The role of Sb in the molecular beam epitaxy growth of 1.30-1.55 mu m wavelength GaInNAs/GaAs quantum well with high indium content

Sb-assisted GaInNAs/GaAs quantum wells (QWs) with high (42.5%) indium content were investigated systematically. Transmission electron microscopy, reflection high-energy electron diffraction and photoluminescence (PL) measurements reveal that Sb acts as a surfactant to suppress three-dimensional growth. The improvement in the 1.55 mu m range is much more apparent than that in the 1.3 mu m range.. which can be attributed to the difference in N composition. The PL intensity and the full-width at half maximum of the 1.55 mu m single-QW were comparable with that of the 1.3 Am QWs. (c) 2006 Elsevier B.V. All rights reserved.

Influence of growth parameters of frequency-radio plasma nitrogen source on extending emission wavelengths from 1.31 mu m to 1.55 mu m GaInNAs/GaAs quantum wells grown by molecular-beam epitaxy

High (42.5%) indium content GaInNAs/GaAs quantum wells with room temperature emission wavelength from 1.3 mu m to 1.5 mu m range were successfully grown by Radio Frequency Plasma Nitrogen source assisted Molecular Beam Epitaxy. The growth parameters of plasma power and N-2 How rate were optimized systematically to improve the material quality. Photoluminescence and transmission electron microscopy measurements showed that the optical and crystal quality of the 1.54 mu m GaInNAs/GaAs QWs was kept as comparable as that in 1.31 mu m.

Post-growth and in situ annealing on GaInNAs(Sb) and their application in 1.55 mu m lasers

Rapid thermal annealing (RTA) has been demonstrated as an important way to improve the crystal quality of GaInNAs(Sb)/GaAs quantum wells. However little investigation has been made into their application in laser growth, especially at a wavelength of 1.55 mu m. When a GaAs-based laser is grown, AlGaAs is usually used for cladding layers. The growth of the p-cladding layer usually takes 30-45 min at a growth temperature higher than that of the GaInNAs(Sb) active region, which affects the material quality. To investigate this effect, various post-growth annealing processes were performed to simulate this process. Great enhancement of the PL intensity was obtained by a two-step process which consisted of annealing first at 700 degrees C for 60 s and then at 600 degrees C for 45 min. We transferred this post-growth annealing to in situ annealing. Finally, a GaInNAsSb laser was grown with a 700 degrees C in situ annealing process. Continuous operation at room temperature of a GaAs-based dilute nitride laser with a wavelength beyond 1.55 mu m was realized for the first time.

1.55-mu m Ridge DFB laser and electroabsorption modulator integrated with buried-ridge-stripe dual-waveguide spot-size converter output

A 1.55-mu m ridge distributed feedback laser and electroabsorption modulator monolithically integrated with a buried-ridge-stripe dual-waveguide spot-size converter (SSC) at the output port for low-loss coupling to a cleaved single-mode optical fiber was fabricated by means of selective area growth, quantum-well intermixing, and dual-core technologies. These devices exhibit threshold current of 28 mA, 3-dB modulation bandwidth of 12.0 GHz, modulator extinction ratios of 25.0-dB dc. The output beam divergence angles of the SSC in the horizontal and vertical directions are as small as 8.0 degrees x 12.6 degrees, respectively, resulting in 3.2-dB coupling loss with a cleaved single-mode optical fiber.

Fabrication of Ge nano-dot heterojunction phototransistors for improved light detection at 1.55 mu m

Heterojunction phototransistors (HPTs) with several Ge/Si nano-dot layers as the absorption region are fabricated to obtain improved light detectivity at 1.55 mu m. The HPT detectors are of n-p-n type with ten layers of Ge(8ML)/Si(45nm) incorporated in the base-collector junction and are grown by an ultrahigh-vacuum chemical-vapor deposition system. The detectors are operated with normal incidence. Because of the good quality of the grown material and fabrication process, the dark current is only 0.71pA/mu m(2) under 5 V bias and the break-down voltage is over 20 V. Compared to the positive-intrinsic-negative (PIN) reference detector with the same absorption layer, the responsivity is improved over 17 times for normal incidence at 1.55 mu m.

High performance of 1.55 mu m DFB integrated with vertically tapered self-aligned spot-size converter

A new type of self-aligned spotsize converter (SSC) integrated 1.55 mum DFB lasers had been proposed in this article. The upper optical confinement layer and the butt-coupled tapered thickness waveguide were regrown simultaneously, which not only offered the separate optimization of the active region and the integrated SSC, but also reduced the difficulty of the butt-joint selective regrowth. The vertical and horizontal far field angles were 9degrees and 12degrees respectively, the 1- dB misalignment tolerance were both 3.6 and 3.4 mum. The directed coupling efficiency to tapered single mode fiber was 48%.

Room temperature 1.55 mu m emission from InAs quantum dots grown on (001)InP substrate by molecular beam epitaxy

Self-assembled InAs nanostructures on (0 0 1)InP substrate have been grown by molecular beam epitaxy (MBE) and evaluated by transmission electron microscopy (TEM) and photoluminescence (PL). It is found that the morphologies of InAs nanostructures depend strongly on the underlying alloy. Through introducing a lattice-matched underlying InAlGaAs layer on InAlAs buffer layer, the InAs quantum dots (QDs) can be much more uniform in size and great improvement in PL properties can be attained at the same time. In particular, 1.55 mu m luminescence at room temperature (RT) can be realized in InAs QDs deposited on (0 0 1)InP substrate with underlying InAlGaAs layer. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

1.55-mu m resonant cavity enhanced photodiode based on MBE grown Ge quantum dots

Self-assembly Ge quantum dots (QD) on Si and Si/Ge mutli-quantum-wells (MQW) are grown by MBE. The island size and island density was investigated by atomics force microscopy. Ten-layer and twenty-layer MQW were selected for photodiode device fabrication. In photoluminescence (PL), a broad peak around 1.55-mu m wavelength was observed with higher peak intensity for the 10-layer MQW which had less defects than the 20-layer sample. Resonant cavity enhanced (RCE) photodiodes were fabricated by bonding on a SOI wafer. Selected responsivity at 1.55 mu m was successfully demonstrated. (c) 2005 Elsevier B.V. All rights reserved.

1.55 mu m Ge islands resonant-cavity-enhanced narrowband detector

The high quality Ge islands material with 1.55 mu m photo-response grown on Sol substrate is reported. Due to the modulation of the cavity formed by the mirrors at the surface and the buried SiO2 interface, seven sharp and strong peaks with narrow linewidth are found. And a 1.55 mu m Ge islands resonant-cavity-enhanced (RCE) detector with narrowband was fabricated by a simple method. The bottom mirror was deposited in the hole formed by anisotropically etching, in a basic solution from the backside of the sample with the buried SiO2 layer in silicon-on-insulator substrate as the etch-stop layer. Reflectivity spectrum indicates that the mirror deposited in the hole has a reflectivity as high as 99% in the range of 1.2-1.65 mu m. The peak responsivity of the RCE detector at 1543.8 nm is 0.028 mA/W and a full width at half maximum of 5 nm is obtained. Compared with the conventional p-i-n photodetector, the responsivity of RCE detector has a nearly threefold enhancement.

High performance 1.55 mu m InGaAsP/InP strained layer quantum well laser diodes fabricated by MOCVD overgrowth method

High performance uncooled 1.55 mu m InGaAsP/InP strained layer quantum well (SL-QW) lasers grown by low pressure metal organic chemical vapor deposition (LP-MOCVD) were reported in this paper. Whole MOCVD over growth method were applied in this work. The threshold currents of 5mA and the highest lasing temperature of 122 degrees C were obtained.

Metamorphic InGaAs p-i-n Photodetectors with 1.75 mu m Cut-Off Wavelength Grown on GaAs

Top-illuminated metamorphic InGaAs p-i-n photodetectors (PDs) with 50% cut-off wavelength of 1.75 mu m at room temperature are fabricated on GaAs substrates. The PDs are grown by a solid-source molecular beam epitaxy system. The large lattice mismatch strain is accommodated by growth of a linearly graded buffer layer to create a high quality virtual InP substrate indium content in the metamorphic buffer layer linearly changes from 2% to 60%. The dark current densities are typically 5 x 10(-6) A/cm(2) at 0 V bias and 2.24 x 10(-4) A/cm(2) at a reverse bias of 5 V. At a wavelength of 1.55 mu m, the PDs have an optical responsivity of 0.48 A/W, a linear photoresponse up to 5 mW optical power at -4 V bias. The measured -3 dB bandwidth of a 32 mu m diameter device is 7 GHz. This work proves that InGaAs buffer layers grown by solid source MBE are promising candidates for GaAs-based long wavelength devices.

1.58 mu m InGaAs quantum well laser on GaAs

We demonstrate the 1.58 mu m emission at room temperature from a metamorphic In0.6Ga0.4As quantum well laser grown on GaAs by molecular beam epitaxy. The large lattice mismatch was accommodated through growth of a linearly graded buffer layer to create a high quality virtual In0.32Ga0.68As substrate. Careful growth optimization ensured good optical and structural qualities. For a 1250x50 mu m(2) broad area laser, a minimum threshold current density of 490 A/cm(2) was achieved under pulsed operation. This result indicates that metamorphic InGaAs quantum wells can be an alternative approach for 1.55 mu m GaAs-based lasers. (C) 2007 American Institute of Physics.

GaAs-based room-temperature continuous-wave 1.59 mu m GaInNAsSb single-quantum-well laser diode grown by molecular-beam epitaxy

Starting from the growth of high-quality 1.3 mu m GaInNAs/GaAs quantum well (QW), the QW emission wavelength has been extended up to 1.55 mu m by a combination of lowering growth rate, using GaNAs barriers and incorporating some amount of Sb. The photoluminescence properties of 1.5 mu m range GaInNAsSb/GaNAs QWs are quite comparable to the 1.3 mu m QWs, revealing positive effect of Sb on improving the optical quality of the QWs. A 1.59 mu m lasing of a GaInNAsSb/GaNAs single-QW laser diode is obtained under continuous current injection at room temperature. The threshold current density is 2.6 kA/cm(2) with as-cleaved facet mirrors. (c) 2005 American Institute of Physics.

Evolution of surface morphology and photoluminescence characteristics of 1.3-mu m In0.5Ga0.5As/GaAs quantum dots grown by molecular beam epitaxy

Evolution of surface morphology and optical characteristics of 1.3-mu m In0.5Ga0.5As/GaAs quantum dots (QDs) grown by molecular beam epitaxy (MBE) are investigated by atomic force microscopy (AFM) and photoluminescence (PL). After deposition of 16 monolayers (ML) of In0.5Ga0.5As, QDs are formed and elongated along the [110] direction when using sub-ML depositions, while large size InGaAs QDs with better uniformity are formed when using ML or super-ML depositions. It is also found that the larger size QDs show enhanced PL efficiency without optical nonlinearity, which is in contrast to the elongated QDs.

Unselective regrowth of 1.5-mu m InGaAsP multiple-quantum-well distributed-feedback buried heterostructure lasers

Unselective regrowth for fabricating 1.5-mu m InGaAsP multiple-quantum well (MQW) distributed-feedback (DFB) buried heterostructure (BH) lasers is developed. The experimental results exhibit superior characteristics, such as a low threshold of 8.5 mA, high slope efficiency of 0.55 mW/mA, circular-like far-field patterns, the narrow line-width of 2.5 MHz, etc. The high performance of the devices effectively proves the feasibility of the new method to fabricate buried heterostructure lasers. (c) 2006 Society of Photo-Optical Instrumentation Engineers.