Annealing effects of sapphire substrate on properties of ZnO films grown by magnetron sputtering

The annealing effects of sapphire substrates on the quality of epitaxial ZnO films grown by dc reactive magnetron sputtering were studied. The atomic steps formed on (0001) sapphire (alpha-Al2O3) substrates surface by annealing at high temperature were analyzed by atomic force microscopy. Their influence on the growth of ZnO films was examined by X-ray diffraction and photoluminescence measurements. Experimental results indicate that the film quality is strongly affected by annealing treatment of the sapphire substrate surface. The optimum annealing temperature of sapphire substrates for ZnO grown by magnetron sputtering is 1400 degrees C for 1 h in air.

Nonpolar a-plane ZnO films fabricated on (302)gamma-LiAlO2 by pulsed laser deposition

Nonpolar a-plane (1 1 2 0) ZnO films are fabricated on (3 0 2)gamma-LiAlO2 substrate by pulsed laser deposition. When substrate temperature is low, c-plane ZnO is dominant. As growth temperature increases to similar to 500 degrees C, pure (1 1 2 0)-oriented ZnO film can be obtained. The X-ray rocking curve of a-plane ZnO film broadens sharply when growth temperature is up to similar to 650 degrees C; such a broadening may be related to the anisotropic lateral growth rate of (1 12 0)-oriented ZnO grains. Atomic force microscopy reveals the surface morphology changes of ZnO films deposited at different temperatures. Raman spectra reveal that a compressive stress exists in the a-plane ZnO film. (C) 2007 Published by Elsevier B.V.

Homoepitaxial growth of ZnO films via low-temperature liquid-phase epitaxy

Homoepitaxial ZnO films have been grown via liquid-phase epitaxy (LPE) on (000 1) oriented ZnO substrates. X-ray rocking curve revealed the high quality of the ZnO films with a FWHM of 40 arc sec. Films of thickness about 20 gm were gown in the temperature range 700-720 degrees C. The growth rate of ZnO films was estimated to be 0.3 mu m h(-1). Atomic force microscope analysis showed that the surface roughness of ZnO films was very low, which further confirmed the high crystallinity of ZnO films. (c) 2006 Elsevier B.V. All rights reserved.

Defects in LPE-grown beta-barium borate (beta-BaB2O4) thin films

Morphological defects in beta-barium borate (beta-BBO) thin films grown on Sr2+ -doped alpha-BBO substrates by liquid phase epitaxy (LPE) technique were studied by scanning electron micrograph (SEM), atomic force microscopy (AFM) and optical spectroscopy. The present results indicate that the main defects exit in beta-BBO thin films are microcracks and hollow structure. The formation of microcrack is due to the lattice mismatch and the difference of thermal expansion coefficients between substrate and film. The hollow structure might be caused during the combination of islands, which formed in the initial stage. (C) 2006 Elsevier GmbH. All rights reserved.

Growth and characterization of ZnO films on (0 0 1), (1 0 0) and (0 1 0) LiGaO2 substrates

ZnO films were fabricated on LiGaO2 (0 0 1), (10 0) and (0 10) planes by RF magnetron sputtering. The structural, morphological and optical properties of as-grown ZnO films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), Raman spectra and photoluminescence (PL) spectra. It is found that the orientation of ZnO films is strongly dependent on the substrate plane. [0 0 0 11, [1 (1) over bar 00] and [11 (2) over bar0] oriented ZnO films are deposited on LiGaO2 (001), (100) and (010), respectively. AFM shows the (0001) ZnO film consists of well-aligned regular hexagonal grains. Raman spectra reveal a tensile stress in the (0 0 0 1) ZnO film and a compressive stress in (110 0) and (112 0) ZnO films. PL spectra of all ZnO films exhibit only a near-band-edge UV emission peak. (C) 2008 Elsevier B.V. All rights reserved.

Structural and optical properties of a-plane ZnO thin films synthesized on γ-LiAlO2 (302) substrates by low pressure metal-organic chemical vapor deposition

Nonpolar a-plane (1120) ZnO thin films have been fabricated on gamma-LiAlO2 (302) substrates via the low-pressure metal-organic chemical vapor deposition. An obvious intensity variation of the E-2 mode in the Raman spectra indicates that there exhibits in-plane optical anisotropy in the a-plane ZnO thin films. Highly-oriented uniform grains of rectangular shape can be seen from the atomic force microscopy images, which mean that the lateral growth rate of the thin films is also anisotropic. It is demonstrated experimentally that a buffer layer deposited at a low temperature (200 degrees C) can improve the structural and optical properties of the epilayer to a large extent. (c) 2007 Elsevier B.V. All rights reserved.

Low temperature growth of c-axis oriented AlN films on gamma-LiAlO2 by radio frequency magnetron sputtering

Aluminum nitride (AlN) films were prepared on gamma-LiAlO2 substrates by radio frequency (rf) magnetron sputtering. The influence of substrate temperature (T-s) and nitrogen (N-2) concentration on film growth was investigated. The X-ray diffraction (XRD) results reveal that highly c-axis oriented AlN films can be obtained in the temperature range from room temperature (RT) to 300 degrees C. A smoother surface and a crystalline quality decrease with increasing N-2 concentration have been observed by XRD and atomic force microscopy (AFM) for the films deposited at lower substrate temperature. On the contrary, the degradation of the surface smoothness and the higher crystalline quality can be observed for the films deposited at a higher substrate temperature with N-2-rich ambient. The growth mechanism which leads to different crystalline quality of the films is discussed. (C) 2008 Elsevier B.V. All rights reserved.

Electrical transport in metallic films

On the basis of the Boltzmann equation, the authors propose a model that includes scattering from both film surfaces and grain boundaries, and have studied the quasiclassical electrical transport in metallic films. The in-plane electric conductivity of metallic films is obtained, and the theoretical results are shown to be in good agreement with experimental data. We also give the relation between temperature coefficient of resistivity and thickness of metallic films and make a comparison with experiment. <(C)> 2004 American Institute of Physics.

Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

ZrO2, films were deposited by electron-beam evaporation with the oxygen partial pressure varying from 3 X 10(-3) Pa to I I X 10(-3) Pa. The phase structure of the samples was characterized by x-ray diffraction (XRD). The thermal absorption of the films was measured by the surface thermal lensing technique. A spectrophotometer was employed to measure the refractive indices of the samples. The laser-induced damage threshold (LIDT) was assessed using a 1064, nm Nd: yttritium-aluminium-garnet pulsed laser at pulse width of 12 ns. The influence of oxygen partial pressure on the microstructure and LIDT of ZrO2 films was investigated. XRD data revealed that the films changed from polycrystalline to amorphous as the oxygen partial pressure increased. The variation of refractive index at 550 nm wavelength indicated that the packing density of the films decreased gradually with increasing oxygen partial pressure. The absorptance of the samples decreased monotonically from 125.2 to 84.5 ppm with increasing oxygen partial pressure. The damage threshold, values increased from 18.5 to 26.7 J/cm(2) for oxygen partial pressures varying from 3 X 10(-3) Pa to 9 X 10(-3) Pa, but decreased to 17.3 J/cm(2) in the case of I I X 10(-3) Pa. (C) 2005 American Vacuum Society.

A New theory for evaluating the number density of inclusions in films

A new formulation derived from thermal characters of inclusions and host films for estimating laser induced damage threshold has been deduced. This formulation is applicable for dielectric films when they are irradiated by laser beam with pulse width longer than tens picoseconds. This formulation can interpret the relationship between pulse-width and damage threshold energy density of laser pulse obtained experimentally. Using this formulation, we can analyze which kind of inclusion is the most harmful inclusion. Combining it with fractal distribution of inclusions, we have obtained an equation which describes relationship between number density of inclusions and damage probability. Using this equation, according to damage probability and corresponding laser energy density, we can evaluate the number density and distribution in size dimension of the most harmful inclusions. (c) 2005 Elsevier B.V. All rights reserved.