Spectroscopy of long wavelength coupled quantum dots

We obtained a low density of coupled InAs/GaAs quantum dots (QDs) with an emission wavelength of around 1.3 mu m at room temperature. Atomic force microscopy and transmission electronic microscopy reveal that the dot size difference and the lateral displacement between the two dots are related to the spacer thickness. Spectroscopy of the coupled QD ensembles is considerably influenced by the spacer thickness.

Anisotropic exchange splitting of excitons in (001)GaAs/Al0.3Ga0.7As superlattice studied by reflectance difference spectroscopy

Anisotropic exchange splitting (AES) is induced by the joint effects of the electron-hole exchange interaction and the symmetry reduction in quantum wells and quantum dots. A model has been developed to quantitatively obtain the electron-hole exchange energy and the hole-mixing energy of quantum wells and superlattices. In this model, the AES and the degree of polarization can both be obtained from the reflectance difference spectroscopy. Thus the electron-hole exchange energy and the hole-mixing energy can be completely separated and quantitatively deduced. By using this model, a (001)5 nm GaAs/7 nm Al0.3Ga0.7As superlattice sample subjected to [110] uniaxial strains has been investigated in detail. The n=1 heavy-hole (1H1E) exciton can be analyzed by this model. We find that the AES of quantum wells can be linearly tuned by the [110] uniaxial strains. The small uniaxial strains can only influence the hole-mixing interaction of quantum wells, but have almost no contribution to the electron-hole exchange interaction. (c) 2008 American Institute of Physics.

Valence band offset of ZnO/4H-SiC heterojunction measured by x-ray photoelectron spectroscopy

The valence band offset (VBO) of the wurtzite ZnO/4H-SiC heterojunction is directly determined to be 1.61 +/- 0.23 eV by x-ray photoelectron spectroscopy. The conduction band offset is deduced to be 1.50 +/- 0.23 eV from the known VBO value, which indicates a type-II band alignment for this heterojunction. The experimental VBO value is confirmed and in good agreement with the calculated value based on the transitive property of heterojunctions between ZnO, SiC, and GaN. (C) 2008 American Institute of Physics.

New observations on the pressure dependence of luminescence from Eu2+-doped MF2 (M = Ca, Sr, Ba) fluorides

The luminescence from Eu2+ ions in MF2 (M = Ca, Sr, Ba) fluorides has been investigated under the pressure range of 0-8 GPa. The emission band originating from the 4f(6)5d(1) -> 4f(7) transition of Eu2+ ions in CaF2 and SrF2 shows the red-shift as increasing pressure with pressure coefficients of -17 meV/GPa for CaF2 and -18 meV/GPa for SrF2. At atmospheric pressure, the emission spectrum of BaF2:Eu2+ comprises two peaks at 2.20 and 2.75 eV from the impurity trapped exciton (ITE) and the self-trapped exciton (STE), respectively. As the pressure is increased, both emission peaks shift to higher energies, and the shifting rate is slowed by the phase transition from the cubic to orthorhombic phase at 4 GPa. Due to the phase transition at 4-5 GPa pressure, the ITE emission disappears gradually, and the STE emission is gradually replaced by the 4f(6)5d(1) -> 4f(7) transition of Eu2+. Above 5 GPa, the pressure behavior of the 4f(6)5d(1) -> 4f(7) transition of EU2+ in BaF2: EU2+ is the same as the normal emission of Eu2+ in CaF2 and SrF2 phosphors.

Evolution of structural defects in SiOx films fabricated by electron cyclotron resonance plasma chemical vapour deposition upon annealing treatment

We study the structural defects in the SiOx film prepared by electron cyclotron resonance plasma chemical vapour deposition and annealing recovery evolution. The photoluminescence property is observed in the as-deposited and annealed samples. [-SiO3](2-) defects are the luminescence centres of the ultraviolet photoluminescence (PL) from the Fourier transform infrared spectroscopy and PL measurements. [-SiO3](2-) is observed by positron annihilation spectroscopy, and this defect can make the S parameters increase. After 1000 degrees C annealing, [-SiO3](2-) defects still exist in the films.

Investigation of native defects and property of bulk ZnO single crystal grown by a closed chemical vapor transport method

Hall effect, Raman scattering, photoluminescence spectroscopy (PL), optical absorption (OA), mass spectroscopy, and X-ray diffraction have been used to study bulk ZnO single crystal grown by a closed chemical vapor transport method. The results indicate that shallow donor impurities (Ga and Al) are the dominant native defects responsible for n-type conduction of the ZnO single crystal. PL and OA results suggest that the as-grown and annealed ZnO samples with poor lattice perfection exhibit strong deep level green photoluminescence and weak ultraviolet luminescence. The deep level defect in as-grown ZnO is identified to be oxygen vacancy. After high-temperature annealing, the deep level photoluminescence is suppressed in ZnO crystal with good lattice perfection. In contrast, the photoluminescence is nearly unchanged or even enhanced in ZnO crystal with grain boundary or mosaic structure. This result indicates that a trapping effect of the defect exists at the grain boundary in ZnO single crystal. (C) 2007 Elsevier B.V. All rights reserved.

Valence band offset of MgO/InN heterojunction measured by x-ray photoelectron spectroscopy

MgO may be a promising gate dielectric and surface passivation film for InN based devices and the valence band offset of MgO/InN heterojunction has been measured by x-ray photoelectron spectroscopy. The valence band offset is determined to be 1.59 +/- 0.23 eV. Given the experimental band gap of 7.83 for the MgO, a type-I heterojunction with a conduction band offset of 5.54 +/- 0.23 eV is found. The accurate determination of the valence and conduction band offsets is important for use of MgO/InN electronic devices. (c) 2008 American Institute of Physics.

Valence band offset of ZnO/GaAs heterojunction measured by x-ray photoelectron spectroscopy

X-ray photoelectron spectroscopy has been used to measure the valence band offset at the ZnO/GaAs heterojunction interface. The valence band offset is determined to be 2.39 +/- 0.23 eV. As a consequence, a type-II heterojunction with a conduction band offset of -0.44 +/- 0.23 eV is found. The directly obtained value is in good agreement with the result of theoretical calculations based on the interface-induced gap states and the chemical electronegativity theory. (c) 2008 American Institute of Physics.

Photoluminescence study of AlGaInP/GaInP quantum well intermixing induced by zinc impurity diffusion

AlGaInP/GaInP quantum well intermixing phenomena induced by Zn impurity diffusion at 540 degrees C were studied using room-temperature photo luminescence (PL) spectroscopy. As the diffusion time increased from 40 to 120 min, PL blue shift taken on the AlGaInP/GaInP quantum well regions increased from 36.3 to 171.6 meV. Moreover, when the diffusion time was equal to or above 60 min, it was observed firstly that a PL red shift occurred with a PL blue shift on the samples. After detailed analysis, it was found that the red-shift PL spectra were measured on the Ga0.51In0.49P buffer layer of the samples, and the mechanism of the PL red shift and the PL blue shift were studied qualitatively. (C) 2007 Elsevier B.V. All rights reserved.

Does an enhanced yellow luminescence imply a reduction of electron mobility in n-type GaN?

It is studied whether there is any regular relationship between the yellow luminescence band and electron mobility of n-type GaN. For a series of GaN samples grown with the same Si doping, it is found that the electron mobility decreases with an increase of relative intensity of yellow luminescence, accompanied by an increase of edge dislocation density. Further research indicates that it is acceptors introduced by edge dislocations which lead to the concomitant changes of yellow luminescence and electron mobility. Similar changes are induced by Si doping in the n-type GaN samples with relatively low edge dislocation density. However, the relationship between the yellow luminescence and electron mobility of n-type GaN is not a simple one. A light Si doping may simultaneously increase yellow luminescence and electron mobility when Si doping plays a dominant role in reducing the carrier scattering. This means that even the intensity of yellow luminescence is often used as an indicator of material quality for GaN, it does not have any monotonous correlation with the electron mobility of GaN. (c) 2007 American Institute of Physics.

Energy band alignment of SiO2/ZnO interface determined by x-ray photoelectron spectroscopy

Thin SiO2 interlayer is the key to improving the electroluminescence characteristics of light emitting diodes based on ZnO heterojunctions, but little is known of the band offsets of SiO2/ZnO. In this letter, energy band alignment of SiO2/ZnO interface was determined by x-ray photoelectron spectroscopy. The valence band offset Delta E-V of SiO2/ZnO interface is determined to be 0.93 +/- 0.15 eV. According to the relationship between the conduction band offset Delta E-C and the valence band offset Delta E-V Delta E-C=E-g(SiO2)-E-g(ZnO)-Delta E-V, and taking the room-temperature band-gaps of 9.0 and 3.37 eV for SiO2 and ZnO, respectively, a type-I band-energy alignment of SiO2/ZnO interface with a conduction band offset of 4.70 +/- 0.15 eV is found. The accurate determination of energy band alignment of SiO2/ZnO is helpful for designing of SiO2/ZnO hybrid devices and is also important for understanding their carrier transport properties. (C) 2009 American Institute of Physics. [DOI 10.1063/1.3204028]

Proton irradiation-induced defects in undoped GaSb studied by positron lifetime spectroscopy and photoluminescence

Undoped GaSb was irradiated by 2.6 MeV protons. The irradiation-induced defects were studied by positron lifetime spectroscopy (PLS) and photoluminescence (PL). Positron lifetime measurements showed that vacancy-type defects were introduced after irradiation, and divacancies were formed at higher irradiation dose. Annealing experiments revealed there were different annealing steps between the as grown and proton-irradiated samples, the reason for which was tentatively attributed to the formation of divacancies in the proton-irradiated samples during annealing. All the vacancy defects could be annealed out at around 500 degrees C. The PL intensity quickly fell down after proton irradiation and decreased with increasing irradiation dose, indicating that irradiation induced non-irradiative recombination centers, whose candidates were assigned to the vacancy defects induced by proton irradiation.

Role of edge dislocation and Si impurity in linking the blue luminescence and yellow luminescence in n-type GaN films

A close relationship is found between the blue and yellow luminescence bands in n-type GaN films, which are grown without intentional acceptor doping. The intensity ratio of blue luminescence to yellow luminescence (I-BL/I-YL) decreases with the increase in edge dislocation densities as demonstrated by the (102) full width at half maximum of x-ray diffraction. In addition, the I-BL/I-YL ratio decreases with the increase in Si doping. It is suggested that the edge dislocation and Si impurity play important roles in linking the blue and yellow luminescence.

Determination of wurtzite InN/cubic In2O3 heterojunction band offset by x-ray photoelectron spectroscopy

In2O3 is a promising partner of InN to form InN/In2O3 heterosystems. The valence band offset (VBO) of wurtzite InN/cubic In2O3 heterojunction is determined by x-ray photoemission spectroscopy. The valence band of In2O3 is found to be 1.47 +/- 0.11 eV below that of InN, and a type-I heterojunction with a conduction band offset (CBO) of 0.49-0.99 eV is found. The accurate determination of the VBO and CBO is important for use of InN/In2O3 based electronic devices.

Measuring spin diffusion of electrons in bulk n-GaAs using circularly dichromatic absorption difference spectroscopy of spin gratings

Circular dichromatic absorption difference spectroscopy is developed to measure the spin diffusion dynamics of electrons in bulk n-GaAs. This spectroscopy has higher detection sensitivity over homodyne detection of spin-grating-diffracted signal. A model to describe circular dichromatic absorption difference signal is derived and used to fit experimental signal to retrieve decaying rate of spin gratings. A spin diffusion constant of D-s=201 +/- 25 cm(2)/s for bulk n-GaAs has been measured at room temperature using this technique and is close to electron diffusion constant (D-c), which is much different from the case in GaAs quantum wells where D-s is markedly less than D-c.