Properties of GaN epilayers with various growth conditions grown by gas source molecular beam epitaxy

GaN epilayers on sapphire (0001) substrates were grown by the gas source molecular beam epitaxy (GSMBE) method using ammonia (NH,) gas as the nitrogen source. Properties of gallium nitride (GaN) epilayers grown under various growth conditions were investigated. The growth rate is up to 0.6 mu m/h in our experiments. Cathodoluminescence, photoluminescence and Hall measurements were used to characterize the films. It was shown that the growth parameters have a significant influence on the GaN properties. The yellow luminescence was enhanced at higher growth temperature. And a blue emission which maybe related to defects or impurity was observed. Although the emission at 3.31 eV can be suppressed by a low-temperature buffer layer, a high-quality GaN epilayer can be obtained without the buffer layer. (C) 1998 Elsevier Science B.V. All rights reserved.

InAs quantum dots in InAlAs matrix on (001)InP substrates grown by molecular beam epitaxy

InAs quantum dots grown on InAlAs lattice-matched to (0 0 1) InP substrates by molecular beam epitaxy are investigated by double-crystal X-ray diffraction, photoluminescence and transmission electron microscopy. The growth process is found to follow the Stranski-Krastanow growth mode. The islands formation is confirmed by the TEM measurements. Strong radiative recombination from the quantum dots and the wetting layer is observed, with room temperature PL emission in the 1.2-1.7 mu m region, demonstrating the potential of the InAs/InAlAs QDs for optoelectronic device applications. (C) 1998 Elsevier Science B.V. All rights reserved.

Ordered InAs quantum dots in InAlAs matrix on (001) InP substrates grown by molecular beam epitaxy

InAs self-organized quantum dots in InAlAs matrix lattice-matched to exactly oriented (001) InP substrates were grown by solid source molecular beam epitaxy (MBE) using the Stranski-Krastanow mode. Preliminary characterizations have been performed using photoluminescence and transmission electron microscopy. The geometrical arrangement of the quantum dots is found to be strongly dependent on the amount of coverage. At low deposition thickness. InAs QDs are arranged in chains along [1(1) over bar0$] directions. Luminescence from the quantum dots and the wetting layer consisting of quantum wells with well widths of 1, 2, and 3 monolayers is observed. (C) 1998 American Institute of Physics.

Characterization of strain relaxation in As ion implanted Si1-xGex epilayers grown by gas source molecular beam epitaxy

Strain relaxation in the As ion implanted Si0.57Ge0.43 epilayers was studied by double-crystal x-ray diffractometry and transmission electron microscopy, and was compared to that in the nonimplanted Si0.57Ge0.43 epilayers. Experimental results show that after rapid thermal annealing (RTA) the x-ray linewidth of the As+-implanted Si0.57Ge0.43 epilayers is narrower than that of the nonimplanted epilayers, and than that of the partially relaxed as-grown samples, which is due primarily to low density of misfit dislocations in the As+-implanted SiGe epilayers. RTA at higher than 950 degrees C results in the formation of misfit dislocations for the nonimplanted structures, and of combinations of dislocations and precipitates (tentatively identified as GeAs) for the As+-implanted epilayers. The results mean that the strain relaxation mechanism of the As+-implanted Si1-xGex epilayers may be different from that of the nonimplanted Si1-xGex epilayers. (C) 1998 American Institute of Physics.

Influence of rapid thermal annealing on the optical properties of gallium nitride grown by gas-source molecular-beam epitaxy

Raman scattering, photoluminescence (PL), and nuclear reaction analysis (MA) have been employed to investigate the effects of rapid thermal annealing (RTA) on GaN films grown on sapphire (0001) substrates by gas-source molecular-beam epitaxy, The Raman spectra showed the presence of the E-2 (high) mode of GaN and shift of this mode from 572 to 568 cm(-1) caused by annealing. The results showed that RTA has a significant effect on the strain relaxation caused by the lattice and thermal expansion misfit between the GaN epilayer and the substrate. The PL peak exhibited a blueshift in its energy position and a decrease in the full width at half maximum after annealing, indicating an improvement in the optical quality of the film. Furthermore, a green luminescence appeared after annealing and increased in intensity with increasing annealing time. This effect was attributed to H concentration variation in the GaN film, which was measured by NRA. A high H concentration exists in as-grown GaN, which can neutralize the deep level, and the H-bonded complex dissociates during RTA, This leads to the appearance of a luminescent peak in the PL spectrum. (C) 1998 American Institute of Physics.

Structural identification of a cubic phase in hexagonal GaN films grown on sapphire by gas-source molecular beam epitaxy

The structural characteristics of gallium nitride (GaN) films grown on sapphire(0001) substrates by gas source molecular beam epitaxy (GSMBE) have been investigated using high-resolution synchrotron irradiation X-ray diffraction and cathodoluminescence with a variable energy electron beam. Besides the well-known GaN hexagonal structure, a small portion of cubic phase GaN was observed. The X-ray measurements provide an essential means for the structural identification of the GaN layers. Arising from the variable penetration depth of the electron beam in the cathodoluminescence measurements, it was found that the fraction of the GaN cubic-phase typically increased as the probing depth was increased. The results suggest that the GaN cubic phase is mostly located near the interface between the substrate and GaN layer due to the initial nucleation.

Molecular beam epitaxy growth of Iny2Al1-y2As/In0.73Ga0.27As/Iny1Al1-y1As/InP P-HEMTs with enhancement conductivity using an intentional nonlattice-matched buffer layer

Pseudomorphic Iny2Al1-y2As/In0.73Ga0.27As/Iny1Al1-y1As (y1 greater than or equal to 0.52) modulation-doped heterostructures with an intentional nonlattice-matched buffer layer were successfully grown by molecular beam epitaxy on (100)InP substrates. Fourier transform photoluminescence and double crystal x-ray diffraction measurements show a superior crystalline quality in the high In content channel, when In mole fraction increases from y1=0.52 to 0.55 in the Iny1Al1-y1As buffer layer. In this case, an increasing of 16.3% and 23.5% for conductivity (mu xn(s)) and mobility, related to the strain compensation in the In0.73Ga0.27As channel, was achieved, respectively, comparing to the structure containing a well-lattice matched buffer layer. With increasing the mismatch further (y1=0.58), a morphology with cross-hatched pattern was observed due to the onset of a large amount of misfit dislocations, and the electronic characterization is not able to be improved continuously. Because we can realize high quality strained P-HEMTs in a relative wide range of equivalent beam flux (EBF) ratios, the stringent control over the constant EBF is not indispensable on this In-based material system. (C) 1997 American Vacuum Society.

1.3 mu m high indium content (42.5%) GaInNAs/GaAs quantum wells grown by molecular beam epitaxy

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum well (QW) samples with 42.5% indium content were successfully grown by molecular beam epitaxy. The growth of well layers was monitored by reflection high-energy electron diffraction (RHEED). Room temperature photoluminescence (PL) peak intensity of the GaIn0.425NAs/GaAs (6 nm / 20 nm) 3QW is higher than, and the full width at half maximum (FWHM) is comparable to, that of In0.425GaAs/GaAs 3QW, indicating improved optical quality due to strain compensation effects by introducing N to the high indium content InGaAs epilayer. The measured (004) X-ray rocking curve shows clear satellite peaks and Pendellosung fringes, suggesting high film uniformity and smooth interfaces. The cross sectional TEM measurements further reveal that there are no structural defects in such high indium content QWs. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Optical properties of inGaAs/GaAs quantum wells grown by Sb-assisted molecular beam epitaxy

It is found that both methods using either continuous Sb supply or pre-deposition of a very thin Sb layer are efficient for the Sb-assisted molecular beam epitaxy growth of highly strained InGaAs/GaAs quantum wells (QWs). The emission of QWs is extended to long wavelength close to 1.25 mu m with high luminescence efficiency at room temperature. The influence of rapid thermal annealing (RTA) on the photoluminescence intensity critically depends on the annealing temperature and duration for highly strained QWs. A relatively low RTA temperature of 700 degrees C with a short duration of 10 s is suggested for optimizing the annealing effect. (c) 2005 Elsevier B.V. All rights reserved.

High Characteristic Temperature 1.3 mu m InAs/GaAs Quantum-Dot Lasers Grown by Molecular Beam Epitaxy

We report the molecular beam epitaxy growth of 1.3 mu m InAs/GaAs quantum-dot (QD) lasers with high characteristic temperature T-0. The active region of the lasers consists of five-layer InAs QDs with p-type modulation doping. Devices with a stripe width of 4 mu m and a cavity length of 1200 mu m are fabricated and tested in the pulsed regime under different temperatures. It is found that T-0 of the QD lasers is as high as 532K in the temperature range from 10 degrees C to 60 degrees C. In addition, the aging test for the lasers under continuous wave operation at 100 degrees C for 72 h shows almost no degradation, indicating the high crystal quality of the devices.

Substrate temperature dependence of ZnTe epilayers grown on GaAs(001) by molecular beam epitaxy

ZnTe thin films have been grown on GaAs(0 0 1) substrates at different temperatures with constant Zn and Te beam equivalent pressures (BEPs) by molecular beam epitaxy (MBE). In situ reflection high-energy electron diffraction (RHEED) observation indicates that two-dimensional (2D) growth mode can be established after around one-minute three-dimensional (3D) nucleation by increasing the substrate temperature to 340 degrees C. We found that Zn desorption from the ZnTe surface is much greater than that of Te at higher temperatures, and estimated the Zn sticking coefficient by the evolution of growth rate. The Zn sticking coefficient decreases from 0.93 to 0.58 as the temperature is elevated from 320 to 400 degrees C. The ZnTe epilayer grown at 360 degrees C displays the narrowest full-width at half-maximum (FWHM) of 660 arcsec from (0 0 4) reflection in double-crystal X-ray rocking curve (DCXRC) measurements. The surface morphology of ZnTe epilayers is strongly dependent on the substrate temperature, and the root-mean-square (RMS) roughness diminishes drastically with the increase in temperature.

Optimization of VI/II pressure ratio in ZnTe growth on GaAs(001) by molecular beam epitaxy

ZnTe epilayers were grown on GaAs(0 0 1) substrates by molecular beam epitaxy (MBE) at different VI/II beam equivalent pressure (BEP) ratios (R-VI/II) in a wide range of 0.96-11 with constant Zn flux. Based on in situ reflection high-energy electron diffraction (RHEED) observation, two-dimensional (2D) growth mode can be formed by increasing the R-VI/II to 2.8. The Te/Zn pressure ratios lower than 4.0 correspond to Zn-rich growth state, while the ratios over 6.4 correspond to Te-rich one. The Zn sticking coefficient at various VI/II ratios are derived by the growth rate measurement. The ZnTe epilayer grown at a R-VI/II of 6.4 displays the narrowest full-width at half-maximum (FWHM) of double-crystal X-ray rocking curve (DCXRC) for (0 0 4) reflection. Atomic force microscopy (AFM) characterization shows that the grain size enlarges drastically with the R-VI/II. The surface root-mean-square (RMS) roughness decreases firstly, attains a minimum of 1.14 nm at a R-VI/II of 4.0 and then increases at higher ratios. It is suggested that the most suitable R-VI/II be controlled between 4.0 and 6.4 in order to grow high-quality ZnTe epitaxial thin films.

High resistance AlGaAs/GaAs quantum cascade detectors grown by solid source molecular beam epitaxy operating above liquid nitrogen temperature

This work was supported by the National Research Projects of China (grant numbers are 60525406, 60736031, 60806018, 60906026, 2006CB604903, 2007AA03Z446 and 2009AA03Z403, 10990100, respectively). The authors would like to thank P Liang, Y Hu, H Sun, X L Zhang, B J Sun, H L Zhen and N Li for their help in processing and characterization.

Molecular beam epitaxy of GaSb on GaAs substrates with AlSb/GaSb compound buffer layers

GaSb films with AlSb/GaSb compound buffer layers were grown by molecular beam epitaxy on GaAs (001) substrates. The crystal quality and optical properties were studied by high resolution transition electron microscopy and low temperature photoluminescence spectra (PL), respectively. It was found that the AlSb/GaSb compound buffer layers can restrict the dislocations into GaSb epilayers. The intensity of PL spectra of GaSb layer becomes large with the increasing the periods of AlSb/GaSb superlattices, indicating that the optical quality of GaSb films is improved.