INTERACTION OF CO WITH SI AND SIO2 DURING RAPID THERMAL ANNEALING

The interaction of Co with Si and SiO2 during rapid thermal annealing has been investigated. Phase sequence, layer morphology, and reaction kinetics were studied by sheet resistance, x-ray diffraction, Auger electron spectroscopy, x-ray photoelectron spectroscopy, and scanning electron microscopy. With increasing annealing temperature, Co film on Si(100) is transformed sequentially into Co2Si, CoSi, and finally CoSi2 which corresponds to the minimum of sheet resistance. No evidence of silicide formation was observed for Co/SiO2 annealed even at the high temperature of 1050-degrees-C.

PHOTOEMISSION-STUDY OF THE INTERFACIAL FORMATION PROCESS AND REACTIONS BETWEEN AL AND HYDROGENATED AMORPHOUS SI

Using photoemission spectroscopy and Auger electron spectroscopy, the interfacial formation process and the reactions between Al and hydrogenated amorphous Si are probed, and annealing behaviors of the Al/a-Si:H system are investigated as well. It is found that a three-dimensional growth of Al metal clusters which includes reacted Al and non-reacted metal Al occurs at the initial Al deposition time, reacted Al and Si alloyed layers exist in the Al/a-Si:H interface, and non-reacted Al makes layer-by-layer growth forming a metal Al layer on the sample surface. The interfacial reactions and element interdiffusion of Al/a-Si:H are promoted under the vacuum annealing.

CONVERGENT-BEAM ELECTRON-DIFFRACTION STUDY OF GE0.5SI0.5/SI STRAINED-LAYER SUPERLATTICES GROWN BY MOLECULAR-BEAM EPITAXY

Side bands due to purely composition and combined composition-strain modulation in plan-view specimens of a nominally Ge0.5Si0.5(5nm)/Si(25nm) superlattice have been obtained by large-angle convergent-beam electron diffraction. The intensities of the side bands have been calculated from a periodic tension-compression model of the superlattice bilayer using the kinematical theory of electron diffraction. Accurate values of elastic strains in the bilayer and of the Ge content can be obtained in this way.

IDENTIFICATION OF THE ENERGY-LEVELS OF SI-RH

Two thermostable levels E(0.31) and E(0.58) related to Rh in Si were observed using deep level transient spectroscopy and double correlation deep level transient spectroscopy techniques. By means of thermal annealing and electron irradiation, the microscopic natures of these levels were identified for the first time. The levels E(0.31) and E(0.58) arise from by the same impurity center but have different charge states. Their microstructures are not related to a pure substitutional Rh atom, but correspond to a complex. This result is compared to our self-consistent theoretical calculation.