Effects of annealing on laser-induced damage threshold of TiO2/SiO2 high reflectors

The mechanism of improving 1064 nm, 12 ns laser-induced damage threshold (LIDT) of TiO2/SiO2 high reflectors (HR) prepared by electronic beam evaporation from 5.1 to 13.1 J/cm(2) by thermal annealing is discussed. Through optical properties, structure and chemical composition analysis, it is found that the reduced atomic non-stoichiometric defects are the main reason of absorption decrease and LIDT rise after annealing. A remarkable increase of LIDT is found at 300 degrees C annealing. The refractive index and film inhomogeneity rise, physical thickness decrease, and film stress changes from compress stress to tensile stress due to the structure change during annealing. (c) 2007 Elsevier B.V. All rights reserved.

Preparation and characterization of nanostructured ZrO2 thin films by glancing angle deposition

ZrO2 films were prepared by electron beam evaporation with glancing angle deposition (GLAD) technique. The as-deposition and annealed ZrO2 films are all amorphous, different from that deposited at normal incidence. Due to the shadowing effect, a highly orientated structure composed of slanted columns formed, and the obtained films became the mixture of slanted columns and voids. The relationship among the effective refractive index, packing density and flux incident angle was investigated. The refractive index and packing density of ZrO2 films decrease with the increase of the incident angle. The in-plane birefringence of GLAD ZrO2 films was calculated. At the packing density of 0.576, the maximum birefringence is 0.037. (c) 2006 Elsevier B.V. All rights reserved.

三硼酸锂晶体上1064 nm, 532 nm, 355 nm三倍频增透膜的设计

采用矢量法设计了三硼酸锂晶体上1064 nm、532 nm和355 nm三倍频增透膜,结果表明1064 nm、532 nm和355 nm波长的剩余反射率分别为0.0017％、0.0002％和0.0013％。根据误差分析,薄膜制备时沉积速率精度控制在＋5.5％时,1064 nm、532 nm和355 nm波长的剩余反射率分别增加至0.20％、0.84％和1.89％。当材料折射率的变化控制在＋3％时,1064 nm处的剩余反射率增大为0.20％,532 nm和355 nm处分别达0.88％和0.24％。与薄膜

Y_2O_3稳定ZrO_2薄膜的结构和光学特性

用电子束蒸发法制备出四种不同Y2O3含量的Y2O3稳定ZrO2（YSZ）薄膜,用X射线衍射和透射光谱测定薄膜的结构和光学性能.结果表明：随着Y2O3含量的增加,ZrO2薄膜从单斜相向高温相（四方相和立方相）转变,获得了结构稳定的YSZ薄膜;YSZ薄膜的晶粒尺寸都比ZrO2薄膜的大,但随着Y2O3加入量的增加,晶粒尺寸有减小的趋势,薄膜表面也趋向光滑平整.所有YSZ薄膜的透射谱线都与ZrO2薄膜相似,在可见光和红外光区都有较高的透过率.Y2O3的加入还可以改变薄膜的折射率,在一定范围内可得到所需的任意折射率

沉积温度对LaF3薄膜性能的影响

abstract {LaF₃ single-layer coatings were prepared by thermal boat evaporation at the deposition temperatures of 189, 255, 277 and 321°C respectively. The crystal structures of the coatings were characterized by X-ray diffraction (XRD). A spectrophotometer was employed to measure its transmittance. Moreover, refractive index, extinction coefficient and cut-off wavelength were obtained from the measured transmittance spectral curve. The residual stress was evaluated by the Stoney's equation and optical interferometer. Laser induce damage threshold (LIDT) was performed by a tripled Nd:YAG laser system. The results show that the crystallization status becomes better with the deposition temperature increasing. Correspondingly, the grain size also gets larger. Meanwhile, the coatings become more compact and the refractive index increases. However, the absorption of coatings seriously rises and the cut-off wavelength drifts to the long wave. In addition, the residual stress also increases and the intrinsic stress plays a determinant role in the coating. The LIDT of the coating also enhances at high temperature.}

沉积速率对热舟蒸发LaF3薄膜性能的影响

用热舟蒸发方法在不同的沉积速率下制备了LaF3单层膜,并对部分单层膜进行了真空退火。分别采用X射线衍射(XRD),Lambda 900 光谱仪和355 nm Nd∶YAG脉冲激光测试了薄膜的晶体结构、透射光谱和激光损伤阈值(LIDT),并通过透射光谱计算得到样品的折射率和消光系数。实验结果表明,增大沉积速率有利于LaF3薄膜的结晶和择优生长,可以提高薄膜的致密性和折射率,但薄膜的抗激光损伤能力有所下降;沉积速率太大,又会恶化薄膜的结晶性能,同时薄膜中产生大量孔洞,薄膜的机械强度降低,导致薄膜的折射率减小和

热舟蒸发LaF_3薄膜的紫外性能研究

研究了沉积温度对热舟蒸发氟化镧薄膜结构和光学性能的影响,沉积温度从200℃上升到350℃,间隔为50℃.采用分光光度计测量了样品的透射率和反射率光谱曲线,并在此基础上进行了光学损耗、光学常数以及带隙和截止波长的计算.采用表面轮廓仪进行了表面形貌和表面粗糙度的标定,采用X射线衍射(XRD)方法测量了不同沉积温度下样品的微结构.发现在短波长波段,随着沉积温度的升高,光学损耗增加,晶粒尺寸增大,表面粗糙度略有增加.不过散射损耗在光学损耗中所占比例均很小,光学损耗的增加主要由吸收损耗引起.随着沉积温度的升高,折射率与消光系数增大,带隙变小,相对应的截止波长向长波方向移动.

Influence of oxygen plasma treatment on properties of ZrO2 films prepared by e-beam evaporation techniques

Zirconia films were prepared by e-beam evaporation, and oxygen plasma treatment was used to modify film properties. Spectrophotometry, x-ray diffractometry (XRD), and atomic force microscopy were used to characterize refractive index, extinction coefficient, rnicrostructure, and surface roughness, respectively. The experimental results indicate that both refractive index and extinction coefficient of the films were reduced slightly after oxygen plasma treatment, with the decrease of intrinsic stress and surface roughness. From XRD spectra, the intensity decrease of the T(110) diffraction peak was clearly observed after the treatment, which was caused by the restructuring of the film atoms. (C) 2008 Elsevier Ltd. All rights reserved.

LiB3O5晶体上四倍频增透膜设计

采用矢量法设计了三硼酸锂（LiB3O5，LBO）晶体上1064nm、532nm、355nm和266nm四倍频增透膜．结果表明，在1064nm、532nm、355nm和266nm波长的剩余反射率分别为0．0019％、0．0031％、0．0061％和0．0047％．根据容差分析，薄膜制备时沉积速率准确度控制在＋6．5％时，基频、二倍频、三倍频和四倍频波长的剩余反射率分别增加至0．24％、0．92％、2．38％和4．37％．当薄膜材料折射率的变化控制在＋3％时，1064nm波长的剩余反射率增大为0．18％，532nm、355nm和266nm波长分别达0．61％，0．59％，0．20％．与薄膜物理厚度相比，膜层折射率对剩余反射率的影响大．对膜系敏感层的分析表明，在1064nm和266nm波长，从入射介质向基底过渡的第二层膜厚度变化对剩余反射率的影响最大，其次是第一膜层．在532nm和355nm波长，从入射介质向基底过渡的第一和第四膜层是该膜系的敏感层．误差分析也表明，薄膜材料的色散对特定波长的剩余反射率具有明显影响，即1064nm、532nm、355nm和266nm波长的剩余反射率分别增加至0．30％、0．23％、0．58％和3．13％．

Investigation on properties of TiO2 thin films deposited at different oxygen pressures

TiO2 thin films were prepared by electron beam evaporation at different oxygen partial pressures. The influences of oxygen partial pressure on optical, mechanical and structural properties of TiO2 thin films were studied. The results showed that with the increase of oxygen partial pressure, the optical transmittance gradually increased, the transmittance edge gradually shifted to short wavelength, and the corresponding refractive index decreased. The residual stresses of all samples were tensile, and the value increased as oxygen partial pressure increasing, which corresponded to the evolutions of the packing densities. The structures of TiO2 thin films all were amorphous because deposition particles did not possess enough energy to crystallize. (C) 2007 Elsevier Ltd. All rights reserved.

SiO_2薄膜折射率的准确拟合分析

精确的光学常数对于设计和制备高品质的光学薄膜非常重要,尤其是那些光学性能对折射率变化敏感的薄膜。SiO_2是一种常用的低折射率材料,因与常用基底折射率相近使其准确拟合有一定难度。实验通过离子束溅射制备了SiO_2单层膜。考虑测量时的误差和基底折射率的影响,采用透射率包络和反射率包络得到了SiO_2的折射率,并用所得折射率进行反演来对这两种途径在实际测量拟合过程中的准确性进行比对。分析表明,剩余反射率在实际的测量过程中误差更小,直接用测量镀膜前后基片的剩余反射率值可以更简便更准确地得到SiO_2的折射率,能达到10~(-2)的精度。

Influence of different substrates on laser induced damage thresholds at 1064 nm of Ta2O5 films

Ta2O5 films are prepared on Si, BK7, fused silica, antireflection (AR) and high reflector (HR) substrates by electron beam evaporation method, respectively. Both the optical property and laser induced damage thresholds (LIDTs) at 1064 nm of Ta2O5 films on different substrates are investigated before and after annealing at 673 K for 12h. It is shown that annealing increases the refractive index and decreases the extinction index, and improves the O/Ta ratio of the Ta2O5 films from 2.42 to 2.50. Moreover, the results show that the LIDTs of the Ta2O5 films are mainly correlated with three parameters: substrate property, substoichiometry defect in the films and impurity defect at the interface between the substrate and the films. Details of the laser induced damage models in different cases are discussed.

Characterization of LaF3 coatings prepared at different temperatures and rates

LaF3 thin films were prepared by thermal boat evaporation at different substrate temperatures and various deposition rates. X-ray diffraction (XRD), Lambda 900 spectrophotometer and X-ray photoelectron spectroscopy (XPS) were employed to study crystal structure, transmittance and chemical composition of the coatings, respectively. Laser-induce damage threshold (LIDT) was determined by a tripled Nd:YAG laser system with a pulse width of 8 ns. It is found that the crystal structure became more perfect and the refractive index increased gradually with the temperature rising. The LIDT was comparatively high at high temperature. In the other hand, the crystallization status also became better and the refractive index increased when the deposition rate enhanced at a low level. If the rate was super rapid, the crystallization worsened instead and the refractive index would lessen greatly. On the whole, the LIDT decreased with increasing rate. (C) 2007 Elsevier B.V. All rights reserved.

Structure and optical properties of Nb2O5 sculptured thin films by glancing angle deposition

Nb2O5 sculptured thin. films deposited by electron beam evaporation with glancing angle deposition were prepared. Nb2O5 sculptured thin. films with tilted columns are optical anisotropy. XRD, SEM, UV-vis-NIR spectra are employed to characterize the microstructure and optical properties. The maximum of birefringence (Delta n) is up to 0.045 at alpha = 70 degrees with packing density of 0.487. With increasing the deposition angle, refractive index and packing density of Nb2O5 STF are decreasing. The relationship among deposition parameter, microstructure and optical properties was investigated in detail. (C) 2008 Elsevier B. V. All rights reserved.

Influence of substoichiometer on the laser-induced damage characters of HfO2 thin films

HfO2 is one of the most important high refractive index materials for depositing high power optical mirrors. In this research, HfO2 thin films were prepared by dual-ion beam reactive sputtering method, and the laser-induced damage thresholds (LIDT) of the sample were measured in 1-on-1 mode for laser with 1064 nm wavelength. The results indicate that the LIDT of the as-grown sample is only 3.96 J/cm(2), but it is increased to 8.98 J/cm(2) after annealing under temperature of 200 degrees C in atmosphere. By measuring the laser weak absorption and SIMS of the samples, we deduced that substoichiometer is the main reason for the low LIDT of the as-grown sample, and the experiment results were well explained with the theory of electronic-avalanche ionization. (C) 2008 Elsevier B.V. All rights reserved.