Preparation and AFM characterization of self-ordered porous alumina films on semi-insulated gaas substrate

Self-ordered porous alumina films on a semi-insulated GaAs substrate were prepared in oxalic acid aqueous solutions by three-step anodization. The I-t curve of anodization process was recorded to observe time effects of anodization. Atomic force microscopy was used to investigate structure and morphology of alumina films. It was revealed that the case of oxalic acid resulted in a self-ordered porous structure, with the pore diameters of 60-70 nm, the pore density of the order of about 10(10) pore cm(-2), and interpore distances of 95-100nm. At the same time the pore size and shape change with the pore widening time. Field-enhanced dissolution model and theory of deformation relaxation combined were brought forward to be the cause of self-ordered pore structure according to I-t curve of anodization and structure characteristics of porous alumina films. (c) 2006 Elsevier Ltd. All rights reserved.

Substrate temperature dependence of ZnTe epilayers grown on GaAs(001) by molecular beam epitaxy

ZnTe thin films have been grown on GaAs(0 0 1) substrates at different temperatures with constant Zn and Te beam equivalent pressures (BEPs) by molecular beam epitaxy (MBE). In situ reflection high-energy electron diffraction (RHEED) observation indicates that two-dimensional (2D) growth mode can be established after around one-minute three-dimensional (3D) nucleation by increasing the substrate temperature to 340 degrees C. We found that Zn desorption from the ZnTe surface is much greater than that of Te at higher temperatures, and estimated the Zn sticking coefficient by the evolution of growth rate. The Zn sticking coefficient decreases from 0.93 to 0.58 as the temperature is elevated from 320 to 400 degrees C. The ZnTe epilayer grown at 360 degrees C displays the narrowest full-width at half-maximum (FWHM) of 660 arcsec from (0 0 4) reflection in double-crystal X-ray rocking curve (DCXRC) measurements. The surface morphology of ZnTe epilayers is strongly dependent on the substrate temperature, and the root-mean-square (RMS) roughness diminishes drastically with the increase in temperature.

Influence of dielectric properties of a substrate upon plasmon resonance spectrum of supported Ag nanoparticles

Plasmon resonance spectra of supported Ag nanoparticles are studied by depositing the particles on different substrates. It was found that the dielectric properties of the substrates have significant effects on the spectral line shape, except the resonance frequency. Beyond the plasmon resonance band, the spectral shape is mainly governed by the dielectric function, particularly its imaginary part, of the substrate. The plasmon resonance band, on the other hand, may be severely distorted if the substrate is absorbing strongly.

Rearch on glass ceramics with negative CTE used as FBG substrate

SPIE; COS; Wuhan Municipal Government

HIGH-RESOLUTION PHOTOLUMINESCENCE STUDIES OF (211) CDTE GROWN ON (211)B GAAS SUBSTRATE

Sharp and rich photoluminescence lines accociated with free exciton (FE), excitons bound to neutral acceptors (A0X) and donors (D0X) in molecular beam epitaxially (MBE) grown (211) CdTe/(211)B GaAs have been reported for the first time. The results show that the (211) CdTe/(211)B GaAs grown under optimized conditions could have as high a crystal perfection as those grown on lattice-matched substrates.

CHANNELING ALIGNMENT FOR EPITAXIAL LIGHT-MASS FILM ON HEAVY-MASS SUBSTRATE

A simple procedure for obtaining a background-free backscattering spectrum of a light-mass film on a heavy-mass substrate by a normal incidence/grazing exit geometry has been described. Using this method such films can be aligned rapidly and accurately, and the impurity or defect information on the films can be obtained without need for realignment. Example is given from MeV Li-3+ analysis of a deposited film of Si on a single crystal substrate of yttria-stabilized, cubic zirconia.

PHOTOLUMINESCENCE SPECTRA OF STRAINED HETEROSTRUCTURE OF INP ON GAAS SUBSTRATE GROWN BY METAL-ORGANIC CHEMICAL VAPOR-DEPOSITION

A high-energy shift of the band-band recombination has been observed in photoluminescence spectra of the strained InP layer grown on GaAs substrate. The InP layer is under biaxial compressive strain at temperatures below the growth temperature, because the thermal expansion coefficient of InP is smaller than that of GaAs. The strain value determined by the energy shift of the band-edge peak is in good agreement with the calculated thermal strain. A band to carbon acceptor recombination is also identified.