Band gap renormalization and carrier localization effects in InGaN/GaN quantum-wells light emitting diodes with Si doped barriers

The optical properties of two kinds of InGaN/GaN quantum-wells light emitting diodes, one of which was doped with Si in barriers while the other was not, are comparatively investigated using time-integrated photoluminescence and time-resolved photoluminescence techniques. The results clearly demonstrate the coexistence of the band gap renormalization and phase-space filling effect in the structures with Si doped barriers. It is surprisingly found that photogenerated carriers in the intentionally undoped structures decay nonexponentially, whereas carriers in the Si doped ones exhibit a well exponential time evolution. A new model developed by O. Rubel, S. D. Baranovskii, K. Hantke, J. D. Heber, J. Koch, P. Thomas, J. M. Marshall, W. Stolz, and W. H. Ruhle [J. Optoelectron. Adv. Mater. 7, 115 (2005)] was used to simulate the decay curves of the photogenerated carriers in both structures, which enables us to determine the localization length of the photogenerated carriers in the structures. It is found that the Si doping in the barriers not only leads to remarkable many-body effects but also significantly affects the carrier recombination dynamics in InGaN/GaN layered heterostructures. (c) 2006 American Institute of Physics.

Exciton localization in In0.15Ga0.85As/GaAs quantum wire structures grown on (553)B-oriented GaAs substrate

Using time-resolved photoluminescence (PL) measurements, we have studied the exciton localization effect in InGaAs/GaAs quantum wire (QWR) structures formed in corrugated narrow InGaAs/GaAs quantum wells (QWs) grown on (553)B GaAs substrate. The PL decay time in the QWR structure was found to be independent of the temperature for T < 70 K, showing a typical dynamical behavior of the localized excitons. This result is in striking contrast to the corresponding quantum well structures, where a linear increase of the PL decay time was observed. In addition, an increase of the exciton lifetime was observed at low temperature for the QWR structure as compared to a reference InGaAs/GaAs quantum well sample (1200 vs 400 ps). The observed longer decay time was attributed to the reduction in the spatial coherence of excitons in the QWR-like structure. In PL measurements, a significant polarization anisotropy was also found in our narrow InGaAs/GaAs QWs grown on (553)B GaAs. (C) 2001 American Institute of Physics.

Effect of ion-induced damage on GaNAs/GaAs quantum wells grown by plasma-assisted molecular beam epitaxy

The effect of ion-induced damage on GaNAs/GaAs quantum wells (QWs) grown by molecular beam epitaxy employing a DC plasma as the N source was investigated. Ion-induced damage results in: (i) an observed disappearance of pendellosung fringes in the X-ray diffraction pattern of the sample; (ii) a drastic decrease in intensity and a broadening in the full-width at half-maximum of photoluminescence spectra. It was shown that ion-induced damage strongly affected the bandedge potential fluctuations of the QWs. The bandedge potential fluctuations for the samples grown with and without ion removal magnets (IRMs) are 44 and 63 meV, respectively. It was found that the N-As atomic interdiffusion at the interfaces of the QWs was enhanced by the ion damage-induced defects. The estimated activation energies of the N-As atomic interdiffusion for the samples grown with and without IRMs are 3.34 and 1.78 eV, respectively. (C) 2001 Elsevier Science B.V. All rights reserved.

Bloch oscillation under a bichromatic laser: Dynamical delocalization and localization, persistent terahertz emission, and harmonics generation

A novel AC driving configuration is proposed for biased semiconductor superlattices, in which the THz driving is provided by an intense bichromatic cw laser in the visible light range. The frequency difference between two components of the laser is resonant with the Bloch oscillation. Thus, multi-photon processes mediated by the conduction (valence) band states lead to dynamical delocalization and localization of the valence (conduction) electrons, and to the formation and collapse of quasi-minibands. Thus, driven Bloch oscillators are predicted to generate persistent THz emission and harmonics of the dipole field, which are tolerant of the exciton and the relaxation effects.

Plasma induced damage in GaN-based light emitting diodes - art. no. 68410X

The effects of plasma induced damage in different conditions of ICP and PECVD processes on LEDs were presented. For ICP mesa etch, in an effort to confirm the effects of dry etch damage on the optical properties of p-type GaN, a photoluminescence (PL) measurement was investigated with different rf chuck power. It was founded the PL intensity of the peak decreased with increasing DC bias and the intensity of sample etched at a higher DC bias of -400V is less by two orders of magnitude than that of the as-grown sample. Meanwhile, In the IN curve for the etched samples with different DC biases, the reverse leakage current of higher DC bias sample was obviously degraded than the lower one. In addition, plasma induced damage was also inevitable during the deposition of etch masks and surface passivation films by PECVD. The PL intensity of samples deposited with different powers sharply decreased when the power was excessive. The PL spectra of samples deposited under the fixed condition with the different processing time were measured, indicating the intensity of sample deposited with a lower power did not obviously vary after a long time deposition. A two-layer film was made in order to improve the compactness of sparse dielectric film deposited with a lower power.

Electron concentration dependence of exciton localization and freeze-out at local potential fluctuations in InN films

InN films with electron concentration ranging from n similar to 10(17) to 10(20) cm(-3) grown by metal-organic chemical vapor deposition (MOCVD) and molecular beam epitaxy (MBE) were investigated by variable-temperature photoluminescence and absorption measurements. The energy positions of absorption edge as well as photoluminescence peak of these InN samples with electron concentration above 10(18) cm(-3) show a distinct S-shape temperature dependence. With a model of potential fluctuations caused by electron-impurity interactions, the behavior can be quantitatively explained in terms of exciton freeze-out in local potential minima at sufficiently low temperatures, followed by thermal redistribution of the localized excitons when the band gap shrinks with increasing temperature. The exciton localization energy sigma (loc) is found to follow the n (5/12) power relation, which testifies to the observed strong localization effects in InN with high electron concentrations.

RBS STUDIES OF THE LATTICE DAMAGE CAUSED BY 1 MEV SI+ IMPLANTATION INTO AL0.3GA0.7AS/GAAS SUPERLATTICES AT ELEVATED-TEMPERATURE

The lattice damage accumulation in GaAs and Al0.3Ga0.7As/GaAs superlattices by 1 MeV Si+ irradiation at room temperature and 350-degrees-C has been studied. For irradiations at 350-degrees-C, at lower doses the samples were almost defect-free after irradiation, while a large density of accumulated defects was induced at a higher dose. The critical dose above which the damage accumulation is more efficient is estimated to be 2 x 10(15) Si/cm2 for GaAs, and is 5 x 10(15) Si/cm2 for Al0.8Ga0.7As/GaAs superlattice for implantation with 1.0 MeV Si ions at 350-degrees-C. The damage accumulation rate for 1 MeV Si ion implantation in Al0.3Ga0.7As/GaAs superlattice is less than that in GaAs.

WANNIER-STARK LOCALIZATION IN INGAAS/GAAS SUPERLATTICES AND ITS APPLICATION TO ELECTROOPTICAL DEVICES

We have observed Wannier-Stark localization in strained In0.2Ga0.8As/GaAs superlattices by low- and room-temperature photocurrent spectra measurements. The experimental results are well in agreement with the theoretical predictions. A large field-induced modulation response of the absorption edge of the superlattices at room temperature suggests the possibilities of the application to the design of various kinds of electro-optical devices operating at a wavelength of 0.98 mum, based on Wannier-Stark localization effects.

WANNIER LOCALIZATION IN GAAS/GAALAS SUPERLATTICES UNDER ELECTRIC-FIELD

We have studied the Wannier-Stark effect in GaAs/GaAlAs short-period superlattices under applied electric field perpendicular to the layers by room- and low-temperature photocurrent measurements. The changes in the transition intensities with biasing are well fitted to a theoretical calculation based on the finite Kronig-Penney model on which the potential of an applied electric field is superposed. With increasing electric field, the 0h peak grows to a maximum while the -1h and +1h peaks monotonousely decrease. By a comparison of the spectra measured at different temperatures, the two peaks in the room temperature photocurrent spectra at relatively low electric field (1.0 X 10(4) V/cm) are identified to be caused by the Wannier localization effect instead of saddle-point excitons.