γ-LiAIO2上非极性ZnO薄膜制备及其光谱性质研究

利用激光脉冲沉积（PLD）技术在（302）γ-LiAIO2衬底上成功生长了非极性的a面（112^-0）γZnO薄膜．衬底温度为350℃时，薄膜是混合取向（a向和C向），以c面ZnO为主，且晶粒尺寸分布很宽；提高温度达500℃，薄膜变为单一的（1120）取向，摇摆曲线半高宽O.65^o，晶粒尺寸分布趋窄，利用偏振透射谱可以明显看出其面内的各向异性．衬底温度650℃下制备的样品晶粒继续长大，虽然摇摆曲线半高宽变大，但光致发光谱（PL）带边发射峰半高宽仅为105meV，比在350℃，500℃下制备的样品小1／5

LiGaO_2衬底上ZnO外延膜的结构与光学特性

采用磁控溅射法在(001)、(100)及(010)LiGaO2衬底上制备了ZnO薄膜,通过X射线衍射(XRD)、原子力显微镜(AFM)、透过光谱以及光致发光谱(PL)对薄膜的结构、形貌及光学性质进行了表征。结果表明LiGaO2衬底不同晶面上制备的ZnO薄膜具有不同的择优取向,在(001)(、100)及(010)LiGaO2上分别获得了[0001][、1100]及[1120]取向的ZnO薄膜;不同取向的ZnO薄膜表面形貌差异较大;薄膜在可见光波段具有较高的透过率;在ZnO薄膜的光致发光谱中只观察到了位于378 nm的紫外发射峰,而深能级发射几乎观察不到,(1100)取向的薄膜紫外发射峰强度最大,半高宽也最小,薄膜光致发光性质的差异主要和晶粒尺寸有关。

Hydrothermal growth and characterization of ZnO crystals

ZnO crystals with dimensions of 30 x 38 x 8 turn 3 have been grown by the hydrothermal method using a mixed solution of KOH, LiOH and H2O2. The growing rates for +c(0001) and -c(000 (1) over bar) were 0.17 and 0.09 mm/day, respectively. The crystal color was very light green for +c sector and dark brown for -c sector. For the +c sector, the resistivity at room temperature was 80 0 cm, the carrier concentration was about 10(4)/cm(3), and the mobility was about 100 cm(2)/Vs. The full-width at half-maximum (FWHM) of double axis X-ray rocking curve for the polished Zn face cut from +c sector was 45 arcsec. The photoluminescence (PL) spectrum and the absorption spectrum of +c part of the crystals at room temperature were also reported and discussed in this paper. (c) 2008 Elsevier B.V. All rights reserved.

Structural and optical properties of a-plane ZnO thin films synthesized on γ-LiAlO2 (302) substrates by low pressure metal-organic chemical vapor deposition

Nonpolar a-plane (1120) ZnO thin films have been fabricated on gamma-LiAlO2 (302) substrates via the low-pressure metal-organic chemical vapor deposition. An obvious intensity variation of the E-2 mode in the Raman spectra indicates that there exhibits in-plane optical anisotropy in the a-plane ZnO thin films. Highly-oriented uniform grains of rectangular shape can be seen from the atomic force microscopy images, which mean that the lateral growth rate of the thin films is also anisotropic. It is demonstrated experimentally that a buffer layer deposited at a low temperature (200 degrees C) can improve the structural and optical properties of the epilayer to a large extent. (c) 2007 Elsevier B.V. All rights reserved.

Studies of magnetic interactions in Ni-doped ZnO from first-principles calculations

The magnetic interactions in Ni-doped ZnO are calculated using GGA and GGA + U method of density functional theory. The following three cases: (i) Ni-doped ZnO, (ii) (Ni, Al)-codoped ZnO, and (iii) (Ni, Li)-codoped ZnO are studied. The ferromagnetic ordering is always favorable for the three cases within GGA method. However, the ferromagnetic state is sometimes favorable after treating within the method of GGA + U. The GGA underestimates the correlated interactions especially when the Ni ions align directly to each other. (C) 2007 Elsevier B.V. All rights reserved.

γ-LiAlO_2上a面ZnO薄膜的光谱特性研究

利用激光脉冲沉积(PLD)技术在(302)γ-LiAlO2衬底上成功生长了非极性的a面(1120)ZnO薄膜,光致发光谱(PL)带边发射峰半峰宽仅为115meV.研究了非极性ZnO薄膜光谱特性的面内各向异性,发现随着入射光偏振方向改变,在偏振透射光谱上,吸收边移动了20meV,这与A、B激子和C激子的能量差一致;而在拉曼光谱上,激发光偏振方向的改变导致E2模式的强度发生明显改变.

Characterization of m-plane ZnO thin film on gamma-LiAlO2 (100) substrate by metal-organic chemical vapor deposition

Non-polar (1 (1) over bar 00)m-plane ZnO thin film has been prepared on gamma-LiAlO2 (100)substrate via the low pressure metal organic chemical vapor deposition. Obvious intensity variation of the E-2 mode in the polarized Raman spectra and the absorption edge shift in the polarized optical transmission spectra indicate that the m-plane film exhibits optical anisotropy, which have applications in certain optical devices, such as the UV modulator and polarization-dependent beam switch. From the atomic force microscopy images, highly-oriented uniform-sized grains of rectangular shape were observed. (c) 2008 Elsevier B.V. All rights reserved.

Enhancement of near-band edge photoluminescence of ZnO thin films by employing MgF2 buffer layer

ZnO/MgF2/ZnO sandwich structure films were fabricated. The effects of a buffer layer on structure and optical properties of ZnO films were investigated by X-ray diffraction, photoluminescence, optical transmittance and absorption measurements. Measurement results showed that the buffer layer had the effects of improving the quality of ZnO films and releasing the residual stresses in the films. The near-band edge emissions of ZnO films deposited on the MgF2 buffer layer were significantly enhanced compared with those deposited on bare substrate due to the smaller lattice mismatch between MgF2 and ZnO than that between fused silica and ZnO. (c) 2006 Elsevier B.V. All rights reserved.

Enhancement of near-band-edge photoluminescence of ZnO thin films in sandwich configuration at room temperature

ZnO/ITO/ZnO sandwich structure films were fabricated. The effects of buffer layer on the structure and optical properties of ZnO films were investigated by x-ray diffraction (XRD), photoluminescence, optical transmittance, and absorption measurements. XRD spectra indicate that a buffer layer has the effects of lowering the grain orientation of ZnO films and increasing the residual stresses in the films. The near-band-edge emissions of ZnO films deposited on both single indium tin oxide (ITO) buffer and ITO/ZnO double buffers are significantly enhanced compared with that deposited on a bare substrate due to the quantum confinement effect. (C) 2006 American Institute of Physics.

Influence of buffer layer thickness on the structure and optical properties of ZnO thin films

A series of ZnO thin films were deposited on ZnO buffer layers by DC reactive magnetron sputtering. The buffer layer thickness determination of microstructure and optical properties of ZnO films was investigated by X-ray diffraction (XRD), photoluminescence (PL), optical transmittance and absorption measurements. XRD results revealed that the stress of ZnO thin films varied with the buffer layer thickness. With the increase of buffer layer thickness, the band gap edge shifted toward longer wavelength. The near-band-edge (NBE) emission intensity of ZnO films deposited on ZnO buffer layer also varied with the increase of thickness due to the spatial confinement increasing the Coulomb interaction between electrons and holes. The PL measurement showed that the optimum thickness of the ZnO buffer layer was around 12 nm. (c) 2005 Elsevier B.V. All rights reserved.

Structure and UV emission of nanocrystal ZnO films by thermal oxidation of ZnS films

ZnO films prepared by the thermal oxidation of the ZnS films through thermal evaporation are reported. The as-deposited ZnS films have transformed to ZnO films completely at 400 degrees C. The 400-700 degrees C annealed films with a preferential c-axis (002) orientation have a hexagonal wurtzite structure. The band gap of ZnO films shifts towards longer wavelength with the increase of the annealing temperature. The relationship between the band gap energy of ZnO films and the grain size is discussed. The shift of the band gap energy can be ascribed to the quantum confinement effect in nanocrystal ZnO films. The photoluminescence spectra of ZnO films show a dominant ultraviolet emission and no deep level or trap state defect emission in the green region. It confirms the absence of interstitial zinc or oxygen vacancies in ZnO films. These results indicate that ZnO film prepared by this simple thermal oxidation method is a promising candidate for optoelectronic devices and UV laser. (c) 2005 Elsevier BN. All rights reserved.