Germanium MOS Capacitors with Hafnium Dioxide and Silicon Dioxide Dielectrics

Germanium (Ge) does not grow a suitable oxide for MOS devices. The Ge/dielectric interface is of prime importance to the operation of photo-detectors and scaled MOSTs. Therefore there is a requirement for deposited or bonded dielectric materials. MOS capacitors have been formed on germanium substrates with three different dielectric materials. Firstly, a thermally grown and bonded silicon dioxide (SiO2) layer, secondly, SiO2 deposited by atmospheric pressure CVD ‘silox’, and thirdly a hafnium oxide (HfO2) high-k dielectric deposited by atomic layer deposition (ALD). Ge wafers used were p-type 1 0 0 2 O cm. C–V measurements have been made on all three types of capacitors to assess the interface quality. ALD HfO2 and silox both display acceptable C–V characteristics. Threshold voltage and maximum and minimum capacitance values closely match expected values found through calculation. However, the bonded SiO2 has non-ideal C–V characteristics, revealing the presence of a high density of interface states. A H2/N2 post metal anneal has a detrimental effect on C–V characteristics of HfO2 and silox dielectrics, causing a shift in the threshold voltage and rise in the minimum capacitance value. In the case of hafnium dioxide, capacitor properties can be improved by performing a plasma nitridation of the Ge surface prior to dielectric deposition.

Comparative analysis of nanoscale MOS device architectures for RF applications

This paper provides valuable design insights for optimizing device parameters for nanoscale planar and vertical SOI MOSFETs. The suitability of nanoscale non-planar FinFETs and classical planar single and double gate SOI MOSFETs for rf applications is examined via extensive 3D device simulations and detailed interpretation. The origin of higher parasitic capacitance in FinFETs, compared to planar MOSFETs is examined. RF figures of merit for planar and vertical MOS devices are compared, based on layout-area calculations.

Second harmonic generation in h-BN and MoS2 monolayers: Role of electron-hole interaction

We study second-harmonic generation in h-BN and MoS$_2$ monolayers using a novel \emph{ab initio} approach based on Many-body theory. We show that electron-hole interaction doubles the signal intensity at the excitonic resonances with respect to the contribution from independent electronic transitions. This implies that electron-hole interaction is essential to describe second-harmonic generation in those materials. We argue that this finding is general for nonlinear optical properties in nanostructures and that the present methodology is the key to disclose these effects.

Electrical Characterisation of SOI Substrates Incorporating WSix Ground Planes

Silicon-on-insulator (SOI) substrates incorporating tungsten silicide ground planes (GPs) have been shown to offer the lowest reported crosstalk figure of merit for application in mixed signal integrated circuits. The inclusion of the silicide layer in the structure may lead to stress or defects in the overlying SOI layers and resultant degradation of device performance. It is therefore essential to establish the quality of the silicon on the GPSOI substrate. MOS capacitor structures have been employed in this paper to characterize these GPSOI substrates for the first time. High quality MOS capacitor characteristics have been achieved with minority carrier lifetime of similar to 0.8 ms. These results show that the substrate is suitable for device manufacture with no degradation in the silicon due to stress or metallic contamination resulting from the inclusion of the underlying silicide layer.

Low temperature surface nitridation processes for dielectric-Ge interfaces

Germanium MOS capacitors have been fabricated with a high-? HfO dielectric using ALD. An in-situ low temperature (250°C) nitrogen plasma treatment on the germanium surface prior to the deposition of HfO was found to be beneficial to the electrical properties of the devices. Germanium MOS capacitors have also been fabricated with a SiO dielectric deposited by an atmospheric pressure CVD 'silox' process. The same low temperature plasma nitridation was found to degrade the electrical properties of the silox devices. The effect of a post-metal anneal in H and N on both types of capacitor structure was also found to degrade device electrical properties. copyright The Electrochemical Society.

Atomic layer deposition of hafnium oxide dielectrics on silicon and germanium substrates

Hafnium oxide films have been deposited at 250 °C on silicon and germanium substrates by atomic layer deposition (ALD), using tetrakis-ethylmethylamino hafnium (TEMAH) and water vapour as precursors in a modified Oxford Instruments PECVD system. Self-limiting monolayer growth has been verified, characterised by a growth rate of 0.082 nm/ cycle. Layer uniformity is approximately within ±1% of the mean value. MOS capacitors have been fabricated by evaporating aluminium electrodes. CV analysis has been used to determine the bulk and interface properties of the HfO 2, and their dependence on pre-clean schedule, deposition conditions and post-deposition annealing. The dielectric constant of the HfO 2 is typically 18. On silicon, best results are obtained when the HfO 2 is deposited on a chemically oxidised hydrophilic surface. On germanium, best results are obtained when the substrate is nitrided before HfO 2 deposition, using an in-situ nitrogen plasma treatment. © Springer Science+Business Media, LLC 2007.