Low-temperature (10 K) infrared measurement of interstitial oxygen in heavily antimony-doped silicon via wafer thinning

A new technique is reported for the rapid determination of interstitial oxygen in heavily Sb-doped silicon. This technique includes wafer thinning and low-temperature 10 K infrared measurement on highly thinned wafers. The fine structure of the interstitial oxygen absorption band around 1136 cm(-1) is obtained. Our results show that this method efficiently reduces free-carrier absorption interference, allowing a high reliability of measurement, and can be used at resistivities down to 1 x 10(-2) Omega cm for heavily Sb-doped silicon.

Temperature dependence of the low-field mobility of a very narrow miniband in the degenerate case

Perpendicular transport in a specially designed, doped and weakly coupled GaAs/AlAs superlattice is investigated. A linear current-voltage at a bias within +/-10 mV and a negative differential velocity effect at a bias of about +/-40 mV are observed at low temperatures. The miniband conductance near zero electric field is studied as a function of temperature. It is found that the measured conductance increases slightly as the temperature increases to about 30 K, decreases as the temperature rises from 30 K to 70 K, and then increases strongly above 70 K, indicating the existence of a mobility gap.

Influence of annealed ohmic contact metals on electron mobility of strained AlGaN/GaN heterostructures

The influence of annealed ohmic contact metals on the electron mobility of a two dimensional electron gas (2DEG) is investigated on ungated AlGaN/GaN heterostructures and AlGaN/GaN heterostructure field effect transistors (AlGaN/GaN HFETs). Current-voltage (I-V) characteristics for ungated AlGaN/GaN heterostructures and capacitance-voltage (C-V) characteristics for AlGaN/GaN HFETs are obtained, and the electron mobility for the ungated AlGaN/GaN heterostructure is calculated. It is found that the electron mobility of the 2DEG for the ungated AlGaN/GaN heterostructure is decreased by more than 50% compared with the electron mobility of Hall measurements. We propose that defects are introduced into the AlGaN barrier layer and the strain of the AlGaN barrier layer is changed during the annealing process of the source and drain, causing the decrease in the electron mobility.

MOCVD-Grown AlGaN/AlN/GaN HEMT Structure with High Mobility GaN Thin Layer as Channel on SiC

AlGaN/AlN/GaN high electron mobility transistor (HEMT) structures with a high-mobility GaN thin layer as a channel are grown on high resistive 6H-SiC substrates by metalorganic chemical vapor deposition. The HEMT structure exhibits a typical two-dimensional electron gas (2DEG) mobility of 1944cm2/(V · s) at room temperature and 11588cm2/(V· s) at 80K with almost equal 2DEG concentrations of about 1.03 × 1013 cm-2 High crystal quality of the HEMT structures is confirmed by triple-crystal X-ray diffraction analysis. Atomic force microscopy measurements reveal a smooth AlGaN surface with a root-mean-square roughness of 0. 27nm for a scan area of 10μm × 10μm. HEMT devices with 0.8μm gate length and 1.2mm gate width are fabricated using the structures. A maximum drain current density of 957mA/mm and an extrinsic transconductance of 267mS/mm are obtained.

MBE Growth of High Electron Mobility InP Epilayers

The molecular beam epitaxial growth of high quality epilayers on （100） InP substrate using a valve phosphorous cracker cell over a wide range of P/In BEP ratio （2.0-7.0） and growth rate （0.437 and 0. 791μm/h）. Experimental results show that electrical properties exhibit a pronounced dependence on growth parameters,which are growth rate, P/In BEP ratio, cracker zone temperature, and growth temperature. The parameters have been optimized carefully via the results of Hall measurements. For a typical sample, 77K electron mobility of 4.57 × 10^4 cm^2/（V · s） and electron concentration of 1.55×10^15 cm^-3 have been achieved with an epilayer thickness of 2.35μm at a growth temperature of 370℃ by using a cracking zone temperature of 850℃.