Small volume laboratory on a chip measurements incorporating the quartz crystal microbalance to measure the viscosity-density product of room temperature ionic liquids

A microfluidic glass chip system incorporating a quartz crystal microbalance (QCM) to measure the square root of the viscosity-density product of room temperature ionic liquids (RTILs) is presented. The QCM covers a central recess on a glass chip, with a seal formed by tightly clamping from above outside the sensing region. The change in resonant frequency of the QCM allows for the determination of the square root viscosity-density product of RTILs to a limit of similar to 10 kg m(-2) s(-0.5). This method has reduced the sample size needed for characterization from 1.5 ml to only 30 mu l and allows the measurement to be made in an enclosed system.

SEM-EDX of morphology of electroless nickel coatings with tin and tungsten

Electroless plating of binary Ni-P, ternary Ni-Sn-P and Ni-W-P, and quaternary Ni-W-Sn-P alloy coatings was carried out in alkalicitrate baths. After the plating, several kinds of test were carried out to determine the improvement in the characteristics and properties due to the additional elements as well as to study the change in behaviour when heat treatment was applied to these coatings. The coatings were subjected to X-ray diffraction analysis where it was found that all the coatings were amorphous. Interesting surface morphology features were examined using scanning electron microscopy. Addition of a third element improved the hardness.

Template-free environmentally friendly synthesis and characterization of unsupported tungsten carbide with a controllable porous framework

Tungsten carbide (WC) with controlled pore size distribution was synthesized using a novel “precursor reassembly” method. The precursor crystal was assembled by mixing ammonium metatungstate (AMT) and ammonium carbonate (AC) in distilled water, followed by hydrothermal treatment. The mesostructure, crystal phase, and amount of deposited graphitic carbon can be conveniently tuned by controlling carburizing atmosphere (CO or a CO/H2 mixture). Moreover, the influence of precursor preparation (AMT/AC mass ratio and hydrothermal temperature) on the materials was also investigated. The resultant materials with low carbon content were mesoporous WCs, which showed high specific surface areas (11.3-20.4 m2 g-1) and adjustable pore-size distributions (average pore size: 15.3-22.3 nm). A mechanism for the formation of WC with a controllable porous framework is proposed. Finally, cyclic voltammetry was used to investigate the inference of different mesoporous structure.

Titania and tungsten doped titania thin films on glass; active photocatalysts

Acidification of an isopropanol solution containing mixtures of [Ti(OPri)(4)] and [W(OEt)(5)] produced solutions from which various TiO2, WO3 and TiO2/WO3 thin films could be obtained by dip coating and annealing. The films were analysed by X-ray diffraction, SEM/EDAX, Raman, electronic spectra, contact angle and photoactivity with respect to destruction of an over layer of stearic acid. The TiO2/WO3 films were shown to be mixtures of two phases TiO2 and WO3 rather than a solid solution TixWyO2. The 2% tungsten oxide doped titania films were shown to be the most effective photocatalysts. All of the TiO2 and TiO2/WO3 films showed light induced superhydrophillicity. (C) 2002 Elsevier Science Ltd. All rights reserved.

Synthesis of mesoporous tungsten carbide-supported platinum and its electrocatalytic activity for methanol oxidation

High activity and stability during oxidation of methanol under the relatively anode environment are two main evaluation criterias for an effective anode electrocatalyst in direct methanol fuel cell (DMFC). Mesoporous WC samples with hollow structure were prepared by gas-solid reaction at the atmosphere of CH(4)/H(2) by using airflow spray dried ammonium metatungstate (AMT). The platinum supported on this material by impregnation-vapor phase deoxidation method served as a less expensive electro anode catalyst. XRD and SEM results showed that Pt particles were well dispersed on the surface of WC. The results showed that the Pt/WC-PME exhibited an attractive catalytic activity, and methanol oxidation process in Pt/WC-PME is affected by liquid-phase mass transfer. The results also indicated that the oxidation can be improved by raising temperatures.