Resumo:
AlGaInAs-InPmicrocylinder lasers connected with an output waveguide are fabricated by planar technology. Room-temperature continuous-wave operation with a threshold current of 8 mA is realized for a microcylinder laser with the radius of 10 mu m and the output waveguide width of 2 mu m. The mode Q-factor of 1.2 x 10(4) is measured from the laser spectrum at the threshold. Coupled mode characteristics are analyzed by 2-D finite-difference time-domain simulation and the analytical solution of whispering-gallery modes. The calculated mode Q-factors of coupled modes are in the same order as the measured value.
Resumo:
The electrical and structural characteristics of secondary defects in regrown amorphous layers formed in n-type Si(100) with a resistivity of 2 OMEGA cm and 6 OMEGA cm using Ge+ ions, has been studied. The amorphous layers with a thickness of 460 nm are formed by implantation of 1 x 10(15) Ge+ cm-2 at an energy of 400 keV. Both conventional furnace and rapid thermal annealing were used to regrow the amorphous layer and the residual defects have been characterised in terms of their concentration depth distribution and activation energies using C-V and DLTS. Structural information has been obtained from RBS and XTEM. By choosing suitable anneal conditions it is possible to eliminate extended defects, apart from a low concentration of end of range dislocation loops. However, a substantial population of electrically active point defects remain after simple low thermal budget anneals. In a sample implanted with 1 x 10(15) Ge+ cm-2 at 400 keV a region of deep donors approximately 460 nm from the surface is always present When the samples are annealed at higher temperatures (> 850-degrees the total deep donor concentration is reduced by one order of magnitude. Other electrically active defects not observable in the low (750-degrees-C) temperature annealed layers become apparent during anneals at intermediate temperatures.
Resumo:
Residual defects in the overlayer of fully annealed SIMOX material have been studied by means of a chemical etching technique. The etching procedure has been calibrated and an optimum recipe is reported. Observations using optical microscopy and transmission electron microscopy have been used to quantify the defect densities and good agreement between the two techniques has been established, confirming that the optimised chemical etching process can be used with confidence to determine the dislocation density for values < 10(7) cm-2.
Resumo:
Interfacial formation processes and reactions between Au and hydrogenated amorphous Si have been studied by photoemission spectroscopy and Auger electron spectroscopy. A three-dimensional growth of Au metal cluster occurs at initial formation of the Au/a-Si:H interface. When Au deposition exceeds a critical time, Au and Si begin interdiffusing and react to create an Au-Si alloy region. Annealing enhances interdiffusion and a Si-rich region exists on the topmost surface of Au films on a-Si:H.
Resumo:
Using photoemission spectroscopy and Auger electron spectroscopy, the interfacial formation process and the reactions between Al and hydrogenated amorphous Si are probed, and annealing behaviors of the Al/a-Si:H system are investigated as well. It is found that a three-dimensional growth of Al metal clusters which includes reacted Al and non-reacted metal Al occurs at the initial Al deposition time, reacted Al and Si alloyed layers exist in the Al/a-Si:H interface, and non-reacted Al makes layer-by-layer growth forming a metal Al layer on the sample surface. The interfacial reactions and element interdiffusion of Al/a-Si:H are promoted under the vacuum annealing.
REGROWTH OF MBE-GAAS FILMS ON SI SUBSTRATES BY HIGH-ENERGY ION-IMPLANTATION AND SUBSEQUENT ANNEALING
Resumo:
InAs thin films with good characteristics were grown on GaAs (0 0 1) substrates by molecular beam epitaxy. Cross-sectional transmission electron microscopy indicated that most of the threading dislocations formed by the interaction of misfit dislocations are annihilated above a small thickness. The high electron mobility and small temperature dependence of InAs epilayers are useful for magnetic sensors which is demonstrated by the properties of Hall effect devices.
Resumo:
The damage removal and strain relaxation in the As+-implanted Si0.57Ge0.43 epilayers were studied by double-crystal x-ray diffractometry and transmission electron microscopy. The results presented in this paper indicate that rapid thermal annealing at temperatures higher than 950 degrees C results in complete removal of irradiation damage accompained by the formation of GeAs precipitates which enhance the removal process of dislocations.
Resumo:
Diffusion of implanted As ion in relaxed Si1-xGex was studied as a function of Ge content over a wide range of Ge fractions (0-43%) and annealing temperature, and was compared to diffusion in Si. Experimental results showed that the As diffusion is enhanced with increasing annealing temperature for certain Ge content and strongly dependent on the higher Ge content and the faster As diffusion.
Resumo:
Rapid thermal annealing of arsenic implanted Si1-xGex was studied by secondary ion-mass spectroscopy (SIMS) and spreading resistance probe (SRP) over a wide range of Ge fractions (0-43%). Redistribution of the implanted arsenic was followed as a function of Ge content and annealing temperature. Arsenic concentration profiles from SIMS indicated that the behavior of implanted arsenic in Si1-xGex after RTA was different from that in Si, and the Si1-xGex samples exhibited box-shaped, concentration-dependent diffusion profiles with increasing Ge content. The maximum concentrations of electrically active arsenic in Si1-xGex was found to decrease with increasing Ge content. Experimental results showed that the arsenic diffusion is enhanced with increasing temperature for certain Ge content and strongly dependent on Ge content, and the higher Ge content, the faster As diffusion.
Resumo:
Thermally stimulated redistribution and precipitation of excess arsenic in Ge0.5Si0.5 alloy has been studied by X-ray photoelectron spectroscopy (XPS), cross sectional transmission electron microscopy (XTEM) and X-ray energy disperse spectrometry (EDS). Samples were prepared by the implantation of 6 X 10(6) As+ cm(-2) and 100 keV with subsequent thermal processing at 800 degrees C and 1000 degrees C for 1 h. The XPS depth profiles from the implanted samples before and after the thermal annealing indicate that there is marked redistribution of the elements in heavily arsenic-implanted Ge0.5Si0.5 alloys during the annealing, including: (1) diffusion of As from the implanted region to the surface; (2) aggregation of Ge in the vicinity of the surface. A high density of precipitates was observed near the surface which were by XTEM and EDS identified as an arsenide. It is suggested that most of the implanted As in Ge0.5Si0.5 alloy exists in the form of GeAs.