SEM-EDX of morphology of electroless nickel coatings with tin and tungsten

Electroless plating of binary Ni-P, ternary Ni-Sn-P and Ni-W-P, and quaternary Ni-W-Sn-P alloy coatings was carried out in alkalicitrate baths. After the plating, several kinds of test were carried out to determine the improvement in the characteristics and properties due to the additional elements as well as to study the change in behaviour when heat treatment was applied to these coatings. The coatings were subjected to X-ray diffraction analysis where it was found that all the coatings were amorphous. Interesting surface morphology features were examined using scanning electron microscopy. Addition of a third element improved the hardness.

Template-free environmentally friendly synthesis and characterization of unsupported tungsten carbide with a controllable porous framework

Tungsten carbide (WC) with controlled pore size distribution was synthesized using a novel “precursor reassembly” method. The precursor crystal was assembled by mixing ammonium metatungstate (AMT) and ammonium carbonate (AC) in distilled water, followed by hydrothermal treatment. The mesostructure, crystal phase, and amount of deposited graphitic carbon can be conveniently tuned by controlling carburizing atmosphere (CO or a CO/H2 mixture). Moreover, the influence of precursor preparation (AMT/AC mass ratio and hydrothermal temperature) on the materials was also investigated. The resultant materials with low carbon content were mesoporous WCs, which showed high specific surface areas (11.3-20.4 m2 g-1) and adjustable pore-size distributions (average pore size: 15.3-22.3 nm). A mechanism for the formation of WC with a controllable porous framework is proposed. Finally, cyclic voltammetry was used to investigate the inference of different mesoporous structure.

Titania and tungsten doped titania thin films on glass; active photocatalysts

Acidification of an isopropanol solution containing mixtures of [Ti(OPri)(4)] and [W(OEt)(5)] produced solutions from which various TiO2, WO3 and TiO2/WO3 thin films could be obtained by dip coating and annealing. The films were analysed by X-ray diffraction, SEM/EDAX, Raman, electronic spectra, contact angle and photoactivity with respect to destruction of an over layer of stearic acid. The TiO2/WO3 films were shown to be mixtures of two phases TiO2 and WO3 rather than a solid solution TixWyO2. The 2% tungsten oxide doped titania films were shown to be the most effective photocatalysts. All of the TiO2 and TiO2/WO3 films showed light induced superhydrophillicity. (C) 2002 Elsevier Science Ltd. All rights reserved.

Synthesis of mesoporous tungsten carbide-supported platinum and its electrocatalytic activity for methanol oxidation

High activity and stability during oxidation of methanol under the relatively anode environment are two main evaluation criterias for an effective anode electrocatalyst in direct methanol fuel cell (DMFC). Mesoporous WC samples with hollow structure were prepared by gas-solid reaction at the atmosphere of CH(4)/H(2) by using airflow spray dried ammonium metatungstate (AMT). The platinum supported on this material by impregnation-vapor phase deoxidation method served as a less expensive electro anode catalyst. XRD and SEM results showed that Pt particles were well dispersed on the surface of WC. The results showed that the Pt/WC-PME exhibited an attractive catalytic activity, and methanol oxidation process in Pt/WC-PME is affected by liquid-phase mass transfer. The results also indicated that the oxidation can be improved by raising temperatures.

Long-Range Lateral Dopant Diffusion in Tungsten Silicide Layers

Novel diode test structures have been manufactured to characterize long-range dopant diffusion in tungsten silicide layers. A tungsten silicide to p-type silicon contact has been characterized as a Schottky barrier rectifying contact with a silicide work function of 4.8 eV. Long-range diffusion of boron for an anneal at 900 °C for 30 min has been shown to alter this contact to become ohmic. Long-range diffusion of phosphorus with a similar anneal alters the contact to become a bipolar n-p diode. Bipolar diode action is demonstrated experimentally for anneal schedules of 30 min at 900 °C, indicating long-range diffusion of phosphorus (~38 µm), SIMS analysis shows dopant redistribution is adversely affected by segregation to the silicide/oxide interface. The concept of conduit diffusion has been demonstrated experimentally for application in advanced bipolar transistor technology. © 2009 IEEE.

Low loading platinum nanoparticles on reduced graphene oxide-supported tungsten carbide crystallites as a highly active electrocatalyst for methanol oxidation

In this study, low loading platinum nanoparticles (Pt NPs) have been highly dispersed on reduced graphene oxide-supported WC nanocrystallites (Pt-WC/RGO) via program-controlled reduction-carburization technique and microwave-assisted method. The scanning electron microscopy and transmission electron microscopy results show that WC nanocrystallites are homogeneously decorated on RGO, and Pt NPs with a size of ca. 3 nm are dispersed on both RGO and WC. The prepared Pt-WC/RGO is used as an electrocatalyst for methanol oxidation reaction (MOR). Compared with the Pt/RGO, commercial carbon-supported Pt (Pt/C) and PtRu alloy (PtRu/C) electrocatalysts, the Pt-WC/RGO composites demonstrate higher electrochemical active surface area and excellent electrocatalytic activity toward the methanol oxidation, such as better tolerance toward CO, higher peak current density, lower onset potential and long-term stability, which could be attributed to the characterized RGO support, highly dispersed Pt NPs and WC nanocrystallites and the valid synergistic effect resulted from the increased interface between WC and Pt. The present work proves that Pt-WC/RGO composites could be a promising alternative catalyst for direct methanol fuel cells where WC plays the important role as a functional additive in preparing Pt-based catalysts because of its CO tolerance and lower price. 

Delamination and wear in drilling of carbon-fiber reinforced plastic composites using multilayer TiAlN/TiN PVD-coated tungsten carbide tools

This study aims to investigate drilling process in carbon-fiber reinforced plastic (CFRP) composites with multilayer TiAlN/TiN PVD-coated tungsten carbide drill. The effect of process parameters have been investigated in drilling of Hexcel M21-T700GC. Thrust force and torque were measured online throughout the drilling experiments. Delamination were observed using optical microscope and analyzed via a developed algorithm based on digital image processing technique. Surface roughness of each hole was measured using a surface profilometer. In addition, the progression of tool wear in various surfaces of drill was observed using tool microscope and measured using image software. Our results indicate that the thrust force and torque increased with the increasing cutting speed and feed rate. Delamination and average surface roughness that rose with the increase in feed rate, however, decreased with the increasing cutting speed. The average surface roughness tended to increase with the increase in feed rate and decrease with the increasing cutting speed in drilling of carbon-fiber reinforced plastic (CFRP). Feed rate was found as the predominant factor on the drilling outputs. Abrasive wear was observed on both flank and relief surfaces, which created edge wear on cutting edges. No sign of chipping or plastic deformation has been observed on the surfaces of drills. © 2012 The Author(s).

ELM-induced transient tungsten melting in the JET divertor

The original goals of the JET ITER-like wall included the study of the impact of an all W divertor on plasma operation (Coenen et al 2013 Nucl. Fusion 53 073043) and fuel retention (Brezinsek et al 2013 Nucl. Fusion 53 083023). ITER has recently decided to install a full-tungsten (W) divertor from the start of operations. One of the key inputs required in support of this decision was the study of the possibility of W melting and melt splashing during transients. Damage of this type can lead to modifications of surface topology which could lead to higher disruption frequency or compromise subsequent plasma operation. Although every effort will be made to avoid leading edges, ITER plasma stored energies are sufficient that transients can drive shallow melting on the top surfaces of components. JET is able to produce ELMs large enough to allow access to transient melting in a regime of relevance to ITER.

Transient W melt experiments were performed in JET using a dedicated divertor module and a sequence of I-P = 3.0 MA/B-T = 2.9 T H-mode pulses with an input power of P-IN = 23 MW, a stored energy of similar to 6 MJ and regular type I ELMs at Delta W-ELM = 0.3 MJ and f(ELM) similar to 30 Hz. By moving the outer strike point onto a dedicated leading edge in the W divertor the base temperature was raised within similar to 1 s to a level allowing transient, ELM-driven melting during the subsequent 0.5 s. Such ELMs (delta W similar to 300 kJ per ELM) are comparable to mitigated ELMs expected in ITER (Pitts et al 2011 J. Nucl. Mater. 415 (Suppl.) S957-64).

Although significant material losses in terms of ejections into the plasma were not observed, there is indirect evidence that some small droplets (similar to 80 mu m) were released. Almost 1 mm (similar to 6 mm(3)) of W was moved by similar to 150 ELMs within 7 subsequent discharges. The impact on the main plasma parameters was minor and no disruptions occurred. The W-melt gradually moved along the leading edge towards the high-field side, driven by j x B forces. The evaporation rate determined from spectroscopy is 100 times less than expected from steady state melting and is thus consistent only with transient melting during the individual ELMs. Analysis of IR data and spectroscopy together with modelling using the MEMOS code Bazylev et al 2009 J. Nucl. Mater. 390-391 810-13 point to transient melting as the main process. 3D MEMOS simulations on the consequences of multiple ELMs on damage of tungsten castellated armour have been performed.

These experiments provide the first experimental evidence for the absence of significant melt splashing at transient events resembling mitigated ELMs on ITER and establish a key experimental benchmark for the MEMOS code.

Comment on "multiconfiguration Dirac-Fock energy levels and radiative rates for Br-like tungsten" by S. Aggarwal, A.K.S. Jha, and M. Mohan [Can. J. Phys. 91, 394 (2013)]

We report calculations of energy levels and oscillator strengths for transitions in W XL, undertaken with the general-purpose relativistic atomic structure package (GRASP) and flexible atomic code (FAC). Comparisons are made with existing results and the accuracy of the data is assessed. Discrepancies with the most recent results of S. Aggarwal et al. (Can. J. Phys. 91, 394 (2013)) are up to 0.4 Ryd and up to two orders of magnitude for energy levels and oscillator strengths, respectively. Discrepancies for lifetimes are even larger, up to four orders of magnitude for some levels. Our energy levels are estimated to be accurate to better than 0.5% (i.e., 0.2 Ryd), whereas results for oscillator strengths and lifetimes should be accurate to better than 20%.

Methanol electro-oxidation on platinum modified tungsten carbides in direct methanol fuel cells: a DFT study

In exploration of low-cost electrocatalysts for direct methanol fuel cells (DMFCs), Pt modified tungsten carbide (WC) materials are found to be great potential candidates for decreasing Pt usage whilst exhibiting satisfactory reactivity. In this work, the mechanisms, onset potentials and activity for electrooxidation of methanol were studied on a series of Pt-modified WC catalysts where the bare W-terminated WC(0001) substrate was employed. In the surface energy calculations of a series of Pt-modified WC models, we found that the feasible structures are mono- and bi-layer Pt-modified WCs. The tri-layer Pt-modified WC model is not thermodynamically stable where the top layer Pt atoms tend to accumulate and form particles or clusters rather than being dispersed as a layer. We further calculated the mechanisms of methanol oxidation on the feasible models via methanol dehydrogenation to CO involving C-H and O-H bonds dissociating subsequently, and further CO oxidation with the C-O bond association. The onset potentials for the oxidation reactions over the Pt-modified WC catalysts were determined thermodynamically by water dissociation to surface OH* species. The activities of these Pt-modified WC catalysts were estimated from the calculated kinetic data. It has been found that the bi-layer Pt-modified WC catalysts may provide a good reactivity and an onset oxidation potential comparable to pure Pt and serve as promising electrocatalysts for DMFCs with a significant decrease in Pt usage.