Metalorganic Chemical Vapor Deposition of GaNAs Alloy Using Dimethylhydrazine as Nitrogen Precursor

GaNAs alloy is grown by metalorganic chemical vapor deposition (MOCVD) using dimethylhydrazine (DMHy) as the nitrogen precursor. High-resolution X-ray diffraction (HRXRD) and secondary ion mass spectrometry (SIMS) are combined in determining the nitrogen contents in the samples. Room temperature photoluminescence (RTPL) measurement is also used in characterizing. The influence of different Ga precursors on GaNAs quality is investigated. Samples grown with triethylgallium (TEGa) have better qualities and less impurity contamination than those with trimethylgallium (TMGa). Nitrogen content of 5.688% is achieved with TEGa. The peak wavelength in RTPL measurement is measured to be 1278.5nm.

High Temperature1.3μm AlGaInAs/In PStrained Multiquantum Well Laser Grownby Metalorganic Vapor Phase Epitaxy

国家863计划

InGaAs/GaAs/InGaP Strained quantum well lasers grown by metalorganic chemical vapor deposition

于2010-11-23批量导入

Polymorphous silicon nanowires synthesized by plasma-enhanced chemical vapor deposition

Polymorphous Si nanowires (SiNWS) have been successfully synthesized on Si wafer by plasma enhanced chemical vapor deposition (PECVD) at 440degreesC,using silane as the Si source and Au as the catalyst. To grow the polymorphous SiNWS preannealing the Si substrate with Au film at 1100 degreesC is needed. The diameters of Si nanowires range from 15 to 100 urn. The structure morphology and chemical composition of the SiNWS have been characterized by high resolution x-ray diffraction, scanning electron microscopy, transmission electron microscopy, as well as energy dispersive x-ray spectroscopy. A few interesting nanowires with Au nanoclusters uniformly distributed in the body of the wire were also produced by this technique.

Thermodynamic analysis of GaSb-GaCl3 vapor phase epitaxy

A thermodynamic model for the GaSb-GaCl3 system in a closed quartz ampoule was proposed. The species in the gas phase are GaCl, GaCl3, Sb-4, Sb-2. The partial pressures of these species and total pressure in the ampoule have been calculated. The calculated results indicate that the equilibrium partial pressures of GaCl, GaCl3, Sb4, Sb2 and the total pressure in the ampoule have strong dependence on temperature, free volume inside the closed ampoule and amount of transport agent GaCl3. The total pressure will give strong influence not only on the flow pattern in the ampoule, but also on the uniformity of the epilayer.

The growth and characterization of GaN grown on a gamma-Al2O3/(001) Si substrate by metalorganic vapor phase epitaxy

Wurtzite single crystal GaN films have been grown onto a gamma-Al2O3/Si(001) substrate in a horizontal-type low pressure MOVPE system. A thin gamma-Al2O3 layer is an intermediate layer for the growth of single crystal GaN on Si although it is only an oriented polycrystal film as shown by reflection high electron diffraction. Moreover, the oxide is not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN layer as studied by transmission electron microscopy. Double crystal x-ray linewidth of (0002) peak of the 1.3 mu m sample is 54 arcmin and the films have heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature is observed by photoluminescence spectroscopy. Raman scattering does not detect any cubic phase coexistence.

Applications of dielectric thin film by electron cyclotron resonance plasma chemical vapor deposition for semiconductor photoelectronic devices

The paper reports a method of depositing SiO2, SiNx, a:Si, Si3N4 and SiOxNy dielectric thin films by electron cyclotron resonance plasma chemical vapor deposition (ECR CVD) on InP, InGaAs and other compound semiconductor optoelectronic devices,and give a technology of depositing dielectric thin films and optical coatings by ECR CVD on Laser's Bars. The experiment results show the dielectric thin films and optical coatings are stable at thermomechanical property,optical properties and the other properties. In addition, the dielectric thin film deposition that there is low leakage current is reported for using as diffusion and ion implatation masks in the paper. In the finally, the dielectric film refractive index can be accurately controlled by the N-2/O-2/Ar gas flow rate.

Influences of initial nitridation process on the optical and structural characterization of GaN layer grown on sapphire (0001) by metalorganic chemical vapor deposition

In this paper. we investigate the influences of the initial nitridation of sapphire substrates on the optical and structural characterizations in GaN films. Two GaN samples with and without 3 min nitridation process were investigated by photoluminescence (PL) spectroscopy in the temperature range of 12-300 K and double-crystal X-ray diffraction (XRD). In the 12 K PL spectra of the GaN sample without nitridation, four dominant peaks at 3.476, 3.409 3.362 and 3.308 eV were observed, which were assigned to donor bound exciton, excitons bound to stacking faults and extended structural defects. In the sample with nitridation, three peaks at 3.453, 3.365. and 3.308 eV were observed at 12 K, no peak related to stacking faults. XRD results at different reflections showed that there are more stacking faults in the samples without nitridation.

Defect states in cubic GaN epilayer grown on GaAs by metalorganic vapor phase epitaxy

Defect states in cubic GaN epilayers grown on GaAs were investigated with the photoluminescence technique. One shallow donor and two acceptors were identified to be involved in relevant optical transitions. The binding energies of the free excitons, the bound excitons. the donor and the acceptors were determined. These values are in good agreement with recent theoretical results.

The content calculation of hexagonal phase inclusions in cubic GaN films on GaAs(001) substrates grown by metalorganic chemical vapor deposition

Cubic GaN(c-GaN) films are grown on GaAs(001) substrates by metalorganic chemical vapor deposition (MOCVD). Two GaN samples were grown with different buffer layer, the deposition time of each was 1 and 3 min, respectively. 4-circle X-ray double crystal diffraction (XRDCD) was used to study the secondary crystallographic phases presented in the c-GaN films. The phase composition of the epilayers was determined by X-ray reciprocal space mapping. The intensities of the c-GaN(002) and h-GaN(10 (1) over bar 1) planes detected in the mapping were investigated by omega scans. The content of the hexagonal phase inclusions in the c-GaN films was calculated to about 1.6 and 7.9%, respectively. The thicker buffer layer is not preferable for growing high quality pure c-GaN films. (C) 2000 Elsevier Science S.A. All rights reserved.

Influences of initial buffer layer deposition on electrical and optical properties in cubic GaN grown on GaAs(100) by metalorganic chemical vapor deposition

We present some results on the effect of initial buffer layer on the crystalline quality of Cubic GaN epitaxial layers grown on GaAs(100) substrates by metalorganic chemical vapor deposition. Photoluminescence and Hall measurements were performed to characterize the electrical and optical properties of cubic GaN. The crystalline quality subsequently grown high-temperature (HT) cubic GaN layers strongly depended on thermal effects during the temperature ramping process after low temperature (LT) growth of the buffer layers. Atomic force microscope (AFM) and reflection high-energy electron diffraction (RHEED) were employed to investigate this temperature ramping process. Furthermore, the role of thermal treatment during the temperature ramping process was identified. Using the optimum buffer layer, the full width at half maxim (FWHM) at room temperature photoluminescence 5.6 nm was achieved. To our knowledge, this is the best FWHM value for cubic GaN to date. The background carrier concentration was as low as 3 x 10(13) cm(-3). (C) 2000 Published by Elsevier Science S.A. All rights reserved.

The influence of thickness on properties of GaN buffer layer and heavily Si-doped GaN grown by metalorganic vapor-phase epitaxy

The physical properties of low-temperature-deposited GaN buffer layers with different thicknesses grown by metal-organic vapor-phase epitaxy have been studied. A tentative model for the optimum thickness of buffer layer has been proposed. Heavily Si-doped GaN layers have been grown using silane as the dopant. The electron concentration of Si-doped GaN reached 1.7 x 10(20) cm(-3) with mobility 30 cm(2)/V s at room temperature. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

The role of zinc dopant and the temperature effect on the controlled growth of InNnanorods in metal-organic chemical vapor deposition system

This work was supported by the National Science Foundation of China (60976008 and 60776015), the Special Funds for Major State Basic Research Project (973 program) of China (2006CB604907), and the 863 High Technology R&D Program of China (2007AA03Z402 and 2007AA03Z451). The authors express their appreciations to Prof. Yongliang Li (Analytical and Testing Center, Beijing Normal University) for FE-SEM measurements, to DrTieying Yang and Prof. Huanhua Wang (Beijing Synchrotron Radiation Facility, Institute of High Energy Physics, Chinese Academy of Sciences) for XRD measurements and helpful discussions.