INTERACTION OF CO WITH SI AND SIO2 DURING RAPID THERMAL ANNEALING

The interaction of Co with Si and SiO2 during rapid thermal annealing has been investigated. Phase sequence, layer morphology, and reaction kinetics were studied by sheet resistance, x-ray diffraction, Auger electron spectroscopy, x-ray photoelectron spectroscopy, and scanning electron microscopy. With increasing annealing temperature, Co film on Si(100) is transformed sequentially into Co2Si, CoSi, and finally CoSi2 which corresponds to the minimum of sheet resistance. No evidence of silicide formation was observed for Co/SiO2 annealed even at the high temperature of 1050-degrees-C.

Polycrystalline silicon thin films and solar cells prepared by rapid thermal CVD

Polycrystalline silicon (poly-Si) films(similar to 10 mu m) were grown from dichlorosilane by a rapid thermal chemical vapor deposition (RTCVD) technique, with a growth rate up to 100 Angstrom/s at the substrate temperature (T-s) of 1030 degrees C. The average grain size and carrier mobility of the films were found to be dependent on the substrate temperature and material. By using the poly-Si films, the first model pn(+) junction solar cell without anti-reflecting (AR) coating has been prepared on an unpolished heavily phosphorus-doped Si wafer, with an energy conversion efficiency of 4.54% (AM 1.5, 100 mW/cm(2), 1 cm(2)).

Rapid thermal annealing of arsenic implanted Si1-xGex epilayers

Rapid thermal annealing of arsenic implanted Si1-xGex was studied by secondary ion-mass spectroscopy (SIMS) and spreading resistance probe (SRP) over a wide range of Ge fractions (0-43%). Redistribution of the implanted arsenic was followed as a function of Ge content and annealing temperature. Arsenic concentration profiles from SIMS indicated that the behavior of implanted arsenic in Si1-xGex after RTA was different from that in Si, and the Si1-xGex samples exhibited box-shaped, concentration-dependent diffusion profiles with increasing Ge content. The maximum concentrations of electrically active arsenic in Si1-xGex was found to decrease with increasing Ge content. Experimental results showed that the arsenic diffusion is enhanced with increasing temperature for certain Ge content and strongly dependent on Ge content, and the higher Ge content, the faster As diffusion.

Microstructure studies of PdGe/Ge ohmic contacts to n-type GaAs formed by rapid thermal annealing

A low resistance and shallow ohmic contact to n-GaAs is performed by using Ge/Pd/GaAs trilayer structure and rapid thermal annealing process. The dependence of specific contact resistivity on the temperature of rapid thermal annealing is investigated. A good ohmic contact is formed after annealing at 400-500 degrees C for 60 s. The best specific contact resistivity is 1.4 x 10(-6) Omega cm(2). Auger electron spectroscopy (AES), secondary ion mass spectrometry (SIMS) and scanning electron microscopy (SEM) are used to analyze the interfacial microstructure. A strong correlation between the contact resistance and the film microstructure is observed.

Photoluminescence enhancement of (NH4)(2)S-x passivated InP surface by rapid thermal annealing

Photoluminescence enhancement of (NH4)(2)S-x passivated InP surface followed by rapid thermal annealing (RTA) has been investigated by using photoluminescence (PL), Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), An increase in PL intensity of up to 10 times was observed after sulfur passivation and RTA treatment compared to unpassivated InP surface. XPS measurement results show that introduction of RTA process can enhance the sulfur remaining on the passivated surface to bond to indium but no evidence of S-P bond is noticeable. Passivation enhancement mechanism is discussed.

Photoluminescence and activation on SI-GaAs by Si+ implantation and following rapid thermal annealing

Photoluminescence (PL) and electrical characteristics of SI-GaAs, Si+-implanted and following rapid thermal annealing (RTA), were investigated, The PL spectra of Si-GA-C-As, Ga-i-Si-As, and V-As-Si-As were obtained. This paper concentrates on the PL peak at 1.36 eV which was proven as an emission of the Si-Ga-V-Ga combination by Si+ + P+ dual implantation. The results indicate that the peak at 1.36 eV appears when the ratio of As:Ga increased during the processing. Also high activation was obtained for the sample under the same conditions. More discussion on the mechanism of Si+ implanted SI-GaAs has been made based on the Morrow model [J. Appl. Phys, 64 (1988) 1889].

COMPARISON OF PROPERTIES OF SOLID-PHASE EPITAXIAL SILICON-ON-SAPPHIRE FILMS RECRYSTALLIZED BY RAPID THERMAL ANNEALING AND FURNACE ANNEALING

Chemically vapour deposited silicon on sapphire (SOS) films 0.25 mu m thick were implanted with Si-28(+) and recrystallized in solid phase by furnace annealing (FA) and IR rapid thermal annealing (RTA) in our laboratory. An improvement in crystalline quality can be obtained using both annealing procedures. After FA, it is hard to retain the intrinsic high resistivity value(10(4)-10(5) Ohm cm) observed in as-grown SOS films, so the improvement process cannot be put to practical use effectively. However, it is demonstrated that by properly adjusting the implantation and RTA conditions, significant improvements in both film quality and film autodoping can be accomplished. This work describes a modified double solid phase epitaxy process in which the intrinsic high resistivities of the as grown SOS films are retained. The mechanism of suppression of Al autodoping is discussed.

Effects of Rapid Thermal Annealing on OpticalProperties of GaInNAs/ GaAs Single Quantum Well Grown by Plasma- Assisted Molecular Beam Epitaxy

国家自然科学基金,国家攀登计划

Light induced rapid thermal diffusion of boron atom in silicon

国家自然科学基金

Influence of the rapid thermal annealing on the properties of thin a-Si films

The variation of the structure, morphology and the electrical properties of thin amorphous silicon films caused by Rapid Thermal Annealing is studied. The films annealed at 1200degreesC for 2 minutes change their structure to polycrystalline and as a result their resistivity decreases by 4 orders of magnitude. Due to the small thickness of the as deposited amorphous silicon the obtained poly-Si is strongly irregular and has many discontinuities in its texture.

Selective intermixing of Ga(In)NAs/GaAs quantum well structures usingSiO(2) encapsulation and rapid thermal annealing

The quantum well intermixing of Ga(In)NAs/GaAs simple quantum well (SQW) using SiO2 encapsulation and rapid thermal annealing has been studied. Obvious enhanced intermixing of GaInNAs/GaAs SQW was observed due to the localized SiO2 capping layer and RTA at temperature between 650degreesC and 900degreesC. The selective intermixing strongly depends on N composition and In composition. An obvious selective intermixing had been found in the samples with small N composition and/or high In composition.

Effect of rapid thermal annealing on the Raman spectrum of Si0.33Ge0.67/Si (100) alloy

The effect of thermal annealing on the Raman spectrum of Si0.33Ge0.67 alloy grown on Si (100) by molecular beam epitaxy is investigated in the temperature range of 550-800 degrees C. For annealing below 700 degrees C, interdiffusion at the interface is negligible and the residual strain plays the dominant role in the Raman shift. The strain-shift coefficients for Si-Ge and Ge-Ge phonon modes are determined to be 915 +/- 215 cm(-1) and 732 +/- 117 cm(-1), respectively. For higher temperature annealing, interdiffusion is significant and strongly affects the Raman shift and the spectral shape.

Structural properties of polycrystalline silicon films formed by pulsed rapid thermal processing

A novel pulsed rapid thermal processing (PRTP) method has been used for realizing the solid-phase crystallization of amorphous silicon films prepared by PECVD. The microstructure and surface morphology of the crystallized films are investigated by X-ray diffraction (XRD) and atomic force microscopy (AFM). The results indicate that this PRTP is a suitable post-crystallization technique for fabricating large-area polycrystalline silicon films with good structural qualities such as large grain size, small lattice microstain and smooth surface morphology on low-cost substrate.