Unselective regrowth of 1.5-mu m InGaAsP multiple-quantum-well distributed-feedback buried heterostructure lasers

Unselective regrowth for fabricating 1.5-mu m InGaAsP multiple-quantum well (MQW) distributed-feedback (DFB) buried heterostructure (BH) lasers is developed. The experimental results exhibit superior characteristics, such as a low threshold of 8.5 mA, high slope efficiency of 0.55 mW/mA, circular-like far-field patterns, the narrow line-width of 2.5 MHz, etc. The high performance of the devices effectively proves the feasibility of the new method to fabricate buried heterostructure lasers. (c) 2006 Society of Photo-Optical Instrumentation Engineers.

Thermal lensing effect in ridge structure InGaN multiple quantum well laser diodes

Time-resolved light-current curves, spectra, and far-field distributions of ridge structure InGaN multiple quantum well laser diodes grown on sapphire substrate are measured with a temporal resolution of 0.1 ns under a pulsed current condition. Results show that the thermal lensing effect clearly improves the confinement of the higher order modes. The thermal lens leads to a lower threshold current for the higher order modes, a higher slope efficiency, and a change in the lasing mode of the device. The threshold current for the higher modes decreases by about 5 mA in every 10 ns in a pulse, and the slope efficiency increases by 7.5 times on the average when higher modes lase. (c) 2006 American Institute of Physics.

Thermal stress analysis for GaInAsP multiple quantum well wafer chemically bonded to Si (100)

An n-InP-based InGaAsP multiple-quantum-well wafer was bonded with p-Si by chemical surface activated bonding at 70 degrees C, and then annealed at 450 degrees C. Different thermal expansion coefficients between InP and Si will induce thermal stresses in the bonded wafer. Planar and cross-sectional distributions of thermal stress in the bonded InP-Si pairs were analyzed by a two-dimensional finite element method. In addition, the normal, peeling, and shear stresses were calculated by an analytic method. Furthermore, x-ray double crystalline diffraction was applied to measure the thermal strain and the strain caused by the mismatching of the crystalline orientation between InP (100) and Si (100). The wavelength redshift of the photoluminescence (PL) spectrum due to thermal strain was investigated via the calculation of the band structure, which is in agreement with the measured PL spectra.

High-quality multiple quantum wells selectively grown on taper-patterned substrates by ultra-low-pressure MOCVD

High quality InGaAsP/InGaAsP multiple quantum wells ( MQWs) have been selectively grown by ultra-low-pressure (22 mbar) metal-organic chemical vapor deposition. A large bandgap energy shift of 46 nm and photoluminescence with FWHM less than 30 meV were obtained with a rather small mask width variation (15-30 mu m). In order to study the uniformity of the MQWs grown in the selective area, novel tapered masks were employed, and the transition effect W the tapered region was also studied. The energy detuning of the tapered region was observed to be saturated at larger ratios of the mask width to the tapered region length.

High-quality multiple quantum wells selectively grown with tapered masks by ultra-low-pressure MOCVD

An InGaAsP/InGaAsP multiple quantum wells (MQWs) selectively grown by ultra-low-pressure (22 mbar) metal-organic chemical vapor deposition was investigated in this article. A 46 nm photoluminescence peak wavelength shift was obtained with a small mask width variation (15-30 mu m). High-quality crystal layers with a photoluminescence (PL) ftill-width-at-half-maximum (FWHM) of less than 30 meV were achieved. Using novel tapered masks, the transition-effect of the tapered region was also studied. The energy detuning of the tapered region was observed to be saturated with the larger ratio of the mask width divided to the tapered region length. (C) 2005 Elsevier B.V. All rights reserved.

Fabrication of metallic air bridges using multiple-dose electron beam lithography

The techniques of fabricating metallic air bridges using different resists in a one-step electron beam lithography are presented. The exposure process employed a single-layer polymethyl methacrylate (PMMA) or photoresists with either different doses in the span and feet areas or with varying acceleration voltage of the electron beam. The process using photoresists with different doses has produced air bridges more stable than what the PMMA method using various acceleration voltages would achieve. Using this method, air bridges up to 12 mu m long have been fabricated. The length and height of these metallic air bridges vary with the photoresist thickness. (c) 2006 American Institute of Physics.

A 1.5 mu m n-type InGaAsP/InGaAsP modulation-doped multiple quantum well DFB laser by MOCVD

1.5 mu m n-type InGaAsP/InGaAsP modulation-doped multiple quantum well (MD-MQW) DFB lasers have been fabricated successfully by low pressure metal organic chemical vapour deposition (LP-MOCVD) technology. The experimental results indicate that n-type MD-MQWs can effectively reduce the threshold Current compared with conventional multiple quantum well DFB lasers. Theoretical analysis indicates that such an effect is due to the much smaller absorption loss and lower Auger recombination, compared with that in an undoped MQW structure. Moreover, the introduction of n-type dopant of suitable levels of concentration in the barrier layers enhances the dynamic characteristics of DFB lasers, due to a coupling between the adjacent quantum well layers and tunnelling-assisted injection, which can reduce the relatively long capture time and increase the effective differential gain 1/X dG/dn .

Influence of cracks generation on the structural and optical properties of GaN/Al0.55Ga0.45N multiple quantum wells

Both cracked and crack-free GaN/Al0.55Ga0.45N multiple quantum wells (MQWs) grown on GaN template by metalorganic chemical vapor deposition have been studied by triple-axis X-ray diffraction, grazing-incidence X-ray reflectivity, atomic force microscope, photoluminescence spectroscopy and low-energy positron annihilation spectroscopy. The experimental results show that cracks generation not only deteriorates the surface morphology, but also leads to a period dispersion and roughens the interfaces of MQWs. The mean density of dislocations in MQWs, determined from the average full-width at half-maximum of to-scan of each satellite peak, has been significantly enhanced by the cracks generation. Furthermore, the measurement of annihilation-line Doppler broadening reveals a higher concentration of negatively charged vacancies in the cracked MQWs. The combination of these vacancies and the high density of edge dislocations are assumed to contribute to the highly enhanced yellow luminescence in the cracked sample. (c) 2005 Elsevier B.V. All rights reserved.

Temperature dependence of photoluminescence of flat and undulated SiGe/Si multiple quantum wells

Photoluminescence (PL) of strained SiGe/Si multiple quantum wells (MQW) with flat and undulated SiGe well layers was studied at different temperature. With elevated temperature from 10K, the no-phonon (NP) peak of the SiGe layers in the flat sample has firstly a blue shift due to the dominant transition converting from bound excitons (BE) to free excitons (FE), and then has a red shift when the temperature is higher than 30K because of the narrowing of the band gap. In the undulated sample, however, monotonous blue shift was observed as the temperature was elevated from 10 K to 287 K. The thermally activated electrons, confined in Si due to type-II band alignment, leak into the SiGe crest regions, and the leakage is enhanced with the elevated temperature. It results in a blue shift of the SiGe luminescence spectra.

Anomalous temperature dependence of photoluminescence in GaInNAs/GaAs multiple quantum wells

Photoluminescence (PL) spectra of GaInNAs/GaAs multiple quantum wells grown on a GaAs substrate by molecular beam epitaxy are measured in a range of temperatures and excitation power densities. The energy position of the dominant PL peak shows an anomalous S-shape temperature dependence instead of the Varshni relation. By careful inspection, especially for the PL under lower excitation power density, two near bandedge peaks are well identified. These are assigned to carriers localized in nitrogen-induced bound states and interband excitonic recombinations, respectively. It is suggested that the temperature-induced switch of such two luminescence peaks in relative intensity causes a significant mechanism responsible for the S-shape shift observed in GaInNAs. A quantitative model based on the thermal depopulation of carriers is used to explain the temperature dependence of the PL peak related to N-induced bound states.

The mechanism of blueshift in excitation-intensity-dependent photo luminescence spectrum of nitride multiple quantum wells

(1 1 (2) over bar 0) GaN/InGaN multiple quantum wells (MQWs) were grown on (1 (2) over bar 0 2) sapphire by metal-organic vapor phase epitaxy. The excitation-intensity-dependent photoluminescence (PL) spectrum of these samples was measured, and no peak shift was observed. This phenomenon was attributed to the absence of piezoelectric field (PEF) along the growth orientation of the (1 1 (2) over bar 0) face MQWs. Our experimental results showed that PEF was the main reason causing peak blueshift in excitation-intensity-dependent PL spectrum of (0 0 0 1) InGaN/GaN NIQWs. It was expected that fabricating (1 1 (2) over bar 0) face nitride device should be a method to avoid PEF and get low-threshold, high-quantum-efficiency and stable-emission-wavelength light-emission devices. (C) 2002 Elsevier Science B.V. All rights reserved.

GaInNAs/GaAs multiple-quantum well resonant-cavity-enhanced photodetectors at 1.3 mu m

A GaInNAs/GaAs multiple quantum well (MQW) resonant-cavity enhanced photodetector (RCF-PD) operated at a wavelength of 1.3 mum with the full width at half maximum of 4nm has been demonstrated. The GaInNAs RCE - PD was grown by molecular beam epitaxy using a homemade ion-removed dc plasma cell as a nitrogen source. GaInNAs/GaAs MQW shows a strong exciton peak at room temperature, which is very beneficial for applications in long-wavelength absorption devices. For a 100 mum diameter RCE-PD, the dark current is 20 and 32 pA at biases of 0 and 6 V, respectively, and the breakdown voltage is - 18 V. The measured 3 dB bandwidth is 308 MHz, which is limited by the resistance of p-type distributed Bragg reflector mirror. The tunable wavelength in a range of 18 nm with the angle of incident light was observed.

Tunnel-regenerated multiple-active-region light-emitting diodes with high efficiency

Tunnel-regenerated multiple-active-region (TRMAR) light-emitting diodes (LEDs) with high quantum efficiency and high brightness have been proposed and fabricated. We have proved experimentally that the efficiency of the electrical luminescence and the on-axis luminous intensity of such TRMAR LEDs scaled linearly approximately with the number of the active regions. The on-axis luminous intensity of such TRMAR LEDs with only 3 mum GaP current spreading layer have exceeded 5 cd at 20 mA dc operation under 15 degrees package. The high-quantum-efficiency and high-brightness LEDs under the low injection level were realized. (C) 2001 American Institute of Physics.

Impurity-free vacancy diffusion technique for InGaAsP/InP multiple quantum well laser structure

Bandgap tuning of the InGaAsP/InP multiple quant um well (MQW) laser structure by the impurity-free vacancy diffusion (IFVD) is investigated using photoluminescence. It has been demonstrated that the effects of the plasma bombardment to the:sample surface involved in the IFVD technique can enhance the intermixing of the InGaAsP/InP MQW laser structure. The reliability of the IFVD technique, particularly the effects of the surface decomposition and the intrinsic defects formed in the growth or preparation of the wafer, has been discussed.

Back-incident SiGe-Si multiple quantum-well resonant-cavity-enhanced photodetectors for 1.3-mu m operation

A back-incident Si-0.65 Ge-0.35/Si multiple quantum-well resonant-cavity-enhanced photodetector operating near 1.3 mum is demonstrated on a separation-by-implantation-oxygen substrate. The resonant cavity is composed of an electron-beam evaporated SiO2-Si distributed Bragg reflector as a top mirror and the interface between the buried SiO2 and the Si substrate as a bottom mirror. We have obtained the responsivity as high as 31 mA/WI at 1.305 mum and the full width at half maximum of 14 nm.