Research on nitrogen implantation energy dependence of the properties of SIMON materials

With different implantation energies, nitrogen ions were implanted into SIMOX wafers in our work. And then the wafers were subsequently annealed to form separated by implantation of oxygen and nitrogen (SIMON) wafers. Secondary ion mass spectroscopy (SIMS) was used to observe the distribution of nitrogen and oxygen in the wafers. The result of electron paramagnetic resonance (EPR) was suggested by the dandling bonds densities in the wafers changed with N ions implantation energies. SIMON-based SIS capacitors were made. The results of the C-V test confirmed that the energy of nitrogen implantation affects the properties of the wafers, and the optimum implantation energy was determined. (c) 2005 Elsevier B.V. All rights reserved.

The transition from Eu3+ to Eu2+ in SiO2(Eu) thin films prepared by ion implantation and co-sputtering

Eu ions doped SiO2 thin films, SiO2( Eu), were prepared by co-sputtering of SiO2 and Eu2O3 and Eu ion implantation into thermally grown SiO2 films. The Eu-L-3-edge X-ray absorption near edge structure (XANES) spectra of SiO2(Eu) films show a doublet absorption peak structure with energy difference of 7 eV, which indicates the conversion of Eu3+ to Eu2+ at high annealing temperature in N-2. The strong blue luminescence of SiO2(Eu) films prepared by ions implantation after films annealed above 1100 degreesC confirms the above argument.

The formation and characteristics of Si1-xCx alloys in Si crystals by means of implantation of cions with different doses

Carbon ions with concentration of (0.6-1.5)% were implanted into silicon crystals at room temperature and Si1-xCx alloys were grown by solid phase epitaxy with high temperature annealing. The formation and characteristics of Si1-xCx alloys under different implanted carbon doses were studied. If the implanted carbon atom concentration was less than 0.6%, carbon atoms would tend to combine with the defects produced during implantation and it was difficult for Si1-xCx alloys to form during annealing at 850-950 degreesC. With the increase of implanted C concentration, almost all implanted carbon atoms would occupy substitution positions to form Si1-xCx alloys, but only part of implanted carbon atoms would occupy the substitution position to form Si1-xCx alloys as the implanted dose increased to 1.5 %. Most Si1-xCx alloy phases would vanish as the annealing temperature was increased higher.

New annealing processes and explanation for novel silicon pn junctions formed by proton implantation

Proton-implanted n-type Si wafers were annealed at 950 degrees C to achieve novel pn junctions. The novel pn junctions are explained by the combined use of four models. The background (e.g. oxygen impurity) of an Si wafer is suggested to play a key role in creating the novel pn junction.

High energy ion implantation enhanced intermixed quantum well structures and their absorption characteristics in passive optical waveguides

We have shown that high energy ion implantation enhanced intermixing (HE-IIEI) technology for quantum well (QW) structures is a powerful technique which can be used to blue shift the band gap energy of a QW structure and therefore decrease its band gap absorption. Room temperature (RT) photoluminescence (PL) and guided-wave transmission measurements have been employed to investigate the amount of blue shift of the band gap energy of an intermixed QW structure and the reduction of band gap absorption, Record large blue shifts in PL peaks of 132 nm for a 4-QW InGaAs/InGaAsP/InP structure have been demonstrated in the intermixed regions of the QW wafers, on whose non-intermixed regions, a shift as small as 5 nm is observed. This feature makes this technology very attractive for selective intermixing in selected areas of an MQW structure. The dramatical reduction in band gap absorption for the InP based MQW structure has been investigated experimentally. It is found that the intensity attenuation for the blue shifted structure is decreased by 242.8 dB/cm for the TE mode and 119 dB/cm for the TM mode with respect to the control samples. Electro-absorption characteristics have also been clearly observed in the intermixed structure. Current-Voltage characteristics were employed to investigate the degradation of the p-n junction in the intermixed region. We have achieved a successful fabrication and operation of Y-junction optical switches (JOS) based on MQW semiconductor optical amplifiers using HE-IIEI technology to fabricate the low loss passive waveguide. (C) 1997 Published by Elsevier Science B.V.

Raman scattering study on diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation

Raman scattering measurements have been performed in diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation, deposition, and post-annealing technique. It is found that the Raman spectrum measured from the implanted surface of the sample shows some new weak modes in addition to the GaAs-like modes which are observed from the unimplanted surface. The new vibrational modes observed are assigned to MnAs-like modes. The coupled LO-phonon plasmon mode, and Mn and As related vibrational modes caused by Mn-ion implantation, deposition, and post-annealing are also observed. Furthermore, the GaAs-like modes are found to be shifted by approximately 4 cm(-1) in the lower frequency side, compared with those observed from the unimplanted surface.

Raman scattering study on vibrational modes in Ga1-xMnxN prepared by Mn-ion implantation

Raman scattering measurements have been carried out on ferromagnetic semiconductor Ga1-xMnxN prepared by Mn-ion implantation and post annealing. The Raman results obtained from the annealed and un-annealed Ga1-xMnxN demonstrate that crystalline quality has been improved in Ga1-xMnxN after annealing. Some new vibrational modes in addition to GaN-like modes are found in the Raman spectra measured from the Ga1-xMnxN where the GaN-like modes are found to be shifted in the higher frequency side than those measured from the bulk GaN. A new vibrational mode observed is assigned to MnN-like mode. Other new phonon modes observed are assigned to disorder-activated modes and Mn-related vibrational modes caused by Mn-ion implantation and post-annealing. (c) 2006 Elsevier Ltd. All rights reserved.

Research on nitrogen implantation energy dependence of the properties of SIMON materials

With different implantation energies, nitrogen ions were implanted into SIMOX wafers in our work. And then the wafers were subsequently annealed to form separated by implantation of oxygen and nitrogen (SIMON) wafers. Secondary ion mass spectroscopy (SIMS) was used to observe the distribution of nitrogen and oxygen in the wafers. The result of electron paramagnetic resonance (EPR) was suggested by the dandling bonds densities in the wafers changed with N ions implantation energies. SIMON-based SIS capacitors were made. The results of the C-V test confirmed that the energy of nitrogen implantation affects the properties of the wafers, and the optimum implantation energy was determined. (c) 2005 Elsevier B.V. All rights reserved.

Effect of the implantation of fluorine on the mobility of channel electron for partially depleted SOI nMOSFET

The mobility of channel electron, for partially depleted Sol nMOSFET in this paper, decreases with the increase of implanted fluorine dose in buried oxide layer. But, the experimental results also show that it is larger for the transistor corresponding to the lowest implantation dose than no implanted fluorine in buried layer. It is explained in tern-is of a "lubricant" model. Mien fluorine atoms are implanted in the top silicon layer, the mobility is the largest. In addition, a positive shift of threshold voltage has also been observed for the transistors fabricated on the Sol wafers processed by the implantation of fluorine. The causes of all the above results are discussed.

Structural and magnetic properties of GaN:Sm:Eu films fabricated by co-implantation method

Diluted-magnetic GaN:Sm:Eu films have been fabricated by co-implantation of Sm and Eu ions into c-plane (0001) GaN films and a subsequent annealing process. The structural, morphological and magnetic characteristics of the samples have been investigated by means of high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM), and superconducting quantum interference device (SQUID). The XRD and AFM analyses show that the annealing process can effectively recover the crystalline degradation caused by implantation. Compared with GaN:Sm films, more defects have been introduced into GaN:Sm:Eu films due to the Eu implantation process. According to the SQUID analysis, GaN:Sm:Eu films exhibit clear room-temperature ferromagnetism. Moreover, GaN:Sm:Eu films show a lower saturation magnetization (Ms) than GaN:Sm films.

RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

INVESTIGATION OF BURIED ALN LAYERS FORMED BY NITROGEN IMPLANTATION INTO AL

The composition and microstructure of buried layers of AlN formed by high energy N+ ion implantation into polycrystalline Al have been determined. Both bulk and evaporated thin films of Al have been implanted with 100 and 200 keV N+ ions to doses of up to 1.8 x 10(18)/cm2. The layers have been characterised using SIMS, XTEM, X-ray diffraction, FTIR, RBS and in terms of their microhardness. It is found that, for doses greater than the critical dose, buried, polycrystalline AlN layers are formed with preferred (100) or (002) orientations, which are sample specific. With increasing dose the nitrogen concentration saturates at the value for stoichiometric AlN although the synthesised compound is found to be rich in oxygen.

REDUCTION OF CRYSTALLINE DISORDER IN MOLECULAR-BEAM EPITAXY GAAS ON SI BY MEV ION-IMPLANTATION AND SUBSEQUENT ANNEALING

Molecular beam epitaxy GaAs films on Si, with thicknesses ranging from 0.9-2.0-mu-m, were implanted with Si ions at 1.2-2.6 MeV to doses in the range 10(15)-10(16) cm-2. Subsequent rapid infrared thermal annealing was carried out at 850-degrees-C for 15 s in a flowing N2 atmosphere. Crystalline quality was analyzed by using Rutherfold backscattering/channeling technique and Raman scattering spectrometry. The experimental results show that the recrystallization process greatly depends on the dose and energy of implanted ions. Complete recrystallization with better crystalline quality can be obtained under proper implantation and subsequent annealing. In the improved layer the defect density was much lower than in the as-grown layer, especially near the interface.

IMPLANTATION ENERGY SELECTION IN MOLECULAR-BEAM EPITAXY GAAS FILMS ON SI SUBSTRATES

GaAs films made by molecular beam epitaxy with thicknesses ranging from 0.9 to 1.25-mu-m on Si have been implanted with Si ions at 1.2 MeV to dose of 1 x 10(15)/cm2. A rapid infrared thermal annealing and white light annealing were then used for recrystallization. Crystalline quality was analysed by using backscattering channeling technique with Li ion beam of 4.2 MeV. The experimental results show that energy selection is important for obtaining better and uniform recrystallized GaAs epilayers.