(111)Si上外延生长六方GaN的TEM观察

利用衍衬、SAED、HRTEM对在（111）Si上外延生长的六方GaN进行了观察分析。GaN外延层与缓冲层和基底的取向关系为(0001)_(GaN)∥(0001)_(AlN)∥(111)_(Si)，[11(2-bar)0]_(GaN)∥[11(2-bar)0]_(AlN)∥[110]_(Si)。GaN外延层中存在倒反畴。GaN中位错以刃型位错为主。In_(0.1) Ga_(0.9) N/GaN的多重量子阱结构（MQW）具有阻挡穿透位错，降低位错密度的作用。

质量分离的双离子束沉积法生长CeO_2（111）/Si薄膜

国家973计划

在Si（111）上外延生长硅化钴薄膜的SEM和XPS研究

于2010-11-23批量导入

Si（111）衬底上IBE法外延生长β-FeSi2薄膜的研究

于2010-11-23批量导入

用低能离子束淀积技术在硅（111）衬底上生长氧化铈外延薄膜

采用质量分离的低能双离子束淀积(IBD)技术,在硅(111)衬底上共淀积,生长了氧化铈外延薄膜。椭圆偏振仪测得,膜厚2000A。俄歇能谱仪测得,外延层内铈、氧分布均匀,具有很好的正化学比。X射线双晶衍射得到明显的氧化铈(111),(222)峰,半高宽≤23''。

Microstructural and compositional characteristics of GaN films grown on a ZnO-buffered Si(111) wafer

Polycrystalline GaN thin films have been deposited epitaxially on a ZnO-buffered (111)-oriented Si substrate by molecular beam epitaxy. The microstructural and compositional characteristics of the films were studied by analytical transmission electron microscopy (TEM). A SiO2 amorphous layer about 3.5 nm in thickness between the Si/ZnO interface has been identified by means of spatially resolved electron energy loss spectroscopy. Cross-sectional and plan-view TEM investigations reveal (GaN/ZnO/SiO2/Si) layers exhibiting definite a crystallographic relationship: [111](Si)//[111](ZnO)//[0001](GaN) along the epitaxy direction. GaN films are polycrystalline with nanoscale grains (similar to100 nm in size) grown along [0001] direction with about 20degrees between the (1 (1) over bar 00) planes of adjacent grains. A three-dimensional growth mode for the buffer layer and the film is proposed to explain the formation of the as-grown polycrystalline GaN films and the functionality of the buffer layer. (C) 2004 Elsevier Ltd. All rights reserved.

MOVPE growth of GaN and LED on (111) MgAl2O4

The growth of wurtzite GaN by low-pressure metalorganic vapor-phase epitaxy on (1 1 1) magnesium aluminate (MgAl2O4) substrates have been studied. The morphological, crystalline, electrical and optical properties are investigated. A p-n junction GaN LED was fabricated on the MgAl2O4 substrate. (C) 1998 Elsevier Science B.V. All rights reserved.

Aluminum induced crystallization of strongly (111) oriented polycrystalline silicon thin film and nucleation analysis

A polycrystalline silicon thin film was fabricated on glass substrate by means of aluminum induced crystallization (AIC). Al and alpha-Si layers were deposited by magnetron sputtering respectively and annealed at 480A degrees C for 1 h to realize layer exchange. The polycrystalline silicon thin film was continuous and strongly (111) oriented. By analyzing the structure variation of the oxidation membrane and lattice mismatch between gamma-Al2O3 and Si, it was concluded that aluminum promoted the formation of (111) oriented silicon nucleus by controlling the orientation of gamma-Al2O3, which was formed at the early stage of annealing.