Structural properties and Raman measurement of AlN films grown on Si (111) by NH3-GSMBE

Epitaxial growth of AlN has been performed by molecular beam epitaxy (MBE) with ammonia. The structural properties of materials were studied by cross-sectional transmission electron microscopy (TEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). XRD and TEM diffraction pattern confirm the AlN is single crystalline 2H-polytype with the epitaxial relationship of (0001)AlNparallel to(111)Si, [11 (2) over bar0](AlN)parallel to[110](Si), [10 (1) over bar0](AlN)parallel to[11 (2) over bar](Si). Micro-Raman scattering measurement shows that the E-2 (high) and A(1) (LO) phonon mode shift 9 cm(-1) toward the low frequency, which shows the existence of large tensile strain in the AlN films. Furthermore, the appearance of forbidden A, (TO) mode and its anomalous shift toward high frequency was found and explained. (C) 2002 Elsevier Science B.V. All rights reserved.

Depth dependence of the tetragonal distortion of a GaN layer on Si(111) studied by Rutherford backscattering/channeling

Rutherford backscattering and channeling have been used to characterize the structure of a GaN layer grown on a Si(111) substrate. The results show that a 1.26 mum GaN epitaxial layer with a rather abrupt interface and a good crystalline quality (chi(min)=3.4%) can be grown on a Si(111) substrate. Using the channeling angular scan around an off-normal <1 (2) over bar 13> axis in the {10 (1) over bar0} plane of the GaN layer, the tetragonal distortion e(T), which is caused by the elastic strain in the epilayer, can be determined. Moreover, the depth dependence of the e(T) can be obtained using this technique. A fully relaxed (e(T)=0) GaN layer for a thickness <2.8 mum is expected. (C) 2002 American Institute of Physics.

Investigation of GaN layer grown on Si(111) substrate using an ultrathin AlN wetting layer

High-quality GaN epilayers were grown on Si (1 1 1) substrate by metalorganic chemical vapor deposition. The growth process was featured by using an ultrathin AlN wetting layer (WL) in combination with a low-temperature (LT) GaN nucleation layer (NL). The full-width at half-maximum (FWHM) of the X-ray rocking curve for the GaN (0 0 0 2) diffraction was 15 arcmin. The dislocation density estimated from TEM investigation was found to be of the order of 10(9)cm(-2). The FWHM of the dominant band edge emission peak of the GaN was measured to be 47 meV by photoluminescence measurement at room temperature. The ultrathin AlN WL was produced by nitridation of the aluminium pre-covered substrate surface. The reflection high-energy electron diffraction showed that the AlN WL was wurtzite and the surface morphology was like the nitridated surface of sapphire by the atomic force microscopy measurement. X-ray photoelectron spectroscopy measurement showed that Si and SixNy at a certain concentration were intermixed in the AlN WL. This study suggests that by employing an appropriate WL combined with a LT NL, high-quality heteroepitaxy is achievable even with large mismatch. (C) 2002 Elsevier Science B.V. All rights reserved.

Characterization of deep levels in Pt-GaN Schottky diodes deposited on intermediate-temperature buffer layers

Gallium nitride (GaN)-based Schottky junctions were fabricated by RF-plasma-assisted molecular beam epitaxy (MBE). The GaN epitaxial layers were deposited on novel double buffer layers that consist of a conventional low-temperature buffer layer (LTBL) grown at 500 degreesC and an intermediate-temperature buffer layer (ITBL) deposited at 690 degreesC. Low-frequency excess noise and deep level transient Fourier spectroscopy (DLTFS) were measured from the devices. The results demonstrate a significant reduction in the density of deep levels in the devices fabricated with the GaN films grown with an ITBL. Compared to the control sample, which was grown with just a conventional LTBL, a three-order-of-magnitude reduction in the deep levels 0.4 eV below the conduction band minimum (Ec) is observed in the bulk of the thin films using DLTFS measurements.

Investigation of {111}A and {111} planes of c-GaN epilayers grown on GaAs(001) by MOCVD

A determination of {1 1 1}A and {1 1 1}B in cubic GaN(c-GaN) was investigated by X-ray diffraction technique in detail. The c-GaN films are grown on GaAs(0 0 1) substrates by metalorganic chemical vapor deposition(MOCVD). The difference of integrated intensities measured by omega scan for the different order diffractions from {1 1 1}A and {1 1 1}B planes in the four-circle diffractometer gives convincing evidence as to which is the {1 1 1}A and which is the {1 1 1}B planes. The lesser deviation between the ratios of /F-h k l/(2)//F-(h) over bar (k) over bar (l) over bar/(2) and the calculated values after dispersion correction for atomic scattering factor shows that the content of parasitic hexagonal GaN(h-GaN) grown on c-GaN{1 1 1}A planes is higher than that on {1 1 1}B planes. The reciprocal space mappings provide additional proof that the h-GaN inclusions in c-GaN films appear as lamellar structure. (C) 2001 Published by Elsevier Science B.V.

Growth and photoluminescence of epitaxial CeO2 film on Si (111) substrate

A CeO2 film with a thickness of about 80nm was deposited by a mass-analysed low-energy dual ion beam deposition technique on an Si(111) substrate. Reflection high-energy electron diffraction and x-ray diffraction measurements showed that the film is a single crystal. The tetravalent state of Ce in the film was confirmed by x-ray photoelectron spectroscopy measurements, indicating that stoichiometric CeO2 was formed. Violet/blue light emission (379.5 nm) was observed at room temperature, which may be tentatively explained by charge transitions from the 4f band to the valence band of CeO2.

Growth mode and strain relaxation of InAs on InP (111)A grown by molecular beam epitaxy

Growth mode and strain relaxation of molecular-beam-epitaxy grown InAs/InAlAs/InP (111)A system have been investigated using reflection high-energy electron diffraction, transmission electron microscopy, atomic force microscopy, and photoluminescence measurements. In direct contrast to the well-studied InAs/GaAs system, our experimental results show that the InAs grown on InAlAs/InP (111)A follows the Stranski-Krastanov mode. Both self-organized InAs quantum dots and relaxed InAs islands are formed depending on the InAs coverage. Intense luminescence signals from both the InAs quantum dots and wetting layer are observed. The luminescence efficiency of (111)A samples is comparable to that of (001) samples, suggesting the feasibility of fabricating quantum dot optoelectronic devices on InP (111)A surfaces. (C) 1999 American Institute of Physics. [S0003-6951(99)01010-4].

MOVPE growth of GaN and LED on (111) MgAl2O4

The growth of wurtzite GaN by low-pressure metalorganic vapor-phase epitaxy on (1 1 1) magnesium aluminate (MgAl2O4) substrates have been studied. The morphological, crystalline, electrical and optical properties are investigated. A p-n junction GaN LED was fabricated on the MgAl2O4 substrate. (C) 1998 Elsevier Science B.V. All rights reserved.

Hydrogen sensors based on Pt-AlGaN/GaN back-to-back Schottky diode

In this paper, platinum (Pt) with a thickness of 45 nm was sputtered on the surface of AlGaN/GaN heterostructure to form the Schottky contact and the back-to-back Schottky diodes were characterized for H-2 sensing at room temperature. Both the forward and reverse current of the devices increased with exposure to H-2 gas, which was attributed to Schottky barrier height reduction caused by hydrogen absorption in the catalytic metals. A shift of 0.7 V at 297 K was obtained at a fixed forward current of 0.1 mA after switching from N-2 to 40% H-2 in N-2. The sensor's responses under different concentrations from 2500 ppm H-2 to 40% H-2 in N-2 at 297 K were investigated. Time response of the sensor at a fixed bias of 1 V was given. Finally, the decrease of the Schottky barrier height and the sensitivity of the sensor were calculated. (C) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Hydrogen sensors based on Pt-AlGN/AIN/GaN Schottky diode - art. no. 68291R

Pt/AlGaN/AlN/GaN Schottky diodes have been fabricated and characterized for H-2 sensing. Platinum (Pt) with a thickness of 20nm was evaporated on the sample to form the Schottky contact. The ohmic contact, formed by evaporated Ti/Al/Ni/Au metals, was subsequently annealed by a rapid thermal treatment at 860 degrees C for 30 s in N-2 ambience. Both the forward and reverse current of the device increased greatly when exposed to H-2 gas. The sensor's responses under different hydrogen concentrations from 500ppm to 10% H-2 in N-2 at 300K were investigated. A shift of 0.45V at 297K is obtained at a fixed forward current for switching from N-2 to 10% H-2 in N-2. Time response of the sensor at a fixed bias of 0.5 V was also measured. The turn-on response of the device was rapid, while the recovery of the sensor at N-2 atmosphere was rather slow. But it recovered quickly when the device was exposed to the air. The decrease in the barrier height of the diode was calculated to be about 160meV upon introduction of 10% H-2 into the ambient. The sensitivity of the sensor is also calculated. Some thermodynamics analyses have been done according to the Langmuir isotherm equation.

Heteroepitaxial Growth of 3C-SiC on Si (111) Substrate using AlN as a Buffer Layer

Using AlN as a buffer layer, 3C-SiC film has been grown on Si substrate by low pressure chemical vapor deposition (LPCVD). Firstly growth of AlN thin films on Si substrates under varied V/III ratios at 1100 degrees was investigated and the (002) preferred orientational growth with good crystallinity was obtained at the V/III ratio of 10000. Annealing at 1300 degrees C indicated the surface morphology and crystallinity stability of AlN film. Secondly the 3C-SiC film was grown on Si substrate with AlN buffer layer. Compared to that without AlN buffer layer, the crystal quality of the 3C-SiC film was improved on the AlN/Si substrate, characterized by X-ray diffraction (XRD) and Raman measurements.

High responsivity ultraviolet photodetector based on crack-free GaN on Si (111)

A Schottky-based metal-semiconductor-metal photodetector is fabricated on 1 mu m-thick, crack-free GaN on Si (I 11) substrate using an optimized AlxGal-xN/AlN complex buffer layer. It exhibits a high responsivity of 4600A/W at 366nm which may be due to both a crack-free sample and high internal gain. The relationship between responsivity and bias voltage is also investigated. The experiment results indicate that the responsivity increases with the bias voltage and shows a tendency to saturate. (c) 2007 WILEY-VCH Verlag GmbH &Co. KGaA, Weinheim.

Molecular beam epitaxial growth of GaN on 3c-SiC/Si(111) substrates using a thick AIN buffer layer

Hexagonal GaN films (similar to 3 mu m) were grown on 3c-SiC/Si(111) and carbonized Si(111) substrates using a thick AlN buffer Cracks are observed on the surface of the GaN film grown on the carbonized Si(111), while no cracks are visible on the 3c-SiC/Si(111). XRD exhibits polycrystalline nature of the GaN film grown on the carbonized Si(111) due to poorer crystalline quality of this substrate. Raman spectra reveal that all GaN layers are under tensile stress, and the GaN layer grown on 3c-SiC/Si(111) shows a very low stress value of sigma(xx) = 0.65 Gpa. In low-temperature Photoluminescence spectra the remarkable donor-acceptor-pair recombination and yellow band can be attributed to the incorporation of Si impurities from the decomposition of SiC.

Study on surface morphology of GaN growth by MOCVD on GaN/Si(111) template

The surface morphology of GaN grown by MOCVD on GaN/Si template was studied. Rough morphology and deep pinhole defects on some surface areas of the samples were observed and studied. The formation of rough morphology is possibly related to Ga-Si alloy produced due to poor thermal stability of template at high temperature. The deep pinhole defects generated are deep down to the surface of MBE-grown GaN/Si template. The stress originated from the large thermal expansion coefficient difference between GaN and Si may be related to the formation of the pinhole defects. The surface morphology of the GaN can be improved by optimizing the GaN/Si template and decreasing the growth temperature.