X-Band GaN Power HEMTs with Power Density of 2.23W/mm Grown on Sapphire by MOCVD

The growth,fabrication,and characterization of 0.2μm gate-length AlGaN/GaN HEMTs,with a high mobility GaN thin layer as a channel,grown on (0001) sapphire substrates by MOCVD,are described.The unintentionally doped 2.5μm thick GaN epilayers grown with the same conditions as the GaN channel have a room temperature electron mobility of 741cm2/(V·s) at an electron concentration of 1.52×1016 cm-3.The resistivity of the thick GaN buffer layer is greater than 108Ω·cm at room temperature.The 50mm HEMT wafers grown on sapphire substrates show an average sheet resistance of 440.9Ω/□ with uniformity better than 96%.Devices of 0.2μm×40μm gate periphery exhibit a maximum extrinsic transconductance of 250mS/mm and a current gain cutoff frequency of77GHz.The AlGaN/GaN HEMTs with 0.8mm gate width display a total output power of 1.78W (2.23W/mm) and a linear gain of 13.3dB at 8GHz.The power devices also show a saturated current density as high as 1.07A/mm at a gate bias of 0.5V.

Effects of Thickness on Properties of ZnO Films Grown on Si by MOCVD

High quality ZnO films are successfully grown on Si（100） substrates by metal-organic chemical vapor deposition at 300℃. The effects of the thickness of the ZnO films on crystal structure, surface morphology,and optical properties are investigated using X-ray diffraction, scanning probe microscopy,and photoluminescence spectra, respectively. It is shown that the ZnO films grown on Si substrates have a highly-preferential C-axis orientation,but it is difficult to obtain the better structural and optical properties of the ZnO films with the increasing of thickness. It is maybe due to that the grain size and the growth model are changed in the growth process.

RF-MBE Grown AlGaN/GaN HEMT Structure with High Al Content

A Si doped AlGaN/GaN HEMT structure with high Al content (x= 44%) in the barrier layer is grown on sapphire substrate by RF-MBE. The structural and electrical properties of the heterostructure are investigated by the triple axis X-ray diffraction and Van der Pauw-Hall measurement, respectively. The observed prominent Bragg peaks of the GaN and AlGaN and the Hall results show that the structure is of high quality with smooth interface.fabricated and characterized. Better DC characteristics, maximum drain current of 1.0A/mm and extrinsic transconductance of 218mS/mm are obtained when compared with HEMTs fabricated using structures with lower Al mole fraction in the AlGaN barrier layer. The results suggest that the high Al content in the AlGaN barrier layer is promising in improving material electrical properties and device performance.

Twinning in Low-Temperature MOCVD Grown GaN on (001) GaAs Substrate

GaN buffer layers (thickness ～60nm) grown on GaAs(001) by low-temperature MOCVD are investigated by X-ray diffraction pole figure measurements using synchrotron radiation in order to understand the heteroepitaxial growth features of GaN on GaAs(001) substrates. In addition to the epitaxially aligned crystallites,their corresponding twins of the first and the second order are found in the X-ray diffraction pole figures. Moreover, { 111 } q scans with χ at 55° reveal the abnormal distribution of Bragg diffractions. The extra intensity maxima in the pole fig ures shows that the process of twinning plays a dominating role during the growth process. It is suggested that the polarity of { 111 } facets emerged on (001) surface will affect the growth-twin nucleation at the initial stages of GaN growth on GaAs(001) substrates. It is proposed that twinning is prone to occurring on { 111 } B, N-terminated facets.

High Temperature Characteristics of 3C-SiC/Si Heterojunction Diodes Grown by LPCVD

The high temperature (300～480K) characteristics of the n-3C-SiC/p-Si heterojunction diodes (HJD) fabricated by low-pressure chemical vapor deposition on Si (100) substrates are investigated.The obtained diode with best rectifying properties has 1.8×104 of ratio at room temperature,and slightly rectifying characteristics with 3.1 of rectification ratio is measured at 480K of an ambient temperature .220V of reverse breakdown voltage is acquired at 300K.Capacitance-voltage characteristics show that the abrupt junction model is applicable to the SiC/Si HJD structure and the built-in voltage is 0.75V.An ingenious equation is employed to perfectly simulate and explain the forward current density-voltage data measured at various temperatures.The 3C-SiC/Si HJD represents a promising approach for the fabrication of high quality heterojunction devices such as SiC-emitter heterojunction bipolar transistors.

Characteristics of AlGaN/GaN HEMTs Grown by Plasma-Assisted Molecular Beam Epitaxy

AlGaN/GaN high electron mobility transistor (HEMT) materials are grown by RF plasma-assisted molecular beam epitaxy (RF-MBE) and HEMT devices are fabricated and characterized. The HEMT materials have a mobility of 1035cm~2/(V ? s) at sheet electron concentration of 1.0 * 10~(13)cm~(-2) at room temperature. For the de-vices fabricated using the malt-rials,a maximum saturation drain-current density of 925mA/mm and a peak extrinsic iransecmductance of IHfimS/mm are obtained on devices with gate length and width of l/-im and 80/im respectively. The f_t, unit-current-gain frequency of the devices,is about 18. 8GHz.

Raman Investigatins of 3C-SiC Films Grown on Si (100) and Sapphire (0001) by LPCVD

The Raman measurements have been performed with the back-scattering geometry on the SiC films grown on Si(100) and sapphire (0001) by LPCVD. Typical TO and LO phonon peaks of 3C-SiC were observed for all the samples grown on Si and apphire substrates, indicating the epilayers are 3C-SiC polytype. Using a free-standing 3C-SiC film removed from Si(100) as a free-stress sample, the stresses of 3C-SiC on Si(100) and sapphire (0001) were estimated according to the shift of TO and LO phonons.

Etching Behavior of GaN/GaAs(001) Epilayers Grown by MOVPE

Wet etching characteristics of cubic GAN (c-GaN) thin films grown on GaAs(001) by metalorganic vapor phase epitaxy (MOVPE) are investigated. The samples are etched in HCl, H_3PO_4, KOH aqueous solutions, and molten KOH at temperatures in the range of 90～300 ℃. It is found that different solution produces different etch figure on the surfaces of a sample. KOH-based solutions produce rectangular pits rather than square pits. The etch pits elongate in [1(1-bar)0] direction, indicating asymmetric etching behavior in the two orthogonal <110> directions. An explanation based on relative reactivity of the various crystallographic planes is employed to interpret qualitatively the asymmetric etching behavior. In addition, it is found that KOH aqueous solution would be more suitable than molten KOH and the two acids for the evaluation of stacking faults in c-GaN epilayers.

1.5μm Self-Aligned Spotsize Converter Integrated DFB Fabricated by Selective Area Grown MOVPE

High performance 1.57μm spotsize converter monolithically integrated DFB is fabricated by the technique of self-aligned selective area growth. The upper optical confinement layer and the butt-coupled tapered thickness waveguide are regrown simultaneously, which not only offeres the separated optimization of the active region and the integrated spotsize converter, but also reduces the difficulty of the butt-joint selective regrowth. The threshold current is as low as 4.4mA. The output power at 49mA is 10.1mW. The side mode suppression ratio (SMSR) is 33.2dB. The vertical and horizontal far field divergence angles are as small as 9° and 15° respectively, the 1dB misalignment tolerance are 3.6μm and 3.4μm.

Effects of Growth Conditions on Optical Properties ofGa In NAs/Ga As Quantum Well Grown by Molecular Beam Epitaxy

中科院基金,国家自然科学基金,国家攀登计划

Effects of Rapid Thermal Annealing on OpticalProperties of GaInNAs/ GaAs Single Quantum Well Grown by Plasma- Assisted Molecular Beam Epitaxy

国家自然科学基金,国家攀登计划

Multi-Wavelength InGaAsP Lasers Grown by LP-MOCVD Selective Area Growth

国家863计划

Al_xGa_（1-x）N and GaN/Al_xGa_（1-x）N Quantum Wells Grown by Gas Sourc

于2010-11-23批量导入

Highly conductive nb-doped BaTiO3 epitaxial thin films grown by laser molecular beam epitaxy

于2010-11-23批量导入

Comparison of GexSi1—x Grown by UHV／CVD from Si2H6／GeH4 and SiH4／GeH4

国家自然科学基金