HMDSO plasma polymerization and thin film optical properties

Thin films were deposited from hexamethyldisiloxane (HMDSO) in a glow discharge supplied with radiofrequency (rf) power. Actino-metric optical emission spectroscopy was used to follow trends in the plasma concentrations of the species SiH (414.2 nm), CH (431.4 nm), CO (520.0 nm), and H (656.3 nm) as a function of the applied rf power (range 5 to 35 W). Transmission infrared spectroscopy (IRS) was employed to characterize the molecular structure of the polymer, showing the presence of Si-H, Si-O-Si, Si-O-C and C-H groups. The deposition rate, determined by optical interferometry, ranged from 60 to 130 nm/min. Optical properties were determined from transmission ultra violet-visible spectroscopy (UVS) data. The absorption coefficient α, the refractive index n, and the optical gap E04 of the polymer films were calculated as a function of the applied power. The refractive index at a photon energy of 1 eV varied from 1.45 to 1.55, depending on the rf power used for the deposition. The absorption coefficient showed an absorption edge similar to other non-crystalline materials, amorphous hydrogenated carbon, and semiconductors. For our samples, we define as an optical gap, the photon energy E04 corresponding to the energy at an absorption of 104 cm-1. The values of E04 decreased from 5.3 to 4.6 as the rf power was increased from 5 to 35 W. © 1995.

LiNbO3 thin films prepared from a polymeric precursor method

LiNbO3 thin films were prepared from polymeric precursor method by dip coating. The precursor films, deposited on Si(111) substrates, were heat-treated from 400°C to 900°C in order to study the heat treatment influence on the crystallinity and microstructure of the final film. The X-ray diffraction patterns showed, in particular, that these films crystallize at low temperature (450°C) and present no preferential orientation. The scanning electron microscopy studies showed that the film microstructure is strongly influenced by the annealing temperature. © 1997 Trans Tech Publications.

Fabrication and characterization of GeO2-PbO optical waveguides

This work presents studies of GeO2-PbO thin films deposited by RF Sputtering for fabrication of rib-waveguide. GeO2-PbO vitreous targets were prepared melting the reagents in alumina crucible. Thin films were deposited at room temperature using pure Ar plasma, at 5 mTorr pressure and RF power of 40 W on substrates of (100) silicon wafers. Rutherford Backscattering Spectroscopy (RBS) analyses were employed for the determination of the chemical elements present in the GeO2-PbO film. Geometry and sidewall of the waveguides were investigated by Scanning Electron Microscopy (SEM). The mode propagation in the waveguide structure of GeO2-PbO thin films was analyzed using an integrated optic simulation software to obtain a monomode propagation. © The Electrochemical Society.

One-dimensional Silicon And Germanium Nanostructures With No Carbon Analogues.

In this work we report new silicon and germanium tubular nanostructures with no corresponding stable carbon analogues. The electronic and mechanical properties of these new tubes were investigated through ab initio methods. Our results show that these structures have lower energy than their corresponding nanoribbon structures and are stable up to high temperatures (500 and 1000 K, for silicon and germanium tubes, respectively). Both tubes are semiconducting with small indirect band gaps, which can be significantly altered by both compressive and tensile strains. Large bandgap variations of almost 50% were observed for strain rates as small as 3%, suggesting their possible applications in sensor devices. They also present high Young's modulus values (0.25 and 0.15 TPa, respectively). TEM images were simulated to help in the identification of these new structures.

Studies on Chemical Bath Deposited Semiconducting Copper Selenide and Iron Sulfide Thin Films Useful For Photovoltaic Applications

Chemical bath deposition (CBD)is one of the simplest, very convient and probably the cheapest method for thin film preparation. Photovoltaic is the cleanest and the most efficient mode of conversion of energy to electrical power. Silicon is the most popular material in this field. The present study on chemical bath deposited semiconducting copper selenide and iron sulfide thin films useful for photovoltaic applications. Semiconducting thin films prepared by chemical deposition find applications as photo detectors, solar control coatings and solar cells. Copper selenide is a p-type semiconductor that finds application in photovolitics. Several heterojunction systems such as Cu2-xSe/ZnSe (for injection electro luminescence), Cu2Se/AgInSe2 and Cu2Se/Si (for photodiodes), Cu2-xSe/CdS, Cu2-xSe/CdSe, CuxSe/InP and Cu2-xSe/Si for solar cells are reported. A maximum efficiency of 8.3% was achieved for the Cu2-xSe/Si cell, various preparation techniques are used for copper selenide like vacuum evaporation, direct reaction, electrodeposition and CBD. Instability of the as-prepared films was investigation and is accounted as mainly due to deviation from stoichiometry and the formation of iron oxide impurity. A sulphur annealing chamber was designed and fabricated for this work. These samples wee also analysed using optical absorption technique, XPS (X-ray Photoelectron Spectroscopy) and XRD.(X-Ray Diffraction).The pyrite films obtained by CBD technique showed amorphous nature and the electrical studies carried out showed the films to be of high resistive nature. Future work possible in the material of iron pyrite includes sulphur annealing of the non-stochiometric iron pyrite CBD thin films in the absence of atmospheric oxygen

Structural-electronic aspects related to the near-infrared light emission of Fe-doped silicon films

The need of efficient (fast and low consumption) optoelectronic devices has always been the driving force behind the investigation of materials with new or improved properties. To be commercially attractive, however, these materials should be compatible with our current micro-electronics industry and/or telecommunications system. Silicon-based compounds, with their matured processing technology and natural abundance, partially comply with such requirements-as long as they emit light. Motivated by these issues, this work reports on the optical properties of amorphous Si films doped with Fe. The films were prepared by sputtering a Si+Fe target and were investigated by different spectroscopic techniques. According to the experimental results, both the Fe concentration and the thermal annealing of the samples induce changes in their atomic structure and optical-electronic properties. In fact, after thermal annealing at similar to 750 degrees C, the samples partially crystallize with the development of Si and/or beta-FeSi(2) crystallites. In such a case, certain samples present light emission at similar to 1500 nm that depends on the presence of beta-FeSi(2) crystallites and is very sensitive to the annealing conditions. The most likely reasons for the light emission (or absence of it) in the considered Fe-doped Si samples are presented and discussed in view of their main structural-electronic characteristics. (C) 2011 Elsevier Ltd. All rights reserved.

One-dimensional silicon and germanium nanostructures with no carbon analogues

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fabrication of sub-100 nm IDT SAW devices on insulating, semiconducting and conductive substrates

This work describes the electron-beam (e-beam) lithography process developed to manufacture nano interdigital transducers (IDTs) to be used in high frequency (GHz) surface acoustic wave (SAW) applications. The combination of electron-beam (e-beam) lithography and lift-off process is shown to be effective in fabricating well-defined IDT finger patterns with a line width below 100 nm with a good yield. Working with insulating piezoelectric substrates brings about e-beam deflection. It is also shown how a very thin organic anti-static layer works well in avoiding this charge accumulation during e-beam lithography on the resist layer. However, the use of this anti-static layer is not required with the insulating piezoelectric layer laying on a semiconducting substrate such as highly doped silicon. The effect of the e-beam dose on a number of different layers (of insulating, insulating on semiconducting, semiconducting, and conductive natures) is provided. Among other advantages, the use of reduced e-beam doses increases the manufacturing time. The principal aim of this work is to explain the interrelation among e-beam dose, substrate nature and IDT structure. An extensive study of the e-beam lithography of long IDT-fingers is provided, in a wide variety of electrode widths, electrode numbers and electrode pitches. It is worthy to highlight that this work shows the influence of the e-beam dose on five substrates of different conductive nature

Synthesis and electronic properties of luminescent silicon nanocrystals and copper indium sulphide quantum dots

In the last decades, nanomaterials, and in particular semiconducting nanoparticles (or quantum dots), have gained increasing attention due to their controllable optical properties and potential applications. Silicon nanoparticles (also called silicon nanocrystals, SiNCs) have been extensively studied in the last years, due to their physical and chemical properties which render them a valid alternative to conventional quantum dots. During my PhD studies I have planned new synthetical routes to obtain SiNCs functionalised with molecules which could ameliorate the properties of the nanoparticle. However, this was certainly challenging, because SiNCs are very susceptible to many reagents and conditions that are often used in organic synthesis. They can be irreversibly quenched in the presence of alkalis, they can be damaged in the presence of oxidants, they can modify their optical properties in the presence of many nitrogen-containing compounds, metal complexes or simple organic molecules. If their surface is not well-passivated, the oxygen can introduce defect states, or they can aggregate and precipitate in several solvents. Therefore, I was able to functionalise SiNCs with different ligands: chromophores, amines, carboxylic acids, poly(ethylene)glycol, even ameliorating functionalisation strategies that already existed. This thesis will collect the experimental procedures used to synthesize silicon nanocrystals, the strategies adopted to functionalise effectively the nanoparticle with different types of organic molecules, and the characterisation of their surface, physical properties and luminescence (mostly photogenerated, but also electrochemigenerated). I also spent a period of 7 months in Leeds (UK), where I managed to learn how to synthesize other cadmium-free quantum dots made of copper, indium and sulphur (CIS QDs). During my last year of PhD, I focused on their functionalisation by ligand exchange techniques, yielding the first example of light-harvesting antenna based on those quantum dots. Part of this thesis is dedicated to them.

Influence of Annealing Heat Treatment and Cr, Mg, and Ti Alloying on the Mechanical Properties of High-Silicon Cast Iron

The influence of annealing on the mechanical properties of high-silicon cast iron for three alloys with distinct chromium levels was investigated. Each alloy was melted either with or without the addition of Ti and Mg. These changes in the chemical composition and heat treatment aimed to improve the material's mechanical properties by inhibiting the formation of large columnar crystals, netlike laminae, precipitation of coarse packs of graphite, changing the length and morphology of graphite, and rounding the extremities of the flakes to minimize the stress concentration. For alloys with 0.07 wt.% Cr, the annealing reduced the impact resistance and tensile strength due to an enhanced precipitation of refined carbides and the formation of interdendritic complex nets. Annealing the alloys containing Ti and Mg led to a decrease in the mechanical strength and an increase in the toughness. Alloys containing approximately 2 wt.% Cr achieved better mechanical properties as compared to the original alloy. However, with the addition of Ti and Mg to alloys containing 2% Cr, the chromium carbide formation was inhibited, impairing the mechanical properties. In the third alloy, with 3.5 wt.% of Cr additions, the mechanical strength improved. The annealing promoted a decrease in both hardness and amount of iron and silicon complex carbides. However, it led to a chromium carbide formation, which influenced the mechanical characteristics of the matrix of the studied material.

Phase transformation and residual stress probed by Raman spectroscopy in diamond-turned single crystal silicon

Single-point diamond turning of monocrystalline semiconductors is an important field of research within brittle materials machining. Monocrystalline silicon samples with a (100) orientation have been diamond turned under different cutting conditions (feed rate and depth of cut). Micro-Raman spectroscopy and atomic force microscopy have been used to assess structural alterations and surface finish of the samples diamond turned under ductile and brittle modes. It was found that silicon undergoes a phase transformation when machined in the ductile mode. This phase transformation is evidenced by the creation of an amorphous surface layer after machining which has been probed by Raman scattering. Compressive residual stresses are estimated for the machined surface and it is observed that they decrease with an increase in the feed rate and depth of cut. This behaviour has been attributed to the formation of subsurface cracks when the feed rate is higher than or equal to 2.5 mu m/rev. The surface roughness was observed to vary with the feed rate and the depth of cut. An increase in the surface roughness was influenced by microcrack formation when the feed rate reached 5.0 mu m/rev. Furthermore, a high-pressure phase transformation induced by the tool/material interaction and responsible for the ductile response of this typical brittle material is discussed based upon the presented Raman spectra. The application of this machining technology finds use for a wide range of high quality components, for example the creation of a micrometre-range channel for microfluidic devices as well as microlenses used in the infrared spectrum range.

Hyperfine interactions in silicon quantum dots

A fundamental interaction for electrons is their hyperfine interaction (HFI) with nuclear spins. HFI is well characterized in free atoms and molecules, and is crucial for purposes from chemical identification of atoms to trapped ion quantum computing. However, electron wave functions near atomic sites, therefore HFI, are often not accurately known in solids. Here we perform an all-electron calculation for conduction electrons in silicon and obtain reliable information on HFI. We verify the outstanding quantum spin coherence in Si, which is critical for fault-tolerant solid state quantum computing.

Comparative study of the adsorption and dissociation of vinylacetic acid and acrylic acid on silicon (001)

In this work, we employ the state of the art pseudopotential method, within a generalized gradient approximation to the density functional theory, to investigate the adsorption process of acrylic acid (AAc) and vinylacetic acid (VAA) on the silicon surface. Our total energy calculations support the proposed experimental process, as it indicates that the chemisorption of the molecule is as follows: The gas phase VAA (AAc) adsorbs molecularly to the electrophilic surface Si atom and then dissociates into H(2)C = CH - COO and H, bonded to the electrophilic and nucleophilic surface silicon dimer atoms, respectively. The activation energy for both processes correspond to thermal activations that are smaller than the usual growth temperature. In addition, the electronic structure, calculated vibrational modes, and theoretical scanning tunneling microscopy images are discussed, with a view to contribute to further experimental investigations.

Semiconducting Sn(3)O(4) nanobelts: Growth and electronic structure

The study of structures based on nonstoichiometric SnO(2-x) compounds, besides experimentally observed, is a challenging task taking into account their instabilities. In this paper, we report on single crystal Sn(3)O(4) nanobelts, which were successfully grown by a carbothermal evaporation process of SnO(2) powder in association with the well known vapor-solid mechanism. By combining the structural data and transport properties, the samples were investigated. The results showed a triclinic semiconductor structure with a fundamental gap of 2.9 eV. The semiconductor behavior was confirmed by the electron transport data, which pointed to the variable range hopping process as the main conduction mechanism, thus giving consistent support to the mechanisms underlying the observed semiconducting character.

Internal Strain Distribution in Freestanding Porous Silicon

Elastic properties of freestanding porous silicon layers fabricated by electrochemical anodization were studied by Raman scattering. Different anodization currents provided different degrees of porosity in the nanometer scale. Raman lines corresponding to the longitudinal optical phonons of crystalline and amorphous phases were observed. The amorphous volume fraction increased and the phonon frequencies for both phases decreased with increasing porosity. A strain distribution model is proposed whose fit to the experimental results indicates that the increasing nanoscale porosity causes strain relaxation in the amorphous domains and strain buildup in the crystalline ones. The present analysis has significant implications on the estimation of the crystalline Si domain's characteristic size from Raman scattering data. (C) 2009 The Electrochemical Society. [DOI: 10.1149/1.3225832] All rights reserved.