Ion bombardment as the initial stage of diamond film growth

It is believed that during the initial stage of diamond film growth by chemical-vapor deposition (CVD), ion bombardment is the main mechanism in the bias-enhanced-nucleation (BEN) process. To verify such a statement, experiments by using mass-separated ion-beam deposition were carried out, in which a pure carbon ion beam, with precisely defined low energy, was selected for investigating the ion-bombardment effect on a Si substrate. The results are similar to those of the BEN process, which supports the ion-bombardment-enhanced-nucleation mechanism. The formation of sp(3) bonding is based on the presumption that the time of stress generation is much shorter than the duration of the relaxation process. The ion-bombarded Si is expected to enhance the CVD diamond nucleation density because the film contains amorphous carbon embedded with nanocrystalline diamond and defective graphite. (C) 2001 American Institute of Physics.

Photoluminescence and Raman scattering of silicon nanocrystals prepared by silicon ion implantion into SiO2 films

Photoluminescence (PL) and Raman spectra of silicon nanocrystals prepared by Si ion implantion into SiO2 layers on Si substrate have been measured at room temperature. Their dependence on annealing temperature was investigated in detail. The PL peaks observed in the as-implanted sample originate from the defects in SiO2 layers caused by ion implantation. They actually disappear after thermal annealing at 800 degrees C. The PL peak from silicon nanocrystals was observed when thermal annealing temperatures are higher than 900 degrees C. The PL peak is redshifted to 1.7 eV and the intensity reaches maximum at the thermal annealing temperature of 1100 degrees C. The characterized Raman scattering peak of silicon nanocrystals was observed by using a right angle scattering configuration. The Raman signal related to the silicon nanocrystals appears only in the samples annealed at temperature above 900 degrees C. It further proves the formation of silicon nanocrystals in these samples. (C) 2000 American Institute of Physics. [S0021-8979(00)00215-2].

Semi-insulating GaAs grown in outer space

A semi-insulating GaAs single crystal ingot was grown in a recoverable satellite, within a specially designed pyrolytic boron nitride crucible, in a power-traveling furnace under microgravity. The characteristics of a compound semiconductor single crystal depends fundamentally on its stoichiometry, i.e. the ration of two types of atoms in the crystal. a practical technique for nondestructive and quantitative measuring stoichiometry in GaAs single crystal was used to analyze the space-grown GaAs single crystal. The distribution of stoichiometry in a GaAs wafer was measured for the first time. The electrical, optical and structural properties of the space-grown GaAs crystal were studied systematically, Device fabricating experiments prove that the quality of field effect transistors fabricated from direct ion-implantation in semi-insulating GaAs wafers has a close correlation with the crystal's stoichiometry. (C) 2000 Elsevier Science S.A. All rights reserved.

Optical properties of nanometer silicon prepared by silicon ion implanted into SiO2 layers

The samples of silicon nanocrystals (nc-Si) were prepared by Si ion implanted into SiO2 layers. Photoluminescence spectra were measured at room temperature and their dependence on thermal annealing was investigated. The experimental results show that PL peaks originate from the defects in SiO2 layers caused by ion implantation when the thermal annealing temperature is lower than 800 C. The PL peak from nc-Si was observed when the thermal annealing temperature was higher than 900 C, and PL intensity reached its maximum at the thermal annealing temperature of 1100 C. As the annealing temperature increases the red shift of PL peak from nc-Si shows the quantum size effect. The characterized Raman scattering peak of nc-Si was observed at the right angle scattering configuration for the first time. It provides further support for the PL measurements.

Structural study of YSi1.7 layers formed by channeled ion beam synthesis

High quality YSi1.7 layers (chi(min) of Y is 3.5%) have been formed by 60 keV Y ion implantation in Si (111) substrates to a dose of 1.0 x 10(17)/cm(2) at 450 degrees C using channeled ion beam synthesis (CIBS). It shows that, compared to the conventional nonchanneled ion beam synthesis, CIBS is beneficial in forming YSi1.7 layers with better quality due to the lower defect density created in the implanted layer. Rutherford backscattering/channeling and x-ray diffraction have been used to study the structure and the strain of the YSi1.7 layers. The perpendicular and parallel elastic strains of the YSi1.7 epilayer are e(perpendicular to) = -0.67% +/- 0.02% and e(parallel to) = +1.04% +/- 0.08%. The phenomenon that a nearly zero mismatch of the YSi1.7/Si (111) system results in a nonpseudomorphic epilayer with a rather large parallel strain relative to the Si substrate (epsilon(parallel to) = +1.09%) is explained, and the model is further used to explain the elastic strain of epitaxial ErSi1.7 and GdSi1.7 rare-earth silicides. (C) 1998 American Vacuum Society.

Structural and magnetic properties of GaN:Sm:Eu films fabricated by co-implantation method

Diluted-magnetic GaN:Sm:Eu films have been fabricated by co-implantation of Sm and Eu ions into c-plane (0001) GaN films and a subsequent annealing process. The structural, morphological and magnetic characteristics of the samples have been investigated by means of high-resolution X-ray diffraction (HRXRD), atomic force microscopy (AFM), and superconducting quantum interference device (SQUID). The XRD and AFM analyses show that the annealing process can effectively recover the crystalline degradation caused by implantation. Compared with GaN:Sm films, more defects have been introduced into GaN:Sm:Eu films due to the Eu implantation process. According to the SQUID analysis, GaN:Sm:Eu films exhibit clear room-temperature ferromagnetism. Moreover, GaN:Sm:Eu films show a lower saturation magnetization (Ms) than GaN:Sm films.

RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

INVESTIGATION OF BURIED ALN LAYERS FORMED BY NITROGEN IMPLANTATION INTO AL

The composition and microstructure of buried layers of AlN formed by high energy N+ ion implantation into polycrystalline Al have been determined. Both bulk and evaporated thin films of Al have been implanted with 100 and 200 keV N+ ions to doses of up to 1.8 x 10(18)/cm2. The layers have been characterised using SIMS, XTEM, X-ray diffraction, FTIR, RBS and in terms of their microhardness. It is found that, for doses greater than the critical dose, buried, polycrystalline AlN layers are formed with preferred (100) or (002) orientations, which are sample specific. With increasing dose the nitrogen concentration saturates at the value for stoichiometric AlN although the synthesised compound is found to be rich in oxygen.

CONSTRUCTION AND APPLICATIONS OF A DUAL MASS-SELECTED LOW-ENERGY ION-BEAM SYSTEM

A direct ion beam deposition system designed for heteroepitaxy at a low substrate temperature and for the growth of metastable compounds has been constructed and tested. The system consists of two mass-resolved low-energy ion beams which merge at the target with an incident energy range 50-25 000 eV. Each ion beam uses a Freeman ion source for ion production and a magnetic sector for mass filtering. While a magnetic quadrupole lens is used in one beam for ion optics, an electrostatic quadrupole lens focuses the other beam. Both focusing approaches provide a current density more than 100-mu-A/cm2, although the magnetic quadrupole gives a better performance for ion energies below 200 eV. The typical current of each beam reaches more than 0.3 mA at 100 eV, with a ribbon beam of about 0.3-0.5 x 2 cm2. The target is housed in an ultrahigh vacuum chamber with a base pressure of 1 x 10(-7) Pa and a typical pressure of 5 x 10(-6) Pa when a noncondensable beam like argon is brought into the chamber. During deposition, the target can be heated to 800-degrees-C and scanned mechanically with an electronic scanning control unit. The dual beam system has been used to grow GaN using a Ga+ and a N+ beam, and to study the oxygen and hydrogen ion beam bombardment effects during carbon ion beam deposition. The results showed that the simultaneous arrival of two beams at the target is particularly useful in compound formation and in elucidation of growth mechanisms.

Correlation of electrical and optical properties in dually Cd+ and N+ ion-implanted GaAs

Cd in GaAs is an acceptor atom and has the largest atomic diameter among the four commonly-used group-II shallow acceptor impurities (Be, Mg, Zn and Cd). The activation energy of Cd (34.7 meV) is also the largest one in the above four impurities, When Cd is doped by ion implantation, the effects of lattice distortion are expected to be apparently different from those samples ion-implanted by acceptor impurities with smaller atomic diameter. In order to compensate the lattice expansion and simultaneously to adjust the crystal stoichiometry, dual incorporation of Cd and nitrogen (N) was carried out into GaAs, Ion implantation of Cd was made at room temperature, using three energies (400 keV, 210 keV, 110 keV) to establish a flat distribution, The spatial profile of N atoms was adjusted so as to match that of Cd ones, The concentration of Cd and N atoms, [Cd] and [N] varied between 1 x 10(16) cm(-3) and 1 x 10(20) cm(-3). Two type of samples, i.e., solely Cd+ ion-implanted and dually (Cd+ + N+) ion-implanted with [Cd] = [N] were prepared, For characterization, Hall effects and photoluminescence (PL) measurements were performed at room temperature and 2 K, respectively. Hall effects measurements revealed that for dually ion-implanted samples, the highest activation efficiency was similar to 40% for [Cd] (= [N])= 1 x 10(18) cm(-3). PL measurements indicated that [g-g] and [g-g](i) (i = 2, 3, alpha, beta,...), the emissions due to the multiple energy levels of acceptor-acceptor pairs are significantly suppressed by the incorporation of N atoms, For [Cd] = [N] greater than or equal to 1 x 10(19) cm(-3), a moderately deep emission denoted by (Cd, N) is formed at around 1.45-1.41 eV. PL measurements using a Ge detector indicated that (Cd, N) is increasingly red-shifted in energy and its intensity is enhanced with increasing [Cd] = [N], (Cd, N) becomes a dominant emission for [Cd] = [N] = 1 x 10(20) cm(-3). The steep reduction of net hole carrier concentration observed for [Cd]/[N] less than or equal to 1 was ascribed to the formation of (Cd, N) which is presumed to be a novel radiative complex center between acceptor and isoelectronic atoms in GaAs.

X-ray-diffraction study of quasipseudomorphic ErSi1.7 layers formed by channeled ion-beam synthesis

ErSi1.7 layers with high crystalline quality (chi(min) of Er is 1.5%) have been formed by 90 keV Er ion implantation to a dose of 1.6X10(17)/cm(2) at 450 degrees C using channeled implantation. The perpendicular and parallel elastic strain e(perpendicular to)=-0.94%+/-0.02% and e(parallel to)=1.24%+/-0.08% of the heteroepitaxial erbium silicide layers have been measured with symmetric and asymmetric x-ray reflections using a double-crystal x-ray diffractometer. The deduced tetragonal distortion e(T(XRD))=e(parallel to)-e(perpendicular to)=2.18%+/-0.10%, which is consistent with the value e(T(RBS))2.14+/-0.17% deduced from the Rutherford backscattering and channeling measurements. The quasipseudomorphic growth of the epilayer and the stiffness along a and c axes of the epilayer deduced from the x-ray diffraction are discussed.

Formation of Fe-N films containing Fe6N2 phase by ion beam assisted deposition

Fe-N films were deposited on Si(100) and GaAs(100) substrates at room temperature by ion beam assisted deposition under various N/ Fe atomic arrival ratio, 0.09, 0.12, 0.15. The results of X-ray diffraction indicated that the film deposited at 0.12 of N/Fe arrival ratio contained a considerable fraction of the Fe16N2 phase which had grown predominantly in the [001] orientation. For the larger N/Fe arrival ratio, a martensite phase with 15 at.% nitrogen was obtained. It was found that a lower deposition temperature (<200 degrees C) was necessary for the formation of the Fe16N2 phase.

The SPER and characteristics of Si1-yCy alloys

\Si1-yCy alloys with carbon composition of 0.5 at.% were successfully grown on n-Si(100) substrate by solid phase epitaxy recraystallization. The result was presented in this paper. With the help of the SiO2 capping layer, rather uniform carbon profile in amorphous Si layer was obtained by dual-energy implantation. Since ion-flow was small and implantation time was long enough, the emergency of beta-SiC was avoided and the dynamic annealing effect was depressed. The pre-amorphization of the Si substrate increased the fraction of the substitutions carbon and the two-step annealing reduced point defects. As a result, Si1-yCy alloys with high quality was recrystallized on Si substrate.

Semi-insulating GaAs grown in outer space

A semi-insulating GaAs single crystal ingot was grown in a recoverable satellite, within a specially designed pyrolytic boron nitride crucible, in a power-traveling furnace under microgravity. The characteristics of a compound semiconductor single crystal depends fundamentally on its stoichiometry, i.e. the ration of two types of atoms in the crystal. a practical technique for nondestructive and quantitative measuring stoichiometry in GaAs single crystal was used to analyze the space-grown GaAs single crystal. The distribution of stoichiometry in a GaAs wafer was measured for the first time. The electrical, optical and structural properties of the space-grown GaAs crystal were studied systematically, Device fabricating experiments prove that the quality of field effect transistors fabricated from direct ion-implantation in semi-insulating GaAs wafers has a close correlation with the crystal's stoichiometry. (C) 2000 Elsevier Science S.A. All rights reserved.