Electron transport properties of MM-HEMT with varied channel indium contents

Transport properties of two-dimensional electron gas (2DEG) are crucial to metamorphic high-electron-mobility transistors (MM-HEMT). We have investigated the variations of subband electron mobility and concentration versus temperature from Shubnikov-de Hass oscillations., and variable temperature Hall measurements. The results indicate that the electrical performance is the best when the In content is 0.65 in the channel for MM-HEMT. When the In content exceeds 0.65, a large lattice mismatch will cause dislocations and result in the decrease of mobility and the fall of performance in materials and devices.

Effects of annealing ambient on the formation of compensation defects in InP

Positron annihilation lifetime (PAL) and photoinduced current transient spectroscopies (PICTS) have been employed to study the formation of compensation defects in undoped InP under different annealing processes with pure phosphorus (PP) ambience and iron phosphide (IP) ambience, respectively. The different annealing ambiences convert the as-grown n-type undoped InP into two types of semi-insulating (SI) states. The positron average lifetimes of as-grown InP, PP SI-InP, and IP SI-InP are found to be 246, 251, and 243 ps, respectively, which are all longer than the bulk lifetime of 240 ps, indicating the existence of vacancy-type positron-trapping defects. For as-grown InP, VInH4 complexes are the dominant defects. They dissociate into VInHn(0less than or equal tonless than or equal to3) acceptor vacancies under PP ambience annealing, compensating the residual shallow donors and turning the material semi-insulating. In forming IP SI-InP, diffusion of iron into V-In complexes under IP ambience annealing produces the substitutional compensation defect Fe-In, causing a shorter positron average lifetime. The PICTS measurements show that a group of vacancy-type defects has been suppressed by iron diffusion during the annealing process, which is in good agreement with the PAL results. (C) 2003 American Institute of Physics.

Deep levels in semi-insulating InP obtained by annealing under iron phosphide ambiance

Deep levels in semi-insulating (SI) InP obtained by annealing in iron phosphide (IP) ambiance have been characterized by optical transient current spectroscopy (OTCS). Compared with the OTCS result of the SI InP prepared by annealing in pure phosphorus (PP) ambiance, the IP SI InP presents only two traps with activation energies of 0.20 and 0.63 eV, respectively. The results suggest that the diffusion of Fe-atoms suppresses the formation of a few defects in the IP SI InP. The nature of deep levels in the IP and PP SI InP has been discussed on the basis of these results. The relation between material property and defects in those SI InP has also been revealed. (C) 2002 American Institute of Physics.

Creation and suppression of point defects through a kick-out substitution process of Fe in InP

Indium antisite defect In-P-related photoluminescence has been observed in Fe-diffused semi-insulating (SI) InP. Compared to annealed undoped or Fe-predoped SI InP, there are fewer defects in SI InP obtained by long-duration, high-temperature Fe diffusion. The suppression of the formation of point defects in Fe-diffused SI InP can be explained in terms of the complete occupation by Fe at indium vacancy. The In-P defect is enhanced by the indium interstitial that is caused by the kick out of In and the substitution at the indium site of Fe in the diffusion process. Through these Fe-diffusion results, the nature of the defects in annealed undoped SI InP is better understood. (C) 2002 American Institute of Physics.

Detection of indium segregation effects in InGaAs/GaAs quantum wells using reflectance-difference spectrometry

The influence of the Indium segregation on the interface asymmetry in InGaAs/GaAs quantum wells have been studied by reflectance-difference spectroscopy (RDS). It is found that the anisotropy of the 2H1E (2HH --> 1E) transition is very sensitive to the degree of the interface asymmetry. Calculations taking into account indium segregation yield good agreement with the observed anisotropy structures. It demonstrates that the anisotropy intensity ratio of the 1L1E (1LH --> 1E) and 2H1E transitions measured by RDS can be used to characterize the interface asymmetry. (C) 2002 Elsevier Science B.V. All rights reserved.

Effect on the optical properties and surface morphology of cubic GaN grown by metalorganic chemical vapor deposition using isoelectronic indium surfactant doping

The surfactant effect of isoelectronic indium doping during metalorganic chemical vapor deposition growth of cubic GaN on GaAs (1 0 0) substrates was studied. Its influence on the optical properties and surface morphology was investigated by using room-temperature photoluminescence (PL) and atomic force microscopy. It is shown that the sample with small amount of In-doping has a narrower PL linewidth, and a smoother surface than undoped cubic GaN layers. A slight red shift of the near-band-edge emission peak was observed. These results revealed that, for small TMIn flow rates, indium played the role of the surfactant doping and effectively improved the cubic GaN film quality; for large TMIn flow rates, the alloying formation of Ga1-xInxN might have occurred. (C) 2002 Elsevier Science B.V. All rights reserved.

Indium doping effect on GaN in the initial growth stage

Three minutes' growth was carried out to investigate the indium-doping effect on initially grown GaN. Indium-doped and undoped samples were grown by low-pressure metalorganic vapor phase epitaxy. Atomic force microscope observation revealed that In-doping modified the morphology of the nuclei. Indium-doping also enhanced wetting between the buffer and nuclei layers, which was also supported by optical transmission. Photoluminescence suggested that indium-doping obviously enhanced band-edge related emission even in the nucleation stage. X-ray diffraction performed on samples grown for 20 minutes indicated improvement of the crystalline quality through indium-doping. The mechanism of the indium-doping effect was discussed.

X-ray diffraction analysis on gallium-indium interdiffusion in quantum dot superlattices

Thermal-induced interdiffusion in InAs/GaAs quantum dot superlattices is studied by high-resolution x-ray diffraction rocking curve and photoluminescence techniques. With increasing annealing temperatures, up to 300 meV a blueshift of the emission peak position and down to 16.6 meV a narrowing of the line width are found in the photoluminescence spectra, and respective intensity of the higher-order satellite peaks to lower-order ones in the x-ray rocking curves decreases. Dynamical theory is employed to simulate the measured x-ray diffraction data. Excellent agreement between the experimental curves and the simulations is achieved when the composition, thickness and stress variations caused by interdiffusion are taken into account. It is found that the significant In-Ga intermixing occurs even in the as-grown InAs/GaAs quantum dots. The estimated diffusion coefficient is 1.8 x 10(-17) cm(2) (.) s(-1) at 650 degreesC, 3.2 x 10(-17) cm(2 .) s(-1) at 750 degreesC, and 1.2 x 10(-14) cm(2 .) s(-1) at 850 degreesC.

Influence of indium composition on the surface morphology of self-organized InxGa1-xAs quantum dots on GaAs substrates

InxGa1-xAs self-organized quantum dots with x=1.0, 0.5, and 0.35 have been grown by molecular beam epitaxy. The areal density, distribution, and shapes have been found to be dependent on x. The dot shape changes from a round shape for x=1.0 to an elliptical shape for x less than or equal to 0.5. The major axis and minor axis of the elliptical InxGa1-xAs dots are along the [(1) over bar 10] and [110] directions, respectively. The ordering phenomenon is also discussed. It is suggested that the dot-dot interaction may play important roles in the self-organization process. (C) 2000 American Institute of Physics. [S0021-8979(00)10701-7].

Indium composition dependence of the size uniformity of InGaAs quantum dots on (311)B GaAs grown by molecular beam epitaxy

The deposition of InxGa1-xAs (0.2 less than or equal to x less than or equal to 0.5) on (311)B GaAs surfaces using solid source molecular beam epitaxy (MBE) has been studied. Both AFM and photoluminescence emission showed that homogeneous quantum dots could be formed on (311)B GaAs surface when indium composition was around 0.4. Indium composition had a strong influence on the size uniformity and the lateral alignment of quantum dots. Compared with other surface orientation, (100) and (n11) A/B (n=1,2,3), photoluminescence measurement confirmed that (311)B surface is the most advantageous in fabricating uniform and dense quantum dots.

Improvement of the photoluminescence from gallium nitride layers grown by MBE with an additional incident indium flux

The effect of using an indium flux during the MBE growth of GaN layers was investigated. The properties of these layers were studied using electron probe microanalysis, secondary ion mass spectroscopy, photoluminescence and cathodoluminescence. The optical properties of the GaN layers are shown to improve as compared with undoped GaN layers grown under nominally the same conditions but without an additional indium flux.

1.3 mu m high indium content (42.5%) GaInNAs/GaAs quantum wells grown by molecular beam epitaxy

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum well (QW) samples with 42.5% indium content were successfully grown by molecular beam epitaxy. The growth of well layers was monitored by reflection high-energy electron diffraction (RHEED). Room temperature photoluminescence (PL) peak intensity of the GaIn0.425NAs/GaAs (6 nm / 20 nm) 3QW is higher than, and the full width at half maximum (FWHM) is comparable to, that of In0.425GaAs/GaAs 3QW, indicating improved optical quality due to strain compensation effects by introducing N to the high indium content InGaAs epilayer. The measured (004) X-ray rocking curve shows clear satellite peaks and Pendellosung fringes, suggesting high film uniformity and smooth interfaces. The cross sectional TEM measurements further reveal that there are no structural defects in such high indium content QWs. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

A study of indium incorporation in In-rich InGaN grown by MOVPE

InGaN/GaN heterostructures have been deposited onto (0 0 0 1) sapphire by our home-made low pressure MOVPE with different growth parameters. It has been noted that the indium incorporation depends by a complex way on a number of factors. In this work, the effect of substrate temperature, trimethylindium input flow and V/III ratio on the indium incorporation has been investigated. Finally, by optimizing the growth parameters, we made a series of single-phase InGaN samples with indium content from 10% up to 45%.

INDIUM OHMIC CONTACTS TO N-ZNSE

The reaction between an indium over layer and high purity MBE grown n-ZnSe chlorine doped (2x 10(18) cm-3) epilayers has been investigated using X-ray diffraction, Rutherford backscattering spectroscopy, X-ray photoelectron and Auger electron spectroscopy, and by electrical function tests (I-V and C-V). Good ohmic contacts were formed after annealing at 250 or 300-degrees-C for a few minutes in forming gas. Annealing at lower or higher temperatures resulted in higher resistance or rectifying contacts. The data show that no compounds were formed at the interface; instead In appeared to diffuse into the ZnSe. High surface doping densities appear to allow an ohmic contact, but the electrical data suggest that compensation effects are also very significant in the formation of the contact. These effects must be considered for successful formation of the ohmic contact.

Non-stoichiometry Related Deep Level Defects in Semi-insulating InP

Semi-insulating (SI) InP materials have been prepared under different stoichiometric conditions, including Fe-doping in indium-rich melt and high temperature annealing undoped wafer in phosphorus and iron phosphide ambients. Deep level defects related with non-stoichiometry have been detected in the SI-InP samples. A close relationship between the material quality of electrical property and native deep defects has been revealed by a comprehensive study of defects in as-grown Fe-doped and annealed undoped SI-InP materials. Fe-doped SI-InP material with low carrier mobility and poor thermal stability contains a high concentration of deep defects with energy levels in the range of 0.1-0.4eV. The suppression of the defects by high temperature annealing undoped InP leads to the manufacture of high quality SI-InP with high mobility and good electrical uniformity. A technology for the growth of high quality SI-InP through stoichiometry control has been proposed based on the results.