Preparation of Semi-Insulating Material by Annealing Undoped InP

Semi-insulating (SI) InP wafers of 50 and 75mm in diameter can be obtained by annealing of undoped liquid encapsulated Czochralski (LEC) InP at 930 ℃ for 80h. The annealing ambient can be pure phosphorus (PP) or iron phosphide (IP). The IP-SI InP wafers have good electrical parameters and uniformity of whole wafer. However, PP-SI InP wafers exhibit poor uniformity and electrical parameters, Photoluminescence which is subtle to deep defect appears in IP-annealed semi-insulating InP. Traps in annealed SI InP are detected by the spectroscopy of photo-induced current transient. The results indicate that there are fewer traps in IP-annealed undoped SI InP than those in as-grown Fe-doped and PP-undoped SI-undoped SI InP. The formation mechanism of deep defects in annealed undoped InP is discussed.

Electrical Transport Properties of Annealed Undoped InP

The electrical properties of annealed undoped n-type InP are studied by temperature dependent Hall effect (TDH) and current-voltage (I-V) measurements for semiconducting and semi-insulating samples, receptively. Defect band conduction in annealed semiconducting InP can be observed from TDH measurement, which is similar to those of as-grown unintentionally doped InP with low carrier concentration and moderate compensation. The I-V curves of annealed undoped SI InP exhibit ohmic property in the applied field region up to the onset of breakdown. Such a result is different from that of as-grown Fe-doped SI InP which has a nonlinear region in I-V curve explained by the theory of space charge limited current.

Photoluminescence characteristics of InP annealed in phosphorus and iron phosphide ambiences

Photo luminescence (PL) spectroscopy has been used to study InP annealed in phosphorus and iron phosphide ambiences. Noticeable PL emissions related with thermally induced defects have been detected in undoped InP annealed in iron phosphide ambience. Origins of the PL emissions have been discussed. (c) 2004 Elsevier Ltd. All rights reserved.

Electron irradiation induced defects in high temperature annealed InP single crystal

Electron irradiation induced defects in InP material which has been formed by high temperature annealing undoped InP in different atmosphere have been studied in this paper. In addition to Fe acceptor, there is no obvious defect peak in the sample before irradiation, whereas five defect peaks with activation energies of 0.23 eV, 0.26 eV, 0.31 eV, 0.37 eV and 0.46 eV have been detected after irradiation. InP annealed in P ambient has more thermally induced defects, and the defects induced by electron irradiation have characteristics of complex defect. After irradiation, carrier concentration and mobility of the samples have suffered obvious changes. Under the same condition, electron irradiation induced defects have fast recovery behavior in the FeP2 ambient annealed InP. The nature of defects, as well as their recovery mechanism and influence on material property have been discussed from the results.

Influence of deep level defects on electrical compensation in semi-insulating InP materials

In this paper, we analyze and compare electrical compensation and deep level defects in semi-insulating ( SI) materials prepared by Fe-doping and high temperature annealing of undoped InP. Influence of deep level defects in the SI-InP materials on the electrical compensation has been studied thermally stimulated current spectroscopy (TSC). Electrical property of the Fe-doped SI-InP is deteriorated due to involvement of a high concentration of deep level defects in the compensation. In contrast, the concentration of deep defects is very low in high temperature annealed undoped SI-InP in which Fe acceptors formed by diffusion act as the only compensation centre to pin the Fermi level, resulting in excellent electrical performance. A more comprehensive electrical compensation model of SI-InP has been given based on the research results.

Annealing and activation of silicon implanted in semi-insulating InP substrates

We have investigated the annealing and activation of silicon implanted in both as-grown Fe-doped semi-insulating (SI) InP substrate and undoped SI InP substrate obtained by annealing high purity conductive InP wafer (wafer-annealed). Si implantations were performed at an energy of 500 keV and a dose of 1 X 10(15) cm(-2). Following the implantations, rapid thermal annealing (RTA) cycles were carried out for 30 s at different temperatures. The results of Raman measurements show that for 700degreesC/30s RTA, the two Si-implanted SI InP substrates have acquired a high degree of lattice recovery and electrical activation. However, further Hall measurements indicate that the carrier concentration of the wafer-annealed SI InP substrate is about three times higher than that of the as-grown Fe-doped SI InP substrate. The difference can be ascribed to the low Fe concentration of the wafer-annealed SI InP substrate.These experimental data imply that the use of the wafer-annealed SI InP substrate can be conducive to the improvement of InP-based device performances. (C) 2003 Elsevier Ltd. All rights reserved.

Microdefects and electrical uniformity of InP annealed in phosphorus and iron phosphide ambiances

Microdefects originating from impurity-dislocation interactions in undoped InP that had been annealed in phosphorus and iron phosphide ambiances have been studied using optical microscopy. The electrical uniformity of the annealed wafer is improved by removing impurity aggregation around dislocations and by eliminating impurity striations in the annealing process. Compared to as-grown Fe-doped semi-insulating (SI) material, SI wafers obtained by annealing undoped InP in iron phosphide ambiances have better uniformity. This is attributed to the avoidance of Fe aggregation around dislocations and dislocation clusters, Fe precipitation and impurity striations, and is related to the use of a low concentration of Fe in the annealed material. The influence of Fe diffusion on the migration of dislocations in the annealing process has been studied and reviewed. (C) 2003 Elsevier B.V. All rights reserved.

Effects of annealing ambient on the formation of compensation defects in InP

Positron annihilation lifetime (PAL) and photoinduced current transient spectroscopies (PICTS) have been employed to study the formation of compensation defects in undoped InP under different annealing processes with pure phosphorus (PP) ambience and iron phosphide (IP) ambience, respectively. The different annealing ambiences convert the as-grown n-type undoped InP into two types of semi-insulating (SI) states. The positron average lifetimes of as-grown InP, PP SI-InP, and IP SI-InP are found to be 246, 251, and 243 ps, respectively, which are all longer than the bulk lifetime of 240 ps, indicating the existence of vacancy-type positron-trapping defects. For as-grown InP, VInH4 complexes are the dominant defects. They dissociate into VInHn(0less than or equal tonless than or equal to3) acceptor vacancies under PP ambience annealing, compensating the residual shallow donors and turning the material semi-insulating. In forming IP SI-InP, diffusion of iron into V-In complexes under IP ambience annealing produces the substitutional compensation defect Fe-In, causing a shorter positron average lifetime. The PICTS measurements show that a group of vacancy-type defects has been suppressed by iron diffusion during the annealing process, which is in good agreement with the PAL results. (C) 2003 American Institute of Physics.

Deep levels in semi-insulating InP obtained by annealing under iron phosphide ambiance

Deep levels in semi-insulating (SI) InP obtained by annealing in iron phosphide (IP) ambiance have been characterized by optical transient current spectroscopy (OTCS). Compared with the OTCS result of the SI InP prepared by annealing in pure phosphorus (PP) ambiance, the IP SI InP presents only two traps with activation energies of 0.20 and 0.63 eV, respectively. The results suggest that the diffusion of Fe-atoms suppresses the formation of a few defects in the IP SI InP. The nature of deep levels in the IP and PP SI InP has been discussed on the basis of these results. The relation between material property and defects in those SI InP has also been revealed. (C) 2002 American Institute of Physics.

Fe-diffusion-induced defects in InP annealed in iron phosphide ambient

Photoluminescence (PL) and photo induced current transient spectroscopy (PICTS) have been used to study deep levels in semi-insulating (SI) InP prepared by annealing undoped InP in pure phosphorus (PP) and iron phosphide (IP) ambient. Defects are much fewer in IP SI-InP than in PP SI-InP. Deep-level-related PL emission could only be detected in IP SI-InP. The results indicate that Fe diffusion inhibits the thermal formation of a number of defects in annealed InP. A complex defect has been formed in the annealing process in the presence of Fe.

Non-stoichiometry Related Deep Level Defects in Semi-insulating InP

Semi-insulating (SI) InP materials have been prepared under different stoichiometric conditions, including Fe-doping in indium-rich melt and high temperature annealing undoped wafer in phosphorus and iron phosphide ambients. Deep level defects related with non-stoichiometry have been detected in the SI-InP samples. A close relationship between the material quality of electrical property and native deep defects has been revealed by a comprehensive study of defects in as-grown Fe-doped and annealed undoped SI-InP materials. Fe-doped SI-InP material with low carrier mobility and poor thermal stability contains a high concentration of deep defects with energy levels in the range of 0.1-0.4eV. The suppression of the defects by high temperature annealing undoped InP leads to the manufacture of high quality SI-InP with high mobility and good electrical uniformity. A technology for the growth of high quality SI-InP through stoichiometry control has been proposed based on the results.

Dynamics of formation of defects in annealed InP

Dynamics of formation of defects in the annealed nominally undoped semi-insulating InP obtained by high pressure, high temperature annealing of high purity materials is proposed. Incorporated hydrogen passivates vacancy at indium site from annihilation forming fully hydrogenated indium vacancy which dissociates leaving large lattice relaxation behind, deep donors, mainly larger complexes involving phosphorus at indium site and isolated hydrogen defects are created in nominally undoped InP after annealing. Also created are acceptor levels such as vacancy at indium site. Carrier charge compensation mechanism in nominally undoped InP upon annealing at high temperature is given. Microscopic models of hydrogen related defects are given. Structural, electronic and vibrational properties of LVMs related to hydrogen as well as their temperature effect are discussed.

Formation mechanism of defects in annealed InP

Dynamical formation mechanism of defects in the annealed nominally undoped semi-insulating InP obtained by high pressure, high temperature annealing of high purity materials is proposed. Local vibrational modes in tenths of InP samples reveal clearly existence of complexes related to hydrogen. Complexes of vacancy at indium site with one to four hydrogen atoms and isolated hydrogen or hydrogen dimers, complexes of hydrogen with various impurities are investigated by FTIR. Hydrogen can acts as an actuator for generation of antistructure defects. Fully hydrogenated indium vacancy dissociates leaving large lattice relaxation behind, deep donors, mainly larger complexes involving phosphorus at indium site and isolated hydrogen defects are created in nominally undoped InP after annealing. Also created are acceptor levels such as vacancy at indium site. Carrier charge compensation mechanism in nominally undoped InP upon annealing at high temperature is given. Microscopic models of hydrogen related defects are given. Structural, electronic and vibrational properties of LVMs related to hydrogen as well as their temperature effect are discussed.

Electrical properties of undoped In0.53Ga0.47As grown on InP substrates by molecular beam epitaxy

A series of 1-mu m-thick undoped In0.53Ga0.47As with different substrate growth temperature (T-g) or different beam flux pressure (BFP) of As were grown on lattice-matched semi-insulating InP (001) substrates by molecular beam epitaxy (MBE). Van der Pauw Hall measurements were carried out for these In0.53Ga0.47As samples. The residual electron concentration decreased with increasing temperature from 77 to 140 K, but increased with increasing temperature from 140 to 300 K. Rapid thermal annealing (RTA) can reduce the residual electron concentration. The residual electron mobility increased with increasing temperature from 77 to 300 K. All these electrical properties are associated with As antisite defects. (c) 2006 Elsevier B.V. All rights reserved.