1.3微米高密度量子点结构及其制备方法

Submitted by zhangdi (zhangdi@red.semi.ac.cn) on 2009-06-04T08:36:34Z No. of bitstreams: 1 dspace.cfg: 33388 bytes, checksum: ac9630d3fdb36a155287a049e8b34eb7 (MD5)

1.58 mu m InGaAs quantum well laser on GaAs

We demonstrate the 1.58 mu m emission at room temperature from a metamorphic In0.6Ga0.4As quantum well laser grown on GaAs by molecular beam epitaxy. The large lattice mismatch was accommodated through growth of a linearly graded buffer layer to create a high quality virtual In0.32Ga0.68As substrate. Careful growth optimization ensured good optical and structural qualities. For a 1250x50 mu m(2) broad area laser, a minimum threshold current density of 490 A/cm(2) was achieved under pulsed operation. This result indicates that metamorphic InGaAs quantum wells can be an alternative approach for 1.55 mu m GaAs-based lasers. (C) 2007 American Institute of Physics.

Metamorphic InGaAs Quantum Well Laser Diodes at 1.5 mu on GaAs Grown by Molecular Beam Epitaxy

We report a 1.5-mu m InGaAs/GaAs quantum well laser diode grown by molecular beam epitaxy on InGaAs metamorphic buffers. At 150 K, for a 1500 x 10 mu m(2) ridge waveguide laser, the lasing wavelength is centred at 1.508 mu m and the threshold current density is 667 A/cm(2) under pulsed operation. The pulsed lasers can operate up to 286 K.

Optical matching layer structures in evanescent coupling photodiodes at a wavelength of 1.55 mu m: physics, design and simulation

We have studied the optical matching layers (OMLs) and external quantum efficiency in the evanescent coupling photodiodes (ECPDs) integrating a diluted waveguide as a fibre-to-waveguide coupler, by using the semi-vectorial beam propagation method (BPM). The physical basis of OML has been identified, thereby a general designing rule of OML is developed in such a kind of photodiode. In addition, the external quantum efficiency and the polarization sensitivity versus the absorption and coupling length are analysed. With an optical matching layer, the absorption medium with a length of 30 mu m could absorb 90% of the incident light at 1.55 mu m wavelength, thus the total absorption increases more than 7 times over that of the photodiode without any optical matching layer.

1.55 mu m Ge islands resonant-cavity-enhanced detector with high-reflectivity bottom mirror

A 1.55 mum Ge islands resonant-cavity-enhanced (RCE) detector with high-reflectivity bottom mirror was fabricated by a simple method. The bottom mirror was deposited in the hole formed by anisotropically etching in a basic solution from the back side of the sample with the buried SiO2 layer in silicon-on-insulator substrate as the etch-stop layer. Reflectivity spectrum indicates that the mirror deposited in the hole has a reflectivity as high as 99% in the range of 1.2-1.65 mum. The peak responsivity of the RCE detector at 1543.8 nm is 0.028 mA/W and a full width at half maximum of 5 nm is obtained. Compared with the conventional p-i-n photodetector, the responsivity of RCE detector has a nearly threefold enhancement. (C) 2004 American Institute of Physics.

Fabrication of 1.55-mu m Si-based resonant cavity enhanced photodetectors using sol-gel bonding

In this work, a novel bonding method using silicate gel as the bonding medium was developed to fabricate an InGaAs narrow-band response resonant cavity enhanced photodetector on a silicon substrate. The bonding was performed at a low temperature of 350 degreesC without any special treatment on bonding surfaces and a Si-based narrow-band response InGaAs photodetector was successfully fabricated, with a quantum efficiency of 34.4% at the resonance wavelength of 1.54 mum, and a full-width at half-maximum of about 27 nm. The photodetector has a linear photoresponse up to 4-mW optical power under 1.5 V or higher reverse bias. The low temperature wafer bonding process demonstrates a great potential in device fabrication.

High-indium-content InxGa1-xAs/GaAs quantum wells with emission wavelengths above 1.25 mu m at room temperature

High-indium-content InxGa1-xAs/GaAs single/multi-quantum well (SQW/MQW) structures have been systematically investigated. By optimizing the molecular-beam epitaxy growth conditions, the critical thickness of the strained In0.475Ga0.525As/GaAs QWs is raised to 7 nm, which is much higher than the value given by the Matthews and Blakeslee model. The good crystalline quality of the strained InGaAs/GaAs MQWs is proved by x-ray rocking curves. Photoluminescence measurements show that an emission wavelength of 1.25 mum at room temperatures with narrower full width at half maximum less than 30 meV can be obtained. The strain relaxation mechanism is discussed using the Matthews-Blakeslee model. (C) 2004 American Institute of Physics.

Enhancement of the spectral width of high-power 1.5 mu m integrated superluminescent light source by quantum well intermixing process

A novel type of integrated InGaAsP superluminescent light source was fabricated based on the tilted ridge-waveguide structure with selective-area quantum well (QW) intermixing. The bandgap structure along the length of the device was modified by impurity free vacancy diffusion QW intermixing, The spectral width was broadened from the 16 nm of the normal devices to 37 nm of the QW intermixing enhanced devices at the same output power level. High superluminescent power (210 mW) was obtained under pulsed conditions with a spectral width of 37 nm.

1.55 mu m GaInNAs resonant-cavity-enhanced photodetector grown on GaAs

We report the design, growth, fabrication, and characterization of a GaAs-based resonant-cavity-enhanced (RCE) GaInNAs photodetector operating at 1.55 mu m. The structure of the device was designed using a transfer-matrix method (TMM). By optimizing the molecular-beam epitaxy growth conditions, six GaInNAs quantum wells were used as the absorption layers. Twenty-five (25)- and 9-pair GaAs/AlAs-distributed Bragg reflectors were grown as the bottom and top mirrors. At 1.55 mu m, a quantum efficiency of 33% with a full width at half maximum of 10 nm was obtained. The dark current density was 3x10(-7) A/cm(2) at a bias of 0 V and 4.3x10(-5) A/cm(2) at a reverse bias of 5 V. The primary time response measurement shows that the device has a rise time of less than 800 ps. (c) 2005 American Institute of Physics.

Molecular beam epitaxy growth and photoluminescence study of room temperature 1.31 mu m (InyGa1-yAs/GaAs1-x Sb-x)/ GaAs bilayer quantum wells

Molecular beam epitaxy (MBE) growth of (InyGa1-yAs/GaAs1-xSbx)/GaAs bilayer quantum well (BQW) structures has been investigated. It is evidenced by photo luminescence (PL) that a strong blue shift of the PL peak energy of 47 meV with increasing PL excitation power from 0.63 to 20 mW was observed, indicating type II band alignment of the BQW. The emission wavelength at room temperature from (InyGa1-yAs/GaAs1-xSbx)/GaAs BQW is longer (above 1.2 μ m) than that from InGaAs/GaAs and GaAsSb/GaAs SQW structures (1.1 μ m range), while the emission efficiency from the BQW structures is comparable to that of the SQW. Through optimizing growth conditions, we have obtained room temperature 1.31 μ m wavelength emission from the (InyGa1-yAs/GaAs1-xSbx)/GaAs BQW. Our results have proved experimentally that the GaAs-based bilayer (InyGa1-yAs/GaAs1-xSbx)/GaAs quantum well is a useful structure for the fabrication of near-infrared wavelength optoelectronic devices. © 2005 Elsevier B.V. All rights reserved.

Room temperature 1.25 mu m emission from high indium content InxGa1-xAs/GaAs quantum wells grown by molecular beam epitaxy

Long-wavelength high indium content InxGa1-xAs/GaAs single/multi quantum wells (QWs) structures have been successfully grown by molecular beam epitaxy. It is evidenced by X-ray measurements that the critical thickness of the well width of InxGa1-xAs/GaAs QWs with an indium content x of 47.5% can be raised up to 7nm without strain relation. 1.25μ m photoluminescence (PL) emission is obtained from the QWs with narrower full-width at half maximum (FWHM) less than 30meV. Our results are important basements which are useful for further fabricating GaAs-based long-wavelength devices. © 2005 Elsevier B.V. All rights reserved.

1.55 mu m spot-size converter with monolithically integrated laser diode by conventional process

A novel 1.55 mum laser diode (LD) with monolithically integrated spot-size converter (SSC) is designed and fabricated using conventional photolithography and the chemical wet etching process. For the laser diode, a ridge double-core structure is employed. For the spot-size converter, a buried double-waveguide structure is incorporated. The laterally tapered active core is designed and optically combined with the thin passive core to control the size of the mode. The threshold current was measured to be 40 mA together with high slope efficiency of 0.35 W A(-1). The beam divergence angles in the horizontal and vertical directions were as small as 14.9degrees and 18.2degrees, respectively.

Structural and optical properties of InAs/GaAs quantum dots emitting at 1.5 mu m

We have demonstrated 1.5 mum light emission from InAs quantum dots (QDs) capped with a thin GaAs layer. The extension of the emission wavelength can be assigned to the large QD height. We also investigate the effect of growth interruption on the PL properties and the shape of InAs QDs fabricated by migration-enhanced growth (MEG). Contrary to expectation, we observed a remarkable blueshift of the emission energy with the growth interruption in MEG mode. Detailed investigations reveal that the blueshift is related to the reduced island height with the growth interruption, which is confirmed by reflection high-energy electron diffraction (RHEED) patterns and atomic force microscopy (AFM) measurement results. Accordingly, the structure changes of the islands are interpreted in terms of thermodynamic and kinetic theories. (C) 2004 Elsevier B.V. All rights reserved.

Metamorphic growth of 1.25-1.29 mu m InGaAs quantum well lasers on GaAs by molecular beam epitaxy

We demonstrate 1.25-1.29 mu m metamorphic laser diodes grown on GaAs by molecular beam epitaxy (MBE) using an alloy-graded buffer layer (GBL). Use of Be in the GBL is effective to reduce surface/interface roughness and improves optical quality. The RMS surface roughness of the optimized metamorphic laser is only two atomic monolayers for 1 x 1 mu m(2). Cross-sectional transmission electron microscopy (TEM) images confirm that most dislocations are blocked in the GBL. Ridge waveguide lasers with 4 mu m wide ridge were fabricated and characterized. The average threshold current under the pulsed excitation is in 170-200 mA for a cavity length of 0.9-1.5 mm. This value can be further reduced to about 100 mA by high-reflectivity coating. Lasers can work in an ambient temperature up to at least 50 degrees C. (c) 2006 Elsevier B.V. All rights reserved.

Unselective regrowth of 1.5-mu m InGaAsP multiple-quantum-well distributed-feedback buried heterostructure lasers

Unselective regrowth for fabricating 1.5-mu m InGaAsP multiple-quantum well (MQW) distributed-feedback (DFB) buried heterostructure (BH) lasers is developed. The experimental results exhibit superior characteristics, such as a low threshold of 8.5 mA, high slope efficiency of 0.55 mW/mA, circular-like far-field patterns, the narrow line-width of 2.5 MHz, etc. The high performance of the devices effectively proves the feasibility of the new method to fabricate buried heterostructure lasers. (c) 2006 Society of Photo-Optical Instrumentation Engineers.