Optimization of VI/II pressure ratio in ZnTe growth on GaAs(001) by molecular beam epitaxy

ZnTe epilayers were grown on GaAs(0 0 1) substrates by molecular beam epitaxy (MBE) at different VI/II beam equivalent pressure (BEP) ratios (R-VI/II) in a wide range of 0.96-11 with constant Zn flux. Based on in situ reflection high-energy electron diffraction (RHEED) observation, two-dimensional (2D) growth mode can be formed by increasing the R-VI/II to 2.8. The Te/Zn pressure ratios lower than 4.0 correspond to Zn-rich growth state, while the ratios over 6.4 correspond to Te-rich one. The Zn sticking coefficient at various VI/II ratios are derived by the growth rate measurement. The ZnTe epilayer grown at a R-VI/II of 6.4 displays the narrowest full-width at half-maximum (FWHM) of double-crystal X-ray rocking curve (DCXRC) for (0 0 4) reflection. Atomic force microscopy (AFM) characterization shows that the grain size enlarges drastically with the R-VI/II. The surface root-mean-square (RMS) roughness decreases firstly, attains a minimum of 1.14 nm at a R-VI/II of 4.0 and then increases at higher ratios. It is suggested that the most suitable R-VI/II be controlled between 4.0 and 6.4 in order to grow high-quality ZnTe epitaxial thin films.

Molecular beam epitaxy of GaSb on GaAs substrates with AlSb/GaSb compound buffer layers

GaSb films with AlSb/GaSb compound buffer layers were grown by molecular beam epitaxy on GaAs (001) substrates. The crystal quality and optical properties were studied by high resolution transition electron microscopy and low temperature photoluminescence spectra (PL), respectively. It was found that the AlSb/GaSb compound buffer layers can restrict the dislocations into GaSb epilayers. The intensity of PL spectra of GaSb layer becomes large with the increasing the periods of AlSb/GaSb superlattices, indicating that the optical quality of GaSb films is improved.

CONSTRUCTION AND APPLICATIONS OF A DUAL MASS-SELECTED LOW-ENERGY ION-BEAM SYSTEM

A direct ion beam deposition system designed for heteroepitaxy at a low substrate temperature and for the growth of metastable compounds has been constructed and tested. The system consists of two mass-resolved low-energy ion beams which merge at the target with an incident energy range 50-25 000 eV. Each ion beam uses a Freeman ion source for ion production and a magnetic sector for mass filtering. While a magnetic quadrupole lens is used in one beam for ion optics, an electrostatic quadrupole lens focuses the other beam. Both focusing approaches provide a current density more than 100-mu-A/cm2, although the magnetic quadrupole gives a better performance for ion energies below 200 eV. The typical current of each beam reaches more than 0.3 mA at 100 eV, with a ribbon beam of about 0.3-0.5 x 2 cm2. The target is housed in an ultrahigh vacuum chamber with a base pressure of 1 x 10(-7) Pa and a typical pressure of 5 x 10(-6) Pa when a noncondensable beam like argon is brought into the chamber. During deposition, the target can be heated to 800-degrees-C and scanned mechanically with an electronic scanning control unit. The dual beam system has been used to grow GaN using a Ga+ and a N+ beam, and to study the oxygen and hydrogen ion beam bombardment effects during carbon ion beam deposition. The results showed that the simultaneous arrival of two beams at the target is particularly useful in compound formation and in elucidation of growth mechanisms.

Study of GSMBE growth and characteristics of high-quality strained In0.63Ga0.37As/InP quantum wells

High-quality compressively strained In0.63Ga0.37As/InP quantum wells with different well widths (1-11 nm) have been grown coherently on InP substrates using a home-made gas source molecular beam epitaxy (GSMBE) system. The indium composition in the wells of the sample was determined by means of high-resolution X-ray diffraction and its computer simulation. it is found that the exciton transition energies determined by photoluminescence (PL) at 10 K are in good agreement with those calculated using a deformation potential model. Sharp and intense peaks for each well can be well resolved in the 10 K PL spectra. For wells narrower than 4 nm, the line width of the PL peaks are smaller than the theoretical values of the line-width broadening due to 1 hit interface fluctuation, showing that the interface fluctuation of our sample is within 1 ML. For wells of 7 and 9 nm, the PL peak widths are as low as 4.5 meV.

Structural ordering and interface morphology in symmetrically strained (GaIn)As/Ga(PAs) superlattices grown on off-oriented GaAs(100)

In this work we investigate the structural properties of symmetrically strained (GaIn)As/GaAs/Ga(PAs)/GaAs superlattices by means of x-ray diffraction, reciprocal-space mapping, and x-ray reflectivity. The multilayers were grown by metalorganic vapor-phase epitaxy on (001) GaAs substrates intentionally off-oriented towards one of the nearest [110] directions. High-resolution triple-crystal reciprocal-space maps recorded for different azimuth angles in the vicinity of the (004) Bragg diffraction clearly show a double periodicity of the x-ray peak intensity that can be ascribed to a lateral and a vertical periodicity occurring parallel and perpendicular to the growth surface. Moreover, from the intensity modulation of the satellite peaks, a lateral-strain gradient within the epilayer unit cell is found, varying from a tensile to a compressive strain. Thus, the substrate off-orientation promotes a lateral modulation of the layer thickness (ordered interface roughness) and of the lattice strain, giving rise to laterally ordered macrosteps. In this respect, contour maps of the specular reflected beam in the vicinity of the (000) reciprocal lattice point were recorded in order to inspect the vertical and lateral interface roughness correlation, A semiquantitative analysis of our results shows that the interface morphology and roughness is greatly influenced by the off-orientation angle and the lateral strain distribution. Two mean spatial wavelengths can be determined, one corresponding exactly to the macrostep periodicity and the other indicating a further interface waviness along the macrosteps. The same spatial periodicities were found on the surface by atomic-force-microscopy images confirming the x-ray results and revealing a strong vertical correlation of the interfaces up to the outer surface.

GSMBE growth and PL investigation of lattice-matched InGaAs/InP quantum wells

Using a home-made gas-source molecular beam epitaxy system, high quality InGaAs quantum wells with different well widths lattice-matched to a (001) InP substrate have been obtained. Sharp and intense peaks for each well can be well resolved in the PL spectra for the sample. For well widths larger than similar to 60 Angstrom, the exciton energies are in good agreement with those of calculation. For wells narrower than 40 Angstrom, our line widths are below the theoretical values of line width broadening due to one monolayer interface fluctuation, showing that the interface fluctuation of our sample is within one monolayer.

Photoluminescence of GaInP under high pressure

Photoluminescence of GaInP under hydrostatic pressure is investigated. The Gamma valley of disordered GaInP shifts sublinearly upwards with respect to the top of the valence band with increasing pressure and this sublinearity is caused by the nonlinear relationship between lattice constant and hydrostatic pressure. The Gamma valleys of ordered GaInP rise more slowly than that of the disordered one and the relationship between the band gap and the pressure can not be explained in the same way. Taking into account the interactions between the Gamma valley and the folded L valleys, as well as, the X valleys, the experimental pressure dependences of the band gap of ordered GaInP epilayers are calculated and fitted quite well using first order perturbation theory. The results indicate that simultaneous ordering along [111] and [100] directions can occur in ordered GaInP. (C) 1996 American Institute of Physics.

Ordering along <111> and <100> directions in GaInP demonstrated by photoluminescence under hydrostatic pressure

Photoluminescence of GaInP epilayers under hydrostatic pressure is investigated. The Gamma valley of disordered GaInP shifts sublinearly upwards with respect to the top of the valence band with increasing pressure and this sublinearity is caused by the nonlinear dependence of lattice constant on the hydrostatic pressure. The Gamma valleys of ordered GaInP epilayers rise slower than that of the disordered one. Considering the interactions between the Gamma valley and folded L and X valleys, the pressure dependence of the band gap of ordered GaInP is calculated and fitted. The results demonstrate that not only ordering along [111] directions but also sometimes simultaneous ordering along [111] and [100] directions can occur in ordered GaInP. (C) 1996 American Institute of Physics.

OPTICAL AND STRUCTURAL-PROPERTIES OF AP-MOVPE GAINP/GAAS HETEROSTRUCTURES

Lattice matched GaInP/GaAs heterostructures were grown by atmospheric pressure-metal organic vapor phase epitaxy (AP-MOVPE). Compositional intermixing of As/P and Ga/In near the heterointerfaces was studied by photoluminescence (PL) spectroscopy. Indium segregation, memory effect of In into GaAs and the carry-over of As in the GaInP layer during the growth process were considered as three major factors giving rise to the anomalous emissions in the PL spectra. Both thermal annealing and zinc doping strongly enhanced the compositional interdiffusion near the heterointerfaces.

High-performance electroabsorption modulator

A 100-μm-long electroabsorption modulator monolithically integrated with passive waveguides at the input and output ports is fabricated through ion implantation induced quantum well intermixing, using only a two-step low-pressure metal-organic vapor phase epitaxial process. An InGaAsP/InGaAsP intra-step quantum well is introduced to the active region to improve the modulation properties. In the experiment high modulation speed and high extinction ratio are obtained simultaneously, the electrical-to-optical frequency response (E/O response) without any load termination reaches to 22 GHz, and extinction ration is as high as 16 dB.

Graded tensile-strained bulk InGaAs/InP superluminescent diode with very wide emission spectrum

A kind of novel broad-band superluminescent diodes (SLDs) using graded tensile-strained bulk InGaAs is developed. The graded tensile-strained bulk InGaAs is obtained by changing only group-III trimethyl-gallium source flow during low-pressure metal organic vapor-phase epitaxy. At the injection current of 200 mA, the fabricated SLDs with such structure demonstrate full-width at half-maximum spectral width of 106 nm and the output light power of 13.6 mW, respectively.

1.78 μm Strained InGaAs-InGaAsP-InP Distributed Feedback Quantum Well Lasers

Ridge-waveguide distributed-feedback(DFB) lasers with highly strained InGaAs/InGaAsP active regions,emitting at 1.78 μm were fabricated by low pressure metal-organic vapor phase epitaxy(LP-MOVPE) and tested.The lasers exhibited threshold current of 33 mA for 900 μm long cavities at room temperature.A maximum light output power of 8 mW from one facet and an external differential quantum efficiency of 7% were also obtained.In oddition,the side mode suppression ratio (SMSR) is 27.5 dB.

Etching Behavior of GaN/GaAs(001) Epilayers Grown by MOVPE

Wet etching characteristics of cubic GAN (c-GaN) thin films grown on GaAs(001) by metalorganic vapor phase epitaxy (MOVPE) are investigated. The samples are etched in HCl, H_3PO_4, KOH aqueous solutions, and molten KOH at temperatures in the range of 90～300 ℃. It is found that different solution produces different etch figure on the surfaces of a sample. KOH-based solutions produce rectangular pits rather than square pits. The etch pits elongate in [1(1-bar)0] direction, indicating asymmetric etching behavior in the two orthogonal <110> directions. An explanation based on relative reactivity of the various crystallographic planes is employed to interpret qualitatively the asymmetric etching behavior. In addition, it is found that KOH aqueous solution would be more suitable than molten KOH and the two acids for the evaluation of stacking faults in c-GaN epilayers.

MOCVD growth of high quality crack-free GaN on Si(III) substrates

High quality crack free GaN epilayers were grown on Si(111) substrates. Low temperature AlN interlayer grown under low V/III ratio was used to effectively eliminate the formation of micro-cracks. It is found that tensile stress in the GaN epilayer decreases as the N/Al ratio decreases used for AlN interlayer growth. The high optical and structural qualities of the GaN/Si samples were characterized by RBS, PL and XRD measurements. The RT-PL FWHM of the band edge emission is only 39.5meV The XRD FWHM of the GaN/Si sample is 8.2arcmin, which is among the best values ever reported.

Single ridge waveguide electroabsorption modulated DFB laser for 2.5Gb/s transmission

In this paper we proposed a single ridge waveguide electroabsorption modulated distributed feedback laser (EML) for long-haul high-speed optical fiber communication system. This EML was successfully fabricated by two step metal organic vapor phase epitaxy (MOVPE) including selective area growth (SAG) and helium partially implantation. No obvious changes of the threshold current (< 0.2 mA), extinction ratio (< 0.1 dB), output power (< 0.2 dBm) and isolation resistance were achieved in the preliminary aging test. With 2.5 Gb/s NRZ modulation, no power penalty was observed after the optical signal was transmitted through 280 Km normal single mode fiber.