氢氧化锂存在下（焦）脱镁叶绿酸-a甲酯的空气重排反应

在氢氧化锂存在下，脱镁叶绿酸-a甲酯（1a）发生空气氧化和重排反应，经盐酸酸化和重氮甲烷甲基化，得到由紫红素-7三甲酯（2）、紫红素-18甲酯（3）、卟吩-P6三甲酯（4）、地质卟啉衍生物（5）和3-环氧乙基-3-去乙烯基紫红素-18甲酯（6）所组成的混合物．用相同的方法处理焦脱镁叶绿酸-a甲酯（1b），则分离出13^2-氧代焦脱镁叶绿酸-a甲酯（7）、15-甲酰基紫红素-5二甲酯（8）、紫红素-18甲酯（3）和3-环氧乙基-3-去乙烯基紫红素-18甲酯（6）-所得新叶绿素衍生物5，6和8的化学结构均经UV，IR，^1H NMR及元素分析得以证实，并对相应的反应提出可能的反应机理．

An auto-focusing method for imaging ellipsometry system

An auto-focusing method based on the image brightness gradient sharpness function is presented for imaging ellipsometry system, in which the image plane of the thin-film specimen is not perpendicular to the optical axis. The clear image of a specimen with large area is obtained by moving the imaging sensor in optical axis direction and around its sensitive surface centre successively. The experimental results demonstrate its feasibility.

An automatic imaging spectroscopic ellipsometer for characterization of nano-film pattern on solid substrate

In order to characterize the physical and spatial properties of nano-film pattern on solid substrates, an automatic imaging spectroscopic ellipsometer (ISE) based on a polarizer - compensator - specimen - analyzer configuration in the visible region is presented. It can provide the spectroscopic ellipsometric parameters psi (x, y, lambda) and Delta (x, y, lambda) of a large area specimen with a lateral resolution in the order of some microns. A SiO2 stepped layers pattern is used to demonstrate the function of the ISE which shows potential application in thin film devices' such as high-throughput bio-chips.

Hydrogen sensors based on Pt-AlGaN/GaN back-to-back Schottky diode

In this paper, platinum (Pt) with a thickness of 45 nm was sputtered on the surface of AlGaN/GaN heterostructure to form the Schottky contact and the back-to-back Schottky diodes were characterized for H-2 sensing at room temperature. Both the forward and reverse current of the devices increased with exposure to H-2 gas, which was attributed to Schottky barrier height reduction caused by hydrogen absorption in the catalytic metals. A shift of 0.7 V at 297 K was obtained at a fixed forward current of 0.1 mA after switching from N-2 to 40% H-2 in N-2. The sensor's responses under different concentrations from 2500 ppm H-2 to 40% H-2 in N-2 at 297 K were investigated. Time response of the sensor at a fixed bias of 1 V was given. Finally, the decrease of the Schottky barrier height and the sensitivity of the sensor were calculated. (C) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

AlGaN/GaN/InGaN/GaN DH-HEMTs structure with an AlN interlayer grown by MOCVD

A novel AlGaN/GaN/GaN/GaN double heterojunction high electron mobility transistors (DH-HEMTS) structure with an AlN interlayer on sapphire substrate has been grown by MOCVD. The structure featured a 6-10 nm In0.1Ga0.9N layer inserted between the GaN channel and GaN buffer. And wer also inserted one ultrathin. AlN interlayer into the Al/GaN/GaN interface, which significantly enhanced the mobility of two-dimensional electron gas (2DEG) existed in the GaN channel. AFM result of this structure shows a good surface morphology and a low dislocation density, with the root-mean-square roughness (RMS) of 0.196 nm for a scan area of 5 mu m x 5 mu m. Temperature dependent Hall measurement was performed on this sample, and a mobility as high as 1950 cm(2)/Vs at room temperature (RT) was obtained. The sheet carrier density was 9.89 x10(12) cm(2), and average sheet resistance of 327 Omega/sq was achieved. The mobility obtained in this paper is about 50% higher than other results of similar structures which have been reported. (c) 2008 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Optical and electrical investigation of low dimensional self-assembled InAs quantum dot field effect transistors

Self-assembled InAs QD dot-in-a-well (DWELL) structures were grown on GaAs substrate by MBE system, and heterojunction modulation-doped field effect transistor (MODFET) was fabricated. The optical properties of the samples show that the photoluminescence of InAs/GaAs self-assembled quantum dot (SAQD) is at 1.265 mu m at 300 K. The temperature-dependence of the abnormal redshift of InAs SAQD wavelength with the increasing temperature was observed, which is closely related with the inhomogeneous size distribution of the InAs quantum dot. According to the electrical measurement, high electric field current-voltage characteristic of the MODFET device were obtained. The embedded InAs QD of the samples can be regard as scattering centers to the vicinity of the channel electrons. The transport property of the electrons in GaAs channel will be modulated by the QD due to the Coulomb interaction. It has been proposed that a MODFET embedded with InAs QDs presents a novel type of field effect photon detector.

Lateral intersubband photocurrent study on InAs/InAlas/InP self-assembled nanostructures

We present lateral intersubband photocurrent (PC) study on self-assembled InAs/InAIAs/InP(001) nanostructures in normal incidence. With the help of interband excitation, a broad PC signal has been observed in the photon energy range of 150-630 meV arising from the bound-to-continuum intersubband absorption in the InAs nanostructures. The large linewidth of the intersubband PC signal is due to the size inhomogeneity of the nanostructures. With the increase of the interband excitation the intersubband PC signal firstly increases with a redshift of PC peak and reaches its maximum, then decreases with no peak shift. The increase and redshift of the PC signal at low excitation level can be explained by the state filling effect. However, the decrease of PC signal at high excitation level may be due to the change of the mobility and lifetime of the electrons. The intersubband PC signal decreases when the temperature is increased, which can be explained by the decrease of the mobility and lifetime of the electrons and the thermal escape of electrons.

Corrugated surfaces formed on GaAs (331)a substrates: The template for laterally ordered InGaAs nanowires

Morphology evolution of high-index (331)A surfaces during molecular beam epitaxy (MBE) growth have been investigated in order to uncover their unique physic properties and fabricate spatially ordered low dimensional nanostructures. Atomic Force Microscope (AFM) measurements have shown that the step height and terrace width of GaAs layers increase monotonically with increasing substrate temperature in conventional MBE. However, this situation is reversed in atomic hydrogen-assisted MBE, indicating that step bunching is partly suppressed. We attribute this to the reduced surface migration length of Ga adatoms with atomic hydrogen. By using the step arrays formed on GaAs (331)A surfaces as the templates, we fabricated laterally ordered InGaAs self-aligned nanowires.

Tuning of emission wavelength of InAs/GaAs quantum dots sandwiched by combination layers

We investigate about controlling of photoluminescence (PL) wavelengths of InAs/GaAs self-assembled quantum dots (QDs) sandwiched with combination strained-buffer layer (CSBL) and combination strained-reducing layer (CSRL). The emission peak position of QDs is red-shifted to 1.37 mu m. The density of the QDs is increased to 1.17x10(10) cm(-2). It is indicated that optical properties of QDs could be improved by optimizing of the buffer and covering layers for the QDs. These results may provide a new way to further developing GaAs-based 1.3 mu m light sources.

Surface morphology evolution of strained InAs/GaAs(331)a films

Surface morphology evolution of strained InAs/GaAs(331)A films was systematically investigated in this paper. Under As-rich conditions, InAs elongated islands aligned along [1 (1) over bar0] are formed at a substrate temperature of 510 degrees C. We explained it as a result of the anisotropic diffusion of adatoms. Under In-rich conditions, striking change has occurred with respect to the surface morphology of the InAs layers. Instead of anisotropic InAs elongated islands, unique island-pit pairs randomly distributed on the whole surface were observed. Using cooperative nucleation mechanisms proposed by Jesson et al. [Phys. Rev. Lett. 77, 1330 (1996)], we interpret the resulting surface morphology evolution.

PREDICTION OF VORTEX-INDUCED VIBRATION OF FLEXIBLE RISER USING AN IMPROVED WAKE-OSCILLATOR MODEL

Based on improving the wake-oscillator model, an analytical model for vortex-induced vibration (VIV) of flexible riser under non-uniform current is presented, in which the variation of added mass at lock-in and the nonlinear relationship between amplitude of response and reduced velocity are considered. By means of empirical formula combining iteration computation, the improved analytical model can be conveniently programmed into computer code with simpler and faster computation process than CFD so as to be suitable to application of practical engineering. This model is validated by comparing with experimental result and numerical simulation. Our results show that the improved model can predict VIV response and lock-in region more accurately. At last, illustrative examples are given in which the amplitude of response of flexible riser experiencing VIV under action of non-uniform current is calculated and effects of riser tension and flow distribution along span of riser are explored. It is demonstrated that with the variation of tension and flow distribution, lock-in region of mode behaves in different way, and thus the final response is a synthesis of response of locked modes.