Modification of emission wavelength of self-assembled In(Ga)As/GaAs quantum dots covered by InxGa1-xAs(0 <= x <= 0.3) layer

Red shifts of emission wavelength of self-organized In(Cla)As/GaAs quantum dots (QDs) covered by 3 nm thick InxGa1-xAs layer with three different In mole fractions (x = 0.1, 0.2 and 0.3, respectively) have been observed. Transmission electron microscopy images demonstrate that the stress along growth direction in the InAs dots was reduced due to introducing the InxGa1-xAs (x = 0.1, 0.2 and 0.3) covering layer instead of GaAs layer. Atomic force microscopy pictures show a smoother surface of InAs islands covered by an In0.2Ga0.8As layer. It is explained by the calculations that the redshifts of the photoluminescence (PL) spectra from the QDs covered by the InxGa1-xAs (x greater than or equal to 0.1) layers were mainly due to the reducing of the strain other than the InAs/GaAs intermixing in the InAs QDs. The temperature dependent PL spectra further confirm that the InGaAs covering layer can effectively suppress the temperature sensitivity of PL emissions. 1.3 mum emission wavelength with a very narrow linewidth of 19.2 mcV at room temperature has been obtained successfully from In,In0.5Ga0.5As/GaAs self-assembled QDs covered by a 3-nm In0.2Ga0.2As strain reducing layer. (C) 2001 Elsevier Science B.V. All rights reserved.

Self-assembled quantum dots, wires and quantum-dot lasers

Molecular beam epitaxy-grown self-assembled In(Ga)As/GaAs and InAs/InAlAs/InP quantum dots (QDs) and quantum wires (QWRs) have been studied. By adjusting growth conditions, surprising alignment. preferential elongation, and pronounced sequential coalescence of dots and wires under specific condition are realized. The lateral ordering of QDs and the vertical anti-correlation of QWRs are theoretically discussed. Room-temperature (RT) continuous-wave (CW) lasing at the wavelength of 960 nm with output power of 3.6 W from both uncoated facets is achieved fi-om vertical coupled InAs/GaAs QDs ensemble. The RT threshold current density is 218 A/cm(2). A RT CW output power of 0.6 W/facet ensures at least 3570 h lasing (only drops 0.83 dB). (C) 2001 Elsevier Science B.V, All rights reserved.

Anisotropic strain in (100) ZnSe epilayers grown on lattice mismatched substrates

We show that part of the reflectance difference resonance near the E-0 energy of ZnSe is due to the anisotropic in-plane strain in the ZnSe thin films, as films grown on three distinctly different substrates, GaAs, GaP, and ZnS, all show the resonance at the same energy. Such anisotropic strain induced resonance is predicted and also observed near the E-1/E-1+Delta(1) energies in ZnSe grown on GaAs. The theory also predicts that there should be no resonance due to strain at, the E-0+Delta(0) energy, which is consistent with experiments. The strain anisotropy is rather independent of the ZnSe layer thickness, or whether the film is strain relaxed. For ZnSe films with large lattice mismatch with substrates, the resonance at the E-1/E-1+Delta(1) energies is absent, very likely due to the poor crystalline quality of the 20 nm or so surface layer. (C) 2000 American Vacuum Society. [S0734-211X(00)05604-3].

Static and dynamic electric field domain formation in a doped GaAs/AlAs superlattice

We have observed the transition from static to dynamic electric field domain formation induced by a transverse magnetic field and the sample temperature in a doped GaAs/AlAs superlattice. The observations can be very well explained by a general analysis of instabilities and oscillations of the sequential tunnelling current in superlattices based solely on the magnitude of the negative differential resistance region in the tunnelling characteristic of a single barrier. Both increasing magnetic field and sample temperature change the negative differential resistance and cause the transition between static and dynamic electric field domain formation. (C) 2000 Elsevier Science B.V. All rights reserved.

Energy band and acceptor binding energy of GaN and AlxGa1-xN

The hole effective-mass Hamiltonian for the semiconductors of wurtzite structure is established, and the effective-mass parameters of GaN and AlxGa1-xN are given. Besides the asymmetry in the z and x, y directions, the linear term of the momentum operator in the Hamiltonian is essential in determining the valence band structure, which is different from that of the zinc-blende structure. The binding energies of acceptor states are calculated by solving strictly the effective-mass equations. The binding energies of donor and acceptor for wurtzite GaN are 20 and 131, 97 meV, respectively, which are inconsistent with the recent experimental results. It is proposed that there are two kinds of acceptors in wurtzite GaN. One kind is the general acceptor such as C, substituting N, which satisfies the effective-mass theory, and the other includes Mg, Zn, Cd etc., the binding energy of which deviates from that given by the effective-mass theory. Experimentally, wurtzite GaN was grown by the MBE method, and the PL spectra were measured. Three main peaks are assigned to the DA transitions from the two kinds of acceptor. Some of the transitions were identified as coming from the cubic phase of GaN, which appears randomly within the predominantly hexagonal material. The binding energy of acceptor in ALN is about 239, 158 meV, that in AlxGa1-xN alloys (x approximate to 0.2) is 147, 111 meV, close to that in GaN. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Self-sustained oscillations caused by magnetic field in a weakly-coupled GaAs/AlAs superlattice

We have investigated the influence of transverse magnetic field B up to 14 T at 1.6 K on the tunneling processes of electric field domains in doped weakly coupled GaAs/AlAs superlattices. Three regimes, i.e, stable field domains, current self-sustained oscillations and averaged field distribution are successively observed with increasing B. The mechanisms of switching-over among these regimes are due to B-induced modification of the dependence of the effective electron drift velocity on electric field. The simulated calculation gives a good agreement with the observed experimental results. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Structural and photoelectric studies on double barrier quantum well infrared detectors

GaAs/AlAs/GaAlAs double barrier quantum well (DBQW) structures are employed for making the 3 similar to 5 mu m photovoltaic infrared (IR) detectors with a peak detectivity of 5x10(11) cmHz(1/2)/W at 80K. The double crystal x-ray diffraction is combined with synchrotron radiation x-ray analysis to determine the exact thickness of GaAs, AlAs and GaAlAs sublayers. The interband photovoltaic (PV) spect ra of the DBQW sample and the spectral response of the IR photocurrent of the devices are measured directly by edge excitation method, providing the information about spatial separation processes of photogenerated carriers in the multiquantum wells and the distribution of built-in field in the active region.

Optical anisotropy of InAs submonolayer quantum wells in a (311) GaAs matrix

The steplike density of states obtained from reflectance-difference spectroscopy demonstrates that ultrathin InAs layers should be regarded as two-dimensional quantum wells rather than isolated clusters, even for the sample with only 1/3 monolayer InAs in (311)-oriented GaAs. The degree of anisotropy is within the intrinsic anisotropy of (311)-oriented ultrathin quantum wells, indicating that there is little structural or strain anisotropy in the InAs islands. (C) 1998 Elsevier Science B.V.

Origin of flat-band voltage sharp roll-off in metal gate/high-k/ultrathin- SiO2/Si p-channel metal-oxide-semiconductor stacks

The origin of the flat band voltage roll-off (V-FB roll-off) in metal gate/high-k/ultrathin-SiO2/Si metal-oxide-semiconductor stacks is analyzed and a model describing the role of the dipoles at the SiO2/Si interface on the V-FB sharp roll-off is proposed. The V-FB sharp roll-off appears when the thickness of the SiO2 interlayer diminishes to below the oxygen diffusion depth. The results derived using our model agree well with experimental data and provide insights to the mechanism of the V-FB sharp roll-off.

Fermi-Level Pinning at Metal/High-k Interface Influenced by Electron State Density of Metal Gate

The Fermi-level pinning (FLP) at the metal/high-k interface and its dependence on the electron state density of the metal gate are investigated. It is found that the FLP is largely determined by the distortion of the vacuum level of the metal which is quantitatively ruled by the electron state density of the metal. The physical origin of the vacuum level distortion of the metal is attributed to an image charge of the interface charge in the metal. Such results indicate that the effective work function of the metal/high-k stack is also governed by the electron state density of the metal.

Molecular-dynamics investigation on polarization retention of barium titanate nanofilm arising from ordered oxygen vacancy

Molecular-dynamics simulations have been carried out to investigate the electric hysteresis of barium titanate nanofilm containing oxygen vacancy ordering array parallel to the {101} crystal plane. The results obtained show a significant weakening of polarization retention from non-zero value to zero as the size of the array was reduced to a critical level, which was attributed to the formation and motion of head-to-head domain wall structure under external field loading process. By comparing with materials containing isolated oxygen vacancies, it was found that the zero retention was due to the oxygen vacancy ordering array rather than to the concentration of oxygen vacancy. Copyright (C) EPLA, 2010

Small-scale turbulent fluctuations beyond Taylor's frozen-flow hypothesis

The space-time cross-correlation function C-T(r, tau) of local temperature fluctuations in turbulent Rayleigh-Benard convection is obtained from simultaneous two-point time series measurements. The obtained C-T(r, tau) is found to have the scaling form C-T(r(E), 0) with r(E)=[(r-U tau)(2)+ V-2 tau(2)](1/2), where U and V are two characteristic velocities associated with the mean and rms velocities of the flow. The experiment verifies the theory and demonstrates its applications to a class of turbulent flows in which the requirement of Taylor's frozen flow hypothesis is not met.

Mechanical Behavior of Nanometer Ni by MD Simulation

The indention simulation of the crystal Ni is carried out by molecular dynamics technique (MD) to study the mechanical behavior at nanometer scales, the indenter tips with sphere shape is used. Some defects such as dislocations, point defects are observed. It is found that defects (dislocations, amorphous) nucleated is from local region near the pin tip or the sample surface. The temperature distribution of local region is analyzed and it can explain our MD simulation result.

Nano-size Effect of Interface Energy and Its Effect on Interface Fracture

An analytical model about size-dependent interface energy of metal/ceramic interfaces in nanoscale is developed by introducing both the chemical energy and the structure stain energy contributions. The dependence of interface energy on the interface thickness is determined by the melting enthalpy, the molar volume, and the shear modulus of two materials composing the interfaces, etc. The analytic prediction of the interface energy and the atomic scale simulation of the interface fracture strength are compared with each other for Ag/MgO and Ni/Al2O3 interfaces, the fracture strength of the interface with the lower chemical interface energy is found to be larger. The potential of Ag/MgO interface related to the interface energy is calculated, and the interface stress and the interface fracture strength are estimated further. The effect of the interface energy on the interface strength and the behind mechanism are discussed.