InAs self-assembled quantum dots grown on an InP (311)B substrate by molecular beam epitaxy

Self-assembled InAs quantum dots (QDs) have been grown by solid-source molecular beam epitaxy on a (311)B InP substrate. Transmission electron microscopy clearly shows that a high density of smaller InAs islands can be obtained by using such a high index substrate. After introducing a lattice-matched underlying In0.52Al0.24Ga0.24As layer, the InAs QDs are much more uniform in size and form two-dimensional well ordered arrays. The photoluminescence (PL) spectra also confirm that the InAs QDs grown on underlying In0.52Al0.24Ga0.24As have a better quality than those grown in the In0.52Al0.48As matrix. A simple calculation indicates that the redshift of the PL peak energy mainly results from InAs QDs on underlying In0.52Al0.24Ga0.24As of large size. (C) 2001 American Institute of Physics.

Structural anisotropy and optical properties of InxGa1-xAs quantum dots on GaAs(001)

InAs and InxGa1-xAs (x = 0.2 and 0.5) self-organized quantum dots (QDs) were fabricated on GaAs(0 0 1) by molecular beam epitaxy (MBE) and characterized by atomic force microscopy (AFM), transmission electron microscopy (TEM), acid photoluminescence polarization spectrum (PLP). Both structural and optical properties of InxGa1-xAs QD layer are apparently different from those of InAs QD layer. AFM shows that InxGa1-xAs QDs tend to be aligned along the [1 (1) over bar 0] direction, while InAs QDs are distributed randomly. TEM demonstrates that there is strain modulation along [1 1 0] in the InxGa1-xAs QD layers. PLP shows that In0.5Ga0.5As islands present optical anisotropy along [1 1 0] and [1 (1) over bar 0] due to structural and strain field anisotropy for the islands. (C) 2001 Elsevier Science B.V. All rights reserved.

X-ray evidence for Ge/Si(001) island columns in multilayer structure

A Ge/Si(0 0 1) multilayer structure is investigated by cross-sectional transmission electron microscopy, atomic force microscopy and double crystal X-lay diffraction. We find that the multilayer-structure-related satellite peaks in the rocking curve exhibit a similar nonuniform broadening and rye fit the zero-order peak with two Lorentz lineshapes. The ratio of the integrated intensity of two peaks is approximately equal with the anal ratio of the top Ge layer deposited between the areas that are and are not occupied by islands. It proves the existence of vertical-aligned island columns from the viewpoint of macroscopic dimension. (C) 2001 Elsevier Science B.V. All rights reserved.

Strain-compensated quantum cascade lasers operating at room temperature

Quantum cascade (QC) lasers based on strain-compensated InxGa(1-x)As/InyAl(1-y)As grown on InP substrate using molecular beam epitaxy is reported. The epitaxial quality is demonstrated by the abundant narrow satellite peaks of double-crystal X-ray diffraction and cross-section transmission electron microscopy of the QC laser wafer. Laser action in quasi-continuous wave operation is achieved at lambda approximate to 3.6-3.7 mum at room temperature (34 degreesC) for 20 mum x 1.6 mm devices, with peak output powers of similar to 10.6mW and threshold current density of 2.7kA/cm(2) at this temperature. (C) 2000 Published by Elsevier Science B.V.

High-performance strain-compensated InGaAs/InAlAs quantum cascade lasers

We report on the realization of quantum cascade (QC) lasers based on strain-compensated InxGa(1-x)As/In(y)A((1-y))As grown on InP substrates using molecular beam epitaxy. X-ray diffraction and cross section transmission electron microscopy have been used to ascertain the quality of the QC laser materials. Quasi-continuous wave lasing at lambda approximate to 3.54-3.7 mum at room temperature was achieved. For a laser with 1.6 mm cavity length and 20 mum ridge-waveguide width,quasi-continuous wave lasing at 34 degreesC persists for more than 30 min, with a maximum power of 11.4 mW and threshold current density of 1.2 kA cm(-2), both record values for QC lasers of comparable wavelength.

Study of self-assembled InAs quantum dot structure covered by InxGa1-xAs(0 <= x <= 0.3) capping layer

InAs self-assembled quantum dots(QDs) covered by 3-nm-thick InxGa1-xAs(0 less than or equal tox less than or equal to0.3) capping layer have been grown on GaAs(100) substrate. Transmission electron microscopy shows that InGaAs layer reduces the strain in the InAs islands,and atomic force microscopy evidences the deposition of InGaAs on the top of InAs islands when x = 0.3.The significant redshift of the photoluminescence (PL) peak energy and the reduction of PL linewidth of InAs quantum dots covered by InGaAs are observed. In addition,InGaAs overgrowth layer suppresses the temperature sensitivity of PL peak energy. Based on our analysis, the strain-reduction and the size distribution of the InAs QDs are the main cause of the redshift and temperature insensitivity of the PL respectively.

Oblique alignment of columns of self-organized Ge/Si(001) islands in multilayer structure

Ge/Si multilayer structures with a bimodal distribution of the island spacing in the first layer have been investigated by atomic-force microscopy and transmission electron microscopy. Besides the vertical alignment, some oblique alignments of stacked islands are observed. The presence of the elastic interaction between islands is responsible for the oblique alignment of stacked islands. (C) 2000 American Institute of Physics. [S0003-6951(00)04644-1].

Formation of InAs quantum dots on low-temperature GaAs epi-layer

InAs self-organized quantum dots (QDs) grown on annealed low-temperature GaAs (LT-GaAs) epi-layers and on normal temperature GaAs buffer layers have been compared by transmission electron microscopy (TEM) and photoluminescence (PL) measurements. TEM evidences that self-organized QDs were formed with a smaller size and larger density than that on normal GaAs buffer layers. It is discussed that local tensile surface strain regions that are preferred sites for InAs islands nucleation are increased in the case of the LT-GaAs buffer layers due to exhibiting As precipitates. The PL spectra show a blue-shifted peak energy with narrower linewidth revealing the improvement of optical properties of the QDs grown on LT-GaAs epi-layers. It suggests us a new way to improve the uniformity and change the energy band structure of the InAs self-organized QDs by carefully controlling the surface stress states of the LT-GaAs buffers on which the QDs are formed. (C) 2000 Elsevier Science B.V. All rights reserved.

Room temperature 1.55 mu m emission from InAs quantum dots grown on (001)InP substrate by molecular beam epitaxy

Self-assembled InAs nanostructures on (0 0 1)InP substrate have been grown by molecular beam epitaxy (MBE) and evaluated by transmission electron microscopy (TEM) and photoluminescence (PL). It is found that the morphologies of InAs nanostructures depend strongly on the underlying alloy. Through introducing a lattice-matched underlying InAlGaAs layer on InAlAs buffer layer, the InAs quantum dots (QDs) can be much more uniform in size and great improvement in PL properties can be attained at the same time. In particular, 1.55 mu m luminescence at room temperature (RT) can be realized in InAs QDs deposited on (0 0 1)InP substrate with underlying InAlGaAs layer. (C) 2000 Published by Elsevier Science B.V. All rights reserved.

Influence of InxGa1-xAs (0 <= x <= 0.3) cap layer on structural and optical properties of self-assembled InAs/GaAs quantum dots

Optical and structural properties of self-organized InAs/GaAs quantum dots (QDs) with InxGa1-xAs or GaAs cover layers grown by molecular beam epitaxy (MBE) have been characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM) and photoluminescence (PL) measurements. The TEM and AFM images show that the surface stress of the InAs QDs was suppressed by overgrowth of a InxGa1-xAs covering layer on the top of the QDs and the uniformity of the QDs preserved. PL measurements reveal that red shifts of the PL emission due to the reduction of the surface strain of the InAs islands was observed and the temperature sensitivity of the PL emission energy was suppressed by overgrowth of InxGa1-xAs layers compared to that by overgrowth of GaAs layers.

Structural and optical properties of self-assembled InAs/GaAs quantum dots covered by InxGa1-xAs (0 <= x <= 0.3)

Optical and structural investigations of InAs quantum dots (QDs) covered by InxGa1-xAs (0 less than or equal to x less than or equal to 0.3) overgrowth layer have been systematically reported. The decrease of strain in the growth direction of InAs quantum dots covered by InGaAs layer instead of GaAs is demonstrated by transmission electron microscopy experiments. In addition, the atomic force microscopy measurement shows that the surface of InAs islands with 3-nm-thick In0.2Ga0.8As becomes flatter. However, the InGaAs islands nucleate on the top of quantum dots during the process of InAs islands covered with In0.3Ga0.7As. The significant redshift of the photoluminescence peak energy and reduction of photoluminescence linewidth of InAs quantum dots covered by InGaAs are observed. The energy gap change of InAs QDs covered by InGaAs could be explained in terms of reducing strain, suppressing compositional mixing, and increasing island height. (C) 2000 American Institute of Physics. [S0021-8979(00)04018-4].

Optical properties of self-assembled ternary In(GA/Al)As quantum dots on (100) and (N 1 1)B InP substrates

In this paper, we investigated the self-assembled quantum dots formed on (100) and (N11)B (N = 2, 3, 4, 5) InP substrates by molecular beam epitaxy (MBE). Two kinds of ternary QDs (In0.9Ga0.1As and In0.9Al0.1As QDs) are grown on the above substrates; Transmission electron microscopy (TEM) and photoluminescence (PL) results confirm QDs formation for all samples. The PL spectra reveal obvious differences in integral luminescence, peak position, full-width at half-maximum and peak shape between different oriented surfaces. Highest PL integral intensity is observed from QDs on (411)B surfaces, which shows a potential for improving the optical properties of QDs by using high-index surface. (C) 2000 Elsevier Science B.V. All rights reserved.

Study of self-assembled InAs quantum dots grown on low temperature GaAs epi-layer

InAs self-organized quantum dots (QDs) grown on annealed low temperature GaAs (LT-GaAs) epi-layer were investigated by transmission electron microscopy (TEM) and photoluminescence (PL) measurement. TEM showed that QDs formed on annealed LT-GaAs epi-layer have a smaller size and a higher density than QDs formed on normal GaAs buffer layer. In addition, the PL spectra analysis showed that the LT-GaAs epi-layer resulted in a blue shift in peak energy, and a narrower linewidth in the PL peak. The differences were attributed to the point defects and As precipitates in annealed LT-GaAs epi-layer for the point defects and As precipitates change the strain field of the surface. The results provide a method to improve the uniformity and change the energy band structure of the QDs by controlling the defects in the LT-GaAs epi-layer.

Structural and photoluminescence properties of In-0.9(Ga/Al)(0.1)As self-assembled quantum dots on InP substrate

Self-assembled In0.9Ga0.1As, In0.9Al0.1As, and InAs quantum dots (QD) were fabricated in an InAlAs matrix lattice-matched to an InP substrate by molecular beam epitaxy. Preliminary characterizations were performed using transmission electron microscopy, photoluminescence, and reflection high-energy electron diffraction. Experimental results reveal clear differences in QD formation, size distribution, and luminescence between the InAs and In-0.9(Ga/Al)(0.1)As samples, which show the potential of introducing ternary compositions to adjust the structural and optical properties of QDs on an InP substrate. (C) 2000 American Institute of Physics. [S0021-8979(00)10213-0].

Tentative analysis of Swirl defects in silicon crystals

Swirl defects in dislocation-free Czochralski (CZ) silicon crystals have been investigated by preferential etching, transmission electron microscopy (TER I) and electron energy loss spectroscopy (EELS) mode of a scanning transmission electron microscope (STEM). Two kinds of Swirl defects have been found with a good correspondence between striated pattern consisting of hillocks and the buried micro-defects. The Swirl defects were identified as perfect dislocation loop cluster and tetrahedral precipitate, respectively. In addition, a kind of tiny micro-defects is found to be distributed preferentially in the vicinity of the Swirl pattern although there is no detectable correspondence between hillocks and the micro-defects. The energy-filtered images have been obtained by the plasma peaks at different parts of a coherent precipitate with the Si matrix. The experimental results show some indications of the existence of oxygen and carbon in the core of the precipitate and suggest that oxygen and carbon may play important roles in the formation of Swirl defect. (C) 2000 Elsevier Science B.V. All rights reserved.