Microstructure and laser-induced damage threshold of ZrO2 coatings dependence on annealing temperature

ZrO2 coatings were deposited on different substrates of Yb:YAG and fused silica by electron beam evaporation. After annealed for 12 h at 673 and 1073 K, respectively, weak absorption of coatings was measured by surface thermal lensing (STL) technique, and then laser-induced damage threshold (LIDT) was determined also. The crystalline phase of ZrO2 coatings and the size of the crystal grain were investigated by X-ray diffraction. It was found that microstructure of ZrO2 coatings was dependent on both annealing temperature and substrate structure, and coatings containing monoclinic phases had higher damage threshold than others. Due to the strong absorption of Yb:YAG, damage threshold of coatings on Yb:YAG was much less than that on fused silica. (C) 2004 Elsevier B.V. All rights reserved.

应用离子后处理技术提高薄膜激光损伤阈值

利用电子束热蒸发方法在K9玻璃基底上沉积氧化锆薄膜,并对其中一些样品用低能O2^+进行了后处理.采用表面热透镜技术测量薄膜样品表面弱吸收,采用显微镜观察样品离子后处理前后的显微缺陷密度.测试结果表明:经离子后处理样品表面的缺陷密度从18.6/mm^2降低到6.2/mm^2,且其激光损伤阈值从15.9 J/cm^2提高到23.1 J/cm^2,样品的平均吸收率从处理前的1.147×10^-4降低到处理后的9.56×10^-5.通过对处理前后样品的表面微缺陷密度、吸收率及损伤形貌等的分析发现:离子后处理可以降

氧分压对ZrO2薄膜激光损伤阈值的影响

在不同的氧分压下用电子束热蒸发的方法制备了ZrO2薄膜。分别通过X射线衍射、光学光谱、热透镜技术、抗激光辐照等测试，对所制备样品的微结构、折射率、吸收率及激光损伤阈值进行了测量。实验结果表明，薄膜中晶粒主要是四方相为主的多晶结构，并且随着氧分压的增加，结晶度、折射率以及弱吸收均逐渐降低。薄膜的激光损伤阈值开始随着氧分压增加从18．5J／cm^2逐渐增加，氧分压为9×10^-3Pa时达到最大，值为26．7J／cm^2，氧分压再增加时则又降低到17．5J／cm^2。由此可见，氧分压引起的薄膜微结构变化是ZrO

Influence of negative ion element impurities on laser induced damage threshold of HfO2 thin film

Negative ion element impurities breakdown model in HfO2 thin film was reported in this paper. The content of negative ion elements were detected by glow discharge mass spectrum analysis (GDMS); HfO2 thin films were deposited by the electron-beam evaporation method. The weak absorption and laser induced damage threshold (LIDT) of HfO2 thin films were measured to testify the negative ion element impurity breakdown model. It was found that the LIDT would decrease and the absorption would increase with increasing the content of negative ion element. These results indicated that negative ion elements were harmful impurities and would speed up the damage of thin film. (c) 2006 Elsevier B.V. All rights reserved.

负离子元素杂质破坏模型

探讨了HfO2薄膜中负离子元素杂质破坏模型，并得出薄膜中的杂质主要来源于镀膜材料。用电子束蒸发方法沉积两种不同Cl元素古量的HfO2薄膜，测定薄膜弱吸收和损伤阈值来验证负离子元素破坏模型。结果表明，随着Cl元素含量的增加薄膜的弱吸收增加损伤阈值减小。这主要是因为负离子元素在蒸发过程中形成挥发性的气源中心而产生缺陷，缺陷在激光辐照过程中又形成吸收中心．因此负离子元素的存在将加速薄膜的破坏。

Investigation on the properties of high reflective mirror prepared by ion-beam sputtering

The single-sided and dual-sided high reflective mirrors were deposited with ion-beam sputtering (IBS). When the incident light entered with 45 degrees, the reflectance of p-polarized light at 1064 nm exceeded 99.5%. Spectrum was gained by spectrometer and weak absorption of coatings was measured by surface thermal lensing (STL) technique. Laser-induced damage threshold (LIDT) was determined and the damage morphology was observed with Lecia-DMRXE microscope simultaneously. The profile of coatings was measured with Mark III-GPI digital interferometer. It was found that the reflectivity of mirror exceeded 99.9% and its absorption was as low as 14 ppm. The reflective bandwidth of the dual-sided sample was about 43 nm wider than that of single-sided sample, and its LIDT was as high as 28 J/cm2, which was 5 J/cm2 higher than that of single-sided sample. Moreover, the profile of dual-sided sample was better than that of substrate without coatings.

High laser-induced damage threshold HfO2 films prepared by ion-assisted electron beam evaporation

HfO2 films were deposited by electron beam evaporation with different deposition parameters. The properties such as refractive index, weak absorption, and laser induced damage thresholds (LIDTs) of these films have been investigated. It was found that when pulsed Nd:YAG 1064 nm laser is used to investigate LIDT of films: Metallic character is the main factor that influences LIDTs of films obtained from Hf starting material by ion-assisted reaction, and films prepared with higher momentum transfer parameter P have fewer metallic character; The ion-assisted reaction parameters are key points for preparing high LIDT films and if the parameters are chose properly, high LIDT films can be obtained. (c) 2004 Elsevier B.V. All rights reserved.

1064nm倍频波长分离膜的制备与性能研究

通过对主膜系添加匹配层并借助计算机对膜系进行优化，设计出结构规整、性能优良的1064ilm倍频波长分离膜。用电子束蒸发及光电极值监控技术在K9玻璃基底上沉积薄膜，将样品置于空气中在260℃温度下进行3h热退火处理。然后用Lambda 900分光光度计测量了样品的光谱性能；用表面热透镜(STL)技术测量了样品的弱吸收值；用调Q脉冲激光装置测试了样品的抗激光损伤阈值(LIDT)。实验结果发现，样品的实验光谱性能与理论光谱性能有很好的一致性。退火前后其光谱性能几乎没有发生温漂，说明薄膜的温度稳定性好；同时退火使

退火对ZrO2薄膜微结构及激光损伤阈值的影响

利用电子束蒸发方法在Yb:YAG晶体和熔融石英衬底上沉积单层ZrO2薄膜,分别在673 K和1 073 K的温度下经过12 h退火以后,通过X射线衍射(XRD)分析了薄膜晶相,计算了薄膜的晶粒尺寸;利用表面热透镜技术获得了薄膜的吸收;测量了退火后薄膜的激光损伤阈值.实验结果表明:两种衬底上的薄膜结构受到退火温度和衬底表面结构的影响,高温退火有利于单斜相的形成,含单斜相的ZrO2薄膜具有较高的激光损伤阈值,而由于衬底的吸收,Yb:YAG晶体上薄膜的损伤阈值远小于石英衬底上薄膜的损伤阈值.

Influence of annealing temperature on structure, optical loss and laser-induced damage threshold of TiO2 thin films

TiO2 thin films are prepared on fused silica with conventional electron beam evaporation deposition. After annealed at different temperatures for 4h, the spectra and XRD patterns of the TiO2 thin film are obtained. Weak absorption of coatings is measured by the surface thermal lensing technique, and laser-induced damage threshold (LIDT) is determined. It is found that with the increasing annealing temperature, the transmittance of TiO2 films decreases. Especially when coatings are annealed at high temperature over 1173K, the optical loss is very serious. Weak absorption detection indicates that the absorption of coatings decreases firstly and then increases, and the absorption and defects play major roles in the LIDT of TiO2 thin films.

Preparation of high laser induced damage threshold antireflection film using interrupted ion assisted deposition

Single layers and antireflection films were deposited by electron beam evaporation, ion assisted deposition and interrupted ion assisted deposition, respectively. Antireflection film of quite high laser damage threshold (18J/cm(2)) deposited by interrupted ion assisted deposition were got. The electric field distribution, weak absorption, and residual stress of films and their relations to damage threshold were investigated. It was shown that the laser induced damage threshold of film was the result of competition of disadvantages and advantages, and interrupted ion assisted deposition was one of the valuable methods for preparing high laser induced damage threshold films. (c) 2007 Optical Society of America

基底对光学薄膜弱吸收测量的影响

对表面热透镜技术测量光学薄膜弱吸收低频调制时不同基底对测量的影响进行了理论分析。用Lambda-900分光光度计测量了K9和石英基底的Ti3O5单层膜的吸收值，将该组样品作为定标片；用表面热透镜装置分别测量了BK7和石英空白基底及HfO2，ZnO两组不同基底不同厚度单层膜样品的吸收。通过分析比较同一工艺条件下镀制的不同基底薄膜样品用与其同种和不同种基底定标片定标测量的结果，表明在低频测量时需要用与测量样品同种基底的定标片定标；不同厚度样品的测量结果表明，在不能严格满足热薄条件时，测量结果需引入修正值。

Influences of CO2 laser annealing on mechanical and laser-induced damage properties of ZrO2 thin films

Zirconium dioxide (ZrO2) thin films were deposited on BK7 glass substrates by the electron beam evaporation method. A continuous wave CO2 laser was used to anneal the ZrO2 thin films to investigate whether beneficial changes could be produced. After annealing at different laser scanning speeds by CO2 laser, weak absorption of the coatings was measured by the surface thermal lensing (STL) technique, and then laser-induced damage threshold (LIDT) was also determined. It was found that the weak absorption decreased first, while the laser scanning speed is below some value, then increased. The LIDT of the ZrO2 coatings decreased greatly when the laser scanning speeds were below some value. A Nomarski microscope was employed to map the damage morphology, and it was found that the damage behavior was defect-initiated both for annealed and as-deposited samples. The influences of post-deposition CO2 laser annealing on the structural and mechanical properties of the films have also been investigated by X-ray diffraction and ZYGO interferometer. It was found that the microstructure of the ZrO2 films did not change. The residual stress in ZrO2 films showed a tendency from tensile to compressive after CO, laser annealing, and the variation quantity of the residual stress increased with decreasing laser scanning speed. The residual stress may be mitigated to some extent at proper treatment parameters. (c) 2007 Elsevier GmbH. All rights reserved.

Influence of substoichiometer on the laser-induced damage characters of HfO2 thin films

HfO2 is one of the most important high refractive index materials for depositing high power optical mirrors. In this research, HfO2 thin films were prepared by dual-ion beam reactive sputtering method, and the laser-induced damage thresholds (LIDT) of the sample were measured in 1-on-1 mode for laser with 1064 nm wavelength. The results indicate that the LIDT of the as-grown sample is only 3.96 J/cm(2), but it is increased to 8.98 J/cm(2) after annealing under temperature of 200 degrees C in atmosphere. By measuring the laser weak absorption and SIMS of the samples, we deduced that substoichiometer is the main reason for the low LIDT of the as-grown sample, and the experiment results were well explained with the theory of electronic-avalanche ionization. (C) 2008 Elsevier B.V. All rights reserved.