure is determined through the direct grazing incidence measurement of (100) reflection which agrees well with the result obtained by extrapolation method. The method for directly determining the in-plane lattice parameters of the GaN layers is also presented. Combined with the biaxial strain model, it derives the lattice parameters corresponding to fully relaxed GaN films. The GaN epilayers show an increasing residual compressive stress with increasing layer thickness when the two dimensional growth stage is established, reaching to a maximum level of -0.89 GPa.

Effects of GaN Capping on the Structural and the Optical Properties of InN Nanostructures Grown by Using MOCVD

InN nanostructures with and without GaN capping layers were grown by using metal-organic chemical vapor deposition. Morphological, structural, and optical properties were systematically studied by using atomic force microscopy, X-ray diffraction (XRD) and temperature-dependent photoluminescence (PL). XRD results show that an InGaN structure is formed for the sample with a GaN capping layer, which will reduce the quality and the IR PL emission of the InN. The lower emission peak at similar to 0.7 eV was theoretically fitted and assigned as the band edge emission of InN. Temperature-dependent PL shows a good quantum efficiency for the sample without a GaN capping layers; this corresponds to a lower density of dislocations and a small activation energy.

Quantitative strain characterization of SiGe heterostructures by high-resolution transmission electron microscopy

We report the quantitative strain characterization in semiconductor heterostructures of silicon-germaniums (Si(0.76)Geo(0.24)) grown on Si substrate by an ultra-high vacuum chemical vapor deposition system. The relaxed SiGe virtual substrate has been achieved by thermal annealing of the SiGe film with an inserted Ge layer. Strain analysis was performed using a combination of high-resolution transmission electron microscopy and geometric phase analysis.

Growth temperature dependences of InN films grown by MOCVD

We investigate the growth temperature dependences of InN films grown by metal organic chemical vapor deposition (MOCVD). Experimental results indicate that growth temperature has a strong effect on the surface morphology, crystalline quality and electrical properties of the InN layer. The increasing growth temperature broadened the v scan's full-width at half-maximum (FWHM) and roughened the surface morphology; whereas the electrical properties improved: As the temperature increased from 460 degrees C to 560 degrees C, room-temperature Hall mobility increased from 98 cm(2)/V s to nearly 800 cm(2)/V s and carrier concentration dropped from 5.29 x 10(19) cm (3) to 0.93 x 10(19) cm (3). The higher growth temperature resulted in more efficient cracking of NH3, which improved Hall mobility and decreased carrier concentration. (C) 2008 Elsevier B.V. All rights reserved.

High Al-content AlInGaN epilayers with different thicknesses grown on GaN/sapphire templates

We studied the structural and optical properties of high Al-content AlInGaN epilayers with different thicknesses grown on GaN/sapphire templates by metalorganic chemical vapor deposition (MOCVD). Direct evidences of the gradual evolution of the content of Al, Ga and In along the growth direction were obtained. When the film thickness was over a certain value, however, the AlInGaN epilayer with constant element contents began to form. These results were also supported by the blue shift and splitting of the photoluminescence (PL) peak. For the thinnest epilayer, the surface was featured with outcrops of threading dislocations (TDs) which suggested a spiral growth mode. With increase in thickness, step-flow growth mode and V-shaped pits were observed, and the steps terminated at the pits. (C) 2008 Elsevier B. V. All rights reserved.

Fracture Properties of LPCVD Silicon Nitride and Thermally Grown Silicon Oxide Thin Films From the Load-Deflection of Long Si3N4 and SiO2/Si3N4 Diaphragms

The bulge test is successfully extended to the determination of the fracture properties of silicon nitride and oxide thin films. This is achieved by using long diaphragms made of silicon nitride single layers and oxide/nitride bilayers, and applying comprehensive mechanical model that describes the mechanical response of the diaphragms under uniform differential pressure. The model is valid for thin films with arbitrary z-dependent plane-strain modulus and prestress, where z denotes the coordinate perpendicular to the diaphragm. It takes into account the bending rigidity and stretching stiffness of the layered materials and the compliance of the supporting edges. This enables the accurate computation of the load-deflection response and stress distribution throughout the composite diaphragm as a function of the load, in particular at the critical pressure leading to the fracture of the diaphragms. The method is applied to diaphragms made of single layers of 300-nm-thick silicon nitride deposited by low-pressure chemical vapor deposition and composite diaphragms of silicon nitride grown on top of thermal silicon oxide films produced by wet thermal oxidation at 950 degrees C and 1050 degrees C with target thicknesses of 500, 750, and 1000 mn. All films characterized have an amorphous structure. Plane-strain moduli E-ps and prestress levels sigma(0) of 304.8 +/- 12.2 GPa and 1132.3 +/- 34.4 MPa, respectively, are extracted for Si3N4, whereas E-ps = 49.1 +/- 7.4 GPa and sigma(0) = -258.6 +/- 23.1 MPa are obtained for SiO2 films. The fracture data are analyzed using the standardized form of the Weibull distribution. The Si3N4 films present relatively high values of maximum stress at fracture and Weibull moduli, i.e., sigma(max) = 7.89 +/- 0.23 GPa and m = 50.0 +/- 3.6, respectively, when compared to the thermal oxides (sigma(max) = 0.89 +/- 0.07 GPa and m = 12.1 +/- 0.5 for 507-nm-thick 950 degrees C layers). A marginal decrease of sigma(max) with thickness is observed for SiO2, with no significant differences between the films grown at 950 degrees C and 1050 degrees C. Weibull moduli of oxide thin films are found to lie between 4.5 +/- 1.2 and 19.8 +/- 4.2, depending on the oxidation temperature and film thickness.

Growth and fabrication of AlGaN/GaN HEMT based on Si(111) substrates by MOCVD

AlGaN/GaN high electron mobility transistor (HEMT) hetero-structures were grown on the 2-in Si (1 1 1) substrate using metal-organic chemical vapor deposition (MOCVD). Low-temperature (LT) AlN layers were inserted to relieve the tension stress during the growth of GaN epilayers. The grown AlGaN/GaN HEMT samples exhibited a maximum crack-free area of 8 mm x 5 mm, XRD GaN (0 0 0 2) full-width at half-maximum (FWHM) of 661 arcsec and surface roughness of 0.377 nm. The device with a gate length of 1.4 mu m and a gate width of 60 mu m demonstrated maximum drain current density of 304 mA/mm, transconductance of 124 mS/mm and reverse gate leakage current of 0.76 mu A/mm at the gate voltage of -10 V. (C) 2008 Published by Elsevier Ltd.

The effect of low temperature AlN interlayers on the growth of GaN epilayer on Si (111) by MOCVD

Low temperature (LT) AlN interlayers were used to effectively reduce the tension stress and micro-cracks on the surface of the GaN epilayer grown on Si (111) substrate. Optical Microscopy (OM), Atomic Force Microscopy (AFM), Surface Electron Microscopy (SEM) and X-Ray Diffraction (XRD) were employed to characterize these samples grown by metal-organic chemical vapor deposition (MOCVD). In addition, wet etching method was used to evaluate the defect of the GaN epilayer. The results demonstrate that the morphology and crystalline properties of the GaN epilayer strongly depend on the thickness, interlayer number and growth temperature of the LT AlN interlayer. With the optimized LT AlN interlayer structures, high quality GaN epilayers with a low crack density can be obtained. (C) 2008 Elsevier Ltd. All rights reserved.

Study of GaN growth on ultra-thin Si membranes

10 mu m-thick ultra-thin Si (111) membranes for GaN epi-layers growth were successfully fabricated on silicon-on-insulator (SOI) substrate by backside etching the handle Si and buried oxide (BOX) layer. Then 1 mu m-thick GaN layers were deposited on these Si membranes by metal-organic chemical vapor deposition (MOCVD). The crack-free areas of 250 mu m, x 250 mu m were obtained on the GaN layers due to the reduction of thermal stress by using these ultra-thin Si membranes, which was further confirmed by the photoluminescence (PL) spectra and the simulation results from the finite element method calculation by using the software of ANSYS. In this paper, a newly developed approach was demonstrated to utilize micromechanical structures for GaN growth, which would improve the material quality of the epi-layers and facilitate GaN-based micro electro-mechanical system (MEMS) fabrication, especially the pressure sensor, in the future applications. (C) 2008 Elsevier Ltd. All rights reserved.