Surface characteristics of SiO2-TiO2 strip fabricated by laser direct writing

SiO2-TiO2 sol-gel films are deposited on SiO2/Si by dip-coating technique. The SiO2-TiO2 strips are fabricated by laser direct writing using all ytterbium fiber laser and followed by chemical etching. Surface structures, morphologies and roughness of the films and strips are characterized. The experimental results demonstrate that the SiO2-TiO2 sol-gel film is loose in Structure and a shrinkage concave groove forms if the film is irradiated by laser beam. The surface roughness of both non-irradiated and laser irradiated areas increases with the chemical etching time. But the roughness of laser irradiated area increases more than that of non-irradiated area under the same etching time. After being etched for 28 s, the surface roughness value of the laser irradiated area increases from 0.3 nm to 3.1 nm.

Structure, magnetization, and low-temperature spin dynamic behavior of zincblende Mn-rich Mn(Ga)As nanoclusters embedded in GaAs

We have fabricated a set of samples of zincblende Mn-rich Mn(Ga)As clusters embedded in GaAs matrices by annealing (Ga,Mn)As films with different nominal Mn content at 650 degrees C. For the samples with Mn content no more than 4.5%, the Curie temperature reaches nearly 360 K. However, when Mn content is higher than 5.4%, the samples exhibit a spin-glass-like behavior. We suggest that these different magnetic properties are caused by the competing result of dipolar and Ruderman-Kittel-Kasuya-Yosida interaction among clusters. The low-temperature spin dynamic behavior, especially the relaxation effect, shows the extreme creeping effect which is reflected by the time constant tau of similar to 10(11) s at 10 K. We explain this phenomenon by the hierarchical model based on the mean-field approach. We also explain the memory effect by the relationship between the correlation function and the susceptibility.

Phase-separation suppression in GaN-rich side of GaNP alloys grown by metal-organic chemical vapor deposition

The GaN-rich side of GaNP ternary alloys has been successfully synthesized by light-radiation heating and low-pressure metal-organic chemical vapor deposition. X-ray diffraction (XRD) rocking curves show that the ( 0002) peak of GaNP shifts to a smaller angle with increasing P content. From the GaNP photoluminescence (PL) spectra, the red shifts from the band-edge emission of GaN are determined to be 73, 78 and 100 meV, respectively, in the GaNP alloys with the P contents of 1.5%, 5.5% and 7.5%. No PL peak or XRD peak related to GaP is observed, indicating that phase separation induced by the short-range distribution of GaP-rich regions in the GaNP layer has been effectively suppressed. The phase-separation suppression in the GaNP layer is associated with the high growth rate and the quick cooling rate under the given growth conditions, which can efficiently restrain the accumulation of P atoms in the GaNP layer.

Growth of crack-free GaN films on Si(111) substrate by using Al-rich AlN buffer layer

GaN epilayers were grown on Si(111) substrate by metalorganic chemical vapor deposition. By using the Al-rich AlN buffer which contains Al beyond stoichiometry, crack-free GaN epilayers with 1 mum thickness were obtained. Through x-ray diffraction (XRD) and secondary ion mass spectroscopy analyses, it was found that a lot of Al atoms have diffused into the under part of the GaN epilayer from the Al-rich AlN buffer, which results in the formation of an AlxGa1-xN layer at least with 300 nm thickness in the 1 mum thick GaN epilayer. The Al fraction x was estimated by XRD to be about 2.5%. X-ray photoelectron spectroscopy depth analysis was also applied to investigate the stoichiometry in the Al-rich buffer before GaN growth. It is suggested that the underlayer AlxGa1-xN originated from Al diffusion probably provides a compressive stress to the upper part of the GaN epilayer, which counterbalances a part of tensile stress in the GaN epilayer during cooling down and consequently reduces the cracks of the film effectively. The method using the Al diffusion effect to form a thick AlGaN layer is really feasible to achieve the crack-free GaN films and obtain a high crystal quality simultaneously. (C) 2004 American Institute of Physics.

Effect of SiO2 encapsulation on the nitrogen reorganization in a GaNAs/GaAs single quantum well

Effects of SiO2 encapsulation and rapid thermal annealing on the optical properties of a GaNAs/GaAs single quantum well (SQW) are studied by low-temperature photoluminescence (LTPL). After annealing at 800degreesC for 30s, a blueshift of the LTPL peak energy for the SiO2-capped region is 25meV and that for the bare region is 0.8meV. The results can attribute to the nitrogen reorganization in the GaNAs/GaAs SQW. It is also shown that the nitrogen reorganization can be obviously enhanced by SiO2 cap-layer. A simple model is used to describe the SiO2-enhanced blueshift of the LTPL peak energy. The estimated activation energy of the N atomic reorganization for the samples annealing with and without SiO2 cap-layer are 2.9eV and 3.1eV, respectively.

Sulfur-induced exciton localization in Te-rich ZnSTe alloy

Exciton localization in Te-rich ZnSTe epilayers has been studied by photoluminescence (PL) and time-resolved PL. The sulfur-related exciton emission is found to dominate the radiative recombination at low temperature and is shifted to the low energy with the increase of S concentration. By measuring the PL dependence on temperature and by analyzing the PL decay process, we have clarified the localization nature of the sulfur-related exciton emission. Furthermore, the difference of the localization effect in Te- and S-rich ZnSTe is also compared and discussed. © 2005 American Institute of Physics.

Memory effect in a system of zincblende Mn-rich Mn(Ga)As nanoclusters embedded in GaAs

Zincblende Mn-rich Mn(Ga)As nanoclusters embedded in GaAs matrices are fabricated by in situ postgrowth annealing diluted magnetic semiconductor (Ga,Mn)As films with Mn concentration ranging from 2.6% to 8% at 650 degrees C. Magnetization measurements show that memory effect and slow magnetic relaxation, the typical characteristics of the spin-glass-like phase, occur below the blocking temperature of 45 K in samples with high Mn concentration, while for samples with low Mn concentration, ferromagnetic order remains up to 360 K. The behavior of low-temperature spin dynamics can be explained by the hierarchical model. (c) 2007 American Institute of Physics.

Local environment of Er3+ in Er-doped Si nanoclusters embedded in SiO2 films

The local environment of Er3+ in heavily Er-doped (Er, 2.5 at. %) Si nanoclusters embedded in SiO2 films annealed at various temperatures was investigated by using the fluorescence-extended x-ray absorption fine structure spectroscopy. The results show that annealing caused a large effect on the local environment of Er3+ surrounded by O atoms and the 1.54 mu m photoluminescence intensity. The correlation between the local environment around Er3+ and the corresponding 1.54 mu m photoluminescence was discussed. (c) 2006 American Institute of Physics.

Nonlinear optical response of nc-Si-SiO2 films studied with femtosecond four-wave mixing technique

Nonlinear optical properties of silicon nanocrystals (nc-Si) embedded in SiO2 films are investigated using time-resolved four-wave mixing technique with a femtosecond laser. the off-resonant third-order nonlinear susceptibility chi((3)) is observed to be 1.3 x 10(-10) esu at 800 nm. The relaxation time of the film is fast as short as 50 fs. The off-resonant nonlinearity is predominantly electronic in origin and enhanced due to quantum confinement.

A micromachined SiO2/silicon probe for neural signal recordings

The development of an implantable five channel microelectrode array is presented for neural signal recordings. The detailed fabrication process is outlined with four masked used. The SEM images show that the probe shank is 1.2mm long, 100 mu m wide and 30 mu m thick with the recording sites spaced 200 mu m apart for good signal isolation. The plot of the single recording site impedance versus frequency is shown by test in vitro and the ompedence declines with the increasing frequency. Experiment in vivo using this probe is under way.

Interface effect on emission properties of Er-doped Si nanoclusters embedded in SiO2 prepared by magnetron sputtering

Er-doped Si nanoclusters embedded in SiO2 (NCSO) films were prepared by radio frequency magnetron sputtering on either silicon or quartz substrates. A 1.16 mu m (1.08 eV) photoluminescence (PL) peak was observed from an Er-doped NCSO film deposited on a Si substrate. This 1.16 mu m peak is attributed to misfit dislocations at the NCSO/Si interface. The emission properties of the 1.16 mu m peak and its correlation with the Er3+ emission (1.54 mu m) have been studied in detail. The observed behavior suggests that the excitation mechanism of the 1.16 mu m PL is in a fashion similar to that shown for Er-doped Si nanoclusters embedded in a SiO2 matrix. (C) 2006 American Institute of Physics.

Photoluminesfcence of Er-doped SiO2 films containing Si nanocrystals and Er

Correlations between Si nanocrystal (nc-Si) related photoluminescence (PL), Er3+ emission and nonradiative defects in the Er-doped SiO2 films containing nc-Si (SRSO) are studied. Upon 514.5 nm laser excitation the erbium-doped SRSO samples exhibit PL peaks at around 0.8 and 1.54 mum, which can be assigned to the electron-hole recombination in nc-Si and the intra-4f transition in Er3+, respectively. With increasing Er3+ content in the films, Er3+ emission becomes intense while the PL at 0.8 mum decreases, suggesting a strong coupling of nc-Si and Er 31 ions. Hydrogen plasma treatment for the samples improve the PL intensities of the 0.8 and 1.54 mum bands, indicating H passivation for the nonradiative defects existing in the samples. Further-more, from the effect of hydrogen treatment for the samples, we observe variation of the number of nonradiative defects with annealing temperatures. (C) 2003 Elsevier Science B.V. All rights reserved.

The plasmon resonance absorption of Ag/SiO2 nanocomposite films

The plasmon resonance absorption of the Ag/SiO2 nanocomposite film is investigated. The measured absorption spectra are compared with those calculated by the Mie theory. The results indicate that the Mie theory on the basis of classical electrodynamics can only partially explain the optical absorption spectra of the Ag/SiO2 nanocomposite film. We believe that the plasmon resonance absorption is mainly an intrinsic quality of the metal particle, and can be explained only with the electronic structure of the metal particle. In the latter, surface resonance state is introduced to systematically discuss the optical absorption spectra of the Ag/SiO2 nanocomposite film. (C) 2003 Elsevier Science B.V. All rights reserved.

Influence of coupling between Er3+, nc-Si and nonradiative centers on photoluminescence from Er3+-doped nc-Si/SiO2 films

Con-elation between nc-Si, Er3+ and nonradiative defects in Er-doped nc-Si/SiO2 films is studied. Upon the 514.5 run laser excitation, the samples exhibit a nanocrystal-related spectrum centered at around 750 nm and an Er3+ luminescence line at 1.54mum. With increasing Er3+ content in the films,the Er3+ emission becomes intense while the photoluminescence at 750 nm decreases. Hydrogen passivation of the samples is shown to result in increases of the two luminescence peaks. However, the effect of hydrogen treatment is different for the samples annealed at different temperatures. The experimental results show that the coupling between Er3+, nc-Si and noradiative centers has a great influence on photoluminescence from nc-Si/SiO2 < Er > films.

Pressure behavior of Te isoelectronic centers in S-rich ZnS1-xTex alloy

The photoluminescence from ZnS1-xTex alloy with 0 < x < 0.3 was investigated under hydrostatic pressure up to 7 GPa. Two peaks were observed in the alloys with x < 0.01, which are related to excitons bound to isolated Te isoelectronic impurities (Te-1 centers) and Te pairs (Te-2 centers), respectively. Only the Te-2 related emissions were observed in the alloys with 0.01 < x < 0.03. The emissions in the alloys with 0.03 < x < 0.3 are attributed to the excitons bound to the Te-n (n greater than or equal to 3) cluster centers. The pressure coefficient of the Te-1 related peak is 89(4) meV/GPa, about 40% larger than that of the band gap of ZnS. On the other hand, the pressure coefficient of the Te-2 related emissions is only 52(4) meV/GPa, about 15% smaller than that of the ZnS band gap. A simple Koster-Slater model has been used to explain the different pressure behavior of the Te-1 and Te-2 centers. The pressure coefficient of the Te-3 centers is 62(2) meV/GPa. Then the pressure coefficients of the Te-n centers decrease rapidly with further increasing Te composition.