3C-SiC/Si材料的生长及其质量表征方法的研究

Submitted by zhangdi (zhangdi@red.semi.ac.cn) on 2009-04-13T11:45:31Z

用于MEMS器件的大面积3C-SiC薄膜的制备方法

Submitted by zhangdi (zhangdi@red.semi.ac.cn) on 2009-06-04T08:36:34Z No. of bitstreams: 1 dspace.cfg: 33388 bytes, checksum: ac9630d3fdb36a155287a049e8b34eb7 (MD5)

Doped polycrystalline 3C-SiC films deposited by LPCVD for radio-frequency MEMS applications

Polycrystalline 3C-SiC films are deposited on SiO2 coated Si substrates by low pressure chemical vapour deposition (LPCVD) with C3H8 and SiH4 as precursors. Controlled nitrogen doping is performed by adding NH3 during SiC growth to obtain the low resistivity 3C-SiC films. X-ray diffraction (XRD) patterns indicate that the deposited films are highly textured (111) orientation. The surface morphology and roughness are determined by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The surface features are spherulitic texture with average grain size of 100 nm, and the rms roughness is 20nm (AFM 5 x 5 mu m images). Polycrystalline 3C-SiC films with highly orientational texture and good surface morphology deposited on SiO2 coated Si substrates could be used to fabricate rf microelectromechanical systems (MEMS) devices such as SiC based filters.

Nature of interfacial defects and their roles in strain relaxation at highly lattice mismatched 3C-SiC/Si (001) interface

Misfit defects in a 3C-SiC/Si (001) interface were investigated using a 200 kV high-resolution electron microscope with a point resolution of 0.194 nm. The [110] high-resolution electron microscopic images that do not directly reflect the crystal structure were transformed into the structure map through image deconvolution. Based on this analysis, four types of misfit dislocations at the 3C-SiC/Si (001) interface were determined. In turn, the strain relaxation mechanism was clarified through the generation of grow-in perfect misfit dislocations (including 90 degrees Lomer dislocations and 60 degrees shuffle dislocations) and 90 partial dislocations associated with stacking faults. (C) 2009 American Institute of Physics. [doi:10.1063/1.3234380]

Synthesis of GaN nanotip triangle pyramids on 3C-SiC epilayer/Si substrates via an in situ In-doping technique

GaN nanotip triangle pyramids were synthesized on 3C-SiC epilayer via an isoelectronic In-doping technique. The synthesis was carried out in a specially designed two-hot-boat chemical vapor deposition system. In (99.999%) and molten Ga (99.99%) with a mass ratio of about 1:4 were used as the source, and pieces of Si (111) wafer covered with 400-500 nm 3C-SiC epilayer were used as the substrates. The products were analyzed by x-ray diffraction, field emission scanning electron microscopy, high-resolution transmission electron microscopy, selected area electron diffraction, Raman spectroscopy, and photoluminescence measurements. Our results show that the as-synthesized GaN pyramids are perfect single crystal with wurtzite structure, which may have potential applications in electronic/photonic devices.

Atomic configurations of dislocation core and twin boundaries in 3C-SiC studied by high-resolution electron microscopy

The defects in 3C-SiC film grown on (001) plane of Si substrate were studied using a 200 kV high-resolution electron microscope with point resolution of 0.2 nm. A posterior image processing technique, the image deconvolution, was utilized in combination with the image contrast analysis to distinguish atoms of Si from C distant from each other by 0.109 nm in the [110] projected image. The principle of the image processing technique utilized and the related image contrast theory is briefly presented. The procedures of transforming an experimental image that does not reflect the crystal structure intuitively into the structure map and of identifying Si and C atoms from the map are described. The atomic configurations for a 30 degrees partial dislocation and a microtwin have been derived at atomic level. It has been determined that the 30 degrees partial dislocation terminates in C atom and the segment of microtwin is sandwiched between two 180 degrees rotation twins. The corresponding stacking sequences are derived and atomic models are constructed according to the restored structure maps for both the 30 degrees partial dislocation and microtwin. Images were simulated based on the two models to affirm the above-mentioned results.

Strain accommodation of 3C-SiC grown on hydrogen-implanted Si (001) substrate

The hydrogen-implanted Si substrate has been used for the fabrication of the "compliant substrate", which can accommodate the mismatch strain during the heteroepitaxy. The compliance of the substrate can be modulated by the energy and dose of implanted hydrogen. In addition, the defects caused by implantation act as the gettering center for the internal gettering of the harmful metallic impurities. Compared with SiC films growth on substrate without implantation. all the measurements indicated that the mismatch strains in the SiC films grown on this substrate have been released and the crystalline qualities have been improved. It is a practical technique used for the compliant substrate fabrication and compatible with the semiconductor industry. (C) 2003 Elsevier B.V. All rights reserved.

In situ doping of 3C-SiC grown on (0001) sapphire substrates by LPCVD

The heteroepitaxial growth of n-type and p-type 3C-SiC on (0001) sapphire substrates has been performed with a supply of SiH4+C2H4+H-2 system by introducing ammonia (NH3) and diborane (B2H6) precursors, respectively, into gas mixtures. Intentionally incorporated nitrogen impurity levels were affected by changing the Si/C ratio within the growth reactor. As an acceptor, boron can be added uniformly into the growing 3C-SiC epilayers. Nitrogen-doped 3C-SiC epilayers were n-type conduction, and boron-doped epilayers were p-type and probably heavily compensated.

Comprehensive analysis of microtwins in the 3C-SiC films on Si(001) substrates

Microtwins in the 3C-SiC films grown on Si(0 0 1) by atmosphere pressure chemical vapor deposition (APCVD) were investigated in detail using X-ray four-circle diffractometry. The Phi scan shows that 3C-SiC films can grow on Si substrates epitaxially and epitaxial relationship is revealed as (0 0 1)(3C) (SiC)parallel to (0 0 1)(Si),[1 1 1](3C-SiC)parallel to [1 1 1](Si). Other diffraction peaks at about 15.8 degrees in x emerged in the pole figures of the (I 1 1) 3C-SiC. We performed the pole figure of (1 0 (1) over bar 0)h-SiC and the reciprocal space mapping from the (1 1 1) reciprocal lattice point of base SiC to the (0 0 2) point of microtwin for the first time, indicating that the diffraction peaks at 15.8 degrees in x result from not hexagonal SiC but microtwins of 3C-SiC, and twin inclusions are estimated to be around 1%. (C) 2001 Published by Elsevier Science B.V.

Microtwins and twin inclusions in the 3C-SiC epilayers grown on Si(001) by APCVD

Microtwins in the 3C-SiC films grown on Si(001) by APCVD were analyzed in detail using an X-ray four-circle diffractometer. The empty set scan shows that 3C-SiC films can grow on Si substrates epitaxially and the epitaxial relationship is revealed as (001)(3C-SiC)//(001)(Si), [111](3C-SiC)//[111](Si). Other diffractions emerged in the pole figures of the (111) 3C-SiC. We performed the (10 (1) over bar0) h-SiC and the reciprocal space mapping of the (002) plane of twins for the first time, finding that the diffractions at chi = 15.8 degrees result from not hexagonal SiC but microtwins of 3C-SiC, and twin inclusions are estimated to be 1%.

Raman study on residual strains in thin 3C-SiC epitaxial layers grown on Si(001)

Raman scattering measurement has been used to study the residual strains in the thin 3C-SiC/Si(001) epilayers with a variation of film thickness from 0.1 to 1.2 mu m. which were prepared by chemical vapor deposition (CVD)growth. Two methods have been exploited to figure our the residual strains and the exact LO bands. The final analyzing results show that residual strains exist in the 3C-SiC epilayers. The average stress is 1.3010 GPa, and the relative change of the lattice constant is 1.36 parts per thousand. Our measurements also show that 3C-SiC phonons are detectable even for the samples with film thickness in the range of 0.1 to 0.2 mu m. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Heteroepitaxial Growth of 3C-SiC on Si (111) Substrate using AlN as a Buffer Layer

Using AlN as a buffer layer, 3C-SiC film has been grown on Si substrate by low pressure chemical vapor deposition (LPCVD). Firstly growth of AlN thin films on Si substrates under varied V/III ratios at 1100 degrees was investigated and the (002) preferred orientational growth with good crystallinity was obtained at the V/III ratio of 10000. Annealing at 1300 degrees C indicated the surface morphology and crystallinity stability of AlN film. Secondly the 3C-SiC film was grown on Si substrate with AlN buffer layer. Compared to that without AlN buffer layer, the crystal quality of the 3C-SiC film was improved on the AlN/Si substrate, characterized by X-ray diffraction (XRD) and Raman measurements.

Heavily doped polycrystalline 3C-SiC growth on SiO2/Si(100) substrates for resonator applications

3C-SiC is a promising material for the development of microelectromechanical systems (MEMS) applications in harsh environments. This paper presents the LPCVD growth of heavily nitrogen doped polycrystalline 3C-SiC films on Si wafers with 2.0 mu m-thick silicon dioxide (SiO2) films for resonator applications. The growth has been performed via chemical vapor deposition using SiH4 and C2H4 precursor gases with carrier gas of H-2 in a newly developed vertical CVD chamber. NH3 was used as n-type dopant. 3C-SiC films were characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS), secondary ion mass spectroscopy (SIMS), and room temperature Hall Effect measurements. It was shown that there is no voids at the interface between 3C-SiC and SiO2. Undoped 3C-SiC films show n-type conduction with resisitivity, Hall mobility, and carrier concentration at room temperature of about 0.56 Omega center dot cm, 54 cm(2)/Vs, and 2.0x 10(17) cm(-3), respectively. The heavily nitrogen doped polycrystalline 3C-SiC with the resisitivity of less than 10(-3) Omega center dot cm was obtained by in-situ doping. Polycrystalline SiC resonators have been fabricated preliminarily on these heavily doped SiC films with thickness of about 2 mu m. Resonant frequency of 49.1 KHz was obtained under atmospheric pressure.

Molecular beam epitaxial growth of GaN on 3c-SiC/Si(111) substrates using a thick AIN buffer layer

Hexagonal GaN films (similar to 3 mu m) were grown on 3c-SiC/Si(111) and carbonized Si(111) substrates using a thick AlN buffer Cracks are observed on the surface of the GaN film grown on the carbonized Si(111), while no cracks are visible on the 3c-SiC/Si(111). XRD exhibits polycrystalline nature of the GaN film grown on the carbonized Si(111) due to poorer crystalline quality of this substrate. Raman spectra reveal that all GaN layers are under tensile stress, and the GaN layer grown on 3c-SiC/Si(111) shows a very low stress value of sigma(xx) = 0.65 Gpa. In low-temperature Photoluminescence spectra the remarkable donor-acceptor-pair recombination and yellow band can be attributed to the incorporation of Si impurities from the decomposition of SiC.

Multi-wafer 3C-SiC heteroepitaxial growth on Si(100) substrates

Epitaxial growth of semiconductor films in multiple-wafer mode is under vigorous development in order to improve yield output to meet the industry increasing demands. Here we report on results of the heteroepitaxial growth of multi-wafer 3C-SiC films on Si(100) substrates by employing a home-made horizontal hot wall low pressure chemical vapour deposition (HWLPCVD) system which was designed to be have a high-throughput, multi-wafer (3x2-inch) capacity. 3C-SiC film properties of the intra-wafer and the wafer-to-wafer including crystalline morphologies, structures and electronics are characterized systematically. The undoped and the moderate NH3 doped n-type 3C-SiC films with specular surface are grown in the HWLPCVD, thereafter uniformities of intra-wafer thickness and sheet resistance of the 3C-SiC films are obtained to be 6%similar to 7% and 6.7%similar to 8%, respectively, and within a run, the deviations of wafer-to-wafer thickness and sheet resistance are less than 1% and 0.8%, respectively.